Fatigue of immature baboon cortical bone

Strain-controlled uniaxial fatigue and monotonic tensile tests were conducted on turned femoral cortical bone specimens obtained from baboons at various ages of maturity. Fatigue loading produced a progressive loss in stiffness and an increase in hysteresis prior to failure, indicating that immature primate cortical bone responds to repeated loading in a fashion similar to that previously observed for adult human cortical bone. Bone fatigue resistance under this strain controlled testing decreased during maturation. Maturation was also associated with an increase in bone dry density, ash fraction and elastic modulus. The higher elastic modulus of more mature bone meant that these specimens were subjected to higher stress levels during testing than more immature bone specimens. Anatomical regions along the femoral shaft exhibited differences in strength and fatigue resistance.     

Dynamic stiffness and crossbridge action in muscle

Small sinusoidal vibrations at 300 HZ were applied to frog sartorius muscle to measure the dynamic stiffness (Young's modulus) throughout the course of tetanus. For a peak-to-peak amplitude of 0.4% the dynamic Young's modulus increased from 1.5 X 10(5) Nm-2 in the resting state to 2 X 10(7) Nm-2 in tetanus. After correction for the external connective tissue, the dynamic Young's modulus of the muscle was almost directly proportional to the tension throughout the development of tetanus. The ratio of dynamic Young's modulus to tensile stress thus remained constant (with a value at 300 Hz of approximately 100), consistently with Huxley and Simmon's identification of the crossbridges as the source of both tension and stiffness. For a single crossbridge the ratio of stiffness to tension was 8.2 X 10(7) m-1 at 300 Hz; it is deduced from literature data that the limiting value at high frequencies is about 1.6 X 10(8) m-1. This ratio is interpreted on Harrington's (1971) model to show that crossbridge action can be explained by a helix-coil transition of about 80 out of the 260 residues in each S-2 myosin strand. It is also shown that a helix-coil model can account for the observed rapid relaxation of muscle without invoking any complex behaviour of the crossbridge head.     

Dynamic response of immature bovine articular cartilage in tension and compression, and nonlinear viscoelastic modeling of the tensile response

Very limited information is currently available on the constitutive modeling of the tensile response of articular cartilage and its dynamic modulus at various loading frequencies. The objectives of this study were to (1) formulate and experimentally validate a constitutive model for the intrinsic viscoelasticity of cartilage in tension, (2) confirm the hypothesis that energy dissipation in tension is less than in compression at various loading frequencies, and (3) test the hypothesis that the dynamic modulus of cartilage in unconfined compression is dependent upon the dynamic tensile modulus. Experiment 1: Immature bovine articular cartilage samples were tested in tensile stress relaxation and cyclical loading. A proposed reduced relaxation function was fitted to the stress-relaxation response and the resulting material coefficients were used to predict the response to cyclical loading. Adjoining tissue samples were tested in unconfined compression stress relaxation and cyclical loading. Experiment 2: Tensile stress relaxation experiments were performed at varying strains to explore the strain-dependence of the viscoelastic response. The proposed relaxation function successfully fit the experimental tensile stress-relaxation response, with R2 = 0.970+/-0.019 at 1% strain and R2 = 0.992+/-0.007 at 2% strain. The predicted cyclical response agreed well with experimental measurements, particularly for the dynamic modulus at various frequencies. The relaxation function, measured from 2% to 10% strain, was found to be strain dependent, indicating that cartilage is nonlinearly viscoelastic in tension. Under dynamic loading, the tensile modulus at 10 Hz was approximately 2.3 times the value of the equilibrium modulus. In contrast, the dynamic stiffening ratio in unconfined compression was approximately 24. The energy dissipation in tension was found to be significantly smaller than in compression (dynamic phase angle of 16.7+/-7.4 deg versus 53.5+/-12.8 deg at 10(-3) Hz). A very strong linear correlation was observed between the dynamic tensile and dynamic compressive moduli at various frequencies (R2 = 0.908+/-0.100). The tensile response of cartilage is nonlinearly viscoelastic, with the relaxation response varying with strain. A proposed constitutive relation for the tensile response was successfully validated. The frequency response of the tensile modulus of cartilage was reported for the first time. Results emphasize that fluid-flow dependent viscoelasticity dominates the compressive response of cartilage, whereas intrinsic solid matrix viscoelasticity dominates the tensile response. Yet the dynamic compressive modulus of cartilage is critically dependent upon elevated values of the dynamic tensile modulus.     

High frequency characteristics of the arterial system

Pressure, flow and diameter were measured in the abdominal aorta of five anesthetized dogs during normal heart beats and heart beats with a superimposed impulse (generated by rapidly injecting a small volume of saline into the system). From Fourier analysis it was found that the impulse enhanced the amplitudes of the higher harmonics so that frequencies up to 80 Hz could be studied. Both the input impedance and apparent phase velocity above 20 Hz were independent of frequency and their average values were designated as characteristic impedance and true phase velocity. Average characteristic impedance for all five animals was 2.0 +/- 0.1 X 10(8) Nsm-5 and average phase velocity was 8.3 +/- 0.6 ms-1. Phase velocities calculated from characteristic impedance (1.76-2.39 X 10(8) Nsm-5) and from the slope of the pressure-diameter relation (0.102-0.25 X 10(-8) Nm-3) were similar to the true phase velocity as defined above (6.79-9.85 ms-1). It may be concluded that the input impedance converges to characteristic impedance and apparent phase velocity converges to phase velocity for high frequencies.     

Near-terminal creep damage does not substantially influence fatigue life under physiological loading

Cortical bone specimens were damaged using repeated blocks of tensile creep loading until a near-terminal amount of creep damage was generated (corresponding to a reduction in elastic modulus of 15%). One group of cortical bone specimens was submitted to the near-terminal damage protocol and subsequently underwent fatigue loading in tension with a maximum strain of 2000 με (Damage Fatigue, n=5). A second group was submitted to cyclic fatigue loading but was not pre-damaged (Control Fatigue, n=5). All but one specimen (a damaged specimen) reached run-out (10 million cycles, 7.7 days). No significant differences in microscopic cracks or other tissue damage were observed between the two groups or between either group and additional, completely unloaded specimens. Our results suggest that damage in cortical bone allograft that is not obvious or associated with a stress riser may not substantially affect its fatigue life under physiologic loading.     

Ca2+/protein modulator-dependent and -independent cyclic GMP phosphodiesterase from hog heart.

Ca2+/protein modulator-dependent and -independent guanosine 3':5'-monophosphate (cGMP) phosphodiesterases were separated from hog heart. The protein modulator-free Ca2+/protein modulator-dependent enzyme was partially purified by repeated DEAE-cellulose column chromatography and heat treatment. The final preparation of this enzyme showed no significant basal activity under the standard assay conditions. Lineweaver-Burk plots of the Ca2+/protein modulator-dependent enzyme activity indicated the presence of only a single kinetic form of the enzyme with Km=2.0 X 10(-6) M for for cGMP, whereas the plots for the independent enzyme were anomalous, showing both high and low K m values for cGMP. The Ca2+/protein modulator-dependent enzyme proved relatively stable at 48 degrees C for 1 h, but the independent form lost its activity under the same conditions. Furthermore, 50% inhibition of the dependent enzyme activity, but only 10% inhibition of the independent enzyme activity, was observed with 0.1 mM adenosine 3':5'-monophosphate (cAMP) when 1 muM cGMP was employed as a substrate.     

Effect of temperature and concentration on rheological behavior of xanthan-carob mixed gels

The gelation and melting behavior of 1∶1, 1∶3 xanthan-carob mixed gels were evaluated at isothermal and non-isothermal states, as a function of total polymer concentrations of 0.1, 0.5 and 1%. A thermal hysteresis was observed between gelation and melting. The higher the polymer concentration, the higher the melting temperature. The gelation points were determined by three criteria. Depending on the criterion used the gelation temperature was different (52 to 70°C). Pseudoequilibrium modulus and elastic active network chain (EANC) concentration were calculated from the plateau modulus in the frequency spectrum. Temperature dependence of the monomeric friction coefficient was estimated from the relaxation time and EANC. Time-temperature superposition theory was not applicable due to dramatic phase transitions occurring during the gelation of X/C mixture.     

Nanostructure and elastic modulus of single trabecula in bovine cancellous bone

We aimed to investigate the elastic modulus of trabeculae using tensile tests and assess the effects of nanostructure at the hydroxyapatite (HAp) crystal scale on the elastic modulus. In the experiments, 18 trabeculae that were at least 3 mm in length in the proximal epiphysis of three adult bovine femurs were used. Tensile tests were conducted using a small tensile testing device coupled with microscopy under air-dried condition. The c-axis orientation of HAp crystals and the degree of orientation were measured by X-ray diffraction. To observe the deformation behavior of HAp crystals under tensile loading, the same tensile tests were conducted in X-ray diffraction measurements. The mineral content of specimens was evaluated using energy dispersive X-ray spectrometry. The elastic modulus of a single trabecula varied from 4.5 to 23.6 GPa, and the average was 11.5±5.0 GPa. The c-axis of HAp crystals was aligned with the trabecular axis and the crystals were lineally deformed under tensile loading. The ratio of the HAp crystal strain to the tissue strain (strain ratio) had a significant correlation with the elastic modulus (r=0.79; P<0.001). However, the mineral content and the degree of orientation did not vary widely and did not correlate with the elastic modulus in this study. It suggests that the strain ratio may represent the nanostructure of a single trabecula and would determine the elastic modulus as well as mineral content and orientation.     

Elastic energy storage in tendons: mechanical differences related to function and age

We investigated the possibility that tendons that normally experience relatively high stresses and function as springs during locomotion, such as digital flexors, might develop different mechanical properties from those that experience only relatively low stresses, such as digital extensors. At birth the digital flexor and extensor tendons of pigs have identical mechanical properties, exhibiting higher extensibility and mechanical hysteresis and lower elastic modulus, tensile strength, and elastic energy storage capability than adult tendons. With growth and aging these tendons become much stronger, stiffer, less extensible, and more resilient than at birth. Furthermore, these alterations in elastic properties occur to a significantly greater degree in the high-load-bearing flexors than in the low-stress extensors. At maturity the pig digital flexor tendons have twice the tensile strength and elastic modulus but only half the strain energy dissipation of the corresponding extensor tendons. A morphometric analysis of the digital muscles provides an estimate of maximal in vivo tendon stresses and suggests that the muscle-tendon unit of the digital flexor is designed to function as an elastic energy storage element whereas that of the digital extensor is not. Thus the differences in material properties between mature flexor and extensor tendons are correlated with their physiological functions, i.e., the flexor is much better suited to act as an effective biological spring than is the extensor.     

Tensile experiments and SEM fractography on bovine subchondral bone

Subchondral bone undecalcified samples, extracted from bovine femoral heads, are subjected to a direct tensile load. The Young's modulus of each sample is determined from repeated tests within the elastic limit. In a last test, the tensile load is increased up to the specimen failure, determining the ultimate tensile strength. The investigation is performed on both dry and wet specimens. The measured Young's modulus for dry samples is 10.3+/-2.5GPa, while that of wet samples is 3.5+/-1.2GPa. The ultimate tensile strengths are 36+/-10 and 30+/-7.5MPa for dry and wet specimens, respectively. SEM micrographs of failure surfaces show characteristic lamellar bone structures, with lamellae composed of calcified collagen fibers. Rudimentary osteon-like structures are also observed. Failure surfaces of wet samples show a marked fiber pull-out, while delamination predominates in dry samples. The obtained results are interpreted on the basis of the deformation mechanisms typical of fiber-reinforced laminated composite materials.     

Analysis of the passive mechanical properties of rat carotid arteries

The passive mechanical properties of rat carotid arteries were studied in vitro. Using a tensile testing machine and a piston pump, intact segments of carotid arteries were subjected to large deformations both in the longitudinal and circumferential directions. Internal pressure, external diameter, length and longitudinal force were measured during the experiment and compared with the in vivo dimensions of the segments prior to excision. The anisotropic mechanical properties of the vessel wall material were analyzed using incremental elastic moduli and incremental Poisson's ratios. The results suggest that there is a characteristic deformation pattern common to all vessels investigated which is highly correlated with the conditions of loading that occur in vivo. That is, under average physiological deformation of the vessel, the longitudinal force is nearly independent of internal pressure. In this range of loading the circumferential incremental elastic modulus is nearly independent of longitudinal strain. However, the longitudinal and radial incremental elastic moduli vary significantly with deformation in this direction. The values of the moduli in all three directions increase with raising internal pressure. The weak coupling between circumferential and longitudinal direction in the wall material of carotid arteries is shown by the small value of the corresponding incremental Poisson's ratios.     

Mechanical properties of a mature biofilm from a wastewater system: from microscale to macroscale level

A fundamental understanding of biofilm mechanical stability is critical in order to describe detachment and develop biofouling control strategies. It is thus important to characterise the elastic deformation and flow behaviour of the biofilm under different modes of applied force. In this study, the mechanical properties of a mature wastewater biofilm were investigated with methods including macroscale compression and microscale indentation using atomic force microscopy (AFM). The mature biofilm was found to be mechanically isotropic at the macroscale level as its mechanical properties did not depend on the scales and modes of loading. However, the biofilm showed a tendency for mechanical inhomogeneity at the microscale level as indentation progressed deeper into the matrix. Moreover, it was observed that the adhesion force had a significant influence on the elastic properties of the biofilm at the surface, subjected to microscale tensile loading. These results are expected to inform a damage-based model for biofilm detachment.     

How is the indentation modulus of bone tissue related to its macroscopic elastic response? A validation study

This work consists of the validation of a novel approach to estimate the local anisotropic elastic constants of the bone extracellular matrix using nanoindentation. For this purpose, nanoindentation on two planes of material symmetry were analyzed and the resulting longitudinal elastic moduli compared to the moduli measured with a macroscopic tensile test. A combined lathe and tensile system was designed that allows machining and testing of cylindrical microspecimens of approximately 4mm in length and 300 microm in diameter. Three bovine specimens were tested in tension and their outer geometry and porosity assessed by synchrotron radiation microtomography. Based on the results of the traction test and the precise outer geometry, an apparent longitudinal Young's modulus was calculated. Results between 20.3 and 27.6 GPa were found that match with previously reported values for bovine compact bone. The same specimens were then characterized by nanoindentation on a transverse and longitudinal plane. A longitudinal Young's modulus for the bone matrix was then derived using the numerical scheme proposed by Swadener and Pharr and the fabric-elasticity relationship by Zysset and Curnier. Based on the matrix modulus and a power law effective volume fraction, an apparent longitudinal Young's modulus was predicted for each microspecimen. This alternative approach provided values between 19.9 and 30.0 GPa, demonstrating differences between 2% and 13% to the values provided by the initial tensile test. This study therefore raises confidence in our nanoindentation protocol of the bone extracellular matrix and supports the underlying hypotheses used to extract the anisotropic elastic constants.     

A miniaturised parallel-plate shearing apparatus for the measurement of cell adhesion

The design and construction of a miniaturised shearing apparatus is described. Cultures (24 h) of an established epithelial cell line (BEB) were exposed to flow conditions in the shearing chamber at 37 degrees C, and subsequently glass coverslip cultures were prepared for photography. The critical shear radius (CSR) was determined by densitometry from a negative film and the minimum distraction force (MDF) at the CSR calculated using predetermined viscosity values of the flow medium. The mean calculated MDF of BEB cells ranged from 1.04-1.36 Nm-2, and was independent of the culture inoculation density (9 to 37 X 10(4) cells cm-2) and the time (5-20 min) of exposure to shearing conditions. The MDF was increased to 3.3 Nm-2 by a 30 min exposure of cultures to concanavalin A (50 micrograms ml-1), and this effect was abolished by treating with mannose (0.05 M). The results demonstrated that the radial flow chamber principle is applicable to the measurement of cell to substratum adhesion of cultured mammalian cells.     

Elevated extracellular calcium concentrations induce type X collagen synthesis in chondrocyte cultures

Chondrocytes at different stages of cellular differentiation were isolated from the tarsal element (immature chondrocytes) and zones 2 and 3 (mature chondrocytes) of 12-d chick embryo tibiotarsus. The chondrocytes from the two sources differed in their cell morphologies, growth rate and production of type X collagen. In 24 h, zone 2 and 3 chondrocytes synthesized 800 times more type X collagen than tarsal chondrocytes. The effect of exogenous CaCl2 (5 and 10 mM) on the synthesis of type X collagen by both mature and immature chondrocytes was tested. After a 72-h incubation of zone 2 and 3 chondrocytes with CaCl2 type X collagen increased 8-fold with 5 mM and 10-fold with 10 mM Ca2+. [3H]Proline incorporation into culture medium and matrix macromolecules increased 11 and 32% with 5 and 10 mM CaCl2, respectively. Type II collagen synthesis was not affected by elevated extracellular Ca2+ during this 72-h period. Similar studies with tarsal chondrocytes demonstrated a time- and dose-dependent response to CaCl2 with type X collagen levels reaching a 4-fold and 15-fold increase over controls with 5 and 10 mM Ca2+, respectively, at 48 h. Elevated extracellular Ca2+ had no effect on cell proliferation. These observations offer the first direct evidence of the induction of type X collagen synthesis with elevated extracellular Ca2+.     

Mechanical response of porous scaffolds for cartilage engineering

Mechanical properties of scaffolds seeded with mesenchymal stem cells used for cartilage repair seem to be one of the critical factors in possible joint resurfacing. In this paper, the effect of adding hyaluronic acid, hydroxyapatite nanoparticles or chitosan nanofibers into the cross-linked collagen I on the mechanical response of the lyophilized porous scaffold has been investigated in the dry state at 37 oC under tensile loading. Statistical significance of the results was evaluated using ANOVA analysis. The results showed that the addition of hyaluronic acid significantly (p<0.05) reduced the tensile elastic modulus and enhanced the strength and deformation to failure of the modified cross-linked collagen I under the used test conditions. On the other hand, addition of hydroxyapatite nanoparticles and chitosan nanofibers, respectively, increased the elastic modulus of the modified collagen ten-fold and four-fold, respectively. Hydroxyapatite caused significant reduction in the ultimate deformation at break while chitosan nanofibers enhanced the ultimate deformation under tensile loading substantially (p<0.05). The ultimate tensile deformation was significantly (p<0.05) increased by addition of the chitosan nanofibers. The enhanced elastic modulus of the scaffold was translated into enhanced resistance of the porous scaffolds against mechanical load compared to scaffolds based on cross-linked neat collagen or collagen with hyaluronic acid with similar porosity. It can be concluded that enhancing the rigidity of the compact scaffold material by adding rigid chitosan nanofibers can improve the resistance of the porous scaffolds against compressive loading, which can provide more structural protection to the seeded mesenchymal stem cells when the construct is implanted into a lesion. Moreover, scaffolds with chitosan nanofibers seemed to enhance cell growth compared to the neat collagen I when tested in vitro as well as the scaffold stability, extending its resorption to more than 10 weeks.     

Thermoelasticity of red blood cell membrane.

The elastic properties of the human red blood cell membrane have been measured as functions of temperature. The area compressibility modulus and the elastic shear modulus, which together characterize the surface elastic behavior of the membrane, have been measured over the temperature range of 2-50 degrees C with micropipette aspiration of flaccid and osmotically swollen red cells. In addition, the fractional increase in membrane surface area from 2-50 degrees C has been measured to give a value for the thermal area expansivity. The value of the elastic shear modulus at 25 degrees C was measured to be 6.6 X 10(-3) dyne/cm. The change in the elastic shear modulus with temperature was -6 X 10(-5) dyne/cm degrees C. Fractional forces were shown to be only on the order of 10-15%. The area compressibility modulus at 25 degrees C was measured to be 450 dyne/cm. The change in the area compressibility modulus with temperature was -6 dyne/cm degrees C. The thermal area expansivity for red cell membrane was measured to be 1.2 X 10(-3)/degrees C. With this data and thermoelastic relations the heat of expansion is determined to be 110-200 ergs/cm2; the heat of extension is 2 X 10(-2) ergs/cm2 for unit extension of the red cell membrane. The heat of expansion is of the order anticipated for a lipid bilayer idealized as twice the behavior of a monolayer at an oil-water interface. The observation that the heat of extension is positive demonstrates that the entropy of the material increases with extension, and that the dominant mechanism of elastic energy storage is energetic. Assuming that the red cell membrane shear rigidity is associated with "spectrin," unit extension of the membrane increases the configurational entropy of spectrin by 500 cal/mol.     

Biomechanics of isolated tomato (Solanum lycopersicum L.) fruit cuticles: the role of the cutin matrix and polysaccharides

The mechanical characteristics of the cuticular membrane (CM), a complex composite biopolymer basically composed of a cutin matrix, waxes, and hydrolysable polysaccharides, have been described previously. The biomechanical behaviour and quantitative contribution of cutin and polysaccharides have been investigated here using as experimental material mature green and red ripe tomato fruits. Treatment of isolated CM with anhydrous hydrogen fluoride in pyridine allowed the selective elimination of polysaccharides attached to or incrusted into the cutin matrix. Cutin samples showed a drastic decrease in elastic modulus and stiffness (up to 92%) compared with CM, which clearly indicates that polysaccharides incorporated into the cutin matrix are responsible for the elastic modulus, stiffness, and the linear elastic behaviour of the whole cuticle. Reciprocally, the viscoelastic behaviour of CM (low elastic modulus and high strain values) can be assigned to the cutin. These results applied both to mature green and red ripe CM. Cutin elastic modulus, independently of the degree of temperature and hydration, was always significantly higher for the ripe than for the green samples while strain was lower; the amount of phenolics in the cutin network are the main candidates to explain the increased rigidity from mature green to red ripe cutin. The polysaccharide families isolated from CM were pectin, hemicellulose, and cellulose, the main polymers associated with the plant cell wall. The three types of polysaccharides were present in similar amounts in CM from mature green and red ripe tomatoes. Physical techniques such as X-ray diffraction and Raman spectroscopy indicated that the polysaccharide fibres were mainly randomly oriented. A tomato fruit CM scenario at the supramolecular level that could explain the observed CM biomechanical properties is presented and discussed.     

Dynamic mechanical characteristics of intact and structurally modified bovine pericardial tissues

Bovine pericardium (BP) is a source of natural biomaterials with a wide range of clinical applications. In the present work we studied the dynamic mechanical behavior of BP in native form and under specific enzymatic degradation with chondroitinase ABC extracted a 17% of the total glycosaminoglycans (GAGs). The GAGs content of native BP was composed mainly from hyaluronan, chondroitine sulfate and dermatan sulfate. Dynamic tensile mechanical testing of BP in the frequency range 0.1-20 Hz demonstrated its viscoelastic nature. The storage modulus was equal to 6.5 (native) and 5.5 (degraded) MPa initially, increased in the region nearby 1 Hz by about 15%. This was related with physical resonance mechanisms activated in this frequency region. The high modulus (modulus of the high linear phase of stress-strain) was equal to 14 (native) and 10 (degraded) MPa, dropped at high frequencies to 7 and 5 Mpa, respectively. The damping, expressed by the hysteresis, was equal to 20% of the loading energy, changed exponentially with the frequency to 30% at 20 Hz. It seemed that of the elastic mechanical parameters, the storage modulus and the high modulus were even slightly dropped as a result of degradation. As a final conclusion, there was evident that GAGs may play a non-negligible role in the dynamic mechanical behavior of BP and, probably in other soft tissue biomechanics. It is suggested that the GAGs content may be considered during the design and chemical modification of biomaterials based on BP and other soft tissues.     

Combinatorial polymer electrospun matrices promote physiologically-relevant cardiomyogenic stem cell differentiation

Myocardial infarction results in extensive cardiomyocyte death which can lead to fatal arrhythmias or congestive heart failure. Delivery of stem cells to repopulate damaged cardiac tissue may be an attractive and innovative solution for repairing the damaged heart. Instructive polymer scaffolds with a wide range of properties have been used extensively to direct the differentiation of stem cells. In this study, we have optimized the chemical and mechanical properties of an electrospun polymer mesh for directed differentiation of embryonic stem cells (ESCs) towards a cardiomyogenic lineage. A combinatorial polymer library was prepared by copolymerizing three distinct subunits at varying molar ratios to tune the physicochemical properties of the resulting polymer: hydrophilic polyethylene glycol (PEG), hydrophobic poly(ε-caprolactone) (PCL), and negatively-charged, carboxylated PCL (CPCL). Murine ESCs were cultured on electrospun polymeric scaffolds and their differentiation to cardiomyocytes was assessed through measurements of viability, intracellular reactive oxygen species (ROS), α-myosin heavy chain expression (α-MHC), and intracellular Ca(2+) signaling dynamics. Interestingly, ESCs on the most compliant substrate, 4%PEG-86%PCL-10%CPCL, exhibited the highest α-MHC expression as well as the most mature Ca(2+) signaling dynamics. To investigate the role of scaffold modulus in ESC differentiation, the scaffold fiber density was reduced by altering the electrospinning parameters. The reduced modulus was found to enhance α-MHC gene expression, and promote maturation of myocyte Ca(2+) handling. These data indicate that ESC-derived cardiomyocyte differentiation and maturation can be promoted by tuning the mechanical and chemical properties of polymer scaffold via copolymerization and electrospinning techniques.