Photoluminescence and thermoluminescence studies of CaAl2O4:Dy3+ phosphor

Calcium aluminate phosphors activated by Dy³⁺ have been prepared by a combustion method at a temperature of 600°C. Photoluminescence (PL) and thermoluminescence (TL) properties of gamma‐irradiated Dy‐doped calcium aluminate were investigated. The PL spectrum shows a broad peak around 488 nm and 573 nm, under 347 nm excitation. Thermoluminescence studies were performed for different concentrations of Dy. Optimum intensity of photoluminescence was found for 0.02 mol% concentration of Dy. It was found that initially the peak TL intensity increases with increasing concentration of Dy in the CaAl₂O₄ host, attains a maximum value for 0.05 mol% concentration and decreases with further increase in the doping concentration due to concentration quenching. Copyright © 2015 John Wiley & Sons, Ltd.