Swift heavy ion induced structural and luminescence characterization of Y2O3:Eu3+ phosphor: a comparative study

We report a comparative study on structural and thermoluminescence modifications of Y₂O₃:Eu³⁺ phosphor induced by 150 MeV Ni⁷⁺, 120 MeV Ag⁹⁺ and 110 MeV Au⁸⁺ swift heavy ions (SHI) in the fluence range 1 × 10¹¹ to 1 × 10¹³ ions/cm². X‐Ray diffraction and transition electron microscopy studies confirm the loss of crystallinity of the phosphors after ion irradiation, which is greater in the case of Au ion irradiation. Structural refinement using the Rietveld method yields the various structural parameters of ion‐irradiated phosphors. Thermoluminescence glow curves of ion‐irradiated phosphors show a small shift in the position of the peaks, along with an increase in intensity with ion fluence. Stopping range of ions in Matter (SRIM) calculations were performed to correlate the change in thermoluminescence properties of various ion‐irradiated phosphors. It shows that the defects created by 110 MeV Au⁸⁺ ions are greater in number. Trapping parameters of ion‐irradiated phosphors were calculated from thermoluminescence data using various glow curve analysis methods. Copyright © 2013 John Wiley & Sons, Ltd.