Adsorption of chromium from aqueous solution by activated alumina and activated charcoal

Cr(VI) is considered to be potentially carcinogenic to humans. Removal of Cr(VI) ions from aqueous solution under different conditions was investigated using activated alumina (AA) and activated charcoal (AC) as adsorbents. Batch mode experiments were conducted to study the effects of adsorbent dose, contact time, pH, temperature and initial concentration of Cr(VI). Results showed that the adsorption of Cr(VI) depended significantly on pH and temperature. Equilibrium studies showed that Cr(VI) had a high affinity for AA at pH 4 and AC at pH 2. For AA, maximum adsorption was found at 25 degrees C, indicating exothermic adsorption, while for AC, maximum adsorption was at 40 degrees C. Freundlich and Langmuir adsorption isotherms were also applied and they showed good fits to the experimental data. The results suggest that both AA and AC could be used as effective adsorbents for the removal of Cr(VI) ions.     

Sorption of Cr(III) onto chelating b-DAEG-sporopollenin and CEP-sporopollenin resins

In the present study, the removal of Cr(III) from aqueous solution was studied using a new chelate-resins (b-DAEG-sporopollenin and CEP-sporopollenin). Mechanisms including ion exchange, complexation and adsorption to the surface are possible in the sorption process. Adsorption analysis results obtained at various concentrations of Cr(III) showed that the adsorption pattern on the resin followed a Langmuir isotherm. Langmuir constant Gamma max and k for Cr(III) were found as 1.23, 84.84 mmol/g for b-DAEG-sporopollenin, 133.33, 10.39 mmol/g for CEP-sporopollenin at 20 +/- 1 degrees C, respectively. In addition, kinetic and thermodynamic parameters such as enthalpy (DeltaH0), free energy (DeltaG0) and entropy (DeltaS0) were calculated and these values show that adsorption of Cr(III) on b-DAEG-sporopollenin and CEP-sporopollenin was an exothermic process and the process of adsorption was favored at high temperatures. Maximum Cr(III) removal was observed near a pH of 6.     

Biosorption of Lead from Industrial Wastewater Using Chrysophyllum albidum Seed Shell

The shell of the seed of Chrysophyllum albidum carbon was used to adsorb lead (Pb) from aqueous solution, the sorption process with respect to its equilibria and kinetics as well as the effects of pH, contact time, adsorbent mass, adsorbate concentration, and particle size on adsorption were also studied. The most effective pH range was found to be between 4.5 and 5 for the sorption of the metal ion. The first-order rate equation by Lagergren was tested on the kinetic data and the adsorption process followed first-order rate kinetics. Isotherm data were analyzed for possible agreement with the Langmuir and Freundlich adsorption isotherms; the Freundlich and Langmuir models for dynamics of metal ion uptake proposed in this work fitted the experimental data reasonably well. However, equilibrium sorption data were better represented by Langmuir model than Freundlich. The adsorption capacity calculated from Langmuir isotherm was 72.1 mg Pb (II) g^{- 1} at initial pH of 5.0 at 30°C for the particle size of 1.00 to 1.25 mm with the use of 2.0 g/100 ml adsorbent mass. The structural features of the adsorbent were characterized by Fourier transform infrared (FTIR) spectrometry; the presence of hydroxyl, carbonyl, amide, and phosphate groups confirms the potential mechanism adsorption of the adsorbent. This readily available adsorbent is efficient in the uptake of Pb (II) ion in aqueous solution, thus, it could be an excellent alternative for the removal of heavy metals and organic matter from water and wastewater.     

Preparation and Characterization of Chemically Modified Silk Cotton Hull Activated Carbon and Its Effects on Cd(II) Removal from Aqueous Solutions

The novel biosorbent silk cotton hull, an agrowaste material, has been successfully utilized for the removal of cadmium(II) from aqueous solutions. The adsorption of cadmium onto three kinds of activated biosorbent has been studied: modified by concentrated sulfuric acid alone (AC), a mixture of concentrated sulfuric acid and hydrogen peroxide (AC1), and a mixture of concentrated sulfuric acid and ammonium persulfate (AC2). The adsorption studies were carried out to optimize the process parameters such as pH, adsorbent dosage, contact time, and initial metal ion concentration. Maximum metal removal was observed at pH 7.0 with a contact time of 90 min at stirring speed of 200 rpm with an adsorbent dosage of 4.0 g L^?1. The sorption isotherms were studied using the Langmuir, Freundlich, and Tempkin isotherm models. The maximum adsorption capacities were 100.00, 142.86, and 142.87 mg g^?1 for AC, AC1, and AC2, respectively. Accordingly, the surface modification of the activated carbons AC1 and AC2 enhanced cadmium removal greatly. The experiments demonstrated that the removal of metal ions followed the pseudo-second-order kinetic model. The sorption mechanism is discussed in terms of the activated surface properties. A relationship between the oxygen content and sorption was found in this novel material. Desorption experiments were carried out using hydrochloric acid with a view to generate the spent adsorbent and to recover the adsorbed metal ions.     

Biosorption of Cr (VI) from aqueous solution by Rhizopus nigricans

The study was aimed to quantify the Cr sorption ability of powdered biomass of Rhizopus nigricans at the best operating conditions. The influence of solution pH, agitation, Cr (VI) concentration, biomass dosage, contact time, biomass particle size and temperature were studied. The optimum pH for biosorption of Cr (VI) was found to be 2.0. Higher adsorption percentage was noted at lower initial concentrations of Cr ions, while the adsorption capacity of the biomass increased with increasing concentration of ions. Optimum biomass dosage was observed as 0.5% (w/v). More than 75% of the ions were removed within 30 min of contact and maximum removal was obtained after 8 h. Biomass particles of smaller size (90 microm) gave maximum adsorption (99.2%) at 100 mg/l concentration. The adsorption capacity increased with increase in temperature and agitation speed and the optimum were determined as 45 degrees C at 120 rpm. Freundlich and Langmuir isotherms were used to evaluate the data and the regression constants were derived. The adsorption rate constant values (Kad) were calculated for different initial concentration of Cr ions and the sorption was found to be higher at lower concentration (100 mg/l) of metal ion.     

Batch removal of chromium(VI) from aqueous solution by Turkish brown coals

The ability of using low-rank Turkish brown coals (Ilgın: BC₁, Beyşehir: BC₂, and Ermenek: BC₃) to remove Cr(VI) from aqueous solutions was studied as a function of contact time, solution pH, temperature, concentration of metal solutions and amount of adsorbent. Their sorption properties were compared with the activated carbon from Chemviron (AQ-30). Adsorption of Cr(VI) uptake is in all cases pH-dependent showing a maximum at equilibrium pH values between 2.0 and 3.2, depending on the biomaterial, that correspond to initial pH values of 2.3 units for BC₁, 3.0 units for BC₂ and 3.2 units for BC₃ and AQ-30. Batch equilibrium tests showed that the Cr(VI) removal was fitted with Freundlich isotherm and the adsorption reached equilibrium in 80 min. It was proceeding effectively into a short acid pH interval (2.0–3.2) where processes of Cr(VI) sorption are maximized. It was observed that the maximum adsorption capacity of 11.2 mM of Cr(VI)/g for Ilgın (BC₁), 12.4 mM of Cr(VI)/g for Beyşehir (BC₂), 7.4 mM of Cr(VI)/g for Ermenek (BC₃) and 6.8 mM of Cr(VI)/g for activated carbon (AQ-30) was achieved at pH of 3.0. The rise in temperature caused a slight decrease in the value of the equilibrium constant (K_c) for the sorption of Cr(VI) ion. The Cr(VI) sorption capacities of Beyşehir and Ilgın brown coals were the same. Ermenek brown coals and activated carbon (AQ-30) showed a similar sorption capacity.     

Effect of organic Cr(III) complexes on chromium speciation

Abstract

Chromium speciation in the presence of organic chromium(III) complexes was investigated using solid-phase extraction. The adsorptions of Cr(VI) and Cr(III) on alumina and pumice powder were studied. Maximum sorption of Cr(VI) was obtained by alumina (90.22%), while Cr(III) was highly adsorbed onto pumice powder (86.65%). This result shows that pumice may be a new and promising adsorbent for Cr(III). The experimental equilibrium data for Cr(VI) adsorption onto alumina and Cr(III) sorption onto pumice were analysed using Langmuir and Freundlich isotherms. The separation and adsorption of Cr(VI), Cr(III) and five organic chromium(III) complexes onto pumice and alumina at different pH values were evaluated. Ethylenediaminetetraacetate (EDTA), oxalate, citrate, glycine, alanine and 8-hydroxyqinoline were used as ligands. Sorption of alanine and ethylenediaminetetraacetate complexes was higher onto alumina than pumice at pH>3. The enhancement of adsorption of chromium(III) complexes onto pumice was achieved by surface modification of pumice using a surfactant, namely hexadecyltrimethylammoniumbromür (HDTMA). The presence of surfactant enhanced the adsorption of Cr(III) citrate, oxalate, glycine and 8-hydroxyquinoline complexes onto pumice. However, the adsorption of EDTA and alanine complexes decreased, with ratio of 13.40% and 4.00% respectively. Here we demonstrate that chromium speciation methods depending on adsorption onto various adsorbents including alumina may lead erroneous results. Analytical measurements were performed by flame AAS, data were obtained by standard addition method.     

Adsorption of chromium from aqueous solution on treated sawdust

The adsorption of Cr(VI) from aqueous solutions on formaldehyde treated sawdust (SD) and sulphuric acid treated sawdust carbon (SDC) of Indian Rosewood, a timber industry waste, was studied at varying Cr(VI) concentrations, adsorbent dose, pH and agitation time. Similar experiments were conducted with commercially available coconut based activated carbon to compare the results. The Cr(VI) adsorption efficiency on SDC was higher than SD. The adsorption followed first order rate expression and Lagergren equation. An initial pH of 3.0 was most favorable for Cr(VI) removal by both the adsorbents. Maximum Cr(VI) was sequestered from the solution within 60 min after the beginning for every experiment. It is proposed that SDC and SD can be potential adsorbents for Cr(VI) removal from dilute solutions.     

Two metal biosorption of chromium and copper by Ca-loaded Laminaria japonica biomass

Cu and Cr sorption capacities of Ca-loaded Laminaria japonica biomass were studied using an equilibrium methodology and evaluation of the sorption performance, and modeling in a two-metal system was carried out with a modified multi-component Langmuir isotherm. The maximum Cu and Cr uptakes calculated from the Langmuir isotherm were 1.59 mmol/g (10.1 wt.%) and 1.81 mmol/g (9.4 wt.%) at pH 4.5, respectively. The desorption efficiency of the Cr-sorbed L. japonica was approximately 5% for 8 h in the 0.1 N HNO₃ solution, while that of Cu-sorbed L. japonica was more than 99% in the 0.1 N HNO₃ solution. The modified Langmuir model gave the following affinity correlated coefficients: 1.12 for Cu and 7.31 for Cr at pH 4.5. The interference of Cr with Cu biosorptive uptake was assessed by ‘cutting’ the three dimensional uptake isotherm surfaces at constant second-metal final concentrations. Equimolar final equilibrium concentrations of Cu and Cr of 1 mM at pH 4.5 reduced Cu and Cr uptakes by 75.5 and 11.0%, respectively.     

Equilibrium isotherm studies for the uptake of cadmium and lead ions onto sugar beet pulp

The adsorption of Cd2+ and Pb2+ on sugar beet pulp (SBP), a low-cost material, has been studied. In the present work, the abilities of native (SBP) to remove cadmium (Cd2+) and lead (Pb2+) ions from aqueous solutions were compared. The (SBP) an industrial by product and solid waste of sugar industry were used for the removal of Cd2+ and Pb2+ ions from aqueous water. Batch adsorption studies were carried out to examine the influence of various parameters such as initial pH, adsorbent dose, initial metal ion concentration, and time on uptake. The sorption process was relatively fast and equilibrium was reached after about 70 min of contact. As much as 70-75% removal of Cd2+ and Pb2+ ions for (SBP) are possible in about 70 min, respectively, under the batch test conditions. Uptake of Cd2+ and Pb2+ ions on (SBP) showed a pH-dependent profile. The overall uptake for the (SBP) is at a maximum at pH 5.3 and gives up to 46.1 mg g(-1) for Cd2+ and at pH 5.0 and gives 43.5 mg g(-1) for Pb2+ for (SBP), which seems to be removed exclusively by ion exchange, physical sorption and chelation. A dose of 8 gL(-1) was sufficient for the optimum removal of both the metal ions. The Freundlich represented the sorption data for (SBP). In the presence of 0.1M NaNO3 the level of metal ion uptake was found to reach its maximum value very rapidly with the speed increasing both with the (SPB) concentration and with increasing initial pH of the suspension. The reversibility of the process was investigated. The desorption of Cd2+ and Pb2+ ions which were previously deposited on the (SBP) back into the deionised water was observed only in acidic pH values during one day study period and was generally rather low. The extent of adsorption for both metals increased along with an increase of the (SBP) dosage. (SBP), which is cheap and highly selective, therefore seems to be a promising substrate to entrap heavy metals in aqueous solutions.     

Immobilized chitosan as biosorbent for the removal of Cd(II), Cr(III) and Cr(VI) from aqueous solutions

The generation of layer-by-layer silicate-chitosan composite biosorbent was studied. The films were evaluated on its stability regarding the polymer leakage and its capability in the removal of Cd(II), Cr(III) and Cr(VI) from an aqueous solution. SEM, EDAX and ATR-IR techniques were applied for material characterization. Silicate-chitosan films with a final layer of silicate demonstrated chitosan retention and had better sorption capacities than those without it. For metal species, such as Cd(II) and Cr(III), the greatest adsorption was obtained when the pH of the solution was 7. When Cr(VI) was evaluated, pH 4 was the optimal for its adsorption. Langmuir and Freundlich isotherms were modeled for the equilibrium data. An 80% of the adsorbed metal was recovered by HNO(3) incubation. This non-covalent immobilization method allowed chitosan surface retention and did not affect its adsorption properties. The use of a coated surface would facilitate sorbent removal from medium after adsorption.     

Biosorption of chromium(III) by two brown algae Macrocystis pyrifera and Undaria pinnatifida: Equilibrium and kinetic study

Two brown algae, Macrocystis pyrifera and Undaria pinnatifida, were employed to remove Cr(III) from aqueous solutions. Both seaweeds were characterized in terms of alginate yields. The alginate contents were 20 and 30% of the dry weight for M. pyrifera and U. pinnatifida, respectively. Kinetics experiments were carried out at different initial pH values. Cr(III) biosorption was affected by the solution pH. The highest metal uptake was found at pH 4 for both biosorbents. Different models were applied to elucidate the rate‐controlling mechanism: pseudo‐first‐order, pseudo‐second‐order, external mass transfer and intra‐particle diffusion. The application of Langmuir, Freundlich and Dubinin–Radushkevich models to the equilibrium data showed a better fitting to the first model. The maximum Cr(III) sorption capacity (q_m) and the affinity coefficient (b) were very similar for both biosorbents: 0.77 mmol/g and 1.20 L/mmol for M. pyrifera and 0.74 mmol/g and 1.06 L/mmol for U. pinnatifida. The free energy of the sorption process was estimated using the Dubinin–Radushkevich isotherm. The values indicate that the processes are chemical sorptions. To evaluate the significance of the ion‐exchange mechanism, the light metals (Ca²⁺, Na⁺, Mg²⁺ and K⁺) and pH were measured during the experiments.     

Esterified coir pith as an adsorbent for the removal of Co(II) from aqueous solution

Coir pith was chemically modified for the adsorption of cobalt(II) ions from aqueous solution. Chemical modification was done by esterification using succinic anhydride followed by activation with NaHCO(3) in order to improve the adsorption of Co(II). Adsorptive removal of Co(II) from aqueous solution onto modified coir pith was evaluated in batch studies under varying conditions of agitation time and metal ion concentration to assess the kinetic and equilibrium parameters. A pseudo-second-order kinetic model fitted well for the sorption of Co(II) onto modified coir pith. Sorption kinetics showed that the loading of Co(II) by this material was quite fast under ambient conditions. The Langmuir and Freundlich equilibrium isotherm models provided excellent fits for the adsorption data, with R(2) of 0.99 and 0.98, respectively. After esterification, the maximum Co(II) sorption loading Q(0); was greatly improved. It is evident that chemically modified adsorbent exhibits better Co(II) removal capability than raw adsorbent suggesting that surface modification of the adsorbent generates more adsorption sites on its solid surface for metal adsorption. A complete recovery of the adsorbed metal ions from the spent adsorbent was achieved by using 1.0N HCl.     

Comparative studies on the adsorption of Cr(VI) ions on to various sorbents

The adsorption of Cr(VI) ions onto various sorbents (chitin, chitosan, ion exchangers; Purolite CT-275 (Purolite I), Purolite MN-500 (Purolite II) and Amberlite XAD-7) was investigated. Batch adsorption experiments were carried out as a function of pH, agitation period and concentration of Cr(VI) ions. The optimum pH for Cr(VI) adsorption was found as 3.0 for chitin and chitosan. The Cr(VI) uptake by ion exchangers was not very sensitive to changes in the pH of the adsorption medium. The maximum chromium sorption occurred at approximately 50 min for chitin, 40 min for Purolite II and 30 min for chitosan, Purolite I and Amberlite XAD-7. The suitability of the Freundlich and Langmuir adsorption models were also investigated for each chromium-sorbent system. Adsorption isothermal data could be accurately interpreted by the Langmuir equation for chitosan, chitin, Purolite I and Purolite II and by the Freundlich equation for chitosan, chitin and Amberlite XAD-7. The chromium(VI) ions could be removed from the sorbents rapidly by treatment with an aqueous EDTA solution and at the same time the sorbent regenerated and also could be used again to adsorb by heavy metal ions. The results showed that, chitosan, which is a readily available, economic sorbent, was found suitable for removing chromium from aqueous solution.     

Biosorption and desorption studies of chromium (III) by free and immobilized Rhizobium (BJVr 12) cell biomass

Experiments with free cell biomass (cells + exopolysaccharides) ofRhizobium BJVr 12 (mungbean isolate) showed that amount ofCr³⁺ ion sorbed is influenced by the amount of biomass toCr³⁺ concentration ratio and time of contact. A ratio of 0.5 gfresh biomass to 10.0 ml 5.03 ppm Cr³⁺ sorbed 0.0275 mg Crequivalent to an uptake of 2.86 mg Cr g-¹ dry biomass and 1.0g: 10.0 ml sorbed 0.0366 mg Cr equivalent to an uptake of 1.9 mg Crg-¹ biomass. Immobilized cell biomass in ceramic beads and inaquacel (a porous cellulose carrier with a charged surface) were moreefficient than free cell biomass in adsorbing Cr(III). A reduction of49.7percnt; of Cr(III) for free cells, 95.6% for cells immobilized inceramic beads and 94.6% for cells in aquacel was achieved after 48hours under shaken conditions. Sorption capacities of immobilized cellbiomass in ceramic beads and aquacel ranged from 5.01 to 5.06 mg Crg^-1 dry cell biomass. The biosorption of Cr³⁺follows generally the Langmuir and Freundlich models of adsorption at lowCr³⁺ concentrations. The Langmuir constant for immobilizedcells in ceramic beads are: Q₀, 0.065 mmol Crg^-1 biomass; b (affinity constant), - 694 lmmol^-1 Cr and for cells in aquacel Q, 0.07 mmol Crg^-1 biomass; b, - 694 l mmol Cr g^-1 Cr. TheFreundlich constants are: K, 0.071 mmol Cr g^-1 biomass; n,0.13 g^-1 biomass l^-1 and for aquacel: K, 0.074mmol g^-1 biomass; n, 0.13 g^-1 biomass. Biotrapsmade up of immobilized cells in ceramic beads and aquacel were tested foradsorbing Cr(III) using two different flow rates: 0.5 ml/min and 1.5 ml/min.A significantly higher amount of Cr(III) was adsorbed at the lower flow rateof 0.5 ml/min. Biosorption of Cr³⁺ is competitive. Thetreatment of a waste water sample containing 6.03 ppm Cr³⁺ andother cations with the biomass reduced the Cr³⁺ concentrationto that much lower than for the test solution containing only Cr. Recoveryof biosorbed Cr(III) was by treatment at a different pH using dilute HClsolution. Recovery was higher for cells imbibed in ceramic beads thanaquacel. Percentage recoveries for cells in aquacel are 46.4% at pH1.0, 33.0% at pH 3.0 and 6.6% at pH 6.0–7.0. For cellsin ceramic beads, percentage recoveries are: 93.1% at pH 1.0,75.6% at pH 3.0 and 16.4% at pH 6.0–7.0. Biosorption ofCr³⁺ by cells immobilized in ceramic beads is reversible butonly partially for cells in aquacel.     

Biosorption of Cr, Cu and Al bySargassum biomass

The biosorption and desorption of Cr, Cu and Al were carried out using brown marine algaeSargassum fluitans biomass, known as the good biosorbent of heavy metals. The content of alginate bound to light metals could be changed by physical and chemical pretreatment. The maximum uptake of Cr, Cu and Al was independent of the alginate content. The maximum uptake of Al was two times(mole basis) than those of Cu and Cr. The aluminum-alginate complex was found in the sorption solution of raw and protonated biomass. Most of Cu, Al and light metals sorbed in the biomass were eluted at pH 1.1. However, only 5 to 10% of Cr sorbed was eluted at pH 1.1. The stoichometric ion exchange between Cu and Ca ion was observed on Cu biosorption with Ca-loaded biomass. A part of Cr ion was bound to biomass as Cr(OH)₂ ⁺ or Cr(OH)²⁺. Al was also bound to biomass as multi-valence ion and interfered with the desorbed Ca ion. The behavior of rawS. fluitans in ten consecutive sorption-desorption cycles has been investigated in a packed bed flow-through-column during a continuous removal of copper from a 35 mg/L aqueous solution at pH 5. The eluant used was a 1%(w/v) CaCl/HCl solution at pH3.     

Removal of perfluorooctane sulfonate from aqueous solution by crosslinked chitosan beads: sorption kinetics and uptake mechanism

The crosslinked chitosan beads were used as an efficient biosorbent to remove perfluorooctane sulfonate (PFOS) from aqueous solution. The chitosan biosorbent had a sorption capacity up to 5.5 mmol/g for PFOS at the equilibrium concentration of 0.33 mmol/L, much higher than some conventional adsorbents. The sorption kinetics indicated that the sorption equilibrium was reached quickly at high pH and low PFOS concentrations, and the adsorbent size also affected the sorption rate to some extent. The double-exponential model described the kinetic data well, and the sorption of PFOS on the chitosan beads was a diffusion-controlled process. Based on the sorption kinetics and adsorbent characterization, the uptake mechanisms including electrostatic and hydrophobic interactions were identified to be responsible for PFOS sorption, and the hemi-micelles and micelles may form in the porous structure due to high PFOS concentrations within the adsorbent, which had the main contribution to the high sorption capacity.     

Activated carbon prepared from biomass as adsorbent: elimination of Ni(II) from aqueous solution.

Activated carbon (AC) prepared from waste Parthenium was used to eliminate Ni(lI) from aqueous solution by adsorption. Batch mode adsorption experiments are carried out, by varying contact time, metal ion concentration, carbon concentration, pH and desorption to assess kinetic and equilibrium parameters. They allowed initial adsorption coefficient, adsorption rate constant and maximum adsorption capacities to be computed. The adsorption data were modeled by using both Langmuir and Freundlich classical adsorption isotherms. The adsorption capacity (Q0) calculated from the Langmuir isotherm was 54.35 mg Ni(II)/g of AC at initial pH of 5.0 and 20 degrees C, for the particle size 250-500 microm. Increase in pH from 2 to 10 increased percent removal of metal ion. The regeneration by HCl of Ni(II)-saturated carbon by HCl, allowed suggestion of an adsorption mechanism by ion-exchange between metal ion and H+ ions on the AC surfaces. Quantitative recovery of Ni(II) was possible with HCl.     

Influence of Bentonite Proportion in Natural Clay on Pb2+ ions Sorption: Response Surface Methodology,Kinetics and Equilibrium Studies

The influence of natural clay's bentonite proportion on Pb²⁺ sorption capacity was investigated using response surface methodology (RSM), kinetics and equilibrium studies. Experiments were conducted at different initial pH (3–7), bentonite to clay ratio (0–100%), initial Pb²⁺ ions concentration (20–120 mg/L) and sorbent dosage (0.2–1 g). Under the RSM study, data obtained from 27 experiments undertaken were found to fitted second-order polynomial model (R² = 0.998 and R²-predicted = 0.994). Analysis of variance showed that the Pb²⁺ sorption capacity was influenced according to the order; initial concentration> mass of adsorbent > initial pH > bentonite proportion. Optimal operating conditions were obtained at initial pH 5, 0.2 g sorbent dosage, 30% bentonite to clay ratio and 100 mg/L Pb²⁺ ion concentration. Regardless of the bentonite proportion, Pb²⁺ sorption kinetics followed pseudo-second-order associated with intra-particle diffusion. The sorption isotherm for the clay which was described by Freundlich yielded higher adsorption capacity (25 mg/g) while that of the bentonite was described by Langmuir model with lower maximum sorption capacity of 15 mg/g. These results suggest that sorption of the Pb²⁺ ions was not likely to significantly impact on the removal of Pb²⁺ ions during electrokinetic remediation process of clay having different proportion of bentonite.     

Chromium Removal from Aqueous System and Industrial Wastewater by Agricultural Wastes

This study involved the development of formaldehyde-treated, deseeded sunflower head waste–based biosorbent (FSH) for the biosorption of Cr(VI) from aqueous solution and industrial wastewater. Batch-mode experiments were conducted to determine the kinetics, sorption isotherms, effect of pH, initial Cr(VI) concentration, biosorbent dose, and contact time. The results demonstrated that FSH can sequester Cr(VI) from the aqueous solution. The maximum sorption occurred at pH = 2.0, biosorbent dose = 4.0 g/L, concentration of 100 mg/L at 25°C at 180 rpm after 2 h contact time. The FSH had an adsorption capacity of 7.85 mg/g for Cr(VI) removal at pH 2.0. The rate of adsorption was rapid, and equilibrium was attained within 2 h. The equilibrium sorption data fitted the Langmuir isotherm model, which was further confirmed by the chi-square test.