Leaching of iron and toxic heavy metals from anaerobically-digested sewage sludge

Summary Heavy metal-loaded sewage sludge was leached abiotically using FeCl₂ and FeCl₃ which are applied in waste water treatment plants to eliminate phosphate and for coagulation. Due to the hydrolyzing nature of ferric iron, ferric chloride (100 mmll L^–1) was able to solubilize more than 90% of copper and zinc and more than 80% of cadmium, with an optimal pulp density of 3% (w/v), after 10 h of exposition at 25°C. Chromium, lead and nickel were solubilized to an extent of 40–70%. With the exception of copper (redoxolysis), all heavy metals monitored were leached following the principle of acidolysis. Chemical leaching with iron resulted in a secondary contamination of sewage sludge (96 g iron per kg dry weight). The insoluble iron compounds which were precipitated for adsorbed to sludge flocks could be resolubilized with oxalic acid (100 mM, pH<3.3) up to an extent of 90%. Iron was leached by acidolysis and held in solution by complexation with oxalic acid. The pH optimum for the treatment of sewage sludge with 100 mmol L^–1 oxalic acid was pH 3.3. At this pH an excessive solubilization of nutrient elements and compounds (phosphorus, nitrogen, alkali and alkali earth elements) could be avoided concomitantly leaching 75% iron. Furthermore the hydrophobicity of the sewage sludge was significantly reduced as a result of treatment with iron chloride.Thiobacillus ferrooxidans (isolated from arsenopyrite and adapted on sewage sludge) utilized ferrous iron as an energy source in the presence of chloride ions (FeCl₂) as efficiently as ferrous sulphate. No toxic effects of oxalic acid onT. ferrooxidans were observed at the prevailing concentration.