Luminescence and energy‐transfer properties of color‐tunable Ca2Mg0.25Al1.5Si1.25O7:Ce3+/Eu2+/Tb3+ phosphors for ultraviolet light‐emitting diodes

A series of Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺/Eu²⁺/Tb³⁺ phosphors was been prepared via a conventional high temperature solid‐state reaction and their luminescence properties were studied. The emission spectra of Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺,Eu²⁺ and Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺,Tb³⁺ phosphors show not only a band due to Ce³⁺ ions (409 nm) but also as a band due to Eu²⁺ (520 nm) and Tb³⁺ (542 nm) ions. More importantly, the effective energy transfer from Ce³⁺ to Eu²⁺ and Tb³⁺ ions was confirmed and investigated by emission/excitation spectra and luminescent decay behaviors. Furthermore, the energy level scheme and energy transfer mechanism were investigated and were demonstrated to be of resonant type via dipole–dipole (Ce³⁺ to Eu²⁺) and dipole–quadrupole (Ce³⁺ to Tb³⁺) reactions, respectively. Under excitation at 350 nm, the emitting color could be changed from blue to green by adjusting the relative doping concentration of Ce³⁺ and Eu²⁺ ions as well as Ce³⁺ and Tb³⁺ ions. The above results indicate that Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺,Eu²⁺/Tb³⁺ are promising single‐phase blue‐to‐green phosphors for application in phosphor conversion white‐light‐emitting diodes. Copyright © 2015 John Wiley & Sons, Ltd.     

Synthesis and photoluminescence characteristics of (Y,Gd)BO3:RE (RE = Eu3+, Ce3+, Dy3+ and Tb3+) phosphors for blue chip and near‐UV white LEDs

A series of Eu³⁺‐, Ce³⁺‐, Dy³⁺‐ and Tb³⁺‐doped (Y,Gd)BO₃ phosphors was synthesized by a solid‐state diffusion method. X‐Ray diffraction confirmed their hexagonal structure and the scanning electron microscopy results showed crystalline particles. The excitation spectra revealed that (Y,Gd)BO₃ phosphors doped with Eu³⁺, Ce³⁺ , Dy³⁺ and Tb³⁺ are effectively excited with near UV‐light of 395 nm/blue light, 364, 351 and 314 nm, respectively. Photoluminescence spectra of Eu³⁺‐, Ce³⁺‐ and Tb³⁺/Dy³⁺‐doped phosphor showed intense emission of reddish orange, blue and white light, respectively. The phosphor Y_0.60Gd_0.38BO₃:Ce_0.02 showed CIE 1931 color coordinates of (0.158, 0.031) and better color purity compared with commercially available blue BAM:Eu²⁺ phosphor. The phosphor (Y,Gd)BO₃ doped with Eu³⁺, Dy³⁺ and Tb³⁺ showed CIE 1931 color coordinates of (0.667, 0.332), (0.251, 0.299) and (0.333, 0.391) respectively. Significant photoluminescence characteristics of the prepared phosphors indicate that they might serve as potential candidates for blue chip and near‐UV white light‐emitting diode applications. Copyright © 2015 John Wiley & Sons, Ltd.     

Luminescent properties of single‐phase Ba2‐x‐1.5y‐1.5zP2O7:xEu2+,yCe3+, zTb3+ phosphors for white light‐emitting diode

A series of Ba₂P₂O₇:xEu²⁺,yCe³⁺,zTb³⁺ phosphors was synthesized via a co‐precipitation method, then their crystal structure, quantum efficiency and luminescent properties were analyzed by XRD and FL, respectively. The results showed that these phosphors not only presented the excitation characteristics of Ba₂P₂O₇:xEu²⁺,zTb³⁺, but also exhibited that of the Ba₂P₂O₇:yCe³⁺,zTb³⁺ phosphor. Meanwhile, the tri‐doped phosphor showed a stronger absorption around 320 nm in contrast with the Eu²⁺/Ce³⁺:Tb³⁺ co‐doped phosphor. Not only can energy transfer from Ce³⁺→Eu²⁺ be observed; the energy transfer mechanism from Eu²⁺ to Tb³⁺ is discussed in the tri‐doped system. Ce³⁺ affects the luminescence properties of Ba₂P₂O₇:xEu²⁺,yCe³⁺,zTb³⁺ phosphors just as the sensitizer whereas Eu²⁺ is considered both as the sensitizer and the activator. The chromaticity coordinates of tri‐doped phosphors excited at 320 nm stayed steadily in the bluish‐white light region,and the emitted color and color temperature (CCT) of these phosphors could be tuned by adjusting the relative contents of Eu²⁺, Ce³⁺ and Tb³⁺. Hence, the single phase Ba₂P₂O₇:xEu²⁺,yCe³⁺,zTb³⁺ phosphors may be considered as potential candidates for white light‐emitting diodes.     

Tunable luminescence properties and energy transfer in LaAl11O18:Eu,Tb phosphor

Eu²⁺ and Tb³⁺ singly doped and co‐doped LaAl₁₁O₁₈ phosphors were prepared by a combustion method using urea as a fuel. The phase structure and photoluminescence (PL) properties of the prepared phosphors were characterized by powder X‐ray diffraction (XRD), scanning electron microscopy (SEM), and photoluminescence excitation and emission spectra. When the content of Eu²⁺ was fixed at 0.01, the emission chromaticity coordinates could be adjusted from blue to green region by tuning the contents of Tb³⁺ ions from 0.01 to 0.03 through an energy transfer (ET) process. The fluorescence data collected from the samples with different contents of Tb³⁺ into LaAl₁₁O₁₈: Eu, show the enhanced green emission at 545 nm associated with ⁵D₄ –⁷F₅ transitions of Tb³⁺. The enhancement was attributed to ET from Eu²⁺ to Tb³⁺, and therefore Eu²⁺ ion acts as a sensitizer (an energy donor) while Tb³⁺ ion as an activator. The ET from Eu²⁺ to Tb³⁺ is performed through dipole–dipole interaction. The ET efficiency and critical distance were also calculated. The present Eu²⁺–Tb³⁺ co‐doped LaAl₁₁O₁₈ phosphor will have potential application for UV convertible white light‐emitting diodes. Copyright © 2015 John Wiley & Sons, Ltd.     

Photoluminescence properties of Ca2Al2O5:RE3+ (RE = Eu,Dy and Tb) phosphors for solid state lighting

Ca₂Al₂O₅:Eu³⁺, Ca₂Al₂O₅:Dy³⁺ and Ca₂Al₂O₅:Tb³⁺ phosphors were synthesized using a combustion synthesis method. The prepared phosphors were characterized by X‐ray powder diffraction for phase purity, by scanning electron microscopy for morphology, and by photoluminescence for emission and excitation measurements. The Ca₂Al₂O₅:Eu³⁺ phosphors could be efficiently excited at 396 nm and showed red emission at 594 nm and 616 nm due to ⁵D₀ → ⁷F₁ and ⁵D₀ → ⁷F₂ transitions. Dy³⁺‐doped phosphors showed blue emission at 482 nm and yellow emission at 573 nm. Ca₂Al₂O₅:Tb³⁺ phosphors showed emission at 545 nm when excited at 352 nm. Concentration quenching occurred in both Eu³⁺ and Dy³⁺phosphors at 0.5 mol%. Photoluminescence results suggested that the aluminate‐based phosphor could be a potential candidate for application in environmentally friendly based lighting technologies.     

Study on luminescence properties of Ce3+ and Eu3+ ions in a nanocrystalline hexagonal Zn4Al22O37 novel system

The present communication is strongly focused on the investigation of synthesis, structural and luminescence properties of cerium (Ce³⁺)- and europium (Eu³⁺)-activated Zn₄Al₂₂O₃₇ phosphors. Ce³⁺- and Eu³⁺-doped Zn₄Al₂₂O₃₇ novel phosphors were prepared using a solution combustion synthesis route. Structural properties were studied using powder X-ray diffraction and high-resolution transverse electron microscopy. The optical properties were studied using ultraviolet–visible light spectroscopy and Fourier transform infrared spectroscopy; luminescence properties were studied using a photoluminescence (PL) technique. The crystal structure of the prepared Zn₄Al₂₂O₃₇ host and Ce³⁺- and Eu³⁺-activated Zn₄Al₂₂O₃₇ phosphors was investigated and was found to have a hexagonal structure. The measured PL emission spectrum of the Ce³⁺-doped Zn₄Al₂₂O₃₇ phosphor showed an intense and broad emission band centred at 421 nm under a 298 nm excitation wavelength. By contrast, the Eu³⁺-doped Zn₄Al₂₂O₃₇ phosphor exhibited two strong and intense emission bands at approximately 594 nm (orange) and 614 nm (red), which were monitored under 395 nm excitation. The Commission Internationale de l’Eclairage (CIE) colour coordinates of the Ce³⁺-doped Zn₄Al₂₂O₃₇ were investigated and found to be x = 0.1567, y = 0.0637 (blue) at 421 nm and for Eu³⁺-doped Zn₄Al₂₂O₃₇ were x = 0.6018, y = 0.3976 (orange) at 594 nm and x = 0.6779, y = 0.3219 (red) at 614 nm emission. The luminescence behaviour of the synthesized phosphors suggested that these phosphors may be used in lighting applications.     

Intensity enhancement of photoluminescence in Tb3+/Eu3+ co-doped Ca14Zn6Al10O35 phosphor for WLEDs

This article focuses on the effect of monovalent cation doping on the optical properties of rare earth (RE = Eu³⁺, Tb³⁺) co-doped Ca₁₄Zn₆Al₁₀O₃₅ which has been synthesized by a low temperature combustion method. Crystalline phase of the Ca₁₄Zn₆Al₁₀O₃₅ phosphor was examined and confirmed by X-ray diffraction measurement. Under near-ultraviolet light excitation Eu³⁺-doped Ca₁₄Zn₆Al₁₀O₃₅ phosphor exhibit characterization of Eu³⁺ emission bands that are located at a maximum wavelength (λ_max) of approximately 470 nm and other peaks centred at 593 nm and 615 nm, respectively. With Tb³⁺-doped Ca₁₄Zn₆Al₁₀O₃₅ phosphor showing a green emission band centred at 544 nm under near-ultraviolet range. Furthermore, we studied the energy transfer process in Eu³⁺/Tb³⁺pair and enhancement in photoluminescence (PL) intensity with doping different charge compensation. Here we obtained the optimum PL emission intensity of the phosphor in broad and intense visible spectral range which may be significant for the fabrication of white light emitting diodes (WLEDs).     

Investigation on luminescence properties of Eu2+‐doped Ba3Al2O5Cl2 phosphor for near‐UV‐excited white LEDs

Ba₃Al₂O₅Cl₂:Eu²⁺ phosphor was prepared by combustion synthesis (CS). The prepared phosphor was excited at 329 nm; the phosphors shows an efficient bluish‐green wide‐band emission centred at 490 nm, which originates from the 4f⁶d¹ → 4f⁷ transition of Eu²⁺ ions. The excitation spectra of the phosphors have a band centred at 329 nm. It was also characterized by XRD, FT–IR for confirmation of phase purity, and FT–IR analysis indicated the vibrations of metal–oxygen (M–O) groups. SEM shows the morphology of the phosphor at the submicron scale. The results indicate that Ba₃Al₂O₅Cl₂:Eu²⁺ phosphor may be applicable for solid‐state lighting purposes. Copyright © 2012 John Wiley & Sons, Ltd.     

Persistent luminescence of CaMgSi2O6:Eu2+,Dy3+ and CaMgSi2O6:Eu2+,Ce3+ phosphors prepared using the solid‐state reaction method

CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors were synthesized using the solid‐state reaction method. X‐Ray diffraction (XRD) and photoluminescence (PL) analyses were used to characterize the phosphors. The XRD results revealed that the synthesized CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors were crystalline and are assigned to the monoclinic structure with a space group C2/c. The calculated crystal sizes of CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors with a main (221) diffraction peak were 44.87 and 53.51 nm, respectively. Energy‐dispersive X‐ray spectroscopy (EDX) confirmed the proper preparation of the sample. The PL emission spectra of CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors have a broad band peak at 444.5 and 466 nm, respectively, which is due to electronic transition from 4f⁶5d¹ to 4f⁷. The afterglow results indicate that the CaMgSi₂O₆:Eu²⁺,Dy³⁺ phosphor has better persistence luminescence than the CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphor. Copyright © 2015 John Wiley & Sons, Ltd.     

Studies on the luminescence properties of cerium co‐doping on Ca2MgSi2O7:Eu2+ phosphor by solid‐state reaction method

Ca₂MgSi₂O₇:Ce³⁺, Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺,Ce³⁺ phosphors were prepared using the solid‐state reaction method. The crystal structures of the sintered phosphors were of melilite type, which has a tetragonal crystallography. The chemical compositions of the sintered phosphors was confirmed by energy dispersive X‐ray spectroscopy. The different thermoluminescence kinetic parameters [activation energy (E), frequency factor (s) and order of the kinetics (b)] of these phosphors were evaluated and compared using the peak shape method. Under ultraviolet excitation, the emission spectra of both Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺,Ce³⁺ phosphors were composed of a broad emission band peaking at 530 nm. When the Ca₂MgSi₂O₇:Eu²⁺ phosphor is co‐doped with Ce³⁺ ions, photoluminescence, afterglow and mechanoluminescence intensity was strongly enhanced. Ca₂MgSi₂O₇:Eu²⁺ showed some afterglow with a short persist time. On incorporation of Ce³⁺, efficient energy transfer from Ce³⁺ to Eu²⁺ was found and the emission intensity of Eu²⁺ was enhanced. The mechanoluminescence intensities of Ca₂MgSi₂O₇:Ce³⁺, Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺,Ce³⁺ phosphors increased proportionally increased with the increase in impact velocity, which suggests that these phosphors can be used as sensors to detect stress in an object.     

Energy transfer in M5(PO4)3 F:Eu2+,Ce3+ (M = Ca and Ba) phosphors

M₅(PO₄)₃ F:Eu²⁺ (M = Ca and Ba) co‐doped with Ce³⁺ phosphors were successfully prepared by the combustion synthesis method. The introduction of co‐dopant (Ce³⁺) into the host enhanced the luminescent intensity of the M₅(PO₄)₃ F:Eu²⁺ (M = Ca and Ba) efficiently. Previously, we have reported the synthesis and photoluminescence properties of same phosphors. The aim of this article is to report energy transfer mechanism between Ce³⁺?Eu²⁺ ions in M₅(PO₄)₃ F:Eu²⁺ (M = Ca and Ba) phosphors, where Ce³⁺ ions act as sensitizers and Eu²⁺ ions act as activators. The M₅(PO₄)₃ F:Eu²⁺ (M = Ca and Ba) co‐doped with Ce³⁺ phosphor exhibits great potential for use in white ultraviolet (UV) light‐emitting diode applications to serve as a single‐phased phosphor that can be pumped with near‐UV or UV light‐emitting diodes. Copyright © 2013 John Wiley & Sons, Ltd.     

Optical and structural properties of composites films based on Ce3+-doped yttrium aluminium garnet nanoparticles embedded in polystyrene

In the present work, attempts have been made to prepare scintillating nanoparticle composite films of Ce³⁺-doped Y₃Al₅O₁₂ (YAG:Ce) embedded in a polystyrene (PS) polymer. A YAG:Ce phosphor has been previously synthesized using the sol–gel method. YAG:Ce-PS composite films of 250 ± 30 μm thickness were prepared using a solvent casting procedure with different PS/solvent concentration and a different mass ratio between nanoparticles of YAG:Ce and PS. X-ray diffraction analysis confirmed that the YAG:Ce powders were successfully prepared. Using thermogravimetric analyses and differential scanning calorimetry, we found that the glass transition temperature (Tg) and thermal degradation were shifted to higher temperatures for composite films relative to pure PS. Photoluminescence showed the yellow emission of the Ce³⁺-doped YAG phosphors, which was attributed to the 5d→4f transition of Ce³⁺ ion and the intensity of the emissions changed with the mass ratio of the YAG:Ce nanoparticles incorporated in the polymer and with the concentration of the polymer solution.     

Synthesis and effect of Ce and Mn co‐doping on photoluminescence characteristics of Ca6AlP5O20:Eu novel phosphors

A series of Ca₆AlP₅O₂₀ doped with rare earths (Eu and Ce) and co‐doped (Eu, Ce and Eu,Mn) were prepared by combustion synthesis. Under Hg‐free excitation, Ca₆AlP₅O₂₀:Eu exhibited Eu²⁺ (486 nm) emission in the blue region of the spectrum and under near Hg excitation (245 nm), Ca₆AlP₅O₂₀:Ce phosphor exhibited Ce³⁺ emission (357 nm) in the UV range. Photoluminescence (PL) peak intensity increased in Ca₆AlP₅O₂₀:Eu,Ce and Ca₆AlP₅O₂₀:Eu, Mn phosphors due to co‐activators of Ce³⁺ and Mn²⁺ ions. As a result, these ions played an important role in PL emission in the present matrix. Ca₆AlP₅O₂₀:Eu, Ce and Ca₆AlP₅O₂₀:Eu, Mn phosphors provided energy transfer mechanisms via Ce³⁺ → Eu²⁺ and Eu²⁺ → Mn²⁺, respectively. Eu ions acted as activators and Ce ions acted as sensitizers. Ce emission energy was well matched with Eu excitation energy in the case of Ca₆AlP₅O₂₀:Eu, Ce and Eu ions acted as activators and Mn ions acted as sensitizers in Ca₆AlP₅O₂₀:Eu, Mn. This study included synthesis of new and efficient phosphate phosphors. The impact of doping and co‐doping on photoluminescence properties and energy transfer mechanisms were investigated and we propose a feasible interpretation. Copyright © 2012 John Wiley & Sons, Ltd.     

Influence of rare earth elements (Y,Gd and Lu) on the luminescent properties of green phosphor ZnMoO4:Tb3+

(Zn,Ln_x)MoO₄:Tb³⁺ (Ln = Y³⁺, Gd³⁺ and Lu³⁺) were prepared using the co‐precipitation method. Phase impurity, morphology and composition were investigated by power X‐ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The experimental results show that crystal structure is not destroyed after doping an appropriate amount of Y³⁺, Gd³⁺ and Lu³⁺. EDS analysis reveals that Y, Gd and Lu have been successfully doped into ZnMoO₄. In addition, the morphology of the phosphors is notably improved, exhibiting homogeneous dispersion morphology and irregular shapes of particle size ~ 0.5–1 µm. The luminescent intensity of (Zn,Ln_x)MoO₄:Tb³⁺ (Ln = Y³⁺, Gd³⁺ and Lu³⁺) phosphor is obviously higher than that of ZnMoO₄:Tb³⁺ phosphor. The energy transfer process between trivalent rare earth ions indicates that the inert earth ions can act as an energy bridge from MoO₄^2‐ to Tb³⁺. Copyright © 2013 John Wiley & Sons, Ltd.     

Synthesis and characterization of blue long‐lasting BaCa2Al8O15:Eu2+, Dy3+ phosphor

We have synthesized and characterized a new BaCa₂Al₈O₁₅:Eu²⁺,Dy³⁺ phosphor prepared by the combustion method. X‐ray diffraction, thermoluminescence, scanning electron microscope, time decay and optical spectral analysis photoluminescence excitation, emission spectra were used to characterize the phosphors. Broadband ultraviolet excited luminescence of the BaCa₂Al₈O₁₅:Eu²⁺,Dy³⁺ was observed in the blue region (λ_max = 435 nm) due to transitions from the 4f⁶5d¹ to the 4f⁷ configuration of the Eu²⁺ ion. Scanning electron microscopy has been used for exploring the morphological properties of the prepared phosphors. The BaCa₂Al₈O₁₅:Eu²⁺ phosphor has a blue afterglow when Dy³⁺ ions were co‐doped. The thermoluminescence spectra show that the Dy³⁺ ion induces a proper trap in the phosphor with a depth of 0.67 eV and results in a long afterglow phosphorescence. Copyright © 2013 John Wiley & Sons, Ltd.     

Design,synthesis and luminescence properties of Ba2YB2O6Cl‐ and Ba2YB2O6F‐based phosphors

Using a high‐temperature solid‐state reaction, the chlorine in Ba₂YB₂O₆Cl is gradually replaced by F, and a new compound with the nominal chemical formula Ba₂YB₂O₆F and two phosphors doped with Ce³⁺ and Eu³⁺, respectively, are obtained. X‐Ray diffraction and photoluminescence spectroscopy are used to characterize the as‐synthesized samples. The as‐synthesized Ba₂YB₂O₆Cl exhibits bright blue emission in the spectral range ~ 330–410 nm with a maximum around 363 nm under X‐ray or UV excitation. Ba₂YB₂O₆F:0.01Ce³⁺ exhibits blue emission in the range ~ 340–570 nm with a maximum around 383 nm. Ba₂YB₂O₆F:0.01Eu³⁺ exhibits a predominantly ⁵D₀–⁷ F₂ emission (~610 nm) and the relative intensities of the ⁵D₀–⁷ F_0,1,2 emissions are tunable under different wavelength UV excitation. The luminescence behaviors of the two phosphors are explained simply in terms of the host composition and site occupancy probability of Ce³⁺ and Eu³⁺, respectively. The results indicate that these phosphors have potential application as a blue phosphor or as a red phosphor. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescent properties of Ca3SiO4Cl2 co‐doped with Ce3+ and Eu2+ for near‐ultraviolet light‐emitting diodes

Ca₃SiO₄Cl₂ co‐doped with Ce³⁺,Eu²⁺ was prepared by high temperature reaction. The structure, luminescent properties and the energy transfer process of Ca₃SiO₄Cl₂: Ce³⁺,Eu²⁺ were investigated. Eu²⁺ ions can give enhanced green emission through Ce³⁺ → Eu²⁺ energy transfer in these phosphors. The green phosphor Ca_2.9775SiO₄Cl₂:0.0045Ce³⁺,0.018Eu²⁺ showed intense green emission with broader excitation in the near‐ultraviolet light range. A green light‐emitting diode (LED) based on this phosphor was made, and bright green light from this green LED could be observed by the naked eye under 20 mA current excitation. Hence it is considered to be a good candidate for the green component of a three‐band white LED. Copyright © 2015 John Wiley & Sons, Ltd.     

Molten salt synthesis and luminescence of Dy3+‐doped Y3Al5O12 phosphors

Dy³⁺‐doped Y₃Al₅O₁₂ phosphors were prepared at a relatively low temperature using molten salt synthesis. The phase of the prepared Dy³⁺‐doped Y₃Al₅O₁₂ phosphors was confirmed using X‐ray powder diffraction. Results indicated that Dy³⁺ doping did not change the Y₃Al₅O₁₂ phase. Following excitation at 352 nm, emission spectra of the Dy³⁺‐doped Y₃Al₅O₁₂ phosphors consisted of blue, yellow, and red emission bands. The influence of Dy³⁺ concentration and excitation wavelength on emission was investigated. The ratio of yellow light to blue light varied with change in Dy³⁺ doping concentration, due to changes in the structure around Dy³⁺. Emission intensities also changed when the excitation wavelength was changed. This variation is luminescence generated a system for tunable white light for Dy³⁺‐doped Y₃Al₅O₁₂ phosphors.     

Optical properties and energy transfer of Eu2+/Ce3+ co‐activated Na3Ca6(PO4)5 phosphor

Ce³⁺/Eu²⁺ co‐doped Na₃Ca₆(PO₄)₅ phosphors were prepared using a combustion‐assisted synthesis method. X‐Ray powder diffraction (XRD) analysis confirmed the formation of a Na₃Ca₆(PO₄)₅ crystal phase. Na₃Ca₆(PO₄)₅:Eu²⁺ phosphors have an efficient bluish‐green emission band that peaks at 489 nm, whereas Ce³⁺‐doped Na₃Ca₆(PO₄)₅ showed a bright emission band at 391 nm. Analysis of the experimental results suggests that enhancement of the Eu²⁺ emission intensity in co‐doped Na₃Ca₆(PO₄)₅:Eu²⁺,Ce³⁺ phosphors is due to a resonance‐type energy transfer from Ce³⁺ to Eu²⁺ ions, which is predominantly governed by an exchange interaction mechanism. These results indicate that Ce³⁺/Eu²⁺ co‐doped Na₃Ca₆(PO₄)₅ is potentially useful as a highly efficient, bluish‐green emitting, UV‐convertible phosphor for white‐light‐emitting diodes. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescent properties and energy transfer in the green phosphors LaBSiO5:Tb3+,Ce3+

LaBSiO₅ phosphors doped with Ce³⁺ and Tb³⁺ were synthesized using the conventional solid‐state method at 1100 °C. The phase purity and luminescent properties of these phosphors are investigated. LaBSiO₅:Tb³⁺ phosphors show intense green emission, and LaBSiO₅ phosphors doped with Ce³⁺ show blue–violet emission under UV light excitation. LaBSiO₅ phosphors co‐doped with Ce³⁺ and Tb³⁺ exhibit blue–violet and green emission under excitation by UV light. The blue–violet emission is due to the 5d–4f transition of Ce³⁺ and the green emission is ascribed to the ⁵D₄ → ⁷ F₅ transition of Tb³⁺. The spectral overlap between the excitation band of Tb³⁺ and the emission band of Ce³⁺ supports the occurrence of energy transfer from Ce³⁺ to Tb³⁺, and the energy transfer process was investigated. Copyright © 2014 John Wiley & Sons, Ltd.