Breathable Carbon‐Free Electrode: Black TiO2 with Hierarchically Ordered Porous Structure for Stable Li–O2 Battery

This paper introduces oxygen‐deficient black TiO₂ with hierarchically ordered porous structure fabricated by a simple hydrogen reduction as a carbon‐ and binder‐free cathode, demonstrating superior energy density and stability. With the high electrical conductivity derived from oxygen vacancies or Ti³⁺ ions, this unique electrode features micrometer‐sized voids with mesoporous walls for the effective accommodation of Li₂O₂ toroid and for the rapid transport of reaction molecules without the electrode being clogged. In the highly ordered architecture, toroidal Li₂O₂ particles are guided to form with a regular size and separation, which induces the most of Li₂O₂ external surface to be directly exposed to the electrolyte. Therefore, large Li₂O₂ toroids (≈300 nm) grown from solution can be effectively charged by incorporating a soluble catalyst, resulting in a very small polarization (≈0.37 V). Furthermore, disordered nanoshell in black TiO₂ is suggested to protect the oxygen‐deficient crystalline core, by which oxidation of Ti³⁺ is kinetically impeded during battery operation, leading to the enhanced electrode stability even in a highly oxidizing environment under high voltage (≈4 V).