Resonant and non‐resonant energy transfer from Ce3+ → X (X = Tb3+, Eu3+ or Dy3+) in NaMgSO4F material

An inorganic NaMgSO₄F fluoride material was prepared by the wet chemical method and studied for its photoluminescence (PL) and resonant–non‐resonant energy transfer (RET and NORET) capabilities between Ce³⁺ → Tb³⁺, Ce³⁺ → Eu³⁺ and Ce³⁺ → Dy³⁺ rare earth ions. The Tb³⁺ emission for Ce³⁺ → Tb³⁺ transfers under ultraviolet (UV) wavelengths peaked at 491, 547, and 586 nm, for excitation at 308 nm due to ⁵D₄ → ⁷F_J (J = 4, 5, 6) transitions. Eu emission spectra were observed at 440 nm (Eu²⁺), 593 nm and 616 nm (Eu³⁺) recorded for different concentrations of materials, whereas Dy³⁺ emission from Ce³⁺ → Dy³⁺ transfer under UV wavelengths peaked at 485 nm and 577 nm due to ⁴F_9/2 → ⁶H_15/2 and ⁶H_13/2 transitions. The purpose of the present study is to understand the RET and NORET effects of Tb³⁺, Eu³⁺ and Dy³⁺ co‐doping in a NaMgSO₄F:Ce³⁺ luminescent material, which could be used as a green‐emitting material for lamp phosphors.