| Abstract: | ZnO nanostructures of different morphology (nanorods, nano‐leaf, nanotubes) were favourably grown using a chemical precipitation process. The prepared ZnO nanostructures were characterized systematically using absorption spectroscopy, emission spectroscopy, X‐ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared studies. XRD results showed the hexagonal wurtzite phase of the synthesized ZnO nanostructures. Structural properties such as average crystallite size, lattice constants, volume of the unit cell, atomic fraction, and structural bonds were also studied. The optical band gap of the synthesized ZnO nanocrystals varied from 3.52 eV to 3.69 eV with high quantum yield of the blue emission (~420 nm). Urbach energy for ZnO nanocrystals was calculated to be 0.702 eV, 0.901 eV, and 0.993 eV for nanorods, nano‐leaf, and tube like ZnO crystals, respectively. Morphology of the fabricated nanostructures was investigated using SEM. Photocatalytic degradation of rhodamine B (Rh B) in solution under UV irradiation was explored with different ZnO morphology. Photocatalytic experiments showed that ZnO nano‐leaf had a higher degradation rate of photocatalytic activity of photodegrading Rh B compared with the other tube shape and rods shape nanostructures. The Rh B dye degraded considerably by ～79.05%, 74.41%, and 69.8% within 120 min in the presence of the as‐fabricated fern nano‐leaf, nanotubes, and nanorods of the ZnO nanocrystals at room temperature. |