Extracellular biosynthesis of silver nanoparticles using Rhizopus stolonifer

Synthesis of silver nanoparticles (AgNPs) has become a necessary field of applied science. Biological method for synthesis of AgNPs by Rhizopus stolonifer aqueous mycelial extract was used. The AgNPs were identified by UV–visible spectrometry, X-ray diffraction (XRD), transmission electron microscopy (TEM) and Fourier transform infrared spectrometry (FT-IR). The presence of surface plasmon band around 420 nm indicates AgNPs formation. The characteristic of the AgNPs within the face-centered cubic (fcc) structure are indicated by the peaks of the X-ray diffraction (XRD) pattern corresponding to (1 1 1), (2 0 0) and (2 2 0) planes. Spherical, mono-dispersed and stable AgNPs with diameter around 9.47 nm were prepared and affirmed by high-resolution transmission electron microscopy (HR-TEM). Fourier Transform Infrared (FTIR) shows peaks at 1426 and 1684 cm^?1 that affirm the presence of coat covering protein the AgNPs which is known as capping proteins. Parameter optimization showed the smallest size of AgNPs (2.86 ± 0.3 nm) was obtained with 10^?2 M AgNO₃ at 40 °C. The present study provides the proof that the molecules within aqueous mycelial extract of R. stolonifer facilitate synthesis of AgNPs and highlight on value-added from R. stolonifer for cost effectiveness. Also, eco-friendly medical and nanotechnology-based industries could also be provided. Size of prepared AgNPs could be controlled by temperature and AgNO₃ concentration. Further studies are required to study effect of more parameters on size and morphology of AgNPs as this will help in the control of large scale production of biogenic AgNPs.