Removal of As(V) from water by pectin based active hydrogels following geochemical approach

Fe(II)-loaded pectin based hydrogels were used to remove As(V) from water. The hydrogels were synthesized by crosslinking pectin 'as such' or in the presence of 2-acrylamido-2-methylpropanesulphonic acid and three crosslinkers. The hydrogels crosslinked with 5% glutaraldehyde showed the maximum uptake of both Fe(II) and As(V). The sorption of As(V) was found to be sensitive to pH and temperature changes, as the maximum sorption was observed at 35 degrees C and 7.0-9.2 pH.     

Synthesis and hydration properties of pH-sensitive p(HEMA)-based hydrogels containing 3-(trimethoxysilyl)propyl methacrylate

An amphiphilic hydrogel network was synthesized from a cross-linked poly(2-hydroxyethyl methacrylate) backbone copolymerized with the monomers 3-(trimethoxysilyl)propyl methacrylate (PMA) and dimethylaminoethyl methacrylate (DMAEMA) using tetraethylene glycol diacrylate (TEGDA) as cross-linker and using the radical initiator system comprising N,N,N',N'-tetramethylethylenediamine and ammonium peroxydisulfate. The degree of hydration of hydrogel slabs was investigated as functions of varying monomer compositions and cross-link density and as a function of pH and ionic strength of the bathing medium. As much as a 45% increase in hydration was observed for hydrogels containing 15 mol % DMAEMA upon reducing the pH of the bathing medium from 8.0 to 2.0. This confirms the pH-modulated swelling of amine-containing hydrogels. Increasing the concentration of TEGDA cross-linker from 3 to 12 mol % in a 10 mol % DMAEMA-containing hydrogel resulted in only a 10% reduction in the degree of hydration of the gel. There was, however, a 40-50% reduction in the degree of hydration of a 15 mol % DMAEMA hydrogel upon increasing the molar composition of PMA from 0 up to 20 mol %. The presence of PMA confers hydrophobic character that reduces hydration and introduces additional cross-links that reduce network mesh size. The water content of the hydrogel was consistently higher in buffers of lower ionic strength. The reversible pH-dependent swelling observed in these studies, along with the control of cross-link density afforded by the PMA component, endows these biocompatible materials with potential for use in pH-controlled drug delivery of more hydrophobic drugs and present new compositions for in vitro and in vivo biocompatibility studies.     

Antibacterial activity and biocompatibility of a chitosan-γ-poly(glutamic acid) polyelectrolyte complex hydrogel

In this study, we prepared a polyelectrolyte complex (PEC) hydrogel comprising chitosan as the cationic polyelectrolyte and γ-poly(glutamic acid) (γ-PGA) as the anionic polyelectrolyte. Fourier transform infrared spectroscopy revealed that ionic complex interactions existed in the chitosan-γ-PGA PEC hydrogels. The compressive modulus increased upon increasing the degree of complex formation in the chitosan-γ-PGA PEC hydrogel; the water uptake decreased upon increasing the degree of complex formation. At the same degree of complex formation, the compressive modulus was larger for the chitosan-dominated PEC hydrogels; the water uptake was larger for the γ-PGA-dominated ones. Scanning electron microscopy images revealed the existence of interconnected porous structures (pore size: 30-100 μm) in all of the chitosan-γ-PGA PEC hydrogels. The chitosan-γ-PGA PEC hydrogels also exhibited antibacterial activity against Escherichia coli and Staphylococcus aureus. In addition, in vitro cell culturing of 3T3 fibroblasts revealed that all the chitosan-γ-PGA PEC hydrogels were effective in promoting cell proliferation, especially the positively charged ones (chitosan-dominated). Therefore, the chitosan-γ-PGA polyelectrolyte hydrogel appears to have potential as a new material for biomedical applications.     

Removal of methylene blue dye from aqueous solution by adsorption onto sodium humate/polyacrylamide/clay hybrid hydrogels

A type of novel hybrid hydrogels from sodium humate (SH), polyacrylamide (PAM), and hydrophilic laponite clay were prepared using potassium persulfate (KPS) as the initiator and N,N'-methylenebisacrylamide (MBA) as the cross-linker. The morphology of the hydrogels was characterized by field emission scanning electron microscope (FESEM). The adsorption-desorption kinetics of methylene blue (MB) were also investigated. It was shown that SH/PAM/clay hydrogels exhibited excellent performance in MB adsorption. The maximum absorption concentration of MB was 800 mg/l/g of hydrogel. The adsorption concentration of hydrogels increased with increasing SH or clay content. Less MB were desorbed with increasing SH content, while the clay content had no significant influence on the amount of MB desorbed. This effect was attributed to the formation of a ionic complex between the imine groups of MB and the ionized carboxylic groups of SH. MB diffusion process was dominant in MB desorption.     

Purification of His-tagged proteins using Ni2+-poly(2-acetamidoacrylic acid) hydrogel

In this study, a new matrix for immobilized metal affinity chromatography (IMAC) using poly(2-acetamidoacrylic acid) (PAAA) hydrogels complexed with Ni(2+) was developed for the purification of the recombinant histidine-tagged green fluorescence protein (His6-GFP). The Ni(2+)-complexed PAAA hydrogel was prepared by polymerizing 2-acetamidoacrylic acid (AAA) and 2,2'-[(1,4-dioxo-1,4-butanediyl)diamino] bis(2-propenoic acid) (DBDBPA) with potassium persulfate in DMSO, followed by Ni(2+) complexation. Confocal laser scanning microscopy was used to determine the binding of His6-GFP to the Ni(2+)-PAAA hydrogel in three-dimensional space. Photoluminescence spectroscopy revealed an 81% binding efficiency of His6-GFP to the Ni(2+)-PAAA hydrogel yielded with a recovery of 59%. The specificity of His6-GFP binding to Ni(2+)-PAAA hydrogel was compared with that of the PAAA hydrogel without Ni(2+). His6-GFP was purified directly from the cell lysate with Ni(2+)-PAAA hydrogel matrix but the PAAA hydrogel without Ni(2+) had no effect. The major advantage of the Ni(2+)-PAAA hydrogel system over current methods, such as Ni-nitrilotriacetic acid (NTA) agarose beads, was the simple and low-cost procedure for preparing the matrix.     

Synthesis and characterization of novel guar gum hydrogels and their use as Cu sorbents

To prepare novel hydrogels for use in water technologies, guar gum was subjected to acid hydrolysis. The depolymerized guar gum obtained there from and the native guar gum were oxidized to their respective polycarboxylic forms using NO_x as oxidant. All these polymers were crosslinked with N,N-methylenebisacrylamide, and were used as Cu²⁺ sorbents. The candidate hydrogel exhibiting the highest uptake was used further to investigate the effect of external stimuli on sorption. The sorption on hydrogels was fast as the highest sorption was observed after 2 h at 40 °C and 20 ppm of Cu²⁺ ions. The hydrogel prepared from the oxidized guar gum afforded the maximum sorption capacity of 125.893 mg g⁻¹. Langmuir and Freundlich isotherms, and pseudo second order kinetics matches the experimental data. The evidence of sorption was obtained by characterizing Cu²⁺-loaded hydrogels by FTIR spectroscopy.     

Iron uptake by hepatopancreas brush border membrane vesicles (BBMV) of the lobster (Homarus americanus)

The uptake of (55)Fe(2+) and solubilized (55)Fe(3+) into brush border membrane vesicles prepared from the hepatopancreas of the Atlantic lobster (Homarus americanus) was investigated. Non-specific surface binding of (55)Fe(2+) at equilibrium to the vesicular surface approximated 57% of total (55)Fe(2+) uptake. (55)Fe(2+) uptake showed temperature sensitivity and was trans-stimulated by a Ca(2+) gradient (at 5mM) directed out. Equilibrated (59)Fe(2+) exchanged for both Cd(2+) and cold Fe(2+). The data obtained in this study are suggestive that at least a portion of ferrous iron absorption may occur by a divalent exchanger mechanism.     

The use of N,N'-diallylaldardiamides as cross-linkers in xylan derivatives-based hydrogels

N,N′-Diallylaldardiamides (DA) were synthesized from galactaric, xylaric, and arabinaric acids, and used as cross-linkers together with xylan (X) derivatives to create new bio-based hydrogels. Birch pulp extracted xylan was derivatized to different degrees of substitution of 1-allyloxy-2-hydroxy-propyl (A) groups combined with 1-butyloxy-2-hydroxy-propyl (B) and/or hydroxypropyl (HP) groups. The hydrogels were prepared in water solution by UV induced free-radical cross-linking polymerization of derivatized xylan polymers without DA cross-linker (xylan derivative hydrogel) or in the presence of 1 or 5 wt % of DA cross-linker (DA hydrogel). Commercially available cross-linker (+)-N,N′-diallyltartardiamide (DAT) was also used. The degree of substitution (DS) of A, B, and HP groups in xylan derivatives was analyzed according to ¹H NMR spectra. The DS values for the cross-linkable A groups of the derivatized xylans were 0.4 (HPX-A), 0.2 (HPX-BA), and 0.4 (X-BA). The hydrogels were examined with FT-IR and elemental analysis which proved the cross-linking successful. Water absorption of the hydrogels was examined in deionized water. Swelling degrees up to 350% were observed. The swollen morphology of the hydrogels was assessed by scanning electron microscopy (SEM). The presence of cross-linkers in DA hydrogels had only a small impact on the water absorbency when compared to xylan derivative hydrogels but a more uniform pore structure was achieved.     

Application of Chitin Hydrogels for Seed Germination,Seedling Growth of Rapeseed

Chitin hydrogels were successfully prepared from chitin solution dissolved in NaOH/urea aqueous solution at low temperature by crosslinking with epichlorohydrin. The experimental results indicated that the chitin hydrogels were hydrophilic, had a microporous structure, and had a large surface area, leading to excellent water uptake ability and water-retention properties. Moreover, they exhibited good mechanical properties and a high equilibrium swelling ratio. The growth indexes of rapeseed, including the germination rate, root length, shoot length, fresh weight and dry weight, for chitin hydrogel (CG2) were not significantly different from those of soil and significantly higher than agar. Chitin hydrogel as a plant growth regulator could promote seed germination and growth when applied to Brassica napus rapeseed sowing. Moreover, chitin was safe and biodegradable so it would be suitable to use as soilless culture media for plant growth. This work provided a new pathway for the application of chitin hydrogels in the agriculture field.     

Synthesis and properties of thermo- and pH-sensitive poly(N-isopropylacrylamide)/polyaspartic acid IPN hydrogels

Various interpenetrating polymer network (IPN) hydrogels with sensitivity to temperature and pH were prepared by introducing the pH-sensitive polymer polyaspartic acid (PASP) hydrogel, into the poly(N-isopropylacrylamide) (PNIPAAm) hydrogel system for the purpose of improving its response rate to temperature. The morphologies and thermal behavior of the prepared IPN hydrogels were studied by both scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). The IPN hydrogels showed a large and uneven porous network structure, without showing the common PNIPAAm hydrogel structure. The paper moreover studied their swelling properties, such as temperature dependence of equilibrium swelling ratio, shrinking kinetics, re-swelling kinetics and oscillatory swelling behavior in water. The swelling experiment results revealed that IPN hydrogels exhibited much faster shrinking and re-swelling in function of the composition ratio of the two network components. These fast responsive hydrogels foster potential applications in biomedical and biotechnology fields.     

Preparation and characterization of a novel pH-sensitive chitosan-g-poly (acrylic acid)/attapulgite/sodium alginate composite hydrogel bead for controlled release of diclofenac sodium

A series of pH-sensitive composite hydrogel beads composed of chitosan-g-poly (acrylic acid)/attapulgite/sodium alginate (CTS-g-PAA/APT/SA) was prepared as drug delivery matrices crosslinked by Ca²⁺ owing to the ionic gelation of SA. The structure and surface morphology of the composite hydrogel beads were characterized by FTIR and SEM, respectively. pH-sensitivity of these composite hydrogels beads and the release behaviors of drug from them were investigated. The results showed that the composite hydrogel beads had good pH-sensitivity. The cumulative release ratios of diclofenac sodium (DS) from the composite hydrogel beads were 3.76% in pH 2.1 solution and 100% in pH 6.8 solutions within 24 h, respectively. However, the cumulative release ratio of DS in pH 7.4 solution reached 100% within 2 h. The DS cumulative release ratio reduced with increasing APT content from 0 to 50 wt%. The drug release was swelling-controlled at pH 6.8.     

Synthesis and characterization of biodegradable cationic poly(propylene fumarate-co-ethylene glycol) copolymer hydrogels modified with agmatine for enhanced cell adhesion

We synthesized positively charged biodegradable hydrogels by cross-linking of agmatine-modified poly(ethylene glycol)-tethered fumarate (Agm-PEGF) and poly(propylene fumarate-co-ethylene glycol) (P(PF-co-EG)) to investigate the effect of the guanidino groups of the agmatine on hydrogel swelling behavior and smooth muscle cell adhesion to the hydrogels. The weight swelling ratio of these hydrogels at pH 7.0 increased from 279 +/- 4 to 306 +/- 7% as the initial Agm-PEGF content increased from 0 to 200 mg/g of P(PF-co-EG), respectively. The diffusional exponents, n, during the initial phase of water uptake were independent of the initial Agm-PEGF content and were determined to be 0.66 +/- 0.08, 0.71 +/- 0.07, and 0.60 +/- 0.05 for respective initial Agm-PEGF contents of 0, 100, and 200 mg/g. The heat of fusion of water present in the hydrogels increased from 214 +/- 11 to 254 +/- 4 J/g as the initial Agm-PEGF content increased from 0 to 200 mg/g. The number of adherent smooth muscle cells increased dose-dependently from 15 +/- 6 to 75 +/- 7% of the initial seeding density as the initial Agm-PEGF content increased from 0 to 200 mg/g. These results suggest that the incorporation of the guanidino groups of agmatine into P(PF-co-EG) hydrogels increases the hydrogel free water content and the total water content of the hydrogels and also enhances cell adhesion to the hydrogels.     

Preparation of pH- and ionic-strength responsive biodegradable fumaric acid crosslinked carboxymethyl cellulose

A novel biodegradable sodium carboxymethyl cellulose (NaCMC)-based hydrogel was synthesized by using fumaric acid (FA) as a crosslinking agent at various ratios. Hydrogels (CMCF) were characterized using Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Swelling behaviors of hydrogels were investigated in distilled water, various salt, and pH solutions. The FTIR results indicated the crosslinking between carboxyl groups of FA with hydroxyl group of NaCMC through ester formation. AFM analyses showed that roughness of hydrogel surface decreased with increasing crosslinker concentration. The swelling capacity decreased with an increase in charge of the metal cation (Al(3+)相似文献   

Biodegradable superabsorbent hydrogels derived from cellulose by esterification crosslinking with 1,2,3,4-butanetetracarboxylic dianhydride

Superabsorbent hydrogels were prepared from native celluloses dissolved in lithium chloride and N-methyl-2-pyrrolidinone (LiCl/NMP) by esterification crosslinking with 1,2,3,4-butanetetracarboxylic dianhydride (BTCA). Subsequent conversion of the unreacted carboxyl groups to sodium carboxylates by the addition of aqueous NaOH was performed to enhance the water affinity of the gels. The absorbency of the products was strongly dependent on the amount of BTCA that was esterified to cellulose, and the highest absorbency was observed for the hydrogel composed of approximately 0.25 molecules of BTCA per anhydroglucose unit (AGU) of cellulose. Furthermore, it was confirmed that the absorbency was enhanced as the average degree of polymerization (DP) of the starting cellulose increased. The use of cotton cellulose with a high DP of about 2400 produced a hydrogel with an absorbency of 720 times its dry weight, which exceeded the absorbency of commercial crosslinked sodium polyacrylate superabsorbent hydrogel (SPA). The hydrogels exhibited good biodegradability, with a maximum degradation of 95% within 7 days using cellulase.     

Preparation and properties of a pH/temperature-responsive carboxymethyl chitosan/poly(N-isopropylacrylamide)semi-IPN hydrogel for oral delivery of drugs

Thermo- and pH-responsive semi-IPN polyampholyte hydrogels were prepared by using carboxymethylchitosan and poly(N-isopropylacrylamide) with N,N'-methylenebisacrylamide (BIS) as the crosslinking agent. The swelling characteristics of these hydrogels at distinct compositions as a function of pH and temperature were investigated. It was found that the semi-IPN hydrogels demonstrated the pH- and temperature-responsive nature of the materials, and it also showed good reversibility. The study on the release of coenzyme A (CoA) showed that within 24h the cumulative release ratio of CoA was 22.6% in pH 2.1 solution and 89.1% in pH 7.4 solution at 37 degrees C, respectively. The release rate of CoA was higher at 37 degrees C than 25 degrees C in a pH 7.4 buffer solution. An increased release rate of CoA was observed with the content of carboxymethylchitosan increasing in the hydrogel at 25 degrees C in pH 7.4 solution. These results show that semi-IPN hydrogel seems to be of great promise in pH-temperature oral drug delivery systems.     

Entrapment and in vitro release of delta-sleep inducing peptide from polymer hydrogels based on modified polyvinyl alcohol

The aim of this study was to entrap delta-sleep inducing peptide (DSIP) in cross-linked poly(vinyl alcohol)-based hydrogels of different structures and to determine kinetics of the peptide release from these hydrogels using an in vitro model. Isotropic and macroporous hydrogels based on poly(vinyl alcohol) acrylic derivative (Acr-PVA) and also macroporous epoxy groups containing hydrogels synthesized by copolymerization of this macromer and glycidyl methacrylate, have been used in this study. Isotropic hydrogels were prepared at positive temperatures while macroporous ones were obtained by formation in cryo-conditions. The peptide was entrapped into macroporous PVA hydrogels by adding the peptide solution onto preformed matrices, while peptide immobilization on PVA-GMA hydrogels, containing free epoxy groups, was carried out by sorption of peptide from its aqueous solution. In the case of DSIP entrapment into isotropic PVA gel the peptide solution was added into the polymer mixture at hydrogel formation. The kinetics of peptide release from hydrogels was studied by incubating matrices in PBS solution (pH 7.4), in physiological solution (0.9% NaCl) and in water. DSIP concentration in supernatants was determined by reverse-phase HPLC. Incubation of macroporous PVA gels in PBS, 0.9% NaCl, and water for 30 min caused release of 74, 70, and 64% DSIP, respectively, and this processes completed within 3 h. From hydrogel containing epoxy groups the release of neither peptide nor its degradation products was observed even after incubation for 48 h. For freshly prepared isotropic hydrogel the release kinetics was as follows: 27 and 78% DSIP were released within first 30 min and 33 h, relatively. For the lyophilized hydrogel samples the peptide release was 63% after incubation for 30 min, while drying of samples at room temperature for 3 days caused significant peptide loss because of its structure damage.     

Synthesis and degradation test of hyaluronic acid hydrogels

Hyaluronic acid (HA) hydrogels prepared with three different crosslinking reagents were assessed by in vitro and in vivo degradation tests for various tissue engineering applications. Adipic acid dihydrazide grafted HA (HA-ADH) was synthesized and used for the preparation of methacrylated HA (HA-MA) with methacrylic anhydride and thiolated HA (HA-SH) with Traut's reagent (imminothiolane). (1)H NMR analysis showed that the degrees of HA-ADH, HA-MA, and HA-SH modification were 69, 29, and 56 mol%, respectively. HA-ADH hydrogel was prepared by the crosslinking with bis(sulfosuccinimidyl) suberate (BS(3)), HA-MA hydrogel with dithiothreitol (DTT) by Michael addition, and HA-SH hydrogel with sodium tetrathionate by disulfide bond formation. According to in vitro degradation tests, HA-SH hydrogel was degraded very fast, compared to HA-ADH and HA-MA hydrogels. HA-ADH hydrogel was degraded slightly faster than HA-MA hydrogel. Based on these results, HA-MA hydrogels and HA-SH hydrogels were implanted in the back of SD rats and their degradation was assessed according to the pre-determined time schedule. As expected from the in vitro degradation test results, HA-SH hydrogel was in vivo degraded completely only in 2 weeks, whereas HA-MA hydrogels were degraded only partially even in 29 days. The degradation rate of HA hydrogels were thought to be controlled by changing the crosslinking reagents and the functional group of HA derivatives. In addition, the state of HA hydrogel was another factor in controlling the degradation rate. Dried HA hydrogel at 37 degrees C for a day resulted in relatively slow degradation compared to the bulk HA hydrogel. There was no adverse effect during the in vivo tests.     

Drug loading into and drug release from pH- and temperature-responsive cylindrical hydrogels

Hydrogels that undergo deformation upon appropriate changes in pH or temperature have considerable promise as drug delivery vehicles. Drug uptake in swelling and nonswelling cylindrical hydrogels and drug release from these into a target fluid are investigated here. A mathematical model for hydrogel-solution composite, a composite of a distributed parameter system (cylindrical hydrogel) and a lumped parameter system (surrounding solution), is developed. The polymer network displacement in a swelling/deswelling hydrogel is described by a stress diffusion coupling model. The analytical solution for network displacement is used to predict solvent intake by swelling hydrogels, solvent efflux from deswelling hydrogels, and changes in pressure, porosity, and effective drug diffusivity. These in turn influence drug uptake during and after hydrogel swelling and drug release from hydrogel during and after deswelling. Numerical results illustrate benefits of hydrogel swelling for drug loading and merits of different modes of drug release. Drug uptake and drug release by temperature-responsive hydrogels are compared with those by hydrogels not subject to deformation.     

Synthesis of diethylaminoethyl dextran hydrogel and its heavy metal ion adsorption characteristics

Epichlorohydrin-crosslinked diethylaminoethyl dextran (DEAE-D/ECH) hydrogel was synthesized by intermolecular side-chain reaction of DEAE-D hydroxyl groups with monomeric crosslinking agent, ECH. Swelling ability, adsorption capacity and metal removal of the hydrogel were profoundly determined and some structural parameters for the hydrogel such as volume of non-swollen gel, percentages of gellation, swelling ratio and equilibrium water content were evaluated in this study. The ability of removing heavy metal ions from Orontes River by the synthesized hydrogel, thoroughly characterized by photometric spectrometer and the adsorption characteristics of metal ions, was investigated as well as surface morphologies of the hydrogel before and after metal adsorption were examined by SEM. Structure of DEAE-D/ECH gel was analyzed by FTIR, TGA, and DSC. Gellation point of binary system reaction between DEAE-D and ECH was determined via monitoring viscosity changes during reaction. The order of affinity based on amount of metal ion uptake was found as follows: Zn(2+)>Mn(2+)>Pb(2+)>Cd(2+).     

Functionalization of pine needles by carboxymethylation and network formation for use as supports in the adsorption of Cr

Pine needles and their carboxymethyl forms were functionalized by network formation with 2-acrylamido-2-methylpropanesulphonic acid (AAmPSA) in the presence of N,N-methylene bisacrylamide. N-Tetramethylethylene diamine and ammonium persulfate were used as accelerator-initiator systems to prepare these hydrogels. The hydrogels were characterized by FTIR, SEM, and nitrogen analysis and for water uptake capacities before and after metal ion sorption with a view to evaluating their use in the removal of toxic ionic species from waste water. A detailed study of Cr⁶⁺ adsorption was carried out as a function of time, temperature, pH, and ionic strength. The thermodynamic parameters of adsorption such as ΔH⁰, ΔS⁰, and ΔG⁰ have been evaluated to understand the underlying mechanism of adsorption. In order to understand their reusability in possible technological applications, biodegradability of these hydrogels and their precursors was studied.