Study of biodegradable polylactide/poly(butylene adipate-co-terephthalate) blends

Both polylactide (PLA) and poly(butylene adipate-co-terephthalate) (PBAT) are biodegradable polymers. They are thermoplastics which can be processed using most conventional polymer processing methods. PLA is high in strength and modulus (63 MPa and 3.4 GPa, respectively) but brittle (strain at break 3.8%) while PBAT is flexible and tough (strain at break approximately 710%). In view of their complementary properties, blending PLA with PBAT becomes a natural choice to improve PLA properties without compromising its biodegradability. In this study, PLA and PBAT were melt blended using a twin screw extruder. Melt elasticity and viscosity of the blends increased with the concentration of PBAT. Crystallization of the PLA component, phase morphology of the blend, mechanical properties, and toughening mechanism were investigated. The blend comprised an immiscible, two-phase system with the PBAT evenly dispersed in the form of approximately 300 nm domains within the PLA matrix. The PBAT component accelerated the crystallization rate of PLA but had little effect on its final degree of crystallinity. With the increase in PBAT content (5-20 wt %), the blend showed decreased tensile strength and modulus; however, elongation and toughness were dramatically increased. With the addition of PBAT, the failure mode changed from brittle fracture of the neat PLA to ductile fracture of the blend as demonstrated by tensile test and scanning electron microcopy (SEM) micrographs. Debonding between the PLA and PBAT domains induced large plastic deformation in PLA matrix ligaments.     

Wet spinning of Bombyx mori silk fibroin dissolved in N-methyl morpholine N-oxide and properties of regenerated fibres

Silk fibroin (SF) was dissolved in N-methyl morpholine N-oxide (NMMO) at a polymer concentration of 13% (w/w); thermal and rheological solution properties were characterized. The melting/crystallization behaviour of NMMO was influenced by SF presence. Melting of NMMO hydrate decreased to 71 degrees C and a cold crystallization peak appeared at 35 degrees C on heating. None crystallization occurred on cooling. Quenching at a temperature of 50 degrees C or higher did not induce any crystallization on heating. Viscosity of SF-NMMO solutions decreased as a function of temperature. At 75 degrees C, viscosity remained constant for 360 min. SF-NMMO dope was spun by using a lab-scale wet spinning line. The extruded filament was coagulated in an ethanol bath. Regenerated SF fibres were collected at different draw ratios and their morphological, physical, and mechanical properties were characterized. Fibre diameters ranged from 133 to 19mum, cross-section was regularly circular, and surface was generally smooth, with a very fine granular aspect. Birefringence increased with increasing the draw ratio, especially when take up and post-spinning draw were coupled. FT-IR spectra and DSC thermograms confirmed that SF fibres crystallized into Silk II structure. The IR crystallinity index did not change as a function of drawing. Regenerated SF fibres undrawn or drawn only during the coagulation step showed the mechanical behaviour typical of a brittle material. However, when both take up and post-spinning draw were applied, fibres displayed a ductile-stable behaviour. Typical values of the mechanical parameters of regenerated SF fibres were: E=8.7 GPa, sigma(b)=120 MPa and epsilon(b)=35%.     

A study of conformational stability of poly(L-alanine), poly(L-valine), and poly(L-alanine)/poly(L-valine) blends in the solid state by (13)C cross-polarization/magic angle spinning NMR

13C cross-polarization/magic angle spinning (CP/MAS) NMR and (1)H T(1rho) experiments of poly(L-alanine) (PLA), poly(L-valine) (PLV), and PLA/PLV blends have been carried out in order to elucidate the conformational stability of the polypeptides in the solid state. These were prepared by adding a trifluoroacetic acid (TFA) solution of the polymer with a 2.0 wt/wt % of sulfuric acid (H(2)SO(4)) to alkaline water. From these experimental results, it is clarified that the conformations of PLA and PLV in their blends are strongly influenced by intermolecular hydrogen-bonding interactions that cause their miscibility at the molecular level.     

In situ copolyesters containing poly(L-lactide) and poly(hydroxyalkanoate) units

In situ copolyesters containing polylactide (PLA) and polyhydroxyalkanoate (PHA) segments were obtained via ring-opening polymerization of L-lactide using PHA as a macroinitiator with stannous octoate as catalyst. Incorporation of PHA (20 wt %) into PLA affords a novel copolymer with Mn values ranging from 25 to 50 KDa and low polydispersities of 1.8-2.3. DSC analysis of the copolymer indicates well-defined crystallization and melting transitions different from the homopolymers and corresponding blend. The polymers were characterized by FT-IR, GPC, DSC, optical microscopy, NMR, and TGA. The results show successful reactivity of PHA as a macroinitiator for the ring-opening polymerization of lactide.     

Plasticization of poly(L-lactide) with poly(propylene glycol)

A new plasticizer for poly(L-lactide) (PLA)-poly(propylene glycol) (PPG) is proposed. The advantage of using PPG is that it does not crystallize, has low glass transition temperature, and is miscible with PLA. PLA was plasticized with PPGs with nominal Mw of 425 and 1000 g/mol. Poly(ethylene glycol) (PEG), long known as a plasticizer for PLA, with nominal Mw of 600 g/mol, was also used to plasticize PLA for comparison. The thermal and tensile properties of PLA and PLA with 5-12.5 wt % of the plasticizers were studied. In blends of PLA with PPGs the glass transition temperature was lower than that of neat PLA. Both PPGs enhanced the crystallizability of PLA albeit less than PEG. All of the plasticizers increased also the ability of PLA to plastic deformation which was reflected in a decrease of yield stress and in an increase of elongation at break. The effect was enhanced by the higher PPG content and also by lower molecular weight of PPG. A phase separation occurred only in the blend containing 12.5 wt % of PPG with higher molecular weight. The evidences of crazing were found in deformed samples of PLA with low plasticizer content, whereas the samples with higher content of plasticizers crystallized due to deformation.     

Modification of brittle polylactide by novel hyperbranched polymer-based nanostructures

The inherent brittleness of polylactide (PLA) poses considerable scientific challenges and limits its large-scale applications. Here, we propose and demonstrate a new industrially relevant methodology to develop a polylactide (PLA)-based nanoblend having outstanding stiffness-toughness balance. In this approach, a hydroxyl functional hyperbranched polymer (HBP) was in-situ cross-linked with a polyanhydride (PA) in the PLA matrix during melt processing. There was formation of new hyperbranched polymer-based cross-linked particles in the PLA matrix. Transmission electron microscopy (TEM) and atomic force microscopy (AFM) revealed the sea-island morphology of PLA-cross-linked HBP blend. The domain size of cross-linked HBP particles in the PLA matrix was less than 100 nm as obtained from TEM. The presence of cross-linked hyperbranched polymer in the PLA matrix exhibited approximately 570% and approximately 847% improvement in the toughness and elongation at break, respectively, as compared to unmodified PLA. The increase in the ductility of modified PLA was related to stress whitening and multiple crazing initiated in the presence of cross-linked HBP particles. Formation of a networked interface as revealed by rheological data was associated with enhanced compatibility of the PLA-cross-linked HBP blend as compared to the PLA/HBP blend. The cross-linking reaction of HBP with PA was confirmed with the help of Fourier transform infrared spectroscopy (FTIR) and low-temperature dynamical mechanical thermal analysis (DMTA).     

三乙酸甘油酯对PLA/PBAT共混体系性能影响

利用转矩流变仪将聚乳酸(PLA)、聚己二酸对苯二甲酸丁二酯(PBAT)和三乙酸甘油酯(GTA)熔融共混,利用差示扫描量热仪(DSC)、动态热机械分析仪(DMA)、万能材料试验机、冲击试验机、扫描电子显微镜(SEM)对共混物的热力学性能、力学性能以及微观形态结构进行测试和表征。实验发现,加入GTA后共混物的两相玻璃化转变温度呈相互靠近趋势,冷结晶温度和熔融温度都降低。当GTA加入量为3份时,共混物中分散相粒径减小,PLA/PBAT/GTA(80/20/3)组分的断裂伸长率得到明显提升,增加了2.6倍,由未加入GTA时的17.7%增长到64.1%。     

乳丝的加工、性能及其应用

乳丝学名为聚乳酸纤维,是一种可生物降解的新型绿色纤维,目前制备方法主要有熔融纺丝、溶液纺丝和静电纺丝等3种方法。作为一种新型的可降解纤维材料,其环保性、吸湿性、透气性、生物相容性以及优良的力学性能决定了其在生物医用、织物面料、非织造材料(如一次性卫生用品、过滤材料等)等很多方面都将得到广泛应用。     

Fabrication and characterization of poly(lactic acid)/acetyl tributyl citrate/carbon black as conductive polymer composites

By using acetyl tributyl citrate (ATBC) as the plasticizer of poly(lactic acid) (PLA) and carbon black (CB) as conductive filler, electrically conductive polymer composites (CPC) with different CB and ATBC contents were prepared. FTIR revealed that the interaction existed between PLA/ATBC matrix and CB filler and ATBC could improve this interaction. The rheology showed that ATBC could obviously decrease the shear viscosity and improve the fluidity of the composites but just the reverse for CB. With the increasing of CB contents, the enforcement effect, storage modulus, and glass-transition temperature increased but the elongation at break decreased. PLA/ATBC/CB composites exhibited the low electrical percolation thresholds of 0.516, 1.20, 2.46, and 2.74 vol % CB at 30, 20, 10, and 0 wt % ATBC. The conductivity of the composite containing 3.98 vol % CB and 30 wt % ATBC reached 1.60 S/cm. Scanning electron microscopy revealed that the addition of ATBC facilitated the dispersion of the CB in the PLA matrix. Water vapor permeability (WVP) showed that, at the same CB contents, the more ATBC contents there were, the less the values of WVP were.     

Morphology and properties of soy protein and polylactide blends

Blends of soy protein (SP) and a semicrystalline polylactide (PLA) were prepared using a twin-screw extruder. The melt rheology, phase morphology, mechanical properties, water resistance, and thermal and dynamic mechanical properties were investigated on specimens prepared by injection molding of these blends. The melt flowability of soy-based plastics was improved through blending with PLA. Scanning electron microscopy revealed that a co-continuous phase structure existed in the blends with soy protein concentrate (SPC) to PLA ratios ranging from 30:70 to 70:30. SPC/PLA blends showed fine co-continuous phase structures, while soy protein isolate (SPI)/PLA blends presented severe phase coarsening. At the same SP to PLA ratios, SPC/PLA blends demonstrated a higher tensile strength than SPI/PLA blends. The water absorption of soy plastics was greatly reduced by blending with PLA. The compatibility was improved by adding 1-5 phr poly(2-ethyl-2-oxazoline) (PEOX) in the blends, and the resulting blends showed an obvious increase in tensile strength and a reduction in water absorption for SPI/PLA blends. The compatibility between SP and PLA was evaluated by mechanical testing, dynamic mechanical analysis (DMA), water absorption, and scanning electron microscopy (SEM) experiments. Differential scanning calorimetry (DSC) revealed that PLA in the blends was mostly amorphous in the injection molded articles, and SP accelerated the cold crystallization and could increase the final crystallinity of PLA in the blends.     

Structural characteristics and properties of Bombyx mori silk fiber obtained by different artificial forcibly silking speeds

To study the spinning condition of natural biopolymer silk, the silk fibers were directly acquired from Bombyx mori silkworm, N140 x C140 by a simple artificial forcibly silking method at the speed of 60, 120, 180 and 240 cm min(-1), respectively and its microstructure and physical properties were evaluated. The fine silk fibers (about 8 microm) were obtained at faster spinning speed, 240 cm min(-1). The tensile properties of silk fibers were remarkably increased with raising the forcibly spinning speeds. The beta-sheet structure contents of silk fibers obtained at higher speed were considerably increased. The fibers obtained by different spinning speeds exhibited a fairly similar X-ray crystallinity, while the degree of molecular orientation increased with decreasing the fiber diameter. The fine silk fibers obtained at higher speed (240 cm min(-1)) exhibited a slightly higher thermal stability, as shown by the upward shift of differential scanning calorimetry (DSC) decomposition temperature.     

聚乳酸基热固性聚氨酯及其形状记忆性能

通过聚乳酸二元醇和聚乳酸-聚己内酯共聚物二元醇与六亚甲基二异氰酸酯(HDI)三聚体交联反应合成了一系列生物基热固性聚氨酯(Bio-PUs)。利用傅里叶红外(FTIR)、差示扫描量热分析(DSC)、热失重分析(TGA)、万能拉伸机和细胞毒性等测试方法对获得的聚乳酸基聚氨酯进行了表征。结果表明,与聚乳酸二元醇相比,聚乳酸-聚己内酯共聚物二元醇降低了生物基热固性聚氨酯的玻璃化温度(Tg),提高了热固性聚氨酯的热稳定性;且聚乳酸-聚己内酯型聚氨酯的力学性能和形状记忆性能更为优异。其中,聚乳酸-聚己内酯共聚物二元醇分子量为3 000时得到的热固性聚氨酯(Bio-PU2-3000)的杨氏模量为277.7 MPa,伸长率为230%;聚乳酸-聚己内酯共聚物二元醇分子量为1 000得到的热固性聚氨酯(Bio-PU2-1000)在人体体温下的形变回复时间仅为93 s。另外,通过显微镜观察到细胞在含聚乳酸基热固性聚氨酯的培养液中生长状态良好,表明制备得到的生物基聚氨酯无细胞毒性。     

Liquid crystalline phase and gel-sol transitions for concentrated microcrystalline cellulose (MCC)/1-ethyl-3-methylimidazolium acetate (EMIMAc) solutions

Liquid crystalline (LC) phase transition and gel-sol transition in the solutions of microcrystalline cellulose (MCC) and ionic liquid (1-ethyl-3-methylimidazolium acetate, EMIMAc) have been investigated through a combination of polarized optical microscope (POM) observation and rheological measurements. Molecular LC phase forms at the 10 wt % cellulose concentration, as observed by POM, whereas the critical gel point is 12.5 wt % by rheological measurements according to the Winter and Chambon theory, for which the loss tangent, tan δ, shows frequency independence. Dramatic decreases of G' and G' in the phase transition temperature range during temperature sweep are observed due to disassembling of the LC domain junctions. The phase diagram describing the LC phase and gel-sol transitions is obtained and the associated mechanisms are elucidated. A significant feature shown in the phase diagram is the presence of a narrow lyotropic LC solution region, which potentially has a great importance for the cellulose fiber wet spinning.     

Lipase-catalyzed copolymerization of omega-pentadecalactone with p-dioxanone and characterization of copolymer thermal and crystalline properties

Candida antarctica Lipase B (CALB), a metal-free enzyme, was successfully employed as catalyst for ring-opening copolymerization of omega-pentadecalactone (PDL) with p-dioxanone (DO) under mild reaction conditions (<80 degrees C, atmospheric pressure). Poly(PDL-co-DO) with high molecular weight (Mw > 30 000) and a wide range of comonomer contents was synthesized using various PDL/DO feed ratios. During the copolymerization reaction, large ring PDL was found to be more reactive than its smaller counterpart DO, resulting in higher PDL/DO unit ratios in polymer chains than the corresponding PDL/DO monomer ratios in the feed. The copolymers were typically isolated in 50-90 wt % yields as the monomer conversion was limited by the equilibrium between monomers and copolymer. 1H and 13C NMR analysis on poly(PDL-co-DO) formed by CALB showed that the copolymers contain nearly random sequences of PDL and DO units with a slight tendency toward alternating arrangements. Copolymerization with PDL was found to remarkably enhance PDO thermal stability. Differential scanning calorimetry (DSC) and wide-angle X-ray scattering (WAXS) results demonstrate high crystallinity in all copolymers over the whole range of compositions. Depending on copolymer composition, the crystal lattice of either PDO or PPDL hosts units of the other comonomer, a behavior typical of an isodimorphic system. In poly(PDL-co-DO), both melting temperature and melting enthalpy display a minimum at 70 mol % DO, that is, at the pseudoeutectic composition. WAXS diffractograms show one crystal phase (that of either PPDL or PDO) on either side of the pseudoeutectic and coexistence of PPDL and PDO crystals at the pseudoeutectic.     

The properties of enzyme-hydrolyzed cellulose in aqueous sodium hydroxide

Pure natural cellulose (softwood pulp) modified with cellulase is allowed to react with sodium hydroxide in a muller, and changes in structure and properties are investigated by FTIR and DSC. The reactivity of cellulose for some dissolving and derivatization processes is shown to be improved by an enzymatic hydrolysis and admixture with sodium hydroxide. The modified cellulose dissolved at 9% (wt) sodium hydroxide at -10 degrees C at 6% pulp consistency, while the DP of cellulose is >350.     

Unique gelation behavior of cellulose in NaOH/urea aqueous solution

A transparent cellulose solution was prepared by mixing 7 wt % NaOH with 12 wt % urea aqueous solution which was precooled to below -10 degrees C and which was able to rapidly dissolve cellulose at ambient temperature. The rheological properties and behavior of the gel-formed cellulose solution were investigated by using dynamic viscoelastic measurement. The effects of temperature, time, cellulose molecular weight, and concentrations on both the shear storage modulus (G') and the loss modulus (G") were analyzed. The cellulose solution having a viscosity-average molecular weight (M(eta)) of 11.4 x 10(4) had its sol-gel transition temperature decreased from 60.3 to 30.5 degrees C with an increase of its concentration from 3 to 5 wt %. The gelation temperature of a 4 wt % cellulose solution dropped from 59.4 to 30.5 degrees C as the M(eta) value was increased from 4.5 x 10(4) to 11.4 x 10(4). Interestingly, at either higher temperature (above 30 degrees C), or lower temperature (below -3 degrees C), or for longer gelation time, gels could form in the cellulose solutions. However, the cellulose solution remains a liquid state for a long time at the temperature range from 0 to 5 degrees C. For the first time, we revealed an irreversible gelation in the cellulose solution system. The gel having been formed did not dissolve even when cooled to the temperature of -10 degrees C, at which it was dissolved previously. Therefore, this indicates that either heating or cooling treatment could not break such stable gels. A high apparent activation energy (E(a)) of the cellulose solution below 0 degrees C was obtained and was used to explain the gel formation under the cooling process.     

Influence of fibre architecture on the biodegradability of FLAX/PLA composites

Polymers derived from renewable resources are known for their low impact on the carbon footprint as they are recyclable by decaying processes. When these materials are blended with natural fibres to form composites, they are also highly suitable for technical applications but maintain their outstanding recycling potential. However, as natural fibres increase the strength and alter the polymers' structure, they can also affect the decaying processes. The objective of this study is to investigate the influence of flax fibre reinforcements on the decaying process of poly(lactic) acid (PLA) in flax – PLA composites under composting conditions. The results indicate that the fibres enhance the biodegradation by enlarging the potential surface contributing to the decaying process. At the same time, the fibres act as channels and distribute water and microorganisms in the composite. The decaying process is attributed to fibre decomposition and hydrolysis of PLA which leads to increased degradation rates for composites with high fibre weight content.     

A bioresorbable, polylactide reservoir for diffusional and osmotically controlled drug delivery

The purpose of this study was to design and characterize a zero-order bioresorbable reservoir delivery system (BRDS) for diffusional or osmotically controlled delivery of model drugs including macromolecules. The BRDS was manufactured by casting hollow cylindrical poly (lactic acid) (PLA): polyethylene glycol (PEG) membranes (10 x 1.6 mm) on a stainless steel mold. Physical properties of the PLA:PEG membranes were characterized by solid-state thermal analysis. After filling with drug (5 fluorouracil [5FU] or fluorescein isothiocyanate [FITC]-dextran:mannitol, 5:95 wt/wt mixture) and sealing with viscous PLA solution, cumulative in vitro dissolution studies were performed and drug release monitored by ultraviolet (UV) or florescence spectroscopy. Statistical analysis was performed using Minitab (Version 12). Differential scanning calorimetry thermograms of PLA:PEG membranes dried at 25 degrees C lacked the crystallization exotherms, dual endothermal melting peaks, and endothermal glass transition observed in PLA membranes dried at -25 degrees C. In vitro release studies demonstrated zero-order release of 5FU for up to 6 weeks from BRDS manufactured with 50% wt/wt PEG (drying temperature, 25 degrees C). The release of FITC dextrans of molecular weights 4400, 42 000, 148 000, and 464 000 followed zero-order kinetics that were independent of the dextran molecular weight. When monitored under different concentrations of urea in the dissolution medium, the release rate of FITC dextran 42 000 showed a linear correlation with the calculated osmotic gradient(DeltaPi). This study concludes that PEG inclusion at 25 degrees C enables manufacture of uniform, cylindrical PLA membranes of controlled permeability. The absence of molecular weight effects and a linear dependence of FITC-dextran release rate on DeltaPi confirm that the BRDS can be modified to release model macromolecules by an osmotically controlled mechanism.     

Analysis of nucleotide myosin complexes in skeletal muscle fibres by DSC and EPR

The internal dynamics and thermal unfolding of fibre bundles prepared from rabbit psoas muscle has been studied in the presence of nucleotides by differential scanning calorimetry (DSC) and electron paramagnetic resonance (EPR) spectroscopy. Using ADP, adenosine 5'-triphosphate (ATP), AMP.PNP and inorganic phosphate analogue orthovanadate (V(i)), AlF(4)(-) and BeF(3)(-), three intermediate states of the ATP hydrolysis cycle were simulated in glycerinated muscle fibres. In the main transition of the DSC pattern, three overlapping endotherms were detected in rigor, four in strongly as well as weakly binding state of myosin to actin. Deconvolution procedure showed that the transition temperature of 67.5 degrees C was the same for rigor and strong binding state of myosin. In contrast, nucleotide binding induced shift of the melting temperatures of 52 degrees C and 67.5 degrees C, appeared a new fourth peak at 74 and 77 degrees C and produced changes in the calorimetric enthalpies. The changes of the parameters of the peak functions suggest global rearrangements of the internal structure in myosin heads in the intermediate states. In the presence of ADP or ATP plus phosphate analogue orthovanadate or beryllium fluoride, aluminium fluoride, the conventional EPR spectra of spin-labeled muscle fibres showed large changes in the ordering of the probe molecules, and a new distribution of spin labels appeared. ATP plus orthovanadate induced the orientation disorder of myosin heads; the random population of spin labels gave evidence of large local conformational and motional changes in the internal structure of myosin heads. Saturation transfer EPR measurements reported increased rotational mobility of spin labels in the presence of ATP plus phosphate analogues corresponding to weakly binding state of myosin to actin.     

Regenerated cellulose-silk fibroin blends fibers

Fibers made of cellulose and silk fibroin at different composition were wet spun from solutions by using N-methylmorpholine N-oxide hydrates (NMMO/H(2)O) as solvent and ethanol as coagulant. Different spinning conditions were used. The fibers were characterized by different techniques: FTIR-Raman, scanning electron microscopy, wide-angle x-ray diffraction, DSC analysis. The results evidence a phase separation in the whole blends compositions. The tensile characterization, however, illustrates that the properties of the blends fibers are higher respect to a linear behaviour between the pure polymers, confirming a good compatibility between cellulose and silk fibroin. The fibers containing 75% of cellulose show better mechanical properties than pure cellulose fibers: modulus of about 23 GPa and strength to break of 307 MPa.