Elastic moduli of excised constricted rat lungs

When airways constrict, the surrounding parenchyma undergoesstretch and distortion. Because of the mechanical interdependence between airways and parenchyma, the material properties of the parenchyma are important factors that modulate the degree ofbronchoconstriction. The purpose of this study was to investigate theeffect of changes in transpulmonary pressure (Ptp) and inducedconstriction on parenchymal bulk (k)and shear (µ) moduli. In excised rat lungs, pressure was measured atthe airway opening, and pressure-volume curves were obtained byimposing step decreases in volume with a calibrated syringe from totallung inflation. Calculation was made ofk during small-volume oscillations (1 Hz). Absolute lung volume at 0 cmH₂O Ptp was obtained bysaline displacement. To calculate µ, a lung-indentation test wasperformed. The lung surface was deformed with a cylindrical punch(diameter = 0.45 cm) in 0.25-mm increments, and the force required toeffect this displacement was measured by a weight balance. Measurementsof k and µ were obtained at 4 and 10 cmH₂O Ptp, and again at 4 cmH₂O Ptp, after delivery ofmethacholine aerosol (100 mg/ml) into the trachea. Values ofk and µ in rat lungs were similar tothose reported in other species. In addition, k and µ were dependent on Ptp. Afterinduced constriction, k and µ increased significantly. That k and µ can increase after induced constriction has important implicationsvis a vis the factors modulating airway narrowing.