Luminescence characterization of Dy and Eu doped Na6Mg(SO4)4 phosphors

A series of single‐phase phosphors based on Na₆Mg(SO₄)₄ (Z_eff = 11.70) doped with Dy and Eu was prepared by the wet chemical method. The photoluminescence (PL) and thermoluminescence (TL) properties of Dy³⁺‐ and Eu³⁺‐activated Na₆Mg(SO₄)₄ phosphors were investigated. The characteristic emissions of Dy³⁺ and Eu³⁺ were observed in the Na₆Mg(SO₄)₄ host. The TL glow curve of the Na₆Mg(SO₄)₄:Dy phosphor consisted of a prominent peak at 234°C and a very small hump at 158°C. The TL sensitivity of the Na₆Mg(SO₄)₄:Dy phosphor was found to be four times less than the commercialized CaSO₄:Dy phosphor. The TL dose–response of the Na₆Mg(SO₄)₄:Dy phosphor was studied from a dose range of 5–10 kGy and the linear dose–response was observed up to 1 kGy which is good for a microcrystalline phosphor. Trapping parameters for both the samples were calculated using the Initial Rise and Chen's peak shape methods.     

Luminescence of Eu and Ce in K3Ca2(SO4)3F fluoride material

A new halophosphor K₃Ca₂(SO₄)₃ F activated by Eu or Ce and K₃Ca₂(SO₄)₃ F:Ce,Eu co‐doped halosulfate phosphor has been synthesized by the co‐precipitation method and characterized for its photoluminescence (PL). The PL emission spectra of the K₃Ca₂(SO₄)₃ F :Ce phosphor show emission at 334 nm when excited at 278 nm due to 5d → 4f transition of Ce³⁺ ions. In the K₃Ca₂(SO₄)₃ F:Eu lattice, Eu²⁺ (440 nm) as well as Eu³⁺ (596 nm and 615 nm) emissions have been observed showing ⁵D₀ → ⁷ F₁ and ⁵D₀ → ⁷ F₂ transition of the Eu³⁺ ion, which is in the blue and red region of the visible spectrum respectively. The trivalent europium ion is very useful for studying the nature of metal coordination in various systems owing to its non‐degenerate emitting ⁵D₀ state. K₃Ca₂(SO₄)₃ F:Ce,Eu is suitable for Ce³⁺ → Eu²⁺ → Eu³⁺ energy transfer in which Ce³⁺and Eu²⁺ play the role of sensitizers and Eu²⁺ and Eu³⁺ act as the activators. The observations presented in this paper are relevant for lamp phosphors. Copyright © 2015 John Wiley & Sons, Ltd.     

New UVA‐emitting BaAlBO3F2:Eu2+ phosphor with PL and TL properties for phototherapy lamp

We present a new phosphor material, BaAlBO₃F₂ doped with Eu²⁺ ions, having emission in the UVA region. The phosphor material is prepared by a simple wet chemical method. Phase confirmation was carried out using the Rietveld refinement program which shows that BaAlBO₃F₂:Eu²⁺ has an hexagonal crystal system. Using a Fourier transform infrared spectroscopy graph, we studied the bond stretching present in the phosphor material. Photoluminescence (PL) characterization, carried out using a RF spectrofluorophotometer, shows two types of PL excitation and emission. Before reduction, emission is in the blue region at 431 nm; after reduction, excitation is at 258 nm and emission is at 361 nm, which is in the UVA region. Some thermoluminescence (TL) studies were carried out in this material for the first time, for example, determination of the trapping parameters, linearity, fading, glow curve convolution and deconvolution (GCCD) function for curve fitting and the T_m–T_stop method for confirmation of the trapped centers in the TL glow peak. Copyright © 2016 John Wiley & Sons, Ltd.     

Characterization and luminescence properties of CaMgSi2O6:Eu2+ blue phosphor

A blue CaMgSi₂O₆:Eu²⁺ phosphor was prepared by the solid‐state reaction method and the phosphor characterized in terms of crystal structure, particle size, photoluminescence (PL), thermoluminescence (TL) and mechanoluminescence (ML) properties using X‐ray diffraction (XRD), transmission electron microscopy (TEM), PL spectroscopy, TLD reader and ML impact technique. The XRD result shows that phosphor is formed in a single phase and has a monoclinic structure with the space group C2/c. Furthermore, the PL excitation spectra of Eu²⁺‐doped CaMgSi₂O₆ phosphor showed a strong band peak at 356 nm and the PL emission spectrum has a peak at 450 nm. The depths and frequency factors of trap centers were calculated using the TL glow curve by deconvolution method in which the trap depths were found to be 0.48 and 0.61 eV. The formation of CaMgSi₂O₆:Eu²⁺ phosphor was confirmed by Fourier transform infrared spectroscopy. The ML intensity increased linearly with the impact velocity of the piston used to deform the phosphor. It was shown that the local piezoelectricity‐induced electron bombardment model is responsible for the ML emission. Finally, the optical properties of CaMgSi₂O₆:Eu²⁺ phosphors are discussed. Copyright © 2015 John Wiley & Sons, Ltd.     

Enhanced luminescence and white light emission from Eu3+‐co‐doped K3Ca2(SO4)3Cl:Dy3+ phosphor with near visible ultraviolet excitation for white LEDs

The luminescent properties of europium (Eu)‐ and dysprosium (Dy)‐co‐doped K₃Ca₂(SO₄)₃Cl halosulfate phosphors were analyzed. This paper reports the photoluminescence (PL) properties of K₃Ca₂(SO₄)₃Cl microphosphor doped with Eu and Dy and synthesized using a cost‐effective wet chemical method. The phosphors were characterized by X‐ray diffraction and scanning electron microscopy. The CIE coordinates were calculated to display the color of the phosphor. PL emission of the prepared samples show peaks at 484 nm (blue), 575 nm (yellow), 594 nm (orange) and 617 nm (red). The emission color of the Eu,Dy‐co‐doped K₃Ca₂(SO₄)₃Cl halophosphor depends on the doping concentration and excitation wavelength. The addition of Eu in K₃Ca₂(SO₄)₃Cl:Dy greatly enhances the intensity of the blue and yellow peaks, which corresponds to the ⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2 transitions of Dy³⁺ ions (under 351 nm excitation). The Eu³⁺/Dy³⁺ co‐doping also produces white light emission for 1 mol% of Eu³⁺, 1 mol% of Dy³⁺ in the K₃Ca₂(SO₄)₃Cl lattice under 396 nm excitation, for which the calculated chromaticity coordinates are (0.35, 0.31). Thus, K₃Ca₂(SO₄)₃Cl co‐doped with Eu/Dy is a suitable candidate for NUV based white light‐emitting phosphors technology. Copyright © 2014 John Wiley & Sons, Ltd.     

Optically stimulated luminescence in LiCaAlF6:Eu2+ phosphor

Results on optically stimulated luminescence (OSL) in LiCaAlF₆:Eu²⁺ are reported. Continuous wave OSL signal as recorded using blue (470 nm) stimulation was found to be ~31% that of standard phosphor lithium magnesium phosphate. The rate of OSL depletion for standard phosphor lithium magnesium phosphate is only three times less as compared with that of LiCaAlF₆:Eu²⁺. Strong photoluminescence (PL) in the near ultraviolet region is observed for LiCaAlF₆:Eu²⁺ with the characteristic Eu²⁺ emission at 369 nm for 254 nm excitation. The thermoluminescence (TL) glow peak for LiCaAlF₆:Eu²⁺ was observed at around 180°C. The glow peak was about six times more intense compared with the dosimetric peak of the well known thermoluminescence dosimetric (TLD) phosphor LiF‐TLD 100. Thus this phosphor deserves much more attention than it has received until now and may be useful as a dosimetric material in radiation dosimetry. Copyright © 2015 John Wiley & Sons, Ltd.     

Synthesis and thermoluminescence characterizations of Sr2B5O9Cl:Dy3+ phosphor for TL dosimetry

The photoluminescence (PL) and thermoluminescence (TL) displayed by Dy‐activated strontium haloborate (Sr₂B₅O₉Cl) were studied. A modified solid‐state reaction was employed for the preparation of the phosphor. Photoluminescence spectra showed blue (484 nm) and yellow (575 nm) emissions due to incorporation of Dy³⁺ into host matrix. The Dy‐doped (0.5 mol%) Sr₂B₅O₉Cl was studied after exposure to γ‐irradiation and revealed a prominent glow curve at 261°C with a small hump around 143°C indicating that two types of traps were generated. The glow peak at the higher temperature side (261°C) was more stable than the lower temperature glow peak. The TL intensity was 1.17 times less than that of the standard CaSO₄:Dy thermoluminescence dosimetry (TLD) phosphor, the phosphor showed a linear dose–response curve for different γ‐ray irradiation doses (0.002–1.25 Gy) and fading of 5–7% was observed for higher temperature peaks upon storage. Trapping parameters and their estimated error values have been calculated by Chen's peak shape method and by the initial rise method. Values of activation energies estimated by both these techniques were comparable. The slight difference in activation energy values calculated by Chen's peak shape method indicated the formation of two kinds of traps Furthermore, slight differences in frequency values are due to various escaping and retrapping probabilities. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescent properties of MAl(SO4)2Br:Eu3+ (M = Sr or Mg) red phosphors for near‐UV light‐emitting diodes

Eu³⁺‐activated MAl(SO₄)₂Br phosphors (where M = Mg or Sr) are successfully prepared using a wet chemical reaction technique. The samples are characterized by X‐ray diffraction (XRD) and photoluminescence (PL) spectroscopies. The XRD pattern revealed that both the samples are microcrystalline in nature. PL of Eu³⁺‐doped SrAl(SO₄)₂Br and MgAl(SO₄)₂Br phosphors exhibited characteristic red emission coming from the ⁵D₀ → ⁷F₂ (616 nm) electron transition, when excited by 396 nm wavelength of light. The maximum intensity of luminescence was observed at a concentration of 1 mol% Eu³⁺. The intensity of the electric dipole transition at 616 nm is greater than that of the magnetic dipole transition at 594 nm. The results showed that MAl(SO₄)₂Br:Eu³⁺, (M = Mg, Sr) phosphors have potential application in near‐UV light‐emitting diodes as efficient red‐emitting phosphor. Copyright © 2014 John Wiley & Sons, Ltd.     

Europium doped Sr2YNbO6 double perovskite phosphor for photoluminescence and thermoluminescence properties

A luminescent double perovskite phosphor Sr₂YNbO₆ doped with Eu³⁺ crystallized to the monoclinic phase and was synthesized successfully via a conventional high-temperature combustion method. The formation of the crystal structure, phase purity, and surface morphology were studied using X-ray diffraction patterns and scanning electron microscopy. The characteristic vibrations between the atoms of the functional groups present in phosphor were studied using Fourier transform infrared spectra analysis. The luminescence properties of the prepared phosphors were investigated in terms of photoluminescence (PL) and thermoluminescence (TL). PL excitation spectra exhibited charge transfer bands and the characteristic 4f⁶ transitions of Eu³⁺. A prominent PL emission was obtained for the phosphor doped with 4 mol% Eu³⁺ under the 396 nm excitation wavelength. PL emission quenching was observed for the higher doping concentrations due to a multipole–multipole interaction. A highly intense PL emission arose due to the hypersensitive ⁵D₀–⁷F₂ electric dipole transition of Eu³⁺ that dominated the emission spectra. The thermal stability of the phosphor was examined through temperature-dependent PL. The TL properties of the Sr₂YNbO₆ double perovskites irradiated with a ⁹⁰Sr beta source at different doses were measured. The double perovskite phosphors under study showed a linear dose–response with increasing beta dose, ranging from 1 Gy to 10 Gy. Trapping parameters of the TL glow curves were determined using Chen's peak shape method and computerized glow curve deconvolution (CGCD). CGCD fitting of the TL glow curves revealed that it was consisted of three major peaks and followed second-order kinetics. The estimated activation energies were determined using different methods and were comparable and significant.     

Optical properties of CaAl(SO4)2Br:RE (RE = Dy,Eu, Ce) novel phosphors

A new phosphor CaAl(SO₄)₂Br doped with Dy, Ce and Eu is reported. Rare earth (Dy, Eu and Ce)‐doped polycrystalline CaAl(SO₄)₂Br phosphors were prepared using a wet chemical reaction method and studied for X‐ray diffraction and photoluminescence (PL) characteristics. Dy³⁺ emission in the CaAl(SO₄)₂Br lattice was observed at 484 and 574 nm in the blue and yellow regions of the spectrum, which are assigned to ⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2 transitions of the Dy³⁺ ion, respectively. While the PL emission spectra of CaAl(SO₄)₂Br:Ce phosphor showed Ce³⁺ emission at 347 nm due to 5d → 4f transition of the Ce³⁺ ion. In a CaAl(SO₄)₂Br:Eu lattice, Eu³⁺ emissions were observed at 593 and 617 nm, coming from the ⁵D₀ → ⁷ F₁ and ⁵D₀ → ⁷ F₂ electron transitions, respectively. The PL study showed that the intensity of electric dipole transition at 617 nm dominates over that of magnetic dipole transition at 590 nm. The maximum PL intensity was obtained for a 1 mol% concentration of Eu³⁺ in CaAl(SO₄)₂Br host lattice. The results showed that the material may be a promising candidate as a blue‐, yellow‐ and red‐emitting phosphor. Copyright © 2013 John Wiley & Sons, Ltd.     

Synthesis and photoluminescence properties of Eu3+‐activated Ba2Mg(PO4)2 phosphor

In this paper, we have reported the photoluminescence (PL) properties of the Ba₂Mg(PO₄)₂:Eu³⁺ phosphor synthesized using a wet chemical method. The preliminary scanning electron microscopy (SEM) investigation of the sample revealed irregular surface morphology with particle sizes in the 10–50 μm range. The strongest PL excitation peak was observed at 396 nm. The emission spectra indicated that this phosphor can be effectively excited by the 396 nm wavelength. Upon 396 nm excitation, the emission spectrum showed characteristics peaks located at 592 nm and 615 nm. These intense orange‐red emission peaks were obtained due to f→f transitions of Eu³⁺ ions. The emission peak at 592 nm is referred to as the magnetic dipole ⁵D₀→⁷F₁ transition and the emission peak at 615 nm corresponded to the electric dipole ⁵D₀→⁷F₂ transition of Eu³⁺. The Commission Internationale de l’Eclairage (CIE) coordinates of the Ba₂Mg(PO₄)₂:Eu³⁺ phosphor were found to be (0.586, 0.412) for wavelength 592 nm and (0.680, 0.319) for wavelength 615 nm situated at the edge of the CIE diagram, indicating high colour purity of phosphors. Due to the high emission intensity and a good excitation profile, Eu³⁺‐doped Ba₂Mg(PO₄)₂ phosphor may be a promising orange‐red phosphor candidate for solid‐state lighting applications.     

Photoluminescence and thermoluminescence characteristics of Sr3B2O6:Eu2+ yellow phosphor

Sr₃B₂O₆:Eu²⁺ yellow phosphor was prepared by the combustion method. The crystalline structure, photoluminescence and thermoluminescence properties of Sr₃B₂O₆:Eu²⁺ were investigated extensively. The X‐ray diffraction result indicates that the Sr₃B₂O₆:Eu²⁺ phosphor exhibited a rhombohedral crystal structure. The emission spectra under a 435 nm excited wavelength showed an intense broad band peaking at 574 nm, which corresponds to the 4f⁶5d¹ → 4f⁷ transition of Eu²⁺ ion. There were two different sites of Sr replaced by Eu in host lattice. The concentration quenching process between Eu²⁺ ions is determined and the corresponding concentration quenching mechanism was verified as dipole‐quadrupole interaction. The glow curve under 3 Gy β‐ ray irradiation had the glow peak at 160°C and the average activation energy was defined as about 0.98 eV. Copyright © 2015 John Wiley & Sons, Ltd.     

Study of luminescence and effect of Dy3+ on NaMgSO4Cl:Ce chlorosulphate phosphor

Chlorosulphate NaMgSO₄Cl phosphor doped with Ce³⁺ and co‐doped by Dy³⁺ prepared by the wet chemical method was studied for its photoluminescence and thermoluminescence (TL) characteristics. The emission spectrum of Ce³⁺ shows dominant peaks at 346 nm (excitation 270 nm) due to 5d → 4f transition. Efficient energy transfer occurs from Ce³⁺ → Dy³⁺ ions. Dy³⁺ emission at 485 nm and 576 nm is due to ⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2 transitions of Dy³⁺ ion respectively. The TL glow curves of NaMgSO₄Cl:Ce and Ce,Dy have been recorded for various concentrations at a heating rate of 2 °C/s irradiated by γ‐rays at a dose rate of 0.995 kGy/h for 1 Gy, which peaks at about 241 °C and 247‐312 °C respectively. Further, in changing the concentration level, the general structure of the intensity is found to increase. The main property of this phosphor is its sensitivity even for low concentrations of rare earth ions and low γ‐ray dose. There is still scope for higher doses of γ‐radiation. The phosphor presented may be used as a lamp phosphor as well as for TL studies. Copyright © 2014 John Wiley & Sons, Ltd.     

Effect of Dy3+ or Eu2+ co‐activator on a BaCa(SO4)2:Ce3+ mixed alkaline earth sulfate phosphor

The individual emission and energy transfer between Ce³⁺ and Eu²⁺ or Dy³⁺ in BaCa(SO₄)₂ mixed alkaline earth sulfate phosphor prepared using a co‐precipitation method is described. The phosphor was characterized by X‐ray diffraction (XRD) and photoluminescence (PL) studies and doped by Ce;Eu and Dy rare earths. All phosphors showed excellent blue–orange emission on excitation with UV light. PL measurements reveal that the emission intensity of Eu²⁺ or Dy³⁺ dopants is greater than when they are co‐doped with Ce³⁺. An efficient Ce³⁺ → Eu²⁺ [²T_2g(4f⁶5d) → ⁸S_7/2(4f₇)] and Ce³⁺ → Dy³⁺ (⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2) energy transfer takes place in the BaCa(SO₄)₂ host. A strong blue emission peak was observed at 462 nm for Eu²⁺ ions and an orange emission peak at 574 nm for Dy³⁺ ions. Hence, this phosphor may be used as a lamp phosphor. Copyright © 2015 John Wiley & Sons, Ltd.     

Luminescence in Li3Al2(PO4)3:Eu2+

A series of efficient Li₃Al₂(PO₄)₃:Eu²⁺ novel phosphors were synthesized by the facile combustion method. The effects of dopant on the luminescence behavior of Li₃Al₂(PO₄)₃ phosphor were also investigated. The phosphors were characterized by X‐ray diffraction, field emission scanning electron microscope and photoluminescence techniques. The result shows that all samples can be excited efficiently by near‐ultraviolet excitation under 310 nm. The emission was observed for Li₃Al₂(PO₄)₃:Eu²⁺ phosphor at 425 nm, which corresponded to the d → f transition. The concentration quenching of Eu²⁺ was observed in Li₃Al₂(PO₄)₃:Eu²⁺ when the Eu concentration was at 0.5 mol%. The prepared powders exhibited intense blue emission at the 425 nm owing to the Eu²⁺ ion by Hg‐free excitation at 310 nm (i.e., solid‐state lighting excitation). Consequently, the availability of such a phosphor will significantly help in the development of blue‐emitting solid‐state lighting applications. Copyright © 2012 John Wiley & Sons, Ltd.     

Mechanoluminescence,thermoluminescence, photoluminescence studies on Ca3Y2Si3O12:RE3+ (RE3+ = Dy3+and Eu3+) phosphors

Dy³⁺ and Eu³⁺ activated Ca₃Y₂Si₃O₁₂ phosphors were synthesized by the solid‐state synthesis method. The phosphors were characterized by X‐ray diffraction (XRD), mechanoluminescence (ML), thermoluminescence (TL) and photoluminescence (PL) to determine structure and luminescence. For ML glow curves, only one peak was observed, as only one type of luminescence centre was formed during irradiation. The Ca₃Y₂Si₃O₁₂:Dy³⁺ TL glow curve showed a single peak at 151.55°C and the Ca₃Y₂Si₃O₁₂:Eu³⁺ TL glow curve peaked at 323°C with a small peak at 192°C, indicating that two types of traps were activated. The trapping parameters for both the samples were calculated using Chen's peak shape method. Dy³⁺‐activated Ca₃Y₂Si₃O₁₂ showed emission at 482 and 574 nm when excited by a 351 nm excitation wavelength, whereas the Eu³⁺‐activated Ca₃Y₂Si₃O₁₂ phosphor PL emission spectra showed emission peaks at 613 nm, 591 nm, 580 nm when excited at 395 nm wavelength. When excited at 466 nm, prominent emission peaks were observed at their respective positions with very slight shifts. Copyright © 2015 John Wiley & Sons, Ltd.     

Fracto‐mechanoluminescence and thermoluminescence properties of UV and γ‐irradiated Ca2Al2SiO7:Ce3+ phosphor

Ce³⁺‐doped calcium aluminosilicate phosphor was prepared by a combustion‐assisted method at an initiating temperature of 600°C. Structural characterization was carried out using X‐ray diffraction (XRD) and scanning electron microscopy (SEM). The absorption spectra of Ca₂Al₂SiO₇:Ce³⁺ showed an absorption edge at 230 nm. The optical characterization of Ca₂Al₂SiO₇:Ce³⁺ phosphor was investigated in a fracto‐mechanoluminescence (FML) and thermoluminescence (TL) study. The peak of ML intensity increased as the height of impact of the moving piston increased. The TL intensity of Ca₂Al₂SiO₇:Ce³⁺ was recorded for different exposure times of UV and γ‐irradiation and it was observed that TL intensity was maximum for a UV irradiation time of 30 min and for a γ‐dose of 1180 Gy. The TL intensity had three peaks for UV irradiation at temperatures 82°C, 125°C and 203°C. Also the TL intensity had a single peak at 152°C for γ‐irradiation. The TL and ML emission spectra of Ca₂Al₂SiO₇:Ce³⁺ phosphor showed maximum emission at 400 nm. The possible mechanisms involved in the TL and ML processes of the Ca₂Al₂SiO₇:Ce³⁺ phosphor are also explained. Copyright © 2015 John Wiley & Sons, Ltd.     

ZnAl2O4:Eu novel phosphor: SEM and mechanoluminescence characterization synthesized by solution combustion technique

Eu doped ZnAl₂O₄ phosphors were synthesized by the solution combustion technique using carbohydrazide as a fuel. Mechanoluminescence (ML) was excited impulsively by dropping a piston of 0.7 kg onto the phosphors. Two distinct peaks were observed in the ML glow curve of the γ‐ray irradiated ZnAl₂O₄:Eu phosphors. Dependence of ML on various parameters as impact velocity of the piston dropped on to it, mass of the sample, gamma ray doses given to the sample and ML spectra have been studied. ML emission spectrum showed the characteristic emission of Eu³⁺ ion in this system. ML is observed to be optimum for the sample having 0.2 mol% of Eu in the ZnAl₂O₄ phosphor. XRD result confirms formation of the phosphors. SEM characterization shows its surface morphology. This novel phosphor may be a potential candidate for dosimetric use due to its linear dose response. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescence characteristics of Na3Ca2(SO4)3F: Ce3+ fluoride material

A new Na₃Ca₂(SO₄)₃F: Ce³⁺ phosphor synthesized by a solid state diffusion method is reported. The photoluminescence study showed a single high intensity emission peak at 307 nm wavelength when excited by UV light of wavelength 278 nm. An unresolved peak of comparatively less intensity was also observed at 357 nm along with the main peak. The characteristic emission of dopant Ce in Na₃Ca₂(SO₄)₃F phosphor clearly indicated that it resides in the host lattice in trivalent form. The emission peak can be attributed to 5d → 4f transition of rare earth Ce³⁺. The prepared sample is also characterized for its thermoluminescence properties. The TL glow curve of prepared sample showed a single broad peak at 147°C. The trapping parameters are also evaluated by Chen's method. The values of trap depth (E) and frequency factor (s) were found to be 0.64 ± 0.002 eV and 1.43 × 10⁷ s^–1 respectively. The study of PL and TL along with evaluation of trapping parameters has been undertaken and discussed for the first time. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescence properties of nanocrystalline Mg2P2O7:Eu phosphor

Thermoluminescence (TL) measurements were carried out on europium (Eu) doped magnesium pyrophosphate (Mg₂P₂O₇) nanopowders using gamma irradiation in the dose range of 0.1 to 3 kGy. The powder samples were successfully synthesized by chemical co‐precipitation synthesis route. The formation and crystallinity of the compound was confirmed by powder X‐ray diffraction (PXRD) pattern. The estimated particle size was found to be in nanometer scale by using Debye Scherer's formula. A scanning electron microscopy (SEM) study was carried out for the morphological characteristics of as synthesized Mg₂P₂O₇:Eu phosphor. Photoluminescence (PL) study was carried out to confirm the presence of the rare‐earth ion and its valence state. The TL analysis of synthesized samples were performed after the irradiation of Mg₂P₂O₇:Eu with cobalt‐60 (⁶⁰Co) gamma rays. The high and low intensity peaks of TL glow curve appeared at around 400 K, 450 K, 500 K and 596 K respectively. The appreciable shift in peak positions has been observed for different concentrations of Eu ion. The trapping parameters, namely activation energy (E), order of kinetics (b) and frequency factor (s) have been determined using thermal cleaning process, peak shape (Chen's) method and glow curve deconvolution (GCD) functions.