A Composite Gel Polymer Electrolyte with High Performance Based on Poly(Vinylidene Fluoride) and Polyborate for Lithium Ion Batteries
Authors:Yusong Zhu  Shiying Xiao  Yi Shi  Yaqiong Yang  Yuyang Hou  Yuping Wu
Institution:New Energy and Materials Laboratory (NEML), Department of Chemistry & Shanghai, Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai, China
Abstract:A composite membrane based on electrospun poly(vinylidene fluoride) (PVDF) and lithium polyvinyl alcohol oxalate borate (LiPVAOB) exhibiting high safety (self‐extinguishing) and good mechanical property is prepared. The ionic conductivity of the as‐prepared gel polymer electrolyte from this composite membrane saturated with 1 mol L?1 LiPF6 electrolyte at ambient temperature can be up to 0.26 mS cm?1, higher than that of the corresponding well‐used commercial separator (Celgard 2730), 0.21 mS cm?1. Moreover, the lithium ion transference in the gel polymer electrolyte at room temperature is 0.58, twice as that in the commercial separator (0.27). Furthermore, the absorbed electrolyte solvent is difficult to evaporate at elevated temperature. Its electrochemical performance is evaluated by using LiFePO4 cathode. The obtained results suggest that this gel‐type composite membrane shows great possibilities for use in large‐capacity lithium ion batteries that require high safety.
Keywords:lithium ion batteries  safety materials  gel polymer electrolytes  polyborates  poly(vinylidene fluoride)
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号