Luminescence properties of barium – gadolinium–titanate ceramics doped with rare‐earth ions (Eu3+ and Tb3+)

Barium‐gadolinium‐titanate (BaGd₂Ti₄O₁₂) powder ceramics doped with rare‐earth ions (Eu³⁺ and Tb³⁺) were synthesized by a solid‐state reaction method. From the X‐ray diffraction spectrum, it was observed that Eu³⁺ and Tb³⁺:BaGd₂Ti₄O₁₂ powder ceramics are crystallized in the form of an orthorhombic structure. Scanning electron microscopy image shows that the particles are agglomerated and the particle size is about 200 nm. Eu³⁺‐ and Tb³⁺‐doped BaGd₂Ti₄O₁₂ powder ceramics were examined by energy dispersive X‐ray analysis, Fourier transform infrared spectroscopy, photoluminescence and thermoluminescence (TL) spectra. Emission spectra of Eu³⁺‐doped BaGd₂Ti₄O₁₂ powder ceramics showed bright red emission at 613 nm (⁵D₀ → ⁷F₂) with an excitation wavelength λ_exci = 408 nm (⁷F₀ → ⁵D₃) and Tb³⁺:BaGd₂Ti₄O₁₂ ceramic powder has shown green emission at 534 nm (⁵D₄ → ⁷F₅) with an excitation wavelength λ_exci = 331 nm ((⁷F₆ → ⁵D₁). TL spectra show that Eu³⁺ and Tb³⁺ ions affect TL sensitivity. Copyright © 2014 John Wiley & Sons, Ltd.     

Thermoluminescence and photoluminescence studies on γ‐ray‐irradiated Ce3+,Tb3+‐doped potassium chloride single crystals

Single crystals of KCl doped with Ce³⁺,Tb³⁺ were grown using the Bridgeman–Stockbarger technique. Thermoluminescence (TL), optical absorption, photoluminescence (PL), photo‐stimulated luminescence (PSL), and thermal‐stimulated luminescence (TSL) properties were studied after γ‐ray irradiation at room temperature. The glow curve of the γ‐ray‐irradiated crystal exhibits three peaks at 420, 470 and 525 K. F‐Light bleaching (560 nm) leads to a drastic change in the TL glow curve. The optical absorption measurements indicate that F‐ and V‐centres are formed in the crystal during γ‐ray irradiation. It was attempted to incorporate a broad band of cerium activator into the narrow band of terbium in the KCl host without a reduction in the emission intensity. Cerium co‐doped KCl:Tb crystals showed broad band emission due to the d–f transition of cerium and a reduction in the intensity of the emission peak due to ⁵D₃–⁷F_j (j = 3, 4) transition of terbium, when excited at 330 nm. These results support that energy transfer occurs from cerium to terbium in the KCl host. Co‐doping Ce³⁺ ions greatly intensified the excitation peak at 339 nm for the emission at 400 nm of Tb³⁺. The emission due to Tb³⁺ ions was confirmed by PSL and TSL spectra. Copyright © 2015 John Wiley & Sons, Ltd.     

Emission analysis of Tb3+‐and Sm3+‐ion‐doped (Li2O/Na2O/K2O) and (Li2O + Na2O/Li2O + K2O/K2O + Na2O)‐modified borosilicate glasses

Four series of borosilicate glasses modified by alkali oxides and doped with Tb³⁺ and Sm³⁺ ions were prepared using the conventional melt quenching technique, with the chemical composition 74.5B₂O₃ + 10SiO₂ + 5MgO + R + 0.5(Tb₂O₃/Sm₂O₃) [where R = 10(Li₂O /Na₂O/K₂O) for series A and C, and R = 5(Li₂O + Na₂O/Li₂O + K₂O/K₂O + Na₂O) for series B and D]. The X‐ray diffraction (XRD) patterns of all the prepared glasses indicate their amorphous nature. The spectroscopic properties of the prepared glasses were studied by optical absorption analysis, photoluminescence excitation (PLE) and photoluminescence (PL) analysis. A green emission corresponding to the ⁵D₄ → ⁷F₅ (543 nm) transition of the Tb³⁺ ions was registered under excitation at 379 nm for series A and B glasses. The emission spectra of the Sm³⁺ ions with the series C and D glasses showed strong reddish‐orange emission at 600 nm (⁴G_5/2 →⁶H_7/2) with an excitation wavelength λ_exci = 404 nm (⁶H_5/2→⁴F_7/2). Furthermore, the change in the luminescence intensity with the addition of an alkali oxide and combinations of these alkali oxides to borosilicate glasses doped with Tb³⁺ and Sm³⁺ ions was studied to optimize the potential alkali‐oxide‐modified borosilicate glass.     

Energy transfer between Ce3+ → Gd3+ or Tb3+ in KNaSO4 microphosphor

KNaSO₄ microphosphor doped with Ce,Gd and Ce,Tb and prepared by a wet chemical method was studied using X‐ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence (PL) characterization. KNaSO₄ has a 5‐µm particle size detected by SEM. KNaSO₄:Ce³⁺,Tb³⁺ showed blue and green emission (at 494 nm, 557 nm, 590 nm) of Tb³⁺ due to ⁵D₄ → ⁷F_J (J = 4, 5, 6) transitions. KNaSO₄:Ce³⁺,Gd³⁺ showed luminescence in the ultraviolet (UV) light region at 314 nm for an excitation at 271 nm wavelength. It was observed that efficient energy transfer took place from Ce³⁺ → Gd³⁺ and Ce³⁺ → Tb³⁺ sublattices indicating that Ce³⁺ could effectively sensitize Gd³⁺ or Tb³⁺ (green emission). Ce³⁺ emission weakened and Gd³⁺ or Tb³⁺ enhanced the emission significantly in KNaSO₄. This paper discusses the development and understanding of photoluminescence and the effect of Tb³⁺ and Gd³⁺ on KNaSO₄:Ce³⁺. Copyright © 2015 John Wiley & Sons, Ltd.     

Photoluminescence properties of aeschynite‐type LaNbTiO6:RE3+ (RE = Tb,Dy, Ho) down‐converting phosphors

In this study, a series of LaNbTiO₆:RE³⁺ (RE = Tb, Dy, Ho) down‐converting phosphors were synthesized using a modified sol–gel combustion method, and their photoluminescence (PL) properties were investigated as a function of activator concentration and annealing temperature. The resultant particles were characterized using X‐ray diffraction, transmission electron microscopy, scanning electron microscopy, UV/Vis diffuse reflectance spectroscopy and PL spectra. The highly crystalline LaNbTiO₆:RE³⁺ (RE = Tb, Dy, Ho) phosphors with an average size of 200–300 nm obtained at 1100°C have an orthorhombic aeschynite‐type structure and exhibit the highest luminescent intensity in our study range. The emission spectra of LaNbTiO₆:RE³⁺ (RE = Tb, Dy, Ho) phosphors under excitations at UV/blue sources are mainly composed of characteristic peaks arising from the f–f transitions of RE³⁺, including 489 nm (⁵D₄ → ⁷F₆) and 545 nm (⁵D₄ → ⁷F₅) for Tb³⁺, 476 and 482 nm (⁴F_9/2 → ⁶H_15/2) and 571 nm (⁴F_9/2 → ⁶H_13/2) for Dy³⁺, and 545 nm (⁵F₄ + ⁵S₂ → ⁵I₈) for Ho³⁺, respectively. The luminescent mechanisms were further investigated. It can be expected that these phosphors are of intense interest and potential importance for many optical applications. Copyright © 2013 John Wiley & Sons, Ltd.     

Synthesis and luminescence properties of Ca3Ga2Si3O12:RE3+ (RE = Eu/Tb) powder phosphors

Rare earth ions (Eu³⁺ or Tb³⁺)‐activated Ca₃ Ga₂ Si₃O₁₂ (CaGaSi) phosphors were synthesized by using a sol–gel method. Photoluminescence spectra of Eu³⁺:CaGaSi phosphors exhibited five emission bands at 578, 592, 612, 652 and 701 nm, which were assigned to the transitions (⁵D₀ → ⁷F₀, ⁷F_1, ⁷F₂, ⁷F₃ and ⁷F₄), respectively, with an excitation wavelength of λ_exci = 392 nm. Among these, the transition ⁵D₀ → ⁷F₂ (612 nm) displayed bright red emission. In the case of Tb³⁺:CaGaSi phosphors, four emission bands were observed at 488 (⁵D₄ → ⁷F₆), 543 (⁵D₄ → ⁷F₅), 584 (⁵D₄ → ⁷F₄) and 614 nm (⁵D₄ → ⁷F₃) from the measurement of PL spectra with λ_exci = 376 nm. Among these, the transition ⁵D₄ → ⁷F₅ at 543 nm displayed bright green emission. The structure and morphology of the phosphors were studied from the measurements of X‐ray diffraction (XRD), scanning electron microscopy (SEM) and energy‐dispersive X‐ray analysis (EDAX) results. Copyright © 2011 John Wiley & Sons, Ltd.     

Synthesis of green emissive terbium(III) complexes for displays: Optical,electrochemical and photoluminescent analysis

A series of heteroleptic terbium(III) complexes with fluorinated 2-thenoyltrifluoroacetone (TTFA) and other heteroaromatic units have been synthesized. The developed heteroleptic complexes were inspected via elemental study, cyclic voltammetry, thermal analysis and spectroscopic investigations. Optical band-gap data proposed the conducting property of prepared complexes. The photoluminescence emission profiles illustrated peaks based on terbium(III) cation (Tb³⁺) positioned at ~617, 586, 546 and 491 nm, imputed to ⁵D₄ to ⁷F_J (J = 3,4,5,6) transitions separately. Most intense peak at 546 nm corresponding to ⁵D₄ → ⁷F₅ transition is accountable for the green emissive character of developed complexes. The luminous character of complexes reveals the sensitization of Tb³⁺ by ligands. Color parameters further corroborates the green emanation of Tb³⁺ complexes. The photometric characteristics of complexes recommended their usages in designing display devices.     

Synthesis and photoluminescence properties of Eu3+‐activated Ba2Mg(PO4)2 phosphor

In this paper, we have reported the photoluminescence (PL) properties of the Ba₂Mg(PO₄)₂:Eu³⁺ phosphor synthesized using a wet chemical method. The preliminary scanning electron microscopy (SEM) investigation of the sample revealed irregular surface morphology with particle sizes in the 10–50 μm range. The strongest PL excitation peak was observed at 396 nm. The emission spectra indicated that this phosphor can be effectively excited by the 396 nm wavelength. Upon 396 nm excitation, the emission spectrum showed characteristics peaks located at 592 nm and 615 nm. These intense orange‐red emission peaks were obtained due to f→f transitions of Eu³⁺ ions. The emission peak at 592 nm is referred to as the magnetic dipole ⁵D₀→⁷F₁ transition and the emission peak at 615 nm corresponded to the electric dipole ⁵D₀→⁷F₂ transition of Eu³⁺. The Commission Internationale de l’Eclairage (CIE) coordinates of the Ba₂Mg(PO₄)₂:Eu³⁺ phosphor were found to be (0.586, 0.412) for wavelength 592 nm and (0.680, 0.319) for wavelength 615 nm situated at the edge of the CIE diagram, indicating high colour purity of phosphors. Due to the high emission intensity and a good excitation profile, Eu³⁺‐doped Ba₂Mg(PO₄)₂ phosphor may be a promising orange‐red phosphor candidate for solid‐state lighting applications.     

Optical properties and energy transfer of Eu2+/Ce3+ co‐activated Na3Ca6(PO4)5 phosphor

Ce³⁺/Eu²⁺ co‐doped Na₃Ca₆(PO₄)₅ phosphors were prepared using a combustion‐assisted synthesis method. X‐Ray powder diffraction (XRD) analysis confirmed the formation of a Na₃Ca₆(PO₄)₅ crystal phase. Na₃Ca₆(PO₄)₅:Eu²⁺ phosphors have an efficient bluish‐green emission band that peaks at 489 nm, whereas Ce³⁺‐doped Na₃Ca₆(PO₄)₅ showed a bright emission band at 391 nm. Analysis of the experimental results suggests that enhancement of the Eu²⁺ emission intensity in co‐doped Na₃Ca₆(PO₄)₅:Eu²⁺,Ce³⁺ phosphors is due to a resonance‐type energy transfer from Ce³⁺ to Eu²⁺ ions, which is predominantly governed by an exchange interaction mechanism. These results indicate that Ce³⁺/Eu²⁺ co‐doped Na₃Ca₆(PO₄)₅ is potentially useful as a highly efficient, bluish‐green emitting, UV‐convertible phosphor for white‐light‐emitting diodes. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescence investigation of novel MgPbAl10O17:Tb3+ green‐emitting phosphor for solid‐state lighting

In this work, we studied the luminescence properties of Tb³⁺‐doped MgPbAl₁₀O₁₇ green phosphor. To understand the excitation mechanism and corresponding emission of the prepared phosphor, its structural, morphological and photoluminescence properties were investigated. In general, for green emission, Tb³ is used as an activator and the obtained excitation and emission spectra indicated that this phosphor can be effectively excited by a wavelength of 380 nm, and exhibits bright green emission centered at 545 nm corresponding to the f → f transition of trivalent terbium ions. The chromaticity coordinates were (C_x = 0.263, C_y = 0.723). The impact of Tb³⁺ concentration on the relative emission intensity was investigated, and the best doping concentration was found to be 2 mol%. This study suggests that Tb³⁺‐doped MgPbAl₁₀O₁₇ phosphor is a strong candidate for a green component in phosphor‐converted white light‐emitting diodes. Copyright © 2015 John Wiley & Sons, Ltd.     

Luminescent properties and energy transfer in the green phosphors LaBSiO5:Tb3+,Ce3+

LaBSiO₅ phosphors doped with Ce³⁺ and Tb³⁺ were synthesized using the conventional solid‐state method at 1100 °C. The phase purity and luminescent properties of these phosphors are investigated. LaBSiO₅:Tb³⁺ phosphors show intense green emission, and LaBSiO₅ phosphors doped with Ce³⁺ show blue–violet emission under UV light excitation. LaBSiO₅ phosphors co‐doped with Ce³⁺ and Tb³⁺ exhibit blue–violet and green emission under excitation by UV light. The blue–violet emission is due to the 5d–4f transition of Ce³⁺ and the green emission is ascribed to the ⁵D₄ → ⁷ F₅ transition of Tb³⁺. The spectral overlap between the excitation band of Tb³⁺ and the emission band of Ce³⁺ supports the occurrence of energy transfer from Ce³⁺ to Tb³⁺, and the energy transfer process was investigated. Copyright © 2014 John Wiley & Sons, Ltd.     

Photoluminescence properties of LiTi2 − xEux(PO4)3 phosphor

A solid‐state reaction route‐based LiTi_{2 ? x}Eu_x(PO₄)₃ was phosphor synthesized for the first time to evaluate its luminescence performance by excitation, emission and lifetime (τ) measurements. The LiTi_{2 ? x}Eu_x(PO₄)₃ phosphor was excited at λ_exci. = 397 nm to give an intense orange–red (597 nm) emission attributed to the ⁵D₀ → ⁷F₁ magnetic dipole (ΔJ = ±1) transition and red (616 nm) emission (⁵D₀ → ⁷F₂), which is an electric dipole (ΔJ = ±2) transition of the Eu³⁺ ion. Beside this, excitation and emission spectra of host LiTi₂(PO₄)₃ powder were also reported. The effect of Eu³⁺ concentration on luminescence characteristics was explained from emission and lifetime profiles. Concentration quenching in the LiTi_{2 ? x}Eu_x(PO₄)₃ phosphor was studied from the Dexter's model. Dipole–quadrupole interaction is found to be responsible for energy transfer among Eu³⁺ ions in the host lattice. The LiTi_{2 ? x}Eu_x(PO₄)₃ phosphor displayed a reddish‐orange colour realized from a CIE chromaticity diagram. We therefore suggest that this new phosphor could be used as an optical material of technological importance in the field of display devices. Copyright © 2016 John Wiley & Sons, Ltd.     

Structural and luminescence properties of Y2‐xGeMoO8:REx (RE = Eu,Tb) phosphors

Y_2‐xGeMoO₈:RE_x (RE = Eu, Tb) phosphors were synthesized using a facile sol–gel method. The morphology and structure of the phosphors were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X‐ray diffraction (XRD); while their luminescent properties were investigated by photoluminescence (PL) spectrometry. Our results reveal that all of these Y_2‐xGeMoO₈:RE_x (RE = Eu, Tb) phosphors adopted the tetragonal phase, belonging to Scheelite (CaWO₄) structure. The obtained YGeMoO₈:Eu phosphors exhibit a strong emission in the red light range which can be assigned to the ⁵D₀ → ⁷F₂ transition of Eu³⁺ when it is excited at 459 nm. Under 392 and 489 nm excitation, the YGeMoO₈:Tb phosphors present predominant green emission (⁵D₄ → ⁷F₅) at 540 nm. The highest emission of the phosphors can be achieved by adjusting the doping concentration to be 0.25 for Eu³⁺ and 0.15 for Tb³⁺, respectively. The promising luminescence properties of these materials indicate that they can be potentially applied to white‐light‐emitting diodes. Copyright © 2013 John Wiley & Sons, Ltd.     

The effects of charge compensation on photoluminescence properties of a new green‐emitting ZnB2O4:Tb3+ phosphor

Charge compensation is an effective way to eliminate charge defects and improve the luminescent intensity of phosphors. In this paper, a new green‐emitting phosphor ZnB₂O₄:Tb³⁺ was prepared by solid‐state reaction at 750°C. The effects of Tb³⁺ doping content and charge compensators (Li⁺, Na⁺ or K⁺) on photoluminescence properties of ZnB₂O₄:Tb³⁺ were investigated. X‐ray powder diffraction analysis confirms the sample has cubic structure of ZnB₂O₄. The excitation and emission spectra indicate that this phosphor can be excited by near ultraviolet light at 378 nm, and exhibits bright green emission with the highest peak at 544 nm corresponding to the ⁵D₄→⁷F₅ transition of Tb³⁺. The critical quenching concentration of Tb³⁺ in ZnB₂O₄ host is 8 mol%. The results of charge compensation show that the emission intensity can be improved by Na⁺ and K⁺. Specifically, K⁺ is the optimal one for ZnB₂O₄:Tb³⁺. Copyright © 2014 John Wiley & Sons, Ltd.     

Optical analysis of Sr3Gd(PO4)3:Pr3+ phosphors for lighting applications

A series of praseodymium (Pr³⁺) ion activated Sr₃Gd_(1−x)(PO₄)₃:xPr³⁺ (0 ≤ x ≤ 2.0 mol%) phosphors were prepared and their structural, compositional and luminescence properties were investigated. The X-ray diffraction profiles indicate that the studied phosphors crystallized into body centred cubic structure and the Pr³⁺ ions have no influence on Sr₃Gd(PO₄)₃ phase. The high-resolution scanning electron microscopy images show the agglomeration of particles that are inter-connected and form irregular shape Sr₃Gd(PO₄)₃ structures. The excitation transitions corresponding to Pr³⁺:³H₄ → ³P_2,1,0 transitions at 445, 471 and 483 nm, respectively, matched well with the emission of blue-light-emitting diode (LED) chip. The emission spectra show strong reddish-orange luminescence through ¹D₂ → ³H₄ transition when excited at 445 nm blue wavelength. The synthesized phosphors have the potential to be used as reddish-orange lighting devices.     

A High‐Energy NASICON‐Type Cathode Material for Na‐Ion Batteries

Over the last decade, Na‐ion batteries have been extensively studied as low‐cost alternatives to Li‐ion batteries for large‐scale grid storage applications; however, the development of high‐energy positive electrodes remains a major challenge. Materials with a polyanionic framework, such as Na superionic conductor (NASICON)‐structured cathodes with formula Na_xM₂(PO₄)₃, have attracted considerable attention because of their stable 3D crystal structure and high operating potential. Herein, a novel NASICON‐type compound, Na₄MnCr(PO₄)₃, is reported as a promising cathode material for Na‐ion batteries that deliver a high specific capacity of 130 mAh g^?1 during discharge utilizing high‐voltage Mn^2+/3+ (3.5 V), Mn^3+/4+ (4.0 V), and Cr^3+/4+ (4.35 V) transition metal redox. In addition, Na₄MnCr(PO₄)₃ exhibits a high rate capability (97 mAh g^?1 at 5 C) and excellent all‐temperature performance. In situ X‐ray diffraction and synchrotron X‐ray diffraction analyses reveal reversible structural evolution for both charge and discharge.     

Luminescence and energy‐transfer properties of color‐tunable Ca2Mg0.25Al1.5Si1.25O7:Ce3+/Eu2+/Tb3+ phosphors for ultraviolet light‐emitting diodes

A series of Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺/Eu²⁺/Tb³⁺ phosphors was been prepared via a conventional high temperature solid‐state reaction and their luminescence properties were studied. The emission spectra of Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺,Eu²⁺ and Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺,Tb³⁺ phosphors show not only a band due to Ce³⁺ ions (409 nm) but also as a band due to Eu²⁺ (520 nm) and Tb³⁺ (542 nm) ions. More importantly, the effective energy transfer from Ce³⁺ to Eu²⁺ and Tb³⁺ ions was confirmed and investigated by emission/excitation spectra and luminescent decay behaviors. Furthermore, the energy level scheme and energy transfer mechanism were investigated and were demonstrated to be of resonant type via dipole–dipole (Ce³⁺ to Eu²⁺) and dipole–quadrupole (Ce³⁺ to Tb³⁺) reactions, respectively. Under excitation at 350 nm, the emitting color could be changed from blue to green by adjusting the relative doping concentration of Ce³⁺ and Eu²⁺ ions as well as Ce³⁺ and Tb³⁺ ions. The above results indicate that Ca₂Mg_0.25Al_1.5Si_1.25O₇:Ce³⁺,Eu²⁺/Tb³⁺ are promising single‐phase blue‐to‐green phosphors for application in phosphor conversion white‐light‐emitting diodes. Copyright © 2015 John Wiley & Sons, Ltd.     

Improving green emission of Tb3+ ions in BaO‐B2O3‐P2O5 glasses by means of Al3+ ions

BaO‐B₂O₃‐P₂O₅ glasses doped with a fixed concentration of Tb³⁺ ions and varying concentrations of Al₂O₃ were synthesized, and the influence of the Al³⁺ ion concentration on the luminescence efficiency of the green emission of Tb³⁺ ions was investigated. The optical absorption, excitation, luminescence spectra and fluorescence decay curves of these glasses were recorded at ambient temperature. The emission spectra of terbium ions when excited at 393 nm exhibited two main groups of bands, corresponding to ⁵D₃ → ⁷F_j (blue region) and ⁵D₄ → 7F_j (green region). From these spectra, the radiative parameters, viz., spontaneous emission probability A, total emission probability A_T, radiative lifetime τ and fluorescent branching ratio β, of different transitions originating from the ⁵D₄ level of Tb³⁺ ions were evaluated based on the Judd‐Ofelt theory. A clear increase in the quantum efficiency and luminescence of the green emission of Tb³⁺ ions corresponding to ⁵D₄ → ⁷F₅ transition is observed with increases in the concentration of Al₂O₃ up to 3.0 mol%. The improvement in emission is attributed to the de‐clustering of terbium ions by Al³⁺ ions and also to the possible admixing of wave functions of opposite parities. Copyright © 2016 John Wiley & Sons, Ltd.     

Impact of ligand environment on optical,luminescence and thermometric behavior of A3(PO4)2:Sm3+ (A = Ca,Sr) phosphors

The present study investigates the impact of the ligand environment on the luminescence and thermometric behavior of Sm³⁺ doped A₃(PO₄)₂ (A = Sr, Ca) phosphors prepared by combustion synthesis. The structural and luminescent properties of Sm³⁺ ions in the phosphate lattices were investigated using powder X-ray diffraction (PXRD) and photoluminescence (PL) techniques. PXRD results of the synthesized phosphors exhibit the expected phases that are in agreement with their respective standards. Fourier-transform infrared (FTIR) spectroscopy confirms the presence of PO₄ vibrational bands. Upon excitation with near ultraviolet light, the PL studies indicated that Sr₃(PO₄)₂:Sm³⁺ phosphors exhibit a yellow light emission, whereas Ca₃(PO₄)₂:Sm³⁺ phosphors exhibit an emission of orange light. The PL emission results are in accordance with the CIE coordinates, with the Sr₃(PO₄)₂:Sm³⁺ phosphors showing coordinates of (0.56, 0.44), and the Ca₃(PO₄)₂:Sm³⁺ phosphors displaying coordinates of (0.60, 0.40). Thermal analysis shows improved stability of Ca₃(PO₄)₂:Sm³⁺ based on lower weight reduction in thermogravimetric analysis. The effect of temperature on the luminescence properties of the phosphor has been examined upon a 405 nm excitation. By using the fluorescence intensity ratio (FIR) method, the temperature responses of the emission ratios from the Sm³⁺: the ⁴F_3/2 → ⁶H_5/2 transition to the ⁴G_5/2 → ⁶H_7/2 and ⁴F_3/2 → ⁶H_5/2 transition to the ⁴G_5/2 → ⁶H_9/2 emissions are characterized. The Ca₃(PO₄)₂:Sm³⁺ phosphors are more sensitive as compared with the Sr₃(PO₄)₂:Sm³⁺ phosphors. The earlier research findings strongly indicate that these phosphors hold great promise as ideal candidates for applications in non-invasive optical thermometry and solid-state lighting devices.     

Preparation and up‐conversion luminescence properties of LaOBr:Yb3+/Er3+ nanofibers via electrospinning

LaOBr:Yb³⁺/Er³⁺ nanofibers were synthesized for the first time by calcinating electrospun PVP/[La(NO₃)₃ + Er(NO₃)₃ + Yb(NO₃)₃ + NH₄Br] composites. The morphology and properties of the final products were investigated in detail using scanning electron microscopy (SEM), energy dispersion spectroscopy (EDS), X‐ray diffractometry (XRD) and fluorescence spectroscopy. The results indicate that LaOBr:Yb³⁺/Er³⁺ nanofibers are tetragonal in structure with a space group of P4/nmm. The diameter of LaOBr:Yb³⁺/Er³⁺ nanofibers is ~ 147 nm. Under the excitation of a 980‐nm diode laser, LaOBr:Yb³⁺/Er³⁺ nanofibers emit strong green and red up‐conversion emission centering at 519, 541 and 667 nm, ascribed to the ²H_11/2, ⁴S_3/2 → ⁴I_15/2 and ⁴ F_9/2 → ⁴I_15/2 energy‐level transitions of Er³⁺ ions, respectively. The up‐conversion luminescent mechanism of LaOBr:Yb³⁺/Er³⁺ nanofibers is advanced. Moreover, near‐infrared emission of LaOBr:Yb³⁺/Er³⁺ nanofibers is obtained under the excitation of a 532‐nm laser. The formation mechanism of LaOBr:Yb³⁺/Er³⁺ nanofibers is proposed. LaOBr:Yb³⁺/Er³⁺ nanofibers could be important up‐conversion luminescent materials. Copyright © 2014 John Wiley & Sons, Ltd.