Flexural properties of repaired heat‐polymerising acrylic resin after wetting with monomer and acetone

doi:10.1111/j.1741‐2358.2009.00321.x
Flexural properties of repaired heat‐polymerising acrylic resin after wetting with monomer and acetone Objectives: Repair strength can be improved by treating fractured surfaces of a denture. Background: This study investigated flexural properties of heat‐polymerised acrylic resin specimens repaired with auto‐polymerising and visible light curing (VLC) resins after the repair surfaces were wetted with monomers or acetone. Materials and Methods: Fifty‐four specimens (65 × 10 × 2.5 mm) were prepared and 48 of them were sectioned to simulate denture fracture. Butt‐joint designed repair surfaces were wetted with heat‐, auto‐polymerising monomers and acetone for 180 s and repaired with auto‐polymerising and VLC resins. After repairs, specimens were subjected to three‐point bending test and flexural strength, strain, fracture load, modulus of elasticity and deflection values were recorded. Data were analysed with Student t and LSD tests (p ≤ 0.05). Results: Overall flexural strength, strain, fracture load and deflection values of specimens repaired with VLC resin were significantly higher than the specimens repaired with auto‐polymerising resin for all types of wetting agent (p < 0.05). Within the wetting agents, heat‐ and auto‐polymerising monomers produced the best mechanical properties, while wetting with acetone did not provide superior effect over both monomers. Conclusion: In clinical use, wetting the repair surfaces may result in stronger repairs. The use of bonding agent in VLC resin repairs in combination with wetting agent results in improved flexural properties.     

Effect of monomer treatment and polymerisation methods on the bond strength of resin teeth to denture base material

Background: The fracture between acrylic denture base material and artificial teeth is a common clinical occurrence in dental prosthodontic practice. Objective: To evaluate the bond strength between acrylic resins and resin denture teeth when submitted by two protocols of monomer liquid application on the tooth surface and using different polymerisation methods. Material and methods: Microwave‐polymerised (Onda‐Cryl), heat‐polymerised (Clássico) and autopolymerising (Jet) acrylic resins and a brand of resin denture teeth (Biotone) were used. The acrylic resins were polymerised according to the cycles: (A) microwave – fast cycle, Onda‐Cryl; (B) microwave – long cycle, Onda‐Cryl; (C) microwave – manufacturer’s cycle, Onda‐Cryl; (T) water bath – long cycle, Clássico and (Q) bench polymerisation cycle, Jet. Thirty specimens were prepared for each polymerisation method; 10 were packed with acrylic resin after 60 s of monomer liquid application on the tooth surface, 10 after 180 s and 10 without any monomer liquid application. For the purpose of the study, a shear test was used. anova and Tukey tests were performed to identify significant differences (α = 0.05). Results: The highest bond strength values were found for monomer surface treatments, regardless of the polymerisation cycles. The highest significant values were found for cycles B (15.4 ± 1.8 MPa), C (11.9 ± 4.9 MPa) and T (15.4 ± 2.6 MPa) for non‐treated and 60 s methylmethacrylate treated groups. Comparing the monomer liquid treatment, they did not differ significantly (p > 0.05), except for cycle A (p < 0.05). Conclusion: Chemical treatment using monomer on the tooth surface prior to the acrylic resin packing improved the bond strength between resin denture tooth and acrylic resin, regardless of monomer liquid treatment protocols. The microwavable resin, polymerised by fast cycle and autopolymerising resin should be avoided for processing denture and denture repairs, respectively.     

Effect of pre-processing methods on bond strength between acrylic resin teeth and acrylic denture base resin

doi: 10.1111/j.1741‐2358.2011.00480.x
Effect of pre‐processing methods on bond strength between acrylic resin teeth and acrylic denture base resin Objectives: This study evaluated the effects of various pre‐processing methods on the bond strength between resin and denture teeth. Backgrounds: Debonding of acrylic resin teeth from denture base material is a problem for patients wearing complete dentures. Materials and Methods: Four experimental groups (n = 30) were investigated by subjecting tooth–resin bonding to tensile loading. Specimens were prepared and tested according to the methods of the International Standards Organization (ISO 22112:2005) using a special assembly. Four pre‐processing surface treatments of teeth were applied: (i) ST₁, no treatment applied (control); (ii) ST₂, wax solvent (Dewaks, Faber Kimya & Ilaç, Turkey); (iii) ST₃, boiling water followed by conditioning with methyl methacrylate (MMA) monomer (Meliodent, Bayer Dental, Germany); (iv) ST₄, boiling water followed by wax solvent agent and finally MMA monomer application. Bond strength test was performed using a universal testing machine. Results: All the strength values of the test groups were within clinically acceptable limits. The lowest values were from the ST₁ group and the highest values were in the ST₄ group. Conclusions: Wax elimination methods affected bonding strength. Application of wax solvent and MMA monomer to the ridge lap surfaces of the teeth gave the best results. In clinical practice, this application procedure may decrease the bonding failure of denture teeth.     

Effect of reline material and denture base surface treatment on the impact strength of a denture base acrylic resin

doi:10.1111/j.1741‐2358.2009.00292.x
Effect of reline material and denture base surface treatment on the impact strength of a denture base acrylic resin Objective: In this study, the effect of relining and surface treatment on the impact strength (IS) of a heat‐polymerising denture base acrylic resin (Lucitone 550‐L) was evaluated. Materials and methods: Rectangular bars of L were made (60 × 6 × 2 mm) and relined (2 mm) with the relining resins Ufi Gel Hard (UH) and Tokuso Rebase Fast (TR). Specimens relined with L and intact L, TR and UH specimens were also made (60 × 6 × 4 mm), for comparison. Before relining, the L surface was left untreated or wetted with methyl methacrylate monomer and/or the bonding agents (BA) supplied by manufacturers of the reline resins. V‐notches were machined at the midpoint of the length of all specimens. The notches were made either across the width (Nw) or across the thickness of the specimens (Nth). The Charpy impact test was performed using a 0.5‐J pendulum, which had been specially designed and constructed. Data were analysed separately for each notch position using one‐way analysis of variance and Tukey honestly significant difference post‐hoc test (p = 0.05). Results: The IS of L was similar to that of L/L. For the Nw notch, treating the denture base L with TR BA and relining with TR reline material produced the highest IS. Conclusion: The IS of specimens made from heat polymerising acrylic resin Lucitone 550 was increased after relining using the hard chairside reline resin TR with its proprietary BA.     

Effect of thermocycling on the flexural and impact strength of urethane-based and high-impact denture base resins

doi: 10.1111/j.1741‐2358.2011.00474.x
Effect of thermocycling on the flexural and impact strength of urethane‐based and high‐impact denture base resins Objective: Mechanical properties of the acrylic resins used for denture fabrication may be influenced by water and temperature. Thus, the aim of this study was to evaluate the effect of thermocycling on the flexural and impact strength of a high‐impact (Lucitone 199) and a urethane‐based denture material (Eclipse). Materials and methods: Flexural strength (64 × 10 × 3.3 mm) and impact strength (60 × 6 × 4 mm) specimens were made following the manufacturers’ instructions and assigned to two groups (n = 10): control (C) – not thermocycled – and T – thermocycled (5000 cycles between 5 and 55°C). Specimens were submitted to three‐point bending and Charpy impact tests. Results: Flexural strength (MPa) and impact strength (kJ/m²) data were analysed with two‐way anova (p = 0.05). The flexural strength of material Eclipse (C, 136.5; T, 130.7) was significantly higher than that of resin Lucitone 550 (C, 99.4; T, 90.1). Material Eclipse exhibited significantly higher impact strength (C, 6.9; T, 5.3) than the resin Lucitone 550 (C, 3.5; T, 3.0). For both materials, a significant decrease in flexural and impact strengths was observed when the specimens were thermocycled. Conclusion: Flexural and impact strengths were higher for Eclipse than for Lucitone 550, in both groups. Thermocycling decreased the flexural and impact strengths of Eclipse and Lucitone 550.     

The effect of long‐term disinfection procedures on hardness property of resin denture teeth

doi: 10.1111/j.1741‐2358.2011.00520.x The effect of long‐term disinfection procedures on hardness property of resin denture teeth Objective: The aim of the study was to evaluate the effect of long‐term disinfection procedures on the Vickers hardness (VHN) of acrylic resin denture teeth. Material and methods: Five acrylic resin denture teeth (Vipi Dent Plus‐V, Trilux–T, Biolux‐B, Postaris‐P and Artiplus‐A) and one composite resin denture teeth (SR‐Orthosit‐O) were embedded in heat‐polymerised acrylic resin within polyvinylchloride tubes. Specimens were stored in distilled water at 37°C for 48 h. Measurements of hardness were taken after the following disinfection procedures: immersion for 7 days in 4% chlorhexidine gluconate or in 1% sodium hypochlorite (CIm and HIm group, respectively) and seven daily cycles of microwave sterilisation at 650 W for 6 min (MwS group). In the WIm group, specimens were maintained in water during the time used to perform the disinfection procedures (7 days). Data were analysed with anova followed by the Bonferroni procedure (α = 0.01). Results: Microwave disinfection decreased the hardness of all acrylic resin denture teeth (p < 0.001). Immersion for 7 days in 4% chlorhexidine gluconate or distilled water had significant effect on the hardness of the acrylic resin denture teeth A (p < 0.01), and 1% sodium hypochlorite on teeth T (p < 0.01). All disinfection procedures decrease the hardness of the composite resin denture teeth (p < 0.01). Teeth O exhibited the highest and teeth V the lowest hardness values in the control group (p < 0.01). Conclusions: Disinfection procedures changed the hardness of resin denture teeth.     

Effect of the physical properties of acrylic resin of overnight immersion in sodium hypochlorite solution

doi:10.1111/j.1741‐2358.2009.00336.x
Effect of the physical properties of acrylic resin of overnight immersion in sodium hypochlorite solution Objectives: This study evaluated colour stability, surface roughness and flexural strength of microwave‐polymerised acrylic resin after overnight immersion in sodium hypochlorite, simulating 180 days use. Materials and methods: Forty disc‐shaped (15 mm × 4 mm) and 40 rectangular specimens (65 mm × 10 mm × 3 mm) were prepared from microwave‐polymerised acrylic resin. The specimens were immersed in 0.5, 1% sodium hypochlorite, Clorox/Calgon and distilled water. Colour measurements (ΔE) were determined by a portable colorimeter. A surface analyser was used to measure roughness (μm). The flexural strength (MPa) was measured using a three‐point bending test in a universal testing machine. Data were evaluated by one‐way anova , followed by Student–Newman–Keuls test (α = 0.05). Results: Statistical analysis found significantly higher colour changes (SNK, p < 0.001) for the 1% sodium hypochlorite, but mean ΔE value quantified by National Bureau of Standards was classified as slight. When comparing the surface roughness, no statistical significance was found among the solutions (anova , p = 0.637). The 1% sodium hypochlorite presented significantly lower flexural strength compared with the control group (SNK, p = 0.034). Conclusion: It was concluded that immersion in 1% sodium hypochlorite solutions for 8 h does influence the colour stability and flexural strength of microwave‐polymerised acrylic resin, during the simulated period of 180 days.     

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resin

doi: 10.1111/j.1741‐2358.2011.00604.x
Effect of the addition of silanated silica on the mechanical properties of microwave heat‐cured acrylic resin Objectives: The purpose of this study was to evaluate fthe flexural strength and Vickers hardness of a microwave energy heat‐cured acrylic resin by adding different concentrations of silane surface‐treated nanoparticle silica. Methods: Acrylic resin specimens with dimensions of 65 × 10 × 2.5 mm were formed and divided into five experimental groups (n = 10) according to the silica concentration added to the acrylic resin mass (weight %) prior to polymerisation : G1, without silica; G2, 0.1% silica; G3, 0.5% silica; G4, 1.0% silica; and G5, 5.0% silica. The specimens were submitted to a three‐point flexural strength test and to the Vickers hardness test (HVN). The data obtained were statistically analysed by anova and the Tukey test (α = 0.05). Results: Regarding flexural strength, G5 differed from the other experimental groups (G1, G2, G3 and G4) presenting the lowest mean, while G4 presented a significantly higher mean, with the exception of group G3. Regarding Vickers hardness, a decrease in values was observed, in which G1 presented the highest hardness compared with the other experimental groups. Conclusion: Incorporating surface‐treated silica resulted in direct benefits in the flexural strength of the acrylic resin activated by microwave energy; however, similar results were not achieved for hardness.     

Bond strength of denture teeth to acrylic resin: effect of thermocycling and polymerisation methods

Background: Failure of bonding between acrylic resin teeth and denture base material is a considerable problem for patients who wear complete dentures. Objective: The purpose of this study was to evaluate the bond strength between acrylic resins and resin denture teeth with different thermocycling and polymerisation methods. Materials and methods: Microwave‐polymerised (Onda‐Cryl), heat‐polymerised (Clássico) and autopolymerising (Jet) acrylic resins and resin denture tooth (Biotone) were used. The acrylic resins were polymerised according to the following: (A) microwave – fast cycle, Onda‐Cryl; (B) microwave – long cycle, Onda‐Cryl; (C) microwave – manufacturer’s cycle, Onda‐Cryl; (T) water bath – long cycle, Clássico; and (Q) bench polymerisation cycle, Jet. Twenty specimens were prepared for each polymerisation method. Ten were thermocycled, and 10 did not receive thermocycling. For the purpose of the study, a shear test was used. Data were analysed with the Kruskal–Wallis test and Dunn’s multiple comparisons test (p = 0.05). Results: Cycles B, C and T were similar (p > 0.05), and had statistically higher bonding values than cycles A and Q (p < 0.05) for the thermocycled and non‐thermocycled groups. For all cycles, there were no statistically significant differences between thermocycled and non‐thermocycled groups (p > 0.05), except for cycle Q (p = 0.0038). Conclusion: Thermocycling decreased the bond strength, but not significantly for microwave and heat‐polymerised cycles. Regarding the bond strength of denture teeth to acrylic resin, the fast microwave polymerisation cycle should be avoided when polymerising Onda‐Cryl acrylic resin. In addition, Jet acrylic resin is not adequate for use in denture repair.     

Effect of microwave treatment on the shear bond strength of different types of commercial teeth to acrylic resin

doi:10.1111/j.1741‐2358.2009.00333.x
Effect of microwave treatment on the shear bond strength of different types of commercial teeth to acrylic resin Objective: The purpose of this study was to verify the effect of microwave treatment on the shear bond strength of commercial types of teeth to acrylic resin, when the glossy ridge laps were unmodified (groups 1 and 5), bur abraded (groups 2 and 6), bur grooved (groups 3 and 7) or etched by monomer (groups 4 and 8). Background: Controversial findings have shown that mechanical or chemical changes in ridge‐lap surface of the tooth increase or decrease the bond strength between tooth and acrylic resin, and the microwave disinfection may cause different changes on this bond strength. Materials and methods: Eighty specimens (n = 10) were made with the acrylic resin bonded to tooth glossy ridge lap, polymerised in water at 74°C for 9 h, and deflasked after flask cooling. Specimens of the groups 5, 6, 7 and 8 were individually immersed in 150 ml of water and submitted to microwave treatment in an oven at 650 W for 3 min. Control specimens (groups 1, 2, 3 and 4) were not microwave treated. Shear bond strength test was performed in an Instron machine with a cross‐speed of 1 mm/min. Collected data were submitted to anova and Tukey’s test (α = 0.05). Results: Microwave treatment decreased the shear bond strength values of the tooth/resin bond. In the microwaved and non‐microwaved procedures, mechanical retention improved the shear bond strength when compared with the control and monomer treatments. Conclusion: Shear bond strength of the tooth/resin bond was influenced by the microwave treatment and different commercial teeth association, and was lower for the Biotone tooth.     

Evaluation of the flexural strength and elastic modulus of resins used for temporary restorations reinforced with particulate glass fibre

doi: 10.1111/j.1741‐2358.2010.00410.x
Evaluation of the flexural strength and elastic modulus of resins used for temporary restorations reinforced with particulate glass fibre Objective: The flexural strength and the elastic modulus of acrylic resins, Dencor, Duralay and Trim Plus II, were evaluated with and without the addition of silanised glass fibre. Materials and methods: To evaluate the flexural strength and elastic modulus, 60 test specimens were fabricated with the addition of 10% ground silanised glass fibres for the experimental group, and 60 without the incorporation of fibres, for the control group, with 20 test specimens being made of each commercial brand of resin (Dencor, Duralay and Trim Plus II) for the control group and experimental group. After the test specimens had been completed, the flexural strength and elastic modulus tests were performed in a universal testing device, using the three‐point bending test. For the specimens without fibres the One‐Way Analysis of Variance and the complementary Tukey test were used, and for those with fibres it was not normal, so that the non‐parametric Mann‐Whitney test was applied. Results: For the flexural strength test, there was no statistical difference (p > 0.05) between each commercial brand of resin without fibres [Duralay 84.32(±8.54), Trim plus 85.39(±6.74), Dencor 96.70(±6.52)] and with fibres (Duralay 87.18, Trim plus 88.33, Dencor 98.10). However, for the elastic modulus, there was statistical difference (p > 0.01) between each commercial brand of resin without fibres [Duralay 2380.64 (±168.60), Trim plus 2740.37(±311.74), Dencor 2595.42(±261.22)] and with fibres (Duralay 3750.42, Trim plus 3188.80, Dencor 3400.75). Conclusion: The result showed that the incorporation of fibre did not interfere in the flexural strength values, but it increased the values for the elastic modulus.     

Bonding acrylic teeth to acrylic resin denture bases: a review

Partial or complete dentures are more commonly constructed for the elderly group of the population. Teeth debonding from the dentures can be frustrating to the patients as well as the dentist. Research has been carried out and is continuing to study the issue of bonding acrylic teeth to the denture base resin. The present review takes into account the majority of research papers published in the last five decades for determining the bond strength. Selection of more compatible combinations of denture base resins and acrylic teeth may reduce the number of prosthesis fractures and the resultant repairs.     

Effect of disinfection and storage on the flexural strength of ocular prosthetic acrylic resins

doi: 10.1111/j.1741‐2358.2011.00570.x Effect of disinfection and storage on the flexural strength of ocular prosthetic acrylic resins Objective: To evaluate the influence of chemical disinfection and storage duration on the flexural strength of acrylic resins commonly used to make ocular prostheses. Methods: A total of 260 samples were manufactured with N1 resin and colourless resin. Both resins were thermopolymerised using a microwave oven. Samples were stored and periodically disinfected and were divided into groups: control (no disinfection) (I), neutral soap (II), Opti‐free (III), Efferdent (IV), 1% hypochlorite (V) or 4% chlorhexidine (VI). The flexural strength was measured before and after 60 and 120 days of storage. Data were analysed by anova and Tukey test (0.05). Results: The flexural strength of the N1 resin was higher than that for the colourless resin. There was a significant difference in the flexural strength before and after 60 and 120 days of storage with disinfection, regardless of the resin and disinfectant. Group I in the initial period exhibited greater flexural strength, with significant difference only in group VI after 120 days. Conclusion: It can be concluded that the flexural strength only changed after 120 days of storage for samples disinfected with chlorhexidine. However, all flexural strength values obtained herein were acceptable clinical limits for the acrylic resins.     

Effect of repeated microwave disinfections on bonding of different commercial teeth to resin denture base

doi: 10.1111/j.1741‐2358.2011.00516.x Effect of repeated microwave disinfections on bonding of different commercial teeth to resin denture base Objective: To verify the influence of repeated microwave disinfections on the shear bond strength of two commercial types of teeth to acrylic resin, when the ridge lap surfaces were unmodified, bur abraded, bur grooved or etched by monomer. Material and methods: Eighty specimens (n = 10) were adhered to the tooth ridge lap surface, polymerised in a water bath at 74°C for 9 h. Microwaved specimens were individually immersed in 150 ml of water and submitted to five simulated disinfections in a microwave oven calibrated at 650 W for 3 min. Control specimens were not microwave treated. Shear bond strength tests were performed in an Instron machine with a cross‐speed of 1 mm/min. The fracture load values were transformed into shear bond strength as a function of the bonding area (0.28 cm²). Data were submitted to anova and Tukey’s test (α = 0.05). Fractured areas were classified as adhesive, cohesive (resin or tooth) or mixed failures. Results: Repeated microwave disinfections increased the shear strength of the tooth/resin bond. Mechanical retention in microwaved and non‐microwaved procedures improved the shear bond strength. Conclusions: The different commercial types of teeth influenced shear bond strength values, with Biotone teeth showing the lower values.     

Fatigue resistance of acrylic resin denture base material reinforced with E-glass fibres

doi: 10.1111/j.1741‐2358.2011.00548.x
Fatigue resistance of acrylic resin denture base material reinforced with E‐glass fibres Objective: The purpose of the study was to determine the effect of different forms and concentrations (2.5, 3, 4, 5% by volume) of glass fibres (chopped strand mat, continuous and woven) on fatigue resistance of acrylic denture base resin. Material and Methods: The fatigue resistance was measured by applying repeated three‐point bending deflection to the specimens, the cycle frequency of 1.05 g and magnitude of deflection of 2.0 mm. The number of loading cycles needed to cause a fracture in the test specimen was considered the fatigue resistance of the specimen. Results: The results of this study revealed that the addition of three different glass fibre forms at all concentrations to acrylic resin did not produce a statistically significant increase in the fatigue resistance (p ≥ 0.05). This study also revealed that there were significant differences (p < 0.05) between glass fibres forms used concerning the effects on the fatigue resistance. Conclusion: This study showed that the woven glass fibres had a definite superiority over the chopped fibres and the continuous fibres in regard to the fatigue resistance of the acrylic denture base resin.     

Antimicrobial and mechanical properties of acrylic resins with incorporated silver-zinc zeolite - part I

Objective: The purpose of this in vitro study was to evaluate the antimicrobial activity of acrylic resins containing different percentages of silver and zinc zeolite, and to assess whether the addition of zeolite alters the flexural and impact strength of the resins. Background: The characteristics of acrylic resins support microorganism development that can threaten the health of the dentures user. Material and methods: A microwave‐polymerised (Onda‐Cryl) and two heat‐polymerised (QC20 and Lucitone 550) acrylic resins were used. The materials were handled according to the manufacturers’ instructions. Fifty rectangular‐shaped specimens (8 × 10 × 4mm) were fabricated from each resin and assigned to 5 groups (n = 10) according to their percentage of Irgaguard B5000 silver–zinc zeolite (0%– control, 2.5%, 5.0%, 7.5% and 10%). Flexural strength and Izod impact strength were evaluated. The antimicrobial activity against two strains of Candida albicans and two strains of Streptococcus mutans was assessed by agar diffusion method. Data were analysed statistically by one‐way anova and Tukey’s test at 5% significance level. Results: The addition of 2.5% of Irgaguard B5000 to the materials resulted in antimicrobial activity against all strains. Flexural strength decreased significantly with the addition of 2.5% (QC20 and Lucitone 550) and 5.0% (Onda‐Cryl) of Irgaguard B5000. The impact strength decreased significantly with the addition of 2.5% (Lucitone 550) and 5.0% (QC20 and Onda‐Cryl) of zeolite. Conclusion: The addition of silver–zinc zeolite to acrylic resins yields antimicrobial activity, but may affect negatively the mechanical properties, depending on the percentage of zeolite.     

The occurrence of porosity in reline acrylic resins. Effect of microwave disinfection

Background: Microwave energy has proved to be an effective method for disinfecting acrylic dentures. However, the effect of microwave heating on the porosity of autopolymerising denture reline resins has not been investigated. Objective: The purpose of the study was to determine the effect of microwave disinfection on the porosity of autopolymerised denture reline materials (Kooliner‐K, New Truliner‐NT, Tokuso Rebase Fast‐TR and Ufi Gel Hard‐UGH) and a conventional heat‐polymerised denture base resin (Lucitone 550‐L). Material and methods: Specimens (10 mm × 20 mm × 1 mm) were obtained from the impression surface of the palatal mucosa in a single person and divided into four groups (n = 5). The porosity was evaluated after polymerisation (C1), after two cycles of microwave disinfection (MW2), after seven cycles of microwave disinfection (MW7) and after 7 days storage in water at 37°C (C2). Specimens from group MW7 were exposed to microwave disinfection daily being stored in water at 37°C between exposures. All the replicas were sputter coated with gold and micrographs/digital images were taken of each replica using scanning electron microscopy at magnification × 100. The SEM micrographs were then examined using an image analyser to determine the number of pores. Comparison between materials and groups were made using Kruskal–Wallis tests. Results: MW7 resulted in a significant increase in the number from the pores of material K, but decreased in number in reline material TR and UGH reline resin. The number of pores in materials NT and L remained unaffected following microwave disinfection. Conclusion: Differences in the porosity amongst the materials and for different experimental conditions were observed following microwave disinfection.     

Effect of long-term water immersion on the fracture toughness of denture base and reline resins

doi: 10.1111/j.1741‐2358.2011.00573.x
Effect of long‐term water immersion on the fracture toughness of denture base and reline resins purpose: This study evaluated the fracture toughness (FT) of one denture base (Lucitone 550 – L) and four hard reline resins [Ufi Gel Hard (UH), Tokuyama Rebase II (TR), New Truliner (NT) and Kooliner (K)], and the effect of long‐term water storage on this property. Materials and methods: Forty specimens (40 × 8 × 4 mm) of each material were made, and FT was assessed after polymerisation (control of reliners), after 48 ± 2 h in water at 37°C (control of denture base resin) and after storage in water at 37°C for 7, 90 or 180 days (all materials). Data (MPa.m^1/2) were analysed by two‐way anova and Games–Howell test (p = 0.05). Results: Resin L exhibited the highest FT mean values. After 180 days of storage, FT mean values of L (3.37), UH (1.53) and K (1.20) were higher than those of the other periods. FT mean values of NT decreased from control (1.63) to 7 days (1.30) and then remained constant. FT mean values of TR (1.13) were similar in all periods of analysis. Conclusion: The denture base resin L showed higher FT mean values than the reline resins. Long‐term water storage increased the FT of L, UH and K, reduced the FT of NT and did not influence the FT of TR.     

Effect of toothbrushing, chemical disinfection and thermocycling procedures on the surface microroughness of denture base acrylic resins

doi: 10.1111/j.1741‐2358.2011.00582.x Effect of toothbrushing, chemical disinfection and thermocycling procedures on the surface microroughness of denture base acrylic resins Objective: This study verified the surface microroughness of denture acrylic resins submitted to toothbrushing, chemical disinfection and thermocycling procedures. Material and methods: Samples were prepared according to conventional, microwaved and boiled resins and submitted to microroughness measurements before and after procedures using a profilometer (Ra). Data were subjected to anova and Tukey’s test (5%). Results: Before thermocycling, a difference was found among treatments for microwaved and boiled resins, with greater values for toothbrushing and lower values for Efferdent and hypochlorite; control was intermediate. Differences among resins were observed for treatments, with higher values for boiled resin and lower values for conventional and microwaved resins. After thermocycling, differences were found for microwaved resin, with a higher value for toothbrushing and a lower value for Efferdent and hypochlorite; control was intermediate. Tooth‐brushed boiled resin presented higher values and hypochlorite lower values; control and Efferdent were intermediates. Differences among resins were seen for treatments, with higher values for boiled resin and lower values for conventional and microwaved resins. Boiled resin presented differences for toothbrushing and hypochlorite, before and after thermocycling procedures were compared. Conclusions: For microwaved and boiled resins, toothbrushing and chemical disinfection promoted different levels of surface microroughness when associated or not with thermocycling.     

Correlation between factors associated with the removable partial dentures use and Candida spp. in saliva

doi: 10.1111/j.1741‐2358.2010.00390.x
Correlation between factors associated with the removable partial dentures use and Candida spp. in saliva Objectives: To correlate the presence and number of Candida spp. in the saliva of wearers of removable partial dentures retained with precision attachments with the proportion of metal/acrylic resin present in the dentures. Methods: Saliva samples from 40 removable partial denture wearers (test) and one paired sample of individuals, non‐wearers of any type of removable denture (control) were collected, seeded, and the colony forming units of Candida counted and identified. The metal/acrylic resin proportion of each denture was quantified, using silicone plates pressed over each denture. Results: Candida spp. was found in the saliva of 80% of the individuals in the test group and 65% of the control, with C. albicans being the most prevalent species. The test group presented with the highest number of colony forming units of Candida per ml of saliva, and there was weak correlation between this number and the metal and resin area of the denture (Pearson’s coefficient of correlation). Greater prevalence and a higher number of colony forming units of Candida per ml of saliva occurred in removable partial denture wearers (p = 0.04) with a weak positive correlation between the metal and resin area and the number of colony forming units of Candida per ml of saliva. However, this correlation was more significant for the area of resin.