| Abstract: | The crystal structures of two polymorphic forms of pachyman triacetate, the fully acetylated derivative of a naturally occuring β-(1 → 3)-D -glucan, were determined by a combination of stereochemical and x-ray diffraction analysis. The two polymorphs could be obtained depending on the temperature and the degree of stretching of film specimens of the substance: polymorph I resulted from stretching 25–50% at 125°C and polymorph II resulted from further stretching to 300% at 215°C. Both polymorphs had previously been shown to have sixfold helical chain conformations, but of unequal pitch. Subsequent detailed structure refinement performed with bond lengths, bond angles, conformational angles, and helix-packing parameters as refinement variables, and the simultaneous minimization of packing and conformational energy and the crystallographic R-factor as refinement criteria, resulted in a complete determination of the two crystal structures. Pachyman triacetate I was found to be a right-handed helix packing with antiparallel polarity and space group P212121 symmetry (unit-cell parameters a = 11.0, b = 19.0, c (fiber repeat) = 22.38 Å). The acetate groups were nearly planar and the O(2) and O(4) acetates were oriented in such a fashion that the carbonyl double-bond nearly eclipsed the corresponding C—H bond of the ring. The O(6) was in the tg position and its acetate was oriented in such a fashion that the bond sequence C(6)—O(6)—C(6C)—C(6M) was nearly trans-planar, with the carbonyl double-bond bisecting the tetrahedral angle formed by C(6) and its two hydrogens. The final R = 0.221. Pachyman triacetate II was similarly found to be a right-handed helix, but packing as a 50:50 mixture of parallel and antiparallel polarities (unit-cell parameters a = 11.49, b = 20.13, c (fiber repeat) = 18.6 Å). The acetate positions in pachyman triacetate II were substantially the same as in pachyman triacetate I. The final R for the 50:50 mixture was 0.234. Probable reasons for the change in packing polarities are discussed, as are the difficulties encountered in the structure refinement of acetate derivatives. |