Graphene nanosheet reinforcement of polyurethane nanocomposite for green and sustainable photoluminescence,superhydrophobic, and anticorrosive paint

A simple and environmentally friendly method was developed for smart and efficient waterborne polyurethane (PUR) paint. Sugarcane bagasse was recycled into reduced graphene oxide nanosheets (rGONSs). Both lanthanide-doped aluminate nanoparticles (LAN; photoluminescent agent, 7–9 nm) and rGONSs (reinforcement agent) were integrated into a waterborne polyurethane to produce a novel photoluminescent, hydrophobic, and anticorrosive nanocomposite coating. Using ferrocene-based oxidation under masked circumstances, graphene oxide nanosheets were produced from sugarcane bagasse. The oxidized semicarbazide (SCB) nanostructures were integrated into polyurethane coatings as a drying, anticorrosion, and crosslinking agent. Polyurethane coatings with varying amounts of phosphor pigment were prepared and subsequently applied to mild steel. The produced paints (LAN/rGONSs@PUR) were tested for their hydrophobicity, hardness, and scratch resistance. Commission Internationale de l'éclairage (CIE) Laboratory parameters and photoluminescence analysis established the opacity and colourimetric properties of the nanocomposite coatings. When excited at 365 nm, the luminescent transparent paints emitted a strong greenish light at 517 nm. The anticorrosion characteristics of the coated steel were investigated. The phosphor-containing (11% w/w) polyurethane coatings displayed the most pronounced anticorrosion capability and long-persistent luminosity. The prepared waterborne polyurethane paints were very photostable and durable.     

Photoluminescent properties of Eu3+‐Eu2+ activated MAl2SixO2x + 4 (M = Mg,Ca, Sr,Ba) phosphors prepared in air

In this paper, MAl₂Si_xO_2x+4:Eu²⁺/Eu³⁺ (Eu²⁺ + Eu³⁺ = 2%, molar ratio; M = Mg, Ca, Sr, Ba; x = 0, 0.5, 1, 1.5, 2) phosphors with different SiO₂ concentrations (the ratio of SiO₂ to MAl₂O₄ is n%, n = 0, 50, 100, 150, 200, respectively) were prepared by high‐temperature solid‐state reaction under atmospheric air conditions. Their structures and photoluminescent properties were systematically researched. The results indicate that Eu³⁺ ions have been reduced and Eu²⁺ ions are obtained in air through the self‐reduction mechanism. The alkaline earth metal ions and doping SiO₂ strongly affect the crystalline phase and photoluminescent properties of samples, including microstructures, relative intensity of Eu²⁺ to Eu³⁺, location of emission lines/bands. It is interesting and important that the emission color and intensities of europium‐doped various phosphors which consist of aluminosilicate matrices prepared under atmospheric air conditions could be modulated by changing the kinds of alkaline earth metal and the content of SiO₂.     

Effect of CaCN2 on the preparation of CaAlSiN3:Eu2+ phosphors

Highly efficient red‐emitting phosphors, CaAlSiN₃:Eu²⁺, were successfully prepared by the solid‐state method using calcium cyanide (CaCN₂) as the single calcium source. The influences of crystallization temperature, crystallization time, calcination mode and compounds ratio on the photoluminescent properties were investigated. The CaAlSiN₃:Eu²⁺ phosphors were obtained with 1 mol% CaCN₂ by a two‐step calcination procedure at 900°C for 2 h and subsequently at 1600°C for 8 h. The CaAlSiN₃:Eu²⁺ phosphors showed the strongest luminescent intensity at 660 nm when excited by 468 nm. With an increase in crystallization time, the maximum wavelength of the emission was shifted from 644 nm to 660 nm.