Hybrid nanofibrous yarns based on N-carboxyethylchitosan and silver nanoparticles with antibacterial activity prepared by self-bundling electrospinning

Hybrid nanofibrous materials with antibacterial activity consisting of yarns from N-carboxyethylchitosan (CECh) and poly(ethylene oxide) (PEO) that contain 5 wt % or 10 wt % silver nanoparticles (AgNPs) were prepared. This was achieved by electrospinning using formic acid as a solvent and as a reducing agent for silver ions. AgNO₃ was used as an Ag⁺-containing salt. Its concentration was selected to be 0.02 mol/L or 0.04 mol/L in order the content of the AgNPs in the electrospun nanofibers to be 5 wt % or 10 wt %, respectively. The self-bundling of the fibers into yarns with a mean diameter of ca. 35 μm was enabled only by using a grounded needle electrode. The reduction of the silver ions to an elemental silver was evidenced by UV-vis spectroscopy, X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The transmission electron microscopy (TEM) analyses revealed that AgNPs formed at AgNO₃ concentration of 0.02 mol/L were with a mean diameter of 4 ± 0.5 nm and were distributed uniformly within the fiber. The increase of AgNO₃ concentration to 0.04 mol/L led to the preparation of AgNPs with a higher mean diameter and a broader diameter distribution as well as to aggregate formation. The performed studies on the antibacterial activity of CECh/PEO/AgNPs fibrous materials against Staphylococcus aureus showed that at AgNPs content of 5 wt % the mats had bacteriostatic, and at AgNPs content of 10 wt %—bactericidal activity.