Genipin cross-linked alginate-chitosan microcapsules: membrane characterization and optimization of cross-linking reaction

The genipin cross-linked alginate-chitosan (GCAC) microcapsule, composed of an alginate core and a genipin cross-linked chitosan membrane, was recently proposed for live cell encapsulation and other delivery applications. This article for the first time describes the details of the microcapsule membrane characterization using a noninvasive and in situ method without any physical or chemical modifications on the samples. Results showed that the cross-linking reaction generated the fluorescent chitosan-genipin conjugates. The cross-linked chitosan membrane was clearly visualized by confocal laser scanning microscopy (CLSM). A straightforward assessment on the membrane thickness and relative intensity was successfully achieved. CLSM studies showed that the shell-like cross-linked chitosan membranes of approximately 37 microm in thickness were formed surrounding the microcapsule. The reaction variables, including cross-linking temperature and time significantly affected the fluorescence intensity of the membranes. Elevating the cross-linking temperature from 4 to 37 degrees C drastically intensified the membrane fluorescence, suggesting the attainment of a high degree of cross-linking on the chitosan membrane. Extended cross-linking time altered the cross-linked membranes in modulation. Although genipin concentration and cross-linking time had little effects on the membrane thickness, cross-linking at higher temperatures tended to form relatively thinner membranes.     

Preparation of Chitosan Cryostructurates with Controlled Porous Morphology and Their Use as 3D-Scaffolds for the Cultivation of Animal Cells

The influence of the conditions of the formation of genipin cross-linked chitosan cryostructurates on the porous morphology and physicochemical properties of these cryostructurates and on the possibility of their use as biopolymer 3D scaffolds for tissue engineering was studied. The chitosan cryostructurates were obtained by freeze-drying a chitosan acetate solution, treating the resulting sponge with an alcohol solution of ammonia to transform the polyaminosaccharide from a salt into a chitosan-base, and then cross-linking the polymer with genipin (the molar ratios of genipin to the number of chitosan amino groups were 0.05, 0.033, and 0.02, respectively). The pore sizes, water-holding capacity, and in vitro biodegradation rate of the cryostructurates were shown to depend on the aforementioned ratio. The properties of the prepared chitosan cryostructurates, the hydrogels formed by chitosan cross-linking with genipin at positive temperatures, and the films cast from genipin-containing chitosan solutions after solvent evaporation were studied and compared. The biocompatibility of the obtained macroporous sponge materials was demonstrated using L929 mouse fibroblasts. Confocal laser microscopy showed that the cells in all of the 3D scaffolds obtained were evenly distributed; they grew and proliferated when cultured in vitro for seven days.     

Chitosan nanogels by template chemical cross-linking in polyion complex micelle nanoreactors

Chitosan covalent nanogels cross-linked with genipin were prepared by template chemical cross-linking of chitosan in polyion complex micelle (PIC) nanoreactors. By using this method, we were able to prepare chitosan nanogels using only biocompatible materials without organic solvents. PIC were prepared by interaction between chitosan (X(n) = 23, 44, and 130) and block copolymer poly(ethylene oxide)-block-poly[sodium 2-(acrylamido)-2-methylpropanesulfonate] (PEO-b-PAMPS) synthesized by single-electron transfer-living radical polymerization (SET-LRP). PIC with small size (diameter about 50 nm) and low polydispersity were obtained up to 5 mg/mL. After cross-linking of chitosan with genipin, the nanoreactors were dissociated by adding NaCl. The dissociation of the nanoreactors and the formation of the nanogels were confirmed by (1)H NMR, DLS, and TEM. The size of the smallest nanogels was about 50 nm in the swollen state and 20 nm in the dry state. The amount of genipin used during reticulation was an important parameter to modulate the size of the nanogels in solution.     

In vitro protein-polysaccharide conjugation: tyrosinase-catalyzed conjugation of gelatin and chitosan

The enzyme tyrosinase was used for the in vitro conjugation of the protein gelatin to the polysaccharide chitosan. Tyrosinases are oxidative enzymes that convert accessible tyrosine residues of proteins into reactive o-quinone moieties. Spectrophotometric and dissolved oxygen studies indicate that tyrosinase can oxidize gelatin and we estimate that 1 in 5 gelatin chains undergo reaction. Oxidized tyrosyl residues (i.e., quinone residues) can undergo nonenzymatic reactions with available nucleophiles such as the nucleophilic amino groups of chitosan. Ultraviolet/visible, (1)H-NMR, and ir provided chemical evidence for the conjugation of oxidized gelatin with chitosan. Physical evidence for conjugation was provided by dynamic viscometry, which indicated that tyrosinase catalyzes the sol-to-gel conversion of gelatin/chitosan mixtures. The gels formed from tyrosinase-catalyzed reactions were observed to differ from gels formed by cooling gelatin. In contrast to gelatin gels, tyrosinase-generated gels had different thermal behavior and were broken by the chitosan-hydrolyzing enzyme chitosanase. These results demonstrate that tyrosinase can be exploited for the in vitro formation of protein-polysaccharide conjugates that offer interesting mechanical properties.     

The effects of different crossing-linking conditions of genipin on type I collagen scaffolds: an in vitro evaluation

The purpose of this paper is to analyze the properties of fabricating rat tail type I collagen scaffolds cross-linked with genipin under different conditions. The porous genipin cross-linked scaffolds are obtained through a two step freeze-drying process. To find out the optimal cross-link condition, we used different genipin concentrations and various cross-linked temperatures to prepare the scaffolds in this study. The morphologies of the scaffolds were characterized by scanning electron microscope, and the mechanical properties of the scaffolds were evaluated under dynamic compression. Additionally, the cross-linking degree was assessed by ninhydrin assay. To investigate the swelling ratio and the in vitro degradation of the collagen scaffold, the tests were also carried out by immersion of the scaffolds in a PBS solution or digestion in a type I collagenase respectively. The morphologies of the non-cross-linked scaffolds presented a lattice-like structure while the cross-linked ones displayed a sheet-like framework. The morphology of the genipin cross-linked scaffolds could be significantly changed by either increasing genipin concentration or the temperature. The swelling ratio of each cross-linked scaffold was much lower than that of the control (non-cross-linked).The ninhydrin assay demonstrated that the higher temperature and genipin concentration could obviously increase the cross-linking efficiency. The in vitro degradation studies indicated that genipin cross-linking can effectively elevate the biostability of the scaffolds. The biocompatibility and cytotoxicity of the scaffolds was evaluated by culturing rat chondrocytes on the scaffold in vitro and by MTT. The results of MTT and the fact that the chondrocytes adhered well to the scaffolds demonstrated that genipin cross-linked scaffolds possessed an excellent biocompatibility and low cytotoxicity. Based on these results, 0.3 % genipin concentrations and 37 °C cross-linked temperatures are recommended.     

In situ forming chitosan hydrogels prepared via ionic/covalent co-cross-linking

In situ forming chitosan hydrogels have been prepared via coupled ionic and covalent cross-linking. Thus, different amounts of genipin (0.05, 0.10, 0.15, and 0.20% (w/w)), used as a chemical cross-linker, were added to a solution of chitosan that was previously neutralized with a glycerol-phosphate complex (ionic cross-linker). In this way, it was possible to overcome the pH barrier of the chitosan solution, to preserve its thermosensitive character, and to enhance the extent of cross-linking in the matrix simultaneously. To investigate the contributions of the ionic cross-linking and the chemical cross-linking, separately, we prepared the hydrogels without the addition of either genipin or the glycerol-phosphate complex. The addition of genipin to the neutralized solution disturbs the ionic cross-linking process and the chemical cross-linking becomes the dominant process. Moreover, the genipin concentration was used to modulate the network structure and performance. The more promising formulations were fully characterized, in a hydrated state, with respect to any equilibrium swelling, the development of internal structure, the occurrence of in vitro degradability and cytotoxicity, and the creation of in vivo injectability. Each of the hydrogel systems exhibited a notably high equilibrium water content, arising from the fact that their internal structure (examined by conventional SEM, and environmental SEM) was highly porous with interconnecting pores. The porosity and the pore size distribution were quantified by mercury intrusion porosimetry. Although all gels became degraded in the presence of lysozyme, their degradation rate greatly depended on the genipin load. Through in vitro viability tests, the hydrogel-based formulations were shown to be nontoxic. The in vivo injection of a co-cross-linking formulation revealed that the gel was rapidly formed and localized at the injection site, remaining in position for at least 1 week.     

Preparation and characterization of novel polymeric microcapsules for live cell encapsulation and therapy

This article describes the preparation and in vitro characterization of novel genipin cross-linked alginate-chitosan (GCAC) microcapsules that have potential for live cell therapy applications. This microcapsule system, consisting of an alginate core with a covalently cross-linked chitosan membrane, was formed via ionotropic gelation between calcium ions and alginate, followed by chitosan coating by polyelectrolyte complexation and covalent cross-linking of chitosan by naturally derived genipin. Results showed that, using this design concept and the three-step procedure, spherical GCAC microcapsules with improved membrane strength, suppressed capsular swelling, and suitable permeability can be prepared. The suitability of this novel membrane formulation for live cell encapsulation was evaluated, using bacterial Lactobacillus plantarum 80 (pCBH1) (LP80) and mammalian HepG2 as model cells. Results showed that capsular integrity and bacterial cell viability were sustained 6 mo postencapsulation, suggesting the feasibility of using this microcapsule formulation for live bacterial cell encapsulation. The metabolic activity of the encapsulated HepG2 was also investigated. Results suggested the potential capacity of this GCAC microcapsule in cell therapy and the control of cell signaling; however, further research is required.     

Psoralen conjugates for visualization of genomic interstrand cross-links localized by laser photoactivation

DNA interstrand cross-links are formed by chemotherapy drugs as well as by products of normal oxidative metabolism. Despite their importance, the pathways of cross-link metabolism are poorly understood. Laser confocal microscopy has become a powerful tool for studying the repair of DNA lesions that can be detected by immunofluorescent reagents. In order to apply this approach to cross-link repair, we have synthesized conjugates of 4,5',8-trimethylpsoralen (TMP) and easily detected compounds such as Lissamine rhodamine B sulfonyl chloride (LRB-SC), biotin, and digoxigenin. These conjugates are activated by UVA, and we have analyzed the intracellular localization of DNA damage and DNA reactivity by confocal and immunofluorescence microscopy. The LRB-SC-TMP conjugate 2 appeared mainly in the mitochondria, while the biotin-TMP conjugate 4 preferentially localized in the cytoplasm. Adducts formed by UVA and digoxigenin conjugates of TMP 7a and 4,5'-dimethylangelicin (DMA) 7b, which forms only monoadducts, were largely localized to the nucleus. Exposure of cells incubated with 7a and 7b to a 364 nm UV laser directed toward defined nuclear regions of interest resulted in localized adduct formation which could be visualized by immunofluorescence. Repair-proficient cells were able to remove the photoadducts, while repair-deficient cells were unable to repair the damage. The results indicated that the digoxigenin-TMP conjugate 7a and digoxigenin-DMA conjugate 7b can be used for studying the repair of laser localized DNA monoadducts and cross-links.     

Enzymatic hydrolysate of geniposide directly acts as cross-linking agent for enzyme immobilization

Enzyme immobilization is a routine biotechnology of many industries such as pharmaceutical, chemical and food. Among the different techniques of enzyme immobilization, cross-linking methods are often used. Geniposide is a natural product extracted from gardenia and its hydrolysate genipin is one of green cross-linking agent for enzyme immobilization, but the environmental pollution and cost of the genipin extraction process have become the main obstacle to its wide application. Enzyme β-glucosidase was immobilized on chitosan by self-catalysis and further used to hydrolyze geniposide. The laccase was immobilized on Nano-SiO₂ through the hydrolysate of geniposide directly acts as cross-linking agent. The simplification of the extraction steps overcomes the obstacles to the widespread use of genipin. Compared with the free laccase, the Nano-SiO₂@laccase exhibited better pH stability and thermal stability. The Nano-SiO₂@laccase was used to degrade Bisphenol A (BPA) and the biodegradation efficiency of the Nano-SiO₂@laccase was 84.3 % after 10 cycles of reusing.     

Preparation and evaluation of decellularized porcine carotid arteries cross-linked by genipin: the preliminary results

Decellularized arteries have been considered as promising scaffolds for small-diameter vascular substitutes. However, weakened mechanical properties, immunological rejection and rapid degradation after transplantation still exist after decellularization. Previous studies indicated that genipin cross-linking can solve these problems. Therefore, genipin was selected as the cross-linking agent for the pre-treatment of decellularized arteries in our study. Histological analysis, scanning electron microscopy, mechanical properties analysis and subcutaneous embedding experiment were adopted to investigate the efficiency of decellularization and the effect of genipin cross-linking on improving mechanical, structural and biological properties of decellularized arteries. Decellularization protocols based on three trypsin concentrations were used to prepare decellularized arteries, after decellularization, arteries were cross-linked with genipin. Results showed that 0.5% trypsin was the most efficient concentration to remove cellular components and preserve ECM. However, mechanical properties of 0.5% trypsin decellularized arteries weakened significantly, while genipin cross-linking improved mechanical properties of decellularized arteries to the same level as fresh arteries. After 4 weeks subcutaneous embedding, cross-linked arteries caused the mildest inflammatory response. In conclusion, genipin could be employed as an ideal cross-linking agent to strengthen mechanical properties, enhance the resistance to degradation and reduce the antigenicity of decellularized arteries for small-diameter blood vessel tissue engineering applications.     

Chitosan cross-linking with a water-soluble,blocked diisocyanate. 2. Solvates and hydrogels

A water-soluble, blocked diisocyante was used to cross-link chitosan under various degrees of solvation, including hydration to form hydrogels. Thermal cross-linking of films cast from various amounts of organic cosolvents was found to increase with increased level of cosolvent up to a solvation level of 17% (w/w) and to be more efficient than for films prepared without cosolvent. Rheological studies revealed that gel modulus increased and gel time decreased with increasing cross-linker content and that gelation kinetics were consistent with a process having an activation energy of 103 kJ/mol. Swelling of hydrogels indicated that, even at high levels of hydration, the increased molecular mobility of reactants allowed for efficient network formation in a concentration-dependent manner. The extent of solvation via equilibrium swelling correlated well with degradative properties of chitosan networks in the presence of Chitinase (E. C. 3.2.1.14) from Streptomyces griseus with stability increasing with decreasing swelling (i.e., increased cross-linking).     

Biodegradablescaffolds based on chitosan: Preparation,properties, and use for the cultivation of animal cells

The influence of the conditions of the formation of chitosan hydrogels crosslinked with glutaraldehyde (GA) or genipin (the polysaccharide molecular weight, pH level, and concentration of the chitosan solution) on the gel time and the properties of biopolymer scaffolds for tissue engineering obtained by the freeze-drying of hydrogels was studied. The resulting scaffolds had different structures (morphology, degree of anisotropy, average pore size) and moisture-retaining capacities. The cytotoxicity of biodegradable scaffolds based on chitosan with a low content of genipin and GA was studied for the first time. Using the L929 mouse fibroblasts model line, we demonstrated that scaffolds based on chitosan with a molecular weight of 320 and 190 kDa crosslinked with genipin and GA (0.005 and 0.01 mol/mol of chitosan amino groups) are biocompatible. Using confocal laser microscopy, we demonstrated that the cells are uniformly distributed in all scaffold samples and they successfully grew and proliferated when cultured in vitro for 4 days.     

Preparation and characterization of novel chitosan/gelatin membranes using chitosan hydrogel

Chitin and chitosan are novel biomaterials. The novel chitosan/gelatin membranes were prepared using the suspension of chitosan hydrogel mixed with gelatin. The prepared chitosan/gelatin membranes were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), mechanical, swelling, and thermal studies. The morphology of these chitosan/gelatin membranes was found to be very smooth and homogeneous. The XRD studies showed that the chitosan/gelatin membranes have good compatibility and interaction between the chitosan and gelatin. The stress and elongation of chitosan/gelatin membranes on wet condition showed excellent when the mixture ratio of gelatin was 0.50. The prepared chitosan/gelatin membranes showed good swelling, mechanical and thermal properties. Cell adhesion studies were also carried out using human MG-63 osteoblast-like cells. The cells incubated with chitosan/gelatin membranes for 24 h were capable of forming cell adhesion. Thus the prepared chitosan/gelatin membranes are bioactive and are suitable for cell adhesion suggesting that these membranes can be used for tissue-engineering applications. Therefore, these novel chitosan/gelatin membranes are useful for biomedical applications.     

Activators of phosphorylase kinase alter the cross-linking of its catalytic subunit to the C-terminal one-sixth of its regulatory alpha subunit

Phosphorylase kinase, a regulatory enzyme of glycogenolysis in skeletal muscle, is a hexadecameric oligomer consisting of four copies each of a catalytic subunit (gamma) and three regulatory subunits (alpha, beta, and delta, the last being endogenous calmodulin). The enzyme is activated by a variety of effectors acting through its regulatory subunits. To probe the quaternary structure of nonactivated and activated forms of the kinase, we used the heterobifunctional, photoreactive cross-linker N-5-azido-2-nitrobenzoyloxysuccinimide. Mono-derivatization of the holoenzyme with the succinimidyl group, followed by photoactivation of the covalently attached azido group, resulted in intramolecular cross-linking to form two distinct heterodimers: a major (alphagamma) and a minor (betadelta) conjugate. Formation of both conjugates was significantly altered in activated conformations of the enzyme induced by phosphorylation, alkaline pH, and several allosteric activators (ADP, exogenous calmodulin/Ca2+, and Ca2+ alone). Of these activating mechanisms, all increased formation of alphagamma, except Ca2+ alone, which inhibited its formation. When cross-linking was carried out at alkaline pH or in the presence of ADP or exogenous calmodulin/Ca2+, the cross-linked enzyme remained activated following removal of the activators; however, cross-linking in the presence of Ca2+ resulted in sustained inhibition. The results indicate that perturbations in the subunit cross-linking forming the alphagamma dimer reflect the subsequent extent of sustained activation of the holoenzyme that is measured. The region cross-linked to the catalytic gamma subunit was confined to the C-terminal 1/6th of the alpha subunit, which contains known regulatory regions. These results suggest that activators of the phosphorylase kinase holoenzyme perturb interactions between the C-terminal region of the inhibitory alpha subunit and the catalytic gamma subunit, ultimately leading to activation of the latter.     

Novel chitosan-based films cross-linked by genipin with improved physical properties

Novel cross-linked chitosan-based films were prepared using the solution casting technique. A naturally occurring and nontoxic cross-linking agent, genipin, was used to form the chitosan and chitosan/poly(ethylene oxide) (PEO) blend networks, where two types of PEO were used, one with a molecular weight of 20 000 g/mol (HPEO) and the other of 600 g/mol (LPEO). Genipin is used in traditional Chinese medicine and extracted from gardenia fruit. Importantly, it overcomes the problem of physiological toxicity inherent in the use of some common synthetic chemicals as cross-linking agents. The mechanical properties and the stability in water of cross-linked and un-crosslinked chitosan and chitosan/PEO blend films were investigated. It was shown that, compared to the transparent yellow, un-cross-linked chitosan/PEO blend films, the genipin-cross-linked chitosan-based film, blue in color, was more elastic, was more stable, and had better mechanical properties. Genipin-cross-linking produced chitosan networks that were insoluble in acidic and alkaline solutions but were able to swell in these aqueous media. The swelling characteristics of the films exhibit sensitivity to the environmental pH and temperature. The surface properties of the films were also examined by contact angle measurements using water and mixtures of water/ethanol. The results showed that, with the one exception of cross-linked pure chitosan in 100% water, the cross-linked chitosan and chitosan/PEO blends were more hydrophobic than un-crosslinked ones.     

Effect of crosslinking in chitosan/aloe vera-based membranes for biomedical applications

The positive interaction between polysaccharides with active phytochemicals found in medicinal plants may represent a strategy to create active wound dressing materials useful for skin repair. In the present work, blended membranes composed of chitosan (Cht) and aloe vera gel were prepared through the solvent casting, and were crosslinked with genipin to improve their properties. Topography, swelling, wettability, mechanical properties and in vitro cellular response of the membranes were investigated. With the incorporation of aloe vera gel into chitosan solution, the developed chitosan/aloe-based membranes displayed increased roughness and wettability; while the genipin crosslinking promoted the formation of stiffer membranes in comparison to those of the non-modified membranes. Moreover, in vitro cell culture studies evidenced that the L929 cells have high cell viability, confirmed by MTS test and calcein-AM staining. The findings suggested that both blend compositions and crosslinking affected the physico-chemical properties and cellular behavior of the developed membranes.     

Swelling and mechanical properties of biopolymer hydrogels containing chitosan and bovine serum albumin

Experimental and theoretical investigations of the swelling and mechanical properties of hydrogels formed from chitosan, bovine serum albumin (BSA), and chitosan/BSA mixtures cross-linked with genipin were performed. The properties of cross-linked chitosan hydrogels were explained in terms of its polyelectrolyte behavior, which led to a gradual increase in swelling ratio below the pK value, but whereby its swelling ability was eliminated by the presence of salt that screened the charges. Comparison of theoretical and experimental calculations of the swelling ratio, however, indicated that complications arising from wastage of cross-links, and formation of polymerized genipin cross-links must be considered before quantitative prediction can be achieved. Cross-linked BSA hydrogels swelled even in the presence of salt, and a marked increase in swelling was observed below pH = 3 that was explained as the result of an acid induced denaturation of the protein that led to unfolding of the molecule. Swollen BSA hydrogels were mechanically weak, however. Composite gels made from a cross-linked mixture of chitosan and BSA exhibited the swelling behavior of BSA combined with the mechanical properties of chitosan and were therefore considered most suitable for use in a gastric environment.     

Immobilization of a keratinolytic protease from Purpureocillium lilacinum on genipin activated-chitosan beads

Keratinase from Purpureocillium lilacinum LPSC # 876 was immobilized on chitosan beads using two different cross-linking agents: glutaraldehyde and genipin. For its immobilization certain parameters were optimized such as cross-linker concentration, activation time and activation temperature. Under optimum conditions, enzyme immobilization resulted to be 96 and 92.8% for glutaraldehyde and genipin, respectively, with an activity recovery reaching up to 81% when genipin was used. The immobilized keratinase showed better thermal and pH stabilities compared to the soluble form, retaining more than 85% of its activity at pH 11 and 74% at 50 °C after 1 h of incubation. The residual activity of immobilized keratinase remained more than 60% of its initial value after five hydrolytic cycles. The results in this study support that glutaraldehyde could be replaced by genipin as an alternative cross-linking eco-friendly agent for enzyme immobilization.     

PAMAM conjugated chitosan through naphthalimide moiety for enhanced gene transfection efficiency

Development of efficient and safe gene carrier is the main hurdle for successful gene therapy till date. Poor water solubility and low transfection efficiency of chitosan are the main drawbacks to be efficient gene carrier for successful gene therapy. In this work, PAMAM conjugated chitosan was prepared through naphthalimide moiety by simple substitution reaction. The synthesis of the chitosan conjugates was confirmed by FTIR, ¹H NMR and XRD analyses. The conjugates showed enhanced DNA binding capability compared to that of unmodified chitosan. Moreover, the conjugates showed minimal cytotoxicity compared to that of polyethyleneimine (PEI, 25 kDa) and also showed good blood compatibility with negligible haemolysis. The transfection efficiency of the conjugate was significantly increased compared to that of unmodified chitosan and it also surpassed the transfection efficiency by PEI. Therefore, PAMAM conjugated chitosan can be used safely as alternate efficient gene delivery vector in gene therapy.     

Efficient gene transfer using reversibly cross-linked low molecular weight polyethylenimine.

Polyethylenimine (PEI) is a polycation with potential application as a nonviral vector for gene delivery. Here we show that after conjugation with homobifunctional amine reactive reducible cross-linking reagents, low molecular weight polyethylenimine efficiently mediates in vitro gene delivery to Chinese hamster ovary (CHO) cells. Two cross-linking reagents, dithiobis(succinimidylpropionate) (DSP) and dimethyl.3,3'-dithiobispropionimidate*2HCl (DTBP), were utilized based on their reactivity and chemical properties. Both reagents react with primary amines to form reducible cross-links; however, unlike DSP, the DTBP cross-linker maintains net polymer charge through amidine bond formation. PEI with a reported weight-average molecular weight (M(w)) of 800 Da was reacted with either DSP or DTBP at PEI primary amine:cross-link reactive group ratios of 1:1 and 2:1. The transfection efficiencies of the resulting cross-linked products were evaluated in CHO cells using a luciferase reporter gene under a cytomegalovirus (CMV) promoter. Our results show that cross-linked polymers mediate variable levels of transfection depending on the cross-linking reagent, the extent of conjugation, and the N/P ratio. In general, we found conjugate size to be proportional to gene transfer efficiency. Using gel retardation analysis, we also evaluate the capacity of the cross-linked polymers to condense plasmid DNA before and after reduction with 45 mM dithiothreitol (DTT). DTT mediated reduction of intra-cross-link disulfide bonds and inhibited condensation of DNA by conjugates cross-linked with DSP at a ratio of 1:1, but had little effect on the remaining polymers. Analogous intracellular reduction of transfection complexes by reduced glutathione could facilitate uncoupling of PEI from DNA to enhance gene expression.