| Abstract: | The crystal structures of (1→3)-α-d-glucan triacetates were studied by X-ray diffraction measurements on fibre diagrams. The oriented films annealed in water at high temperature were of higher crystallinity and occurred as two crystalline polymorphs (GTA I and GTA II) depending on the samples and also the annealing temperature. All reflections in GTA I were indexed with a pseudo-orthorhombic unit cell with a = 1·753, b = 3·018 and c(fibre axis) = 1·205 nm. From the fibre repeat data coupled with the density data and the presence of only the (003) reflection on the meridian, an extended three-fold helical structure was proposed. Although some reflections in GTA II split from the layer lines, the basic unit cell was a monoclinic system with a = 1·685, b = 3·878, c (fibre axis) = 1·210 nm and γ = 112·2°. A similar three-fold structure to GTA I was proposed from the almost identical fibre repeat and the conformational analysis on (1→3)-α-d-glucan. It was concluded that, on acetylation, the d-glucan structure changed from the fully extended two-fold helix to the extended three-fold accompanied by some extent of chain shrinking. |