Experimental and theoretical study of mechanoluminescence and lyoluminescence of Li3PO4: RE (RE=Dy and Tb) phosphors

Li₃PO₄ phosphors prepared by solid‐state diffusion technique and lyoluminescence (LL) as well as mechanoluminescence (ML) studies are reported. Dy‐ and Tb‐activated phosphors show dosimetric characteristics using LL and ML techniques. The energy levels and hence trapping and detrapping of charge carriers in the material can be studied using ML. Li₃PO₄ phosphor can be used in the dosimetric applications for ionizing radiation. By using the LL technique, the LL characteristics of Li₃PO₄ may be useful for high radiation doses. We also report a more detailed theoretical understanding of the mechanism of LL and ML. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescence analysis of SrGa2Si2O8: RE3+ (RE = Dy,Tm) phosphors

This article reports on the luminescence properties of rare earth (Dy³⁺ and Tm³⁺)ions doped SrGa₂Si₂O₈ phosphor were studied. SrGa₂Si₂O₈phosphors weresynthesizedby employing solid state reaction method.From the measured X‐ray diffraction (XRD) pattern of the samplemonoclinic phase structure has been observed. Thermoluminescenceand Mechanoluminescence properties of the γ‐ray irradiated samples have been studied. Photoluminescence spectra of Dy³⁺ activated SrGa₂Si₂O₈phosphor has been measured with an excitation wavelength at 348 nm,and it shows two emission bands at 483 and 574 nm due to ⁴F_9/2 → ⁶H_15/2 and ⁴F_9/2 → ⁶H_13/2 transitions respectively. Whereas the photoluminescence spectra of Tm³⁺ activated SrGa₂Si₂O₈ phosphor has been measured with an excitation wavelength at 359 nm and it exhibits two emission bands at 454 and 472 nm due to ¹D₂ → ³F₄ and¹G₄ → ³H₆ transitions respectively. In thermoluminescence study, γ‐irradiatedthermoluminescence glow curve of SrGa₂Si₂O₈:Dy³⁺ phosphor shows two well defined peaks at 293 °C (peak1)and 170 °C (peak2) whereas thermoluminescence glow curve of SrGa₂Si₂O₈:Tm³⁺ phosphor shows peaks at 292 °C (peak1) and 184 °C (peak2) indicating that two sets of traps are being activated within the particular temperature range and the trapping parameters associated with the prominent glow peaks of SrGa₂Si₂O₈:Dy³⁺ and SrGa₂Si₂O₈:Tm³⁺ are calculated using Chen's peak shape and initial rise method.From the Mechanoluminescence study, only one glow peak has been observed. Copyright © 2016 John Wiley & Sons, Ltd.