Piezoelectric properties of poly-β-hydroxybutyrate and copolymers of β-hydroxybutyrate and β-hydroxyvalerate

The shear piezoelectricity was observed in oriented films of poly-β-hydroxybutyrate (PHB) and copolymers of β-hydroxybutyrate (HB) and β-hydroxyvalerate (HV). The piezoelectric stress constant 3₁₄ = e′₁₄ ? ie″₁₄ (polarization/strain), the piezoelectric strain constant d₁₄ = d′₁₄ ? id″₁₄ (polarization/stress), the elastic constant c = c′ + ic″ and the dielectric constant = ′ ? i″ were determined at a frequency of 10 Hz over a temperature range from ?150° to +150°C. Piezoelectric relaxations as well as elastic and dielectric relaxations were clearly observed at the glass transition temperature of about 15°C. In order to evaluate the piezoelectric constants (e₂ and d₂) for the piezoelectric phase which consists of the crystalline region and the oriented non-crystalline region, a spherical dispersion two phase model was utilized. Assuming the appropriate fixed values for the elastic and dielectric constants in the piezoelectric phase, d₂ and d₂ were calculated as a function of temperature. For a PHB and a copolymer (17 HV/83 HB), e₂ and d₂ showed relaxations, leading to a conclusion that the instantaneous piezoelectric constant in the crystalline phase is constant independent of temperature but the piezoelectric constant in the oriented non-crystalline phase is relaxational and has the opposite sign. For a copolymer (25 HV/75 HB) and a chloroform treated copolymer (17 HV/83 HB), e₂ and d₂ were constant independent of temperature, indicating that the oriented non-crystalline phase has disappeared owing to the increased molecular flexibility due to copolymerization or annealing in chloroform vapour.