Influence of manufacturing variables on the characteristics and effectiveness of chitosan products. II. Coagulation of activated sludge suspensions

Chitosan samples manufactured under different conditions were compared for effectiveness of coagulating an activated sludge suspension grown on vegetable canning wastes. Computer analysis of data from Buchner funnel filterability tests resulted in quadratic polynomial equations describing the response curves for volume of filtrate versus dosage, expressed as g/liter chitosan/100 g sludge suspended solids (SSS). The quotient of the filtrate volume and dosage at the inflection points of the equations obtained for 10 test samples and 1 commercial chitosan sample were compared to evaluate the response (effectiveness) per unit amount for each chitosan product. The product made by a standard procedure (deproteinated with 3% NaOH at 100°C for 1 hr, demineralized with 1N HCL at ambient temperature for 30 min, and deacetylated with 50% NaOH at 145–150°C under N₂ for 5 or 15 min) gave the best performance as a coagulating agent for this activated sludge system. Other products, including the commercial preparation, required higher dosages to achieve the same effectiveness. Products deacetylated in the presence of sir rather than nitrogen decreased waste treatment effectiveness, which approximated the trends of reduced viscosity and molecular-weight distribution. The products containing minerals were less effective than products from which minerals had been removed prior to deacetylation, but they were more effective than the enzyme treated sample and the commercial product. In general, although chitosan products obtained after 15 min deacetylation were more effective than those receiving 5 min deacetylation, effectiveness did not correlate linearly with viscosity and molecular-weight distribution trends. However, chitosan products deacetylated for 15 min did show that the higher-molecular-weight products (0.65–1.1 × 10⁶) were more effective coagulating agents for activated sludge than the manufactured product having the lowest molecular weight (0.47 × 10⁶) and the commercial reference sample (0.56 × 10⁶). Thus, higher values for molecular weight were predictive of greater effectiveness for coagulation of activated sludge suspensions.     

Effects of degree of deacetylation on enzyme immobilization in hydrophobically modified chitosan

Chitosan is a deacetylated form of the polysaccharide chitin. Over the last decade, researchers have employed reductive amination to hydrophobically modify chitosan to induce a micellar structure. These micellar polymers have been used for a variety of purposes including drug delivery and enzyme immobilization and stabilization. However, commercial sources of chitosan vary in their degree of deacetylation and there remains a paucity of information regarding how this can impact the modified polymer’s functionality for enzyme immobilization. This paper, therefore, evaluates the effect that the degree of deacetylation has on the hydrophobic modification of medium molecular weight chitosan via reductive amination with long chain aldehydes and the resulting changes in enzyme activity after the immobilization of glucose oxidase in the micellar polymeric structure. The chitosan was deacetylated to differing degrees via autoclaving in 40–45% NaOH solutions and characterized using NMR, viscosity measurements, and differential scan calorimetry. Results suggest that a high degree of deacetylation provides optimal enzyme immobilization properties (i.e. high activity), but that the deacetylation method begins to significantly decrease the polymer molecular weight after a 20 min autoclave treatment, which negatively affects immobilized enzyme activity.     

High yield production of monomer-free chitosan oligosaccharides by pepsin catalyzed hydrolysis of a high deacetylation degree chitosan

The high molecular weight of chitosan, which results in a poor solubility at neutral pH values and high viscosity aqueous solutions, limits its potential uses in the fields of food, health and agriculture. However, most of these limitations are overcome by chitosan oligosaccharides obtained by enzymatic hydrolysis of the polymer. Several commercial enzymes with different original specificities were assayed for their ability to hydrolyze a 93% deacetylation degree chitosan and compared with a chitosanase. According to the patterns of viscosity decrease and reducing end formation, three enzymes--cellulase, pepsin and lipase A--were found to be particularly suitable for hydrolyzing chitosan at a level comparable to that achieved by chitosanase. Unlike the appreciable levels of both 2-amino-2-deoxy-D-glucose and 2-acetamido-2-deoxy-D-glucose monomers released from chitosan by the other enzymes after a 20h-hydrolysis (4.6-9.1% of the total product weight), no monomer could be detected following pepsin cleavage. As a result, pepsin produced a higher yield of chitosan oligosaccharides than the other enzymes: 52% versus as much as 46%, respectively. Low molecular weight chitosans accounted for the remaining 48% of hydrolysis products. The calculated average polymerization degree of the products released by pepsin was around 16 units after 20h of hydrolysis. This product pattern and yield are proposed to be related to the bond cleavage specificity of pepsin and the high deacetylation degree of chitosan used as substrate. The optimal reaction conditions for hydrolysis of chitosan by pepsin were 40 degrees C and pH 4.5, and an enzyme/substrate ratio of 1:100 (w/w) for reactions longer than 1h.     

Upgrading the preparation of high-quality chitosan from Procambarus clarkii wastes over the traditional isolation of shrimp chitosan

Crustacean waste is one of the most severe issues, posing significant environmental and health risks. This study aims to improve managing marine waste by isolating chitosan from Procambarus clarkii by devising a new methodology, incorporating technical steps, e.g., washing, decolorization and deacetylation under a reflexive condenser and dialysis purification. A comparison was made between the prepared P. clarkii chitosan and four types of shrimp chitosans: commercial, high, low, and nano. The obtained chitosan has a low molecular weight and viscosity compared to the commercial shrimp chitosan used in various applications. P. clarkii chitosan was prepared in high quality from a cheap source, as its color and quality were better than those of the commercial shrimp chitosan. The new methodology has successfully extracted chitosan from P. clarkii in a good quality and high purity, achieving 89% deacetylation, high solubility, high purity, and medium molecular weight. Analysis of the different chitosan samples with Fourier transform infrared spectroscopy (FTIR), atomic force microscopy, Raman spectrum referred indicated high similarity between the chitosan different types, regardless of its source. The 3D image of P. clarkii showed the distance between the highest and most profound points of extracted chitosan is 728.94 nm, revealing homogeneous, smooth surfaces, apparently free of pores and cracks. FTIR and Raman spectrum of P. clarkii indicated various functional groups, e.g., alcohol, amines, amides, and phenols. These active groups are responsible for about 60% of the antioxidant activity of that product. Evaluating the quality traits indicated the excellence of the chitosan prepared from P. clarkii, especially in color, viscosity, and antioxidant activity, nominating it for different food applications.     

不同脱乙酰度和分子量壳聚糖的神经亲和性研究

研究了四种不同脱乙酰度和分子量的壳聚糖与神经细胞的亲和性。利用酶联免疫技术（ELISA）测定了人血清白蛋白和纤粘蛋白在四种壳聚糖膜上的吸附量,并利用圆二色柱（CD）测定了人血清白蛋白吸附在四种壳矣糖膜上的二极结构。通过研究它们对胎鼠大脑皮层细胞（FMCC）生长的影响,发现在这四种壳聚糖中,分子量较大的两种壳聚糖更有利于神经细胞的生长,许多轴突聚集成树干状。     

Effective production of chitinase and chitosanase byStreptomyces griseus HUT 6037 using colloidal chitin and various degrees of deacetylation of chitosan

The advantages of the organismStreptomyces griseus HUT 6037 is that the chitinase and chitosanase using chitinaceouse substrate are capable of hydrolyzing both amorphous and crystalline chitin and chitosan. We attempted to investigate the optimization of induction protocol for high-level production and secretion of chitosanase and the influence of chitin and partially deacetylated chitosan sources (75–99% deactylation). The maximum specific activity of chitinase has been found at 5 days cultivation with the 48 hours induction time using colloidal chitin as a carbon source. To investigate characteristic of chitosan activity according to substrate, we used chitosan with various degree of deacetylation as a carbon source and found that this strain accumulates chitosanase in the culture medium using chitosanaceous substrates rather than chitinaceous substrates. The highest chitosanase activity was also presented on 4 days with 99% deacetylated chitosan. The partially 53% deacetylated chitosan can secrete both chitinase and chitosanase which was defined as a soluble chitosan. The specific activities of chitinase and chitosanase were 0.89 at 3 days and 1.33 U/mg protein at 5 days, respectively. It indicate that chitosanase obtained fromS. griseus HUT 6037 can hydrolyze GlcNAc-GlcN and GlcN-GlcN linkages by exo-splitting manner. This activity increased with increasing degree of deacetylation of chitosan. It is the first attempt to investigate the effects of chitosanase on various degrees of deacetylations of chitosan byS. griseus HUT 6037. The highest specific activity of chitosanase was obtained with 99% deacetylated chitosan.     

新型缓释片剂辅料甲壳胺的研究 Ⅰ:甲壳胺性质对药物溶出的影响

本文以非甾体抗炎药吲哚美辛为模型药物制备了骨架型缓释片剂,以体外溶出为检验指标,考察了甲壳胺的脱乙酰度、表观粘度及用量对药物释放的影响,并确定了甲壳胺的脱乙酰度及粘度范围。实验结果表明,缓释作用随脱乙酰度升高而降低;随用量增多而增强;粘度对药物释放的影响随脱乙酰度不同而不同。脱乙酰度为85％的甲壳胺,其缓释作用随表观粘度的增大而增大;脱乙酰度为75％的甲壳胺缓释作用随粘度升高而降低。     

Chitosan topical gel formulation in the management of burn wounds

Wound healing properties of chitosan with different molecular weight and degree of deacetylation ranges have been examined. The macroscopic image and histopathology were examined using chitosan, Fucidin^® ointment and to blank. The rate of contraction was evaluated by determination of the unclosed area as a function of time. The treated wounds were found to contract at the highest rate with high molecular weight–high degree of deacetylation chitosan-treated rats as compared to untreated, treated, and Fucidin^® ointment-treated rats. Wounds treated with high molecular weight chitosan had significantly more epithelial tissue (p < 0.05) than wounds with any other treatment and the best re-epithelization and fastest wounds closure were found with the high molecular weight chitosan treatment group. Histological examination and collagenase activity studies revealed advanced granulation tissue formation and epithelialization in wounds treated with high molecular weight chitosan (p < 0.05). High molecular weight with high degree of deacetylation chitosan samples therefore demonstrates potential for use as a treatment system for dermal burns.     

Molecular weight distribution of chitosan isolated from Mucor rouxii under different culture and processing conditions

The isolation of chitosan from a fungal source offers the potential of a product with controlled physicochemical properties not obtainable by the commercial chemical conversion of crustacean chitin. A variety of culture and processing protocols using Mucor rouxii were studied for their effects on biomass yield and chitosan molecular weight. Weight-averaged molecular weight determined by gel permeation chromotography ranged from 2.0 x 10(5) to approximately 1.4 x 10(6) daltons. The chitosan yield ranged from 5% to 10% of total biomass dry weight and from 30% to 40% of the cell wall. Of the culture parameters studied, length of incubation and medium composition effected biomass production and molecular weight. Modification of the processing protocol, including the type and strength of acid, and cell wall disruption in acid prior to refluxing were used to optimize the efficiency of chitosan extraction.The degree of deacetylation of fungal and commercial chitosans was compared using infrared spectrometry, titration, and first derivative of UV absorbance spectrometry. The chitosan obtained directly from the fungal cell wall had a higher degree of deacetylation than commercial chitosan from the chemical conversion process.     

Investigating chitin deacetylation and chitosan hydrolysis during vegetative growth in Magnaporthe oryzae

Chitin deacetylation results in the formation of chitosan, a polymer of β1,4‐linked glucosamine. Chitosan is known to have important functions in the cell walls of a number of fungal species, but its role during hyphal growth has not yet been investigated. In this study, we have characterized the role of chitin deacetylation during vegetative hyphal growth in the filamentous phytopathogen Magnaporthe oryzae. We found that chitosan localizes to the septa and lateral cell walls of vegetative hyphae and identified 2 chitin deacetylases expressed during vegetative growth—CDA1 and CDA4. Deletion strains and fluorescent protein fusions demonstrated that CDA1 is necessary for chitin deacetylation in the septa and lateral cell walls of mature hyphae in colony interiors, whereas CDA4 deacetylates chitin in the hyphae at colony margins. However, although the Δcda1 strain was more resistant to cell wall hydrolysis, growth and pathogenic development were otherwise unaffected in the deletion strains. The role of chitosan hydrolysis was also investigated. A single gene encoding a putative chitosanase (CSN) was discovered in M. oryzae and found to be expressed during vegetative growth. However, chitosan localization, vegetative growth, and pathogenic development were unaffected in a CSN deletion strain, rendering the role of this enzyme unclear.     

Effect of Chitosan, Chitin and some Aminosugars on Growth of Various Soilborne Phytopathogenic Fungi

The effect of bleached chitin, 66% and 91% deacetylated chitosan, respectively, as well as some aminosugars on in vitro radial growth of several phytopathogenic oomycetes and deuteromycets was studied In contrast to chitin, chitosan was inhibitory to the fungi The antifungal activity depended on the degree of deacetylation, the particle diameter of the polymer, the growth medium and the pH. Likewise, deacetylation of the monomers different media varied, indicating a possible counteraction by the carbohydrate sources.     

Antimicrobial textile treated with chitosan from Aspergillus niger mycelial waste

The waste biomass of Aspergillus niger, following citric acid production, was used as a source for fungal chitosan extraction. The produced chitosan was characterized with deacetylation degree of 89.6%, a molecular weight of 25,000 dalton, 97% solubility in 1% acetic acid solution and comparable FT-IR spectra to standard shrimp chitosan. Fungal chitosan was applied as a cotton fabric finishing agent using pad-dry-cure method. The topographical structure of chitosan-treated fabrics (CTF) was much improved compared with control fabrics. CTF, after durability tests, exhibited a powerful antimicrobial activity against both E. coli and Candida albicans, the captured micrographs for E. coli cells contacted with CTF showed a complete lysis of cell walls with the prolonging contact time. The produced antimicrobial CTF could be proposed as a suitable material for many medical and hygienic applications.     

New chitin,chitosan, and O-carboxymethyl chitosan sources from resting eggs of Daphnia longispina (Crustacea); with physicochemical characterization,and antimicrobial and antioxidant activities

The paper describes the isolation and characterization of chitin and chitosan from Daphnia longispina resting eggs harvested from a reservoir. Resting eggs are fertilized eggs that are encased in chitinous shells called ‘ephippia’ and which ensure the survival of the Daphnia population in adverse conditions. The chitin-content of D. longispina resting eggs was found to be 23 ～ 25% and the chitosan (having a 70 ～ 75% deacetylation degree) yield of the chitin was 76 ～ 77%. This high chitin-content indicates that D. longispina resting eggs can be exploited as a chitin source. The structure and thermal properties of chitin, extracted from D. longispina resting eggs, were characterized by employing Fourier transform infrared spectroscopy, thermogravimetric analysis, X-ray diffraction and scanning electron microscopy. The crystallinity of the chitin was found to be very low (48%). Physicochemicallycharacterized chitosan and the produced O-carboxymethyl chitosan were tested for their antimicrobial and antioxidant activity. It has been observed that chitosan displays antimicrobial activity against all pathogenic bacteria, whereas O-carboxymethyl chitosan only exhibits inhibition activity against L. garvieae, L. Monocytogenes ATCC 7644, Y. enterocolitica NCTC 11175 and S. aureus ATCC 25923. In a free radical scavenging activity assay, the IC₅₀ values of chitosan, O-carboxymethyl chitosan and butylated hydroxytoluene were found to be 23.01, 56.43 and 0.05, respectively. The ferric-reducing power of O-carboxymethyl chitosan (EC₅₀ = 8.30) indicated higher activity than chitosan (EC₅₀ = 10.12).     

Characterization and Quantification of Chitosan Extracted from Nacre of the Abalone Haliotis tuberculata and the Oyster Pinctada maxima

This study was performed to characterize and quantify chitosan by simple physicochemical methods (infrared spectroscopy and potentiometric measurements). These procedures were validated with well-characterized chitosan before being used to investigate chitosan in nacre of the abalone Haliotis tuberculata and of the giant oyster Pinctada maxima. Potentiometric study revealed a chitosan extract from the nacre of H. tuberculata with a degree of deacetylation of around 88% and an intrinsic pK of 6.5. According to infrared and potentiometric data, a low yield (η) of extraction was calculated (η= 0.064%). For experiments performed on the nacre of P. maxima, and in spite of more stringent deacetylation conditions, results suggested that a chitin-protein complex (η= 0.053%) was isolated rather than chitosan. Received February 16, 2000; accepted July 4, 2000.     

Chitin and chitosan from Basidiomycetes

Chitinous material was isolated from the mycelium of seven species of Basidiomycetes to evaluate the possibility of using fungal biomass as a source of chitin and chitosan. Such material was characterised for its purity, degree of acetylation and crystallinity. Chitin yields ranged between 8.5 and 19.6% dry weight and the chitosan yield was approximately 1%. The characteristics of the fungal chitins were similar to those of commercial chitin. Chitosans, with a low degree of acetylation, comparable with that of commercial chitosan, were obtained by the chemical deacetylation of fungal chitins.     

Morphological and surface properties of electrospun chitosan nanofibers

Nonwoven fiber mats of chitosan with potential applications in air and water filtration were successfully made by electrospinning of chitosan and poly(ethyleneoxide) (PEO) blend solutions. Electrospinning of pure chitosan was hindered by its limited solubility in aqueous acids and high degree of inter- and intrachain hydrogen bonding. Nanometer-sized fibers with fiber diameter as low as 80 +/- 35 nm without bead defects were made by electrospinning high molecular weight chitosan/PEO (95:5) blends. Fiber formation was characterized by fiber shape and size and was found to be strongly governed by the polymer molecular weight, blend ratios, polymer concentration, choice of solvent, and degree of deacetylation of chitosan. Weight fractions of polymers in the electrospun nonwoven fibers mats were determined by thermal gravimetric analysis and were similar to ratio of polymers in the blend solution. Surface properties of fiber mats were determined by measuring the binding efficiency of toxic heavy metal ions like chromium, and they were found to be related with fiber composition and structure.     

Comparison in antioxidant action between α-chitosan and β-chitosan at a wide range of molecular weight and chitosan concentration

Antioxidant activity in α- and β-chitosan at a wide range of molecular weight (Mw) and chitosan concentration (CS) was determined by 1,1-diphenyl-2-picrylhydrazyl (DPPH) radical scavenging activity, reducing ability, chelating ability, and hydroxyl radical scavenging activity. The form of chitosan (FC) had significant (P <0.05) effect on all measurements except DPPH radical scavenging activity, and antioxidant activity was dependent on Mw and CS. High Mw (280–300 kDa) of β-chitosan had extremely lower half maximal effective concentrations (EC₅₀) than α-chitosan in DPPH radical scavenging activity and reducing ability. The 22–30 kDa of α- and β-chitosan showed significantly (P <0.05) higher activities in DPPH radical scavenging, reducing ability, and hydroxyl radical scavenging than samples at other Mw, while chelating ability was the highest in 4–5 kDa chitosan. CS had significant effect on all measurements and the effect was related to Mw. The antioxidant activity of 280–300 kDa chitosan was affected by coil-overlap concentrations (C¹) in the CS range of 4–10 mg/mL, forming entanglements. Reducing ability and hydroxyl radical scavenging activity were more predominant action in antioxidant activity of chitosan as shown by the lower EC₅₀ values than those in other antioxidant measurements.     

Effects of Spray Drying on Physicochemical Properties of Chitosan Acid Salts

The effects of spray-drying process and acidic solvent system on physicochemical properties of chitosan salts were investigated. Chitosan used in spray dryings was obtained by deacetylation of chitin from lobster (Panulirus argus) origin. The chitosan acid salts were prepared in a laboratory-scale spray drier, and organic acetic acid, lactic acid, and citric acid were used as solvents in the process. The physicochemical properties of chitosan salts were investigated by means of solid-state CP-MAS ¹³C nuclear magnetic resonance (NMR), X-ray powder diffraction (XRPD), differential scanning calorimetry, and Fourier transform infrared spectrometry (FTIR) and near-infrared spectroscopy. The morphology of spray-dried chitosan acid salts showed tendency toward higher sphericity when higher temperatures in a spray-drying process were applied. Analysis by XRPD indicated that all chitosan acid salts studied were amorphous solids. Solid-state ¹³C NMR spectra revealed the evidence of the partial conversion of chitosan acetate to chitin and also conversion to acetyl amide form which appears to be dependent on the spray-drying process. The FTIR spectra suggested that the organic acids applied in spray drying may interact with chitosan at the position of amino groups to form chitosan salts. With all three chitosan acid salts, the FTIR bands at 1,597 and 1,615 cm⁻¹ were diminished suggesting that –NH groups are protonated. The FTIR spectra of all chitosan acid salts exhibited ammonium and carboxylate bands at 1,630 and 1,556 cm⁻¹, respectively. In conclusion, spray drying is a potential method of preparing acid salts from chitosan obtained by deacetylation of chitin from lobster (P. argus) origin.     

Effect of dietary chitosans with different viscosity on plasma lipids and lipid peroxidation in rats fed on a diet enriched with cholesterol

To investigate the effect of dietary chitosan on lipid metabolism, male SD (Sprague-Dawley) rats were fed a cholesterol-enriched diet containing 5% cellulose (CE), 5% chitosan (CCS; high viscosity), or 5% chitosan (FCS; low viscosity) for 4 weeks. The two types of chitosan with a comparable degree of deacetylation had a different molecular weight and intrinsic viscosity. Significantly (p < 0.05) lower plasma total cholesterol, LDL-cholesterol and VLDL-cholesterol concentrations were observed in the rats fed on the chitosan diets. In addition, chitosan significantly increased the fecal cholesterol and triglyceride contents. Although no significant difference in body weight was found among the dietary groups, the rats fed on the chitosan diets had lower relative liver weight when compared with those fed on the cellulose diet. Both of the chitosan groups had significantly lower liver total lipid and total cholesterol contents compared to the cellulose group, although the FCS group was less effective. The plasma and liver thiobarbituric acid reactive substances (TBAR) values were similar in the CE and FCS groups, while the CCS group had increased liver TBAR values. Although a significant increase in liver glucose-6-phosphate dehydrogenase activity was observed in the CCS group, no significant change was found in the FCS group. The observed influence of chitosans with different viscosity on the plasma lipid level, liver lipids and lipid peroxidation suggests that, while the hypocholesterolemic action of chitosans with different viscosity was similar, changes in the liver lipids and liver peroxidation status depended on their molecular weight when the deacetylation degree was comparable.