Sol–gel synthesis and luminescence property of Sr4Al2O7:Re3+,R+ (Re = Eu and Dy; R = Li,Na and K) phosphors for white LEDs

Sr₄Al₂O₇:Eu³⁺ and Sr₄Al₂O₇:Dy³⁺ phosphors with alkali metal substitution were prepared using a sol–gel method. The effects of a charge compensator R on the structure and luminescence of Sr₄Al₂O₇:Re³⁺,R⁺ (Re = Eu and Dy; R = Li, Na and K) phosphors were investigated in detail. Upon heating to 1400°C, the structure of the prepared samples was that of the standard phase of Sr₄Al₂O₇. Under ultraviolet excitation, all Sr₄Al₂O₇:Eu³⁺,R⁺ samples exhibited several narrow emission peaks ranging from 550 to 700 nm due to the 4f → 4f transition of Eu³⁺ ions. All Sr₄Al₂O₇:Dy³⁺,R⁺ phosphors showed two emission peaks at 492 and 582 nm, due to the ⁴F_9/2 → ⁶H_15/2 and ⁴F_9/2 → ⁶H_13/2 transitions of Dy³⁺ ions, respectively. The luminescence intensity of Sr₄Al₂O₇:Re³⁺,R⁺ (Re = Eu and Dy; R = Li, Na and K) phosphors improved markedly upon the addition of charge compensators, promoting their application in white light‐emitting diodes with a near‐ultraviolet chip.