Nifedipine loaded chitosan microspheres prepared by emulsification phase-separation

A high yield of nifedipine-chitosan microspheres could be obtained using an emulsification phase-separation method. A high level of entrapment of nifedipine in the microspheres was achieved. The microspheres exhibited excellent swelling properties. Differential scanning calorimetry, X-ray diffractometry, and scanning electron microscopy confirmed that at 1.84% loading, nifedipine was dispersed molecularly. The microspheres exhibited faster release at low loadings compared to high loadings. Fitting the data to the coupled Fickian/case II equation, showed that at low loadings polymer relaxation coefficients (k₂) were high. As the polymer content increased in the microspheres, the value of n (diffusional exponent characteristic of the release mechanism) approached one, which is indicative of zero order.     

Interpenetrating polymer network (IPN) hydrogel microspheres for oral controlled release application

Interpenetrating polymer network (IPN) hydrogel microspheres of sodium carboxymethyl cellulose (NaCMC) and poly(vinyl alcohol) (PVA) were prepared by water-in-oil (w/o) emulsion crosslinking method for oral controlled release delivery of a non-steroidal anti-inflammatory drug, diclofenac sodium (DS). The microspheres were prepared with various ratios of NaCMC to PVA, % drug loading and extent of crosslinking density at a fixed polymer weight. The prepared microspheres with loose and rigid surfaces were evidenced by scanning electron microscope (SEM). Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) analysis confirmed the IPN formation. Differential scanning calorimetry (DSC) study was performed to understand the dispersion nature of drug after encapsulation. The in vitro drug release study was extensively evaluated depending on the process variables in both acid and alkaline media. All the formulations exhibited satisfactory physicochemical and in vitro release characteristics. Release data indicated a non-Fickian trend of drug release from the formulations. Based on the results of this study suggest that DS loaded IPN microspheres were suitable for oral controlled release application.     

Preparation and in vitro evaluation of xanthan gum facilitated superabsorbent polymeric microspheres

Interpenetrating polymer network (IPN) hydrogel microspheres of xanthan gum (XG) based superabsorbent polymer (SAP) and poly(vinyl alcohol) (PVA) were prepared by water-in-oil (w/o) emulsion crosslinking method for sustained release of ciprofloxacin hydrochloride (CIPRO). The microspheres were prepared with various ratios of hydrolyzed SAP to PVA and extent of crosslinking density. The prepared microspheres with loose and rigid surfaces were evidenced by scanning electron microscope (SEM). Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) analysis confirmed the IPN formation. Differential scanning calorimetry (DSC) study was performed to understand the dispersion nature of drug after encapsulation. The in vitro drug release study was extensively evaluated depending on the process variables in both acidic and alkaline media. All the formulations exhibited satisfactory physicochemical and in vitro release characteristics. Release data indicated a non-Fickian trend of drug release from the formulations. Based on the results, this study suggest that CIPRO loaded IPN microspheres were suitable for sustained release application.     

Nifedipine loaded chitosan microspheres: characterization of internal structure

In the present investigation, a simple technique was employed to obtain cross-sections of unloaded and nifedipine loaded chitosan microspheres. Microspheres, adhering to a polymerized resin block, were cut with an ultramicrotome and viewed with a scanning electron microscope. Unloaded microspheres exhibited a uniform dense matrix structure while crystals of nifedipine were clearly visible in the drug-loaded microspheres. At 2% drug loading, however, no crystals could be seen in the microspheres indicating that either the drug was molecularly dispersed or dissolved in the matrix at this concentration. This was confirmed by powder X-ray diffractometry studies where no peak due to crystalline nifedipine was observed. At high Span 85 concentration (1.5% w/v), the external surface of the microspheres collapsed, but the internal structure remained dense. When the drug was dispersed in the chitosan solution with stirring during preparation, the entrapment was good and the shape of the crystals was changed. The internal structure of the microspheres following dissolution exhibited the presence of pores.     

Nifedipine loaded chitosan microspheres: characterization of internal structure

In the present investigation, a simple technique was employed to obtain cross-sections of unloaded and nifedipine loaded chitosan microspheres. Microspheres, adhering to a polymerized resin block, were cut with an ultramicrotome and viewed with a scanning electron microscope. Unloaded microspheres exhibited a uniform dense matrix structure while crystals of nifedipine were clearly visible in the drug-loaded microspheres. At 2% drug loading, however, no crystals could be seen in the microspheres indicating that either the drug was molecularly dispersed or dissolved in the matrix at this concentration. This was confirmed by powder X-ray diffractometry studies where no peak due to crystalline nifedipine was observed. At high Span 85 concentration (1.5% w/v), the external surface of the microspheres collapsed, but the internal structure remained dense. When the drug was dispersed in the chitosan solution with stirring during preparation, the entrapment was good and the shape of the crystals was changed. The internal structure of the microspheres following dissolution exhibited the presence of pores.     

Encapsulation of protein nanoparticles into uniform-sized microspheres formed in a spinning oil film

A new spinning oil film (SOF) solid-in-oil-in-oil emulsion process was developed to produce uniform-sized proteinloaded biodegradable microspheres. A thin SOF on a cylindrical rotor was used to shear droplets from a nozzle tip to control droplet size. The resulting microspheres with low polydispersity (6%) produced a low burst (6%–11%) release even at high loadings (13%–18% encapsulated solids, 8%–12% protein). The SOF process had a high yield and did not require the presence of water, which can cause protein denaturation, or surfactants, which may be unwanted in the final product. Amorphous protein and crystalline excipient solids were encapsulated into 3 different polymers, giving a homogenous drug distribution throughout the microspheres, and an essentially complete protein encapsulation efficiency (average=99%). In contrast, large burst release was observed for polydisperse microspheres produced by a conventional emulsification technique, particularly for microspheres smaller than 25 μm in diameter, which gave 93% burst at 15% loading. The uniform encapsulation of high loadings of proteins into microspheres with low polydispersity in an anhydrous process is of practical interest in the development of controlled-release protein therapeutics. Published: December 6, 2005     

Preparation of biodegradable microspheres and matrix devices containing naltrexone

In this study, the use of biodegradable polymers for microencapsulation of naltrexone using solvent evaporation technique is investigated. The use of naltrexone microspheres for the preparation of matrix devices is also studied. For this purpose, poly(L-lactide) (PLA) microspheres containing naltrexone prepared by solvent evaporation technique were compressed at temperatures above the Tg of the polymer. The effect of different process parameters, such as drug/polymer ratio and stirring rate during preparation of microspheres, on the morphology, size distribution, and in vitro drug release of microspheres was studied. As expected, stirring rate influenced particle size distribution of microspheres and hence drug release profiles. By increasing the stirring speed from 400 to 1200 rpm, the mean diameter of microspheres decreased from 251 μm to 104 μm. The drug release rate from smaller microspheres was faster than from larger microspheres. However, drug release from microspheres with low drug content (20% wt/wt) was not affected by the particle size of microspheres. Increasing the drug content of microspheres from 20% to 50% wt/wt led to significantly faster drug release from microspheres. It was also shown that drug release from matrix devices prepared by compression of naltrexone microspheres is much slower than that of microspheres. No burst release was observed with matrix devices. Applying higher compression force, when compressing microspheres to produce tablets, resulted in lower drug release from matrix devices. The results suggest that by regulating different variables, desired release profiles of naltrexone can be achieved using a PLA microparticulate system or matrix devices.     

Taste Masking by Spray-Drying Technique

The purpose of this research was to develop the taste-masked microspheres of intensely bitter drug ondansetron hydrochloride (OSH) by spray-drying technique. The bitter taste threshold value of OSH was determined. Three different polymers viz. Chitosan, Methocel E15 LV, and Eudragit E100 were used for microsphere formation, and the effect of different polymers and drug–polymer ratios on the taste masking and release properties of microspheres was investigated. The microspheres were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy, Drug loading, in vitro bitter taste evaluation, and drug-release properties. The taste masking was absent in methocel microspheres at all the drug–polymer ratios. The Eudragit microspheres depicted taste masking at 1:2 drug–polymer ratio whereas with Chitosan microspheres the taste masking was achieved at 1:1 drug–polymer ratio. The drug release was about 96.85% for eudragit microspheres and 40.07% for Chitosan microspheres in 15 min.     

Evaluation of Ionotropic Cross-Linked Chitosan/Gelatin B Microspheres of Tramadol Hydrochloride

Microspheres of tramadol hydrochloride (TM) for oral delivery were prepared by complex coacervation method without the use of chemical cross-linking agents such as glutaraldehyde to avoid the toxic reactions and other undesirable effects of the chemical cross-linking agents. Alternatively, ionotropic gelation was employed by using sodium-tripolyphosphate as cross-linking agent. Chitosan and gelatin B were used as polymer and copolymer, respectively. All the prepared microspheres were subjected to various physicochemical studies, such as drug–polymer compatibility by thin layer chromatography (TLC) and Fourier transform infrared (FTIR) spectroscopy, surface morphology by scanning electron microscopy, frequency distribution, drug entrapment efficiency, in vitro drug release characteristics and release kinetics. The physical state of drug in the microspheres was determined by differential scanning calorimetry (DSC) and X-ray diffractometry (XRD). TLC and FTIR studies indicated no drug–polymer incompatibility. All the microspheres showed initial burst release followed by a fickian diffusion mechanism. DSC and XRD analysis indicated that the TM trapped in the microspheres existed in an amorphous or disordered-crystalline status in the polymer matrix. From the preliminary trials, it was observed that it may be possible to formulate TM microspheres by using biodegradable natural polymers such as chitosan and gelatin B to overcome the drawbacks of TM and to increase the patient compliance.     

Spray-dried mucoadhesive microspheres: Preparation and transport through nasal cell monolayer

The purpose of this research was to prepare spray-dried mucoadhesive microspheres for nasal delivery. Microspheres composed of hydroxypropyl methylcellulose (H), chitosan (CS), carbopol 934P (CP) and various combinations of these mucoadhesive polymers, and maltodextrin (M), colloidal silicon dioxide (A), and propylene glycol (P) as filler and shaper, were prepared by spray-drying technique. Using propranolol HCl as a model drug, microspheres were prepared at loadings exceedings 80% and yields between 24% and 74%. Bulky, free flowing microspheres that had median particle size between 15 and 23 μm were obtained. Their zeta potential was according to the charge of polymer. Adhesion time of mucoadhesive microspheres on isolated pig intestine was ranked, CS>CP: H>CP>H, while the rank order of swelling was CP>CS>H. Increasing the amount of CP in CP∶H formulations increased the percentage of swelling. Infrared (IR) spectra showed no interaction between excipients used except CS with acetic acid. The release of drug from CP and CP∶H microspheres was slower than the release from H and CS microspheres, correlated to their viscosity and swelling. Long lag time from the CP microspheres could be shortened when combined with H. The permeation of drug through nasal cell monolayer corresponded to their release profiles. These microspheres affected the integrity of tight junctions, relative to their swelling and charge of polymer. Cell viability was not affected except from CS microspheres, but recovery could be obtained. In conclusion, spray-dried microspheres of H, CS, CP, and CP∶H could be prepared to deliver drug through nasal cell monolayer via the opening of tight junction without cell damaging. Published: February 10, 2006     

Albumin microspheres as carriers for the antiarthritic drug celecoxib

The present study investigates the preparation of celecoxib-loaded albumin microspheres and the biodistribution of technetium-99m (^99mTc)-labeled celecoxib as well as its microspheres after intravenous administration. Microspheres were prepared using a natural polymer BSA using emulsification chemical cross-linking method. The prepared microspheres were characterized for entrapment efficiency, particle size, and in vitro drug release. Surface morphology was studied by scanning electron microscopy. Biodistribution studies were performed by radiolabeling celecoxib (CS) and its microspheres (CMS) using^99mTc and injecting arthritic rats intravenously. The geometric mean diameter of the microspheres was found to be 5.46 μm. In vitro release studies indicated that the microspheres sustained the release of the drug for }6 days. Radioactivity measured in different organs after intravenous administration of celecoxib solution showed a significant amount of radioactivity in the liver and spleen. In case of celecoxib-loaded microspheres, a significant amount of radioactivity accumulated in the lungs. No significant difference (P>.1) in the radioactivity was observed between the inflamed joint and the noninflamed joint following intravenous injection of^99mTc-CS. However, in case of the microspheres (CMS), the radioactivity present in the inflamed joint was 2.5-fold higher than in the noninflamed joint. The blood kinetic studies revealed that celecoxib-loaded albumin microspheres exhibited prolonged circulation than the celecoxib solution.     

In Vitro and In Vivo Evaluations of PLGA Microspheres Containing Nalmefene

Poor patient compliance, untoward reactions and unstable blood drug levels after the bolus administration are impeding the pharmacotherapy for insobriety. A long-acting preparation may address these limitations. The aim of this paper was to further investigate the in vitro characteristics and in vivo performances of nalmefene microspheres. Nalmefene was blended with poly (lactide-co-glycolide) (PLGA) to prepare the target microspheres by an O/O emulsification solvent evaporation method. The prepared microspheres exhibited a controlled release profile of nalmefene in vitro over 4 weeks, which was well fitted with a first-order model. In vitro degradation study showed that the drug release in vitro was dominated by both drug diffusion and polymer degradation mechanisms. Pharmacokinetics study indicated that the prepared microspheres could provide a relatively constant of nalmefene plasma concentration for at least one month in rats. The in vivo pharmacokinetics profile was well correlated with the in vitro drug release. Pharmacodynamics studies revealed that the drug loaded microspheres could produce a long-acting antagonism efficacy on rats. These results demonstrated the promising application of injectable PLGA microspheres containing nalmefene for the long-term treatment of alcohol dependence.     

Ethylcellulose-Based Matrix-Type Microspheres: Influence of Plasticizer RATIO as Pore-Forming Agent

In this study, ethylcellulose (EC)-based microsphere formulations were prepared without and with triethyl citrate (TEC) content of 10% and 30% by water-in-oil emulsion-solvent evaporation technique. Diltiazem hydrochloride (DH) was chosen as a hydrophilic model drug and used at different drug/polymer ratios in the microspheres. The aim of the work was to evaluate the influence of plasticizer ratio on the drug release rate and physicochemical characteristics of EC-based matrix-type microspheres. The resulting microspheres were evaluated for encapsulation efficiency, particle size and size distribution, surface morphology, total pore volume, thermal characteristics, drug release rates, and release mechanism. Results indicated that the physicochemical properties of microspheres were strongly affected by the drug/polymer ratio investigated and the concentration of TEC used in the production technique. The surface morphology and pore volume of microspheres significantly varied based on the plasticizer content in the formulation. DH release rate from EC-based matrix-type microspheres can be controlled by varying the DH to polymer and plasticizer ratios. Glass transition temperature values tended to decrease in conjunction with increasing amounts of TEC. Consequently, the various characteristics of the EC microspheres could be modified based on the plasticized ratio of TEC.     

Synthesis and characterization of semi-interpenetrating polymer network microspheres of acrylamide grafted dextran and chitosan for controlled release of acyclovir

Semi-interpenetrating polymer network (IPN) microspheres of acrylamide grafted on dextran (AAm-g-Dex) and chitosan (CS) were prepared by emulsion-crosslinking method using glutaraldehyde (GA) as a crosslinker. The grafting efficiency was found to be 94%. Acyclovir, an antiviral drug with limited water solubility, was successfully encapsulated into IPN microspheres by varying the ratio of AAm-g-Dex and CS, % drug loading and amount of GA. Microspheres were characterized by FT-IR spectroscopy to assess the formation of IPN structure and to confirm the absence of chemical interactions between drug, polymer and crosslinking agent. Particle size was measured using laser light scattering technique. Microspheres with average particle sizes in the range of 265–388 μm were obtained. Differential scanning calorimetry (DSC) and X-ray diffraction (X-RD) studies were performed to understand the crystalline nature of drug after encapsulation into IPN microspheres. Acyclovir encapsulation of up to 79.6% was achieved as measured by UV spectroscopy. Both equilibrium and dynamic swelling studies were performed in 0.1 N HCl. Diffusion coefficients (D) and diffusional exponents (n) for water transport were determined using an empirical equation. In vitro release studies indicated the dependence of drug release rates on both the extent of crosslinking and amount of AAm-g-Dex used in preparing microspheres; the slow release was extended up to 12 h. The release rates were fitted to an empirical equation to compute the diffusional exponent (n), which indicated non-Fickian trend for the release of acyclovir.     

Preparation and characterization of temperature-sensitive poly(N-isopropylacrylamide)-b-poly(D,L-lactide) microspheres for protein delivery

Temperature-sensitive diblock copolymers, poly(N-isopropylacrylamide)-b-poly(D,L-lactide) (PNIPAAm-b-PLA) with different PNIPAAm contents were synthesized and utilized to fabricate microspheres containing bovine serum albumin (BSA, as a model protein) by a water-in-oil-in-water double emulsion solvent evaporation process. XPS analysis showed that PNIPAAm was a dominant component of the microspheres surface. BSA was well entrapped within the microspheres, and more than 90% encapsulation efficiency was achieved. The in vitro degradation behavior of microspheres was investigated using SEM, NMR, FTIR, and GPC. It was found that the microspheres were erodible, and polymer degradation occurred in the PLA block. Degradation of PLA was completed after 5 months incubation in PBS (pH 7.4) at 37 degrees C. A PVA concentration of 0.2% (w/v) in the internal aqueous phase yielded the microspheres with an interconnected porous structure, resulting in fast matrix erosion and sustained BSA release. However, 0.05% PVA produced the microspheres with a multivesicular internal structure wrapped with a dense skin layer, resulting in lower erosion rate and a biphasic release pattern of BSA that was characterized with an initial burst followed by a nonrelease phase. The microspheres made from PNIPAAm-b-PLA with a higher portion of PNIPAAm provided faster BSA release. In addition, BSA release from the microspheres responded to the external temperature changes. BSA release was slower at 37 degrees C (above the LCST) than at a temperature below the LCST. The microspheres fabricated with PNIPAAm-b-PLA having a 1:5 molar ratio of PNIPAAm to PLA and 0.2% (w/v) PVA in the internal aqueous phase provided a sustained release of BSA over 3 weeks in PBS (pH 7.4) at 37 degrees C.     

Glutaraldehyde and glyoxal cross-linked chitosan microspheres for controlled delivery of centchroman

Glutaraldehyde and glyoxal cross-linked microspheres were prepared using chitosan with different molecular weights (MWs) and degrees of deacetylation (DDAs) for sustained release of centchroman under physiological conditions. The DDA in chitosan was determined by different methods, and the samples were categorized as chitosan with low (48%), medium (62%), and high (75%) DDA. The size and shape of the microspheres were determined by scanning electron microscopy (SEM), and hydrophobicity was determined by adsorption of Rose Bengal dye on microspheres cross-linked with glutaraldehyde or glyoxal. The effect of MW, DDA, and degree of cross-linking in microspheres was studied on the degree of swelling, as well as by the loading and release of centchroman. The glyoxal cross-linked microspheres were more compact and hydrophobic and showed better sustained release in companion to chitosan microspheres and glutaraldehyde cross-linked microspheres. The linear fractional release of centchroman with the square root of time indicated a Fickian behavior of centchroman, and the microspheres also showed zero-order release kinetics for centchroman.     

Synthesis and properties of star-shaped polylactide attached to poly(amidoamine) dendrimer

Star-shaped polylactide was synthesized by bulk polymerization of lactide with poly(amidoamine) (PAMAM) dendrimer as initiator, which was marked as PAMAM-g-PLA for simplicity. The nonlinear architecture of PAMAM-g-PLA was confirmed by gel permeation chromatograph, nuclear magnetic resonance, and differential scanning calorimetry analysis. Unlike the linear polylactide (PLA) with similar molecular weight, PAMAM-g-PLA had a higher hydrophilicity and a faster degradation rate because of shortened polymer chains and increased polar terminal endgroups due to its branch structure. The highly branched structure significantly accelerated the release of water-soluble bovine serum albumin from PAMAM-g-PLA microspheres, whereas the linear PLA with similar molecular weight exhibited an initial time lag release. This star polymer may have potential applications for hydrophilic drug delivery in tissue engineering, including growth factor and antibodies to induce tissue regeneration, by adjusting the chain lengths of PLA branches.     

Novel interpenetrating polymer network microspheres of chitosan and methylcellulose for controlled release of theophylline

Interpenetrating polymer network (IPN) microspheres of chitosan (CS) and methylcellulose (MC) were prepared by emulsion-crosslinking in the presence of glutaraldehyde (GA) as a crosslinker. Theophylline (THP), an antiasthmatic drug was encapsulated into IPN microspheres under varying ratios of MC and CS, % drug loading and amount of GA added. IPNs have shown better mechanical properties than pure CS. Cross-link density of the matrices was significantly affected by the amount of GA and MC. Microspheres were characterized by Fourier transform infrared (FTIR) spectroscopy to assess the formation of IPN structure and to confirm the absence of chemical interactions between drug, polymer and crosslinking agent. Particle size was measured by laser light scattering technique. Microspheres with the average particle sizes ranging from 119 to 318 μm were produced. Differential scanning calorimetry (DSC) and X-ray diffraction (X-RD) studies were performed to understand the crystalline nature of drug after encapsulation into IPN microspheres. Theophylline encapsulation of up to 82% was achieved as measured by UV spectrometer. Equilibrium swelling was performed in distilled water. In vitro release studies were performed in both 0.1 N HCl and pH 7.4 buffer solutions. These data indicated a dependence of drug release on the extent of crosslinking and amount of MC added during the preparation of microspheres. The release was extended up to 12 h and release rates were fitted to an empirical equation to compute the diffusional parameters, which indicated a slight deviation from the Fickian trend for the release of theophylline.     

一种白细胞介素 -12 缓释微球制备及体外表征

目的:开发一种白细胞介素-12(IL-12)长效缓释微球剂型。方法:采用水包油-油包固(S/O/W)法制备了白介素-12因子多糖微粒的聚乳酸-聚羟基乙酸共聚物(PLGA-PLA)微球,研究了微球的表面形态和粒径大小,并且运用ELISA方法考察了微球的体外释放效果和免疫活性。结果:本方法制备的白介素-12因子微球光滑圆整,体外缓释达45天,累积释放率近90%。结论:本方法制备的白介素-12因子微球,不仅具有有效地保护IL-12蛋白活性,同时实现长效缓释的目标,是一种可行的IL-12缓释方案。     

Synthesis and Characterization of PLGA Shell Microcapsules Containing Aqueous Cores Prepared by Internal Phase Separation

The preparation of microcapsules consisting of poly(d,l-lactide-co-glycolide) (PLGA) polymer shell and aqueous core is a clear challenge and hence has been rarely addressed in literature. Herein, aqueous core-PLGA shell microcapsules have been prepared by internal phase separation from acetone-water in oil emulsion. The resulting microcapsules exhibited mean particle size of 1.1?±?0.39 μm (PDI?=?0.35) with spherical surface morphology and internal poly-nuclear core morphology as indicated by scanning electron microscopy (SEM). The incorporation of water molecules into PLGA microcapsules was confirmed by differential scanning calorimetry (DSC). Aqueous core-PLGA shell microcapsules and the corresponding conventional PLGA microspheres were prepared and loaded with risedronate sodium as a model drug. Interestingly, aqueous core-PLGA shell microcapsules illustrated 2.5-fold increase in drug encapsulation in comparison to the classical PLGA microspheres (i.e., 31.6 vs. 12.7%), while exhibiting sustained release behavior following diffusion-controlled Higuchi model. The reported method could be extrapolated to encapsulate other water soluble drugs and hydrophilic macromolecules into PLGA microcapsules, which should overcome various drawbacks correlated with conventional PLGA microspheres in terms of drug loading and release.