A Cu‐Based Nanoparticulate Film as Super‐Active and Robust Catalyst Surpasses Pt for Electrochemical H2 Production from Neutral and Weak Acidic Aqueous Solutions

Electrocatalysts that are stable and highly active at low overpotential (η) under mild conditions as well as cost‐effective and scalable are eagerly desired for potential use in photo‐ and electro‐driven hydrogen evolution devices. Here the fabrication and characterization of a super‐active and robust Cu‐Cu_xO‐Pt nanoparticulate electrocatalyst is reported, which displays a small Tafel slope (44 mV dec^?1) and a large exchange current density (1.601 mA cm^?2) in neutral buffer solution. The catalytic current density of this catalyst film reaches 500 mA cm^?2 at η = ?390 ± 12 mV and 20 mA cm^?2 at η = ?45 ± 3 mV, which are significantly higher than the values displayed by Pt foil and Pt/C electrodes in neutral buffer solution and even comparable with the activity of Pt electrode in 0.5 m H₂SO₄ solution.     

One‐Step Controllable Synthesis of Catalytic Ni4Mo/MoOx/Cu Nanointerfaces for Highly Efficient Water Reduction

Currently, in addition to the electroactive non‐noble metal water‐splitting electrocatalysts, a scalable synthetic route and simple activity enhancement strategy is also urgently needed. In particular, the well‐controlled synthesis of the well‐recognized metal–metal nanointer face in a single step remains a key challenge. Here, the synthesis of Cu‐supported Ni₄Mo nanodots on MoO_x nanosheets (Ni₄Mo/MoO_x) with controllable Ni₄Mo particle size and d‐band structure is reported via a facile one‐step electrodeposition process. Density functional theory (DFT) calculations reveal that the active open‐shell effect from Ni‐3d‐band optimizes the electronic configuration. The Cu‐substrate enables the surface Ni–Mo alloy dots to be more electron‐rich, forming a local connected electron‐rich network, which boosts the charge transfer for effective binding of O‐related species and proton–electron charge exchange in the hydrogen evolution reaction. The Cu‐supported Ni₄Mo/MoO_x shows an ultralow overpotential of 16 mV at a current density of 10 mA cm^?2 in 1 m KOH, demonstrating the smallest overpotential, at loadings as low as 0.27 mg cm^?2, among all non‐noble metal catalysts reported to date. Moreover, an overpotential of 105 mV allows it to achieve a current density of 250 mA cm^?2 in 70 °C 30% KOH, a remarkable performance for alkaline hydrogen evolution with competitive potential for applications.     

Crystalline Ni(OH)2/Amorphous NiMoOx Mixed‐Catalyst with Pt‐Like Performance for Hydrogen Production

The achievement of effective alkaline hydrogen production from water electrolysis is an active field of research. Herein, an integrated electrode composed of crystalline Ni(OH)₂ and amorphous NiMoO_x is fabricated onto nickel foam (denoted as Ni(OH)₂–NiMoO_x/NF). The hydrogen evolution reaction (HER) kinetics are optimized along with phase transformation process during soaking operation. An overpotential of 36 mV to drive 10 mA cm^?2 along with the low Tafel slope of 38 mV dec^?1 reveals the catalyst's excellent HER performance and a Heyrovsky‐step‐controlled HER mechanism. When assembled into a urea‐assisted water electrolyzer, a voltage of 1.42 V can reach 10 mA cm^?2. Further experiments and Fourier transform infrared spectroscopy (FTIR) results illustrate the synergy effect between crystalline and amorphous areas and the optimized water dissociation step. Crystalline Ni(OH)₂ serves as the scissor for water dissociation in an alkali environment to produce H*, while the amorphous NiMoO_x layer serves as the location for H* adsorption and H₂ desorption.     

Corrosion and Alloy Engineering in Rational Design of High Current Density Electrodes for Efficient Water Splitting

Alongside rare‐earth metals, Ni, Fe, Co, Cu are some of the critical materials that will be in huge demand thanks to growth in clean‐energy sector. Herein scrap stainless steel wires (SSW) from worn‐out tires are employed as a support material for catalyst integration in the hydrogen evolution reaction (HER). In addition, SSW by corrosion engineering is exercised as an in situ formed freestanding robust electrode for the oxygen evolution reaction (OER). By superficial corrosion of SSW, inherent active species are unmasked in the form of Ni/FeOOH nanocrystallites displaying efficient water oxidation by reaching 500 mA cm^?2 at low overpotential (η₅₀₀) of 287 mV in 1 m KOH. Similarly, cathode scrap SSW with active (alloy) coatings of MoNi₄ catalyzes the HER at η_‐200 = 77 mV, with a low activation energy (E_a = 16.338 kJ mol^?1) and high durability of 150 h. Promisingly, when used in industrial conditions, 5 m KOH, 343 K, these electrodes demonstrate abnormal activity by yielding high anodic and cathodic current density of 1000 mA cm^?2 at η = 233 mV and η = 161 mV, respectively. This work may inspire researchers to explore and reutilize high‐demand metals from scrap for addressing critical material shortfalls in clean‐energy technologies.     

Ultrathin High Surface Area Nickel Boride (NixB) Nanosheets as Highly Efficient Electrocatalyst for Oxygen Evolution

The overriding obstacle to mass production of hydrogen from water as the premium fuel for powering our planet is the frustratingly slow kinetics of the oxygen evolution reaction (OER). Additionally, inadequate understanding of the key barriers of the OER is a hindrance to insightful design of advanced OER catalysts. This study presents ultrathin amorphous high‐surface area nickel boride (Ni_x B) nanosheets as a low‐cost, very efficient and stable catalyst for the OER for electrochemical water splitting. The catalyst affords 10 mA cm^?2 at 0.38 V overpotential during OER in 1.0 m KOH, reducing to only 0.28 V at 20 mA cm^?2 when supported on nickel foam, which ranks it among the best reported nonprecious catalysts for oxygen evolution. Operando X‐ray absorption fine‐structure spectroscopy measurements reveal prevalence of NiOOH, as well as Ni‐B under OER conditions, owing to a Ni‐B core@nickel oxyhydroxide shell (Ni‐B@NiO_x H) structure, and increase in disorder of the NiO_x H layer, thus revealing important insight into the transient states of the catalyst during oxygen evolution.     

In Situ Grown Bimetallic MOF‐Based Composite as Highly Efficient Bifunctional Electrocatalyst for Overall Water Splitting with Ultrastability at High Current Densities

A newly designed water‐stable NH₂‐MIL‐88B(Fe₂Ni)‐metal–organic framework (MOF), in situ grown on the surface of a highly conducting 3D macroporous nickel foam (NF), termed NFN‐MOF/NF, is demonstrated to be a highly efficient bifunctional electrocatalyst for overall water splitting with ultrastability at high current densities. The NFN‐MOF/NF achieves ultralow overpotentials of 240 and 87 mV at current density of 10 mA cm^?2 for the oxygen evolution reaction and hydrogen evolution reaction, respectively, in 1 m KOH. For the overall water splitting, it requires only an ultralow cell voltage of 1.56 V to reach the current density of 10 mA cm^?2, outperforming the pairing of Pt/C on NF as the cathode and IrO₂ on NF as the anode at the same catalyst loading. The stability of the NFN‐MOF/NF catalyst is also outstanding, exhibiting only a minor chronopotentiometric decay of 7.8% at 500 mA cm^?2 after 30 h. The success of the present NFN‐MOF/NF catalyst is attributed to the abundant active centers, the bimetallic clusters {Fe₂Ni(µ₃‐O)(COO)₆(H₂O)₃}, in the MOF, the positive coupling effect between Ni and Fe metal ions in the MOF, and synergistic effect between the MOF and NF.     

Ni Strongly Coupled with Mo2C Encapsulated in Nitrogen‐Doped Carbon Nanofibers as Robust Bifunctional Catalyst for Overall Water Splitting

It is urgently required to develop highly efficient and stable bifunctional non‐noble metal electrocatalysts for both the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) for water splitting. In this study, a facile electrospinning followed by a post‐carbonization treatment to synthesize nitrogen‐doped carbon nanofibers (NCNFs) integrated with Ni and Mo₂C nanoparticles (Ni/Mo₂C‐NCNFs) as water splitting electrocatalysts is developed. Owing to the strong hydrogen binding energy on Mo₂C and high electrical conductivity of Ni, synergetic effect between Ni and Mo₂C nanoparticles significantly promote both HER and OER activities. The optimized hybrid (Ni/Mo₂C(1:2)‐NCNFs) delivers low overpotentials of 143 mV for HER and 288 mV for OER at a current density of 10 mA cm^?2. An alkaline electrolyzer with Ni/Mo₂C(1:2)‐NCNFs as catalysts for both anode and cathode exhibits a current density of 10 mA cm^?2 at a voltage of 1.64 V, which is only 0.07 V larger than the benchmark of Pt/C‐RuO₂ electrodes. In addition, an outstanding long‐term durability during 100 h testing without obvious degradation is achieved, which is superior to most of the noble‐metal‐free electrocatalysts reported to date. This work provides a simple and effective approach for the preparation of low‐cost and high‐performance bifunctional electrocatalysts for efficient overall water splitting.     

Copper–Nickel Nitride Nanosheets as Efficient Bifunctional Catalysts for Hydrazine‐Assisted Electrolytic Hydrogen Production

Electrocatalytic water splitting is one of the sustainable and promising strategies to generate hydrogen fuel but still remains a great challenge because of the sluggish anodic oxygen evolution reaction (OER). A very effective approach to dramatically decrease the input cell voltage of water electrolysis is to replace the anodic OER with hydrazine oxidation reaction (HzOR) due to its lower thermodynamic oxidation potential. Therefore, developing the low‐cost and efficient HzOR catalysts, coupled with the cathodic hydrogen evolution reaction (HER), is tremendously important for energy‐saving electrolytic hydrogen production. Herein, a new‐type of copper–nickel nitride (Cu₁Ni₂‐N) with rich Cu₄N/Ni₃N interface is rationally constructed on carbon fiber cloth. The 3D electrode exhibits extraordinary HER performance with an overpotential of 71.4 mV at 10 mA cm^?2 in 1.0 m KOH, simultaneously delivering an ultralow potential of 0.5 mV at 10 mA cm^?2 for HzOR in a 1.0 m KOH/0.5 m hydrazine electrolyte. Moreover, the electrolytic cell utilizing the synthesized Cu₁Ni₂‐N electrode as both the cathode and anode display a cell voltage of 0.24 V at 10 mA cm^?2 with an excellent stability over 75 h. The present work develops the promising copper–nickel‐based nitride as a bifunctional electrocatalyst through hydrazine‐assistance for energy‐saving electrolytic hydrogen production.     

High‐Performance Hydrogen Evolution by Ru Single Atoms and Nitrided‐Ru Nanoparticles Implanted on N‐Doped Graphitic Sheet

The most efficient electrocatalyst for the hydrogen evolution reaction (HER) is a Pt‐based catalyst, but its high cost and nonperfect efficiency hinder wide‐ranging industrial/technological applications. Here, an electrocatalyst of both ruthenium (Ru) single atoms (SAs) and N‐doped‐graphitic(G_N)‐shell‐covered nitrided‐Ru nanoparticles (NPs) (having a Ru‐N_x shell) embedded on melamine‐derived G_N matrix { 1 : [Ru(SA)+Ru(NP)@RuN_x@G_N]/G_N}, which exhibits superior HER activity in both acidic and basic media, is presented. In 0.5 m H₂SO₄/1 m KOH solutions, 1 shows diminutive “negative overpotentials” (?η = |η| = 10/7 mV at 10 mA cm^?2, lowest ever) and high exchange current densities (4.70/1.96 mA cm^?2). The remarkable HER performance is attributed to the near‐zero free energies for hydrogen adsorption/desorption on Ru(SAs) and the increased conductivity of melamine‐derived G_N sheets by the presence of nitrided‐Ru(NPs). The nitridation process forming nitrided‐Ru(NPs), which are imperfectly covered by a G_N shell, allows superb long‐term operation durability. The catalyst splits water into molecular oxygen and hydrogen at 1.50/1.40 V (in 0.1 m HClO₄/1 m KOH), demonstrating its potential as a ready‐to‐use, highly effective energy device for industrial applications.     

Rational Design of Core@shell Structured CoSx@Cu2MoS4 Hybridized MoS2/N,S‐Codoped Graphene as Advanced Electrocatalyst for Water Splitting and Zn‐Air Battery

A novel hybrid of small core@shell structured CoS_x@Cu₂MoS₄ uniformly hybridizing with a molybdenum dichalcogenide/N,S‐codoped graphene hetero‐network (CoS_x@Cu₂MoS₄‐MoS₂/NSG) is prepared by a facile route. It shows excellent performance toward the oxygen reduction reaction (ORR), oxygen evolution reaction (OER), and hydrogen evolution reaction (HER) in alkaline medium. The hybrid exhibits rapid kinetics for ORR with high electron transfer number of ≈3.97 and exciting durability superior to commercial Pt/C. It also demonstrates great potential with remarkable stability for HER and OER, requiring low overpotential of 118.1 and 351.4 mV, respectively, to reach a current density of 10 mA cm^?2. An electrolyzer based on CoS_x@Cu₂MoS₄‐MoS₂/NSG produces low cell voltage of 1.60 V and long‐term stability, surpassing a device of Pt/C + RuO₂/C. In addition, a Zn‐air battery using cathodic CoS_x@Cu₂MoS₄‐MoS₂/NSG catalyst delivers a high cell voltage of ≈1.44 V and a power density of 40 mW cm^?2 at 58 mA cm^?2, better than the state‐of‐the‐art Pt/C catalyst. These achievements are due to the rational combination of highly active core@shell CoS_x@Cu₂MoS₄ with large‐area and high‐porosity MoS₂/NSG to produce unique physicochemical properties with multi‐integrated active centers and synergistic effects. The outperformances of such catalyst suggest an advanced candidate for multielectrocatalysis applications in metal‐air batteries and hydrogen production.     

Boronization‐Induced Ultrathin 2D Nanosheets with Abundant Crystalline–Amorphous Phase Boundary Supported on Nickel Foam toward Efficient Water Splitting

The conversion of crystalline metal–organic frameworks (MOFs) into metal compounds/carbon hybrid nanocomposites via pyrolysis provides a promising solution to design electrocatalysts for electrochemical water splitting. However, pyrolyzing MOFs generally involves a complex high‐temperature treatment, which can destroy the coordinated surroundings within MOFs, and as a result not taking their full advantage of their electrolysis properties. Herein, a simple and room‐temperature boronization strategy is developed to convert nickel zeolite imidazolate framework (Ni‐ZIF) nanorods into ultrathin Ni‐ZIF/Ni? B nanosheets with abundant crystalline–amorphous phase boundaries. The combined experiment, and theoretical calculation results disclose that the ultrathin thickness allows fast electron transfer and ensures increased exposure of surface coordinatively unsaturated active sites while the crystalline–amorphous interface elaborately changes the potential‐determining step to energetically favorable intermediates. As a result, Ni‐ZIF/Ni? B nanosheets supported on nickel foam (NF) require overpotentials of 67 mV for the hydrogen evolution reaction and 234 mV for the oxygen evolution reaction to achieve a current density of 10 mA cm^?2. Remarkably, Ni‐ZIF/Ni? B@NF as a bifunctional electrocatalyst for overall water splitting enables an alkaline electrolyzer with 10 mA cm^?2 at an ultralow cell voltage of 1.54 V. The present work may open a new avenue to the design of MOF‐derived composites for electrocatalysis.     

Self‐Assemble and In Situ Formation of Ni1−xFexPS3 Nanomosaic‐Decorated MXene Hybrids for Overall Water Splitting

Herein, the authors present the development of novel 0D–2D nanohybrids consisting of a nickel‐based bimetal phosphorus trisulfide (Ni_1?xFe_xPS₃) nanomosaic that decorates on the surface of MXene nanosheets (denoted as NFPS@MXene). The nanohybrids are obtained through a facile self‐assemble process of transition metal layered double hydroxide (TMLDH) on MXene surface; followed by a low temperature in situ solid‐state reaction step. By tuning the Ni:Fe ratio, the as‐synthesized NFPS@MXene nanohybrids exhibit excellent activities when tested as electrocatalysts for overall water splitting. Particularly, with the initial Ni:Fe ratio of 7:3, the obtained Ni_0.7Fe_0.3PS₃@MXene nanohybrid reveals low overpotential (282 mV) and Tafel slope (36.5 mV dec^?1) for oxygen evolution reaction (OER) in 1 m KOH solution. Meanwhile, the Ni_0.9Fe_0.1PS₃@MXene shows low overpotential (196 mV) for the hydrogen evolution reaction (HER) in 1 m KOH solution. When integrated for overall water splitting, the Ni_0.7Fe_0.3PS₃@MXene || Ni_0.9Fe_0.1PS₃@MXene couple shows a low onset potential of 1.42 V and needs only 1.65 V to reach a current density of 10 mA cm^?2, which is better than the all noble metal IrO₂ || Pt/C electrocatalyst (1.71 mV@10 mA cm^?2). Given the chemical versatility of Ni_1?xFe_xPS₃ and the convenient self‐assemble process, the nanohybrids demonstrated in this work are promising for energy conversion applications.     

Transforming Nickel Hydroxide into 3D Prussian Blue Analogue Array to Obtain Ni2P/Fe2P for Efficient Hydrogen Evolution Reaction

For the first time, a 3D Prussian blue analogue (PBA) with well‐defined spatial organization is fabricated by using a nickel hydroxide array as a precursor. The nickel hydroxide arrays are synthesized in titanium foil and reacted with K₃[Fe(CN)₆]. The plate‐like morphology of the nickel hydroxide is perfectly preserved and combined with abundant PBA nanocubes. After phosphidation at 350 °C, the obtained sample demonstrated excellent hydrogen evolution reaction (HER) activity in both acid and alkaline solutions to reach a current density of 10 mA cm^?2 with an overpotential of only 70 and 121 mV, respectively. With an overpotential of 266 mV, it can reach a larger current density of 500 mA cm^?2 in acid. The efficient HER activity of the obtained sample is mainly ascribed to its structural advantage with various active metal sites derived from the nickel hydroxide and PBA precursor. In addition, long‐term stability measurements have verified the good performance of the obtained sample in acid and alkaline solutions. An increment of overpotential of only 8 and 9 mV is observed, in the acid and alkaline solutions respectively. Beyond these assets, it is supposed that the strategy to synthesize 3D PBA arrays from nickel hydroxide can be extended to other metal–organic frameworks arrays for more electrochemical applications.     

Low Band Gap Benzimidazole COF Supported Ni3N as Highly Active OER Catalyst

Covalent organic frameworks (COFs) have structures and morphologies closely resembling graphenes, whose modular construction permits atomic‐level manipulations. This, combined with their porous structure, makes them excellent catalyst supports. Here, the high electrocatalytic activity of a composite, formed by supporting Ni₃N nanoparticles on a benzimidazole COF, for oxygen evolution reaction is shown. The composite oxidizes alkaline water with a near‐record low overpotential of 230 mV @ 10 mA cm^?2 (η ₁₀). This high activity is attributed to the ability of the COF to confine the Ni₃N nanoparticles to size regimes otherwise difficult to obtain and to its low band gap character (1.49 eV) arising from the synergy between the conducting Ni₃N nanoparticles and the π‐conjugated COF. The COF itself, as a metal‐free self‐standing framework, has an oxygen evolution reaction activity with η ₁₀ of 400 mV. The periodic structure of the COF makes it serve as a matrix to disperse the catalytically active Ni₃N nanoparticles favoring their high accessibility and thereby good charge‐transport within the composite. This is evident from the amount of O₂ evolved (230 mmol h^?1 g^?1), which, to the best of our knowledge, is the highest reported. The work reveals the emergence of COF as supports for electrocatalysts.     

Eutectic‐Derived Mesoporous Ni‐Fe‐O Nanowire Network Catalyzing Oxygen Evolution and Overall Water Splitting

The development of efficient and abundant water oxidation catalysts is essential for the large‐scale storage of renewable energy in the form of hydrogen fuel via electrolytic water splitting, but still remains challenging. Based upon eutectic reaction and dealloying inheritance effect, herein, novel Ni‐Fe‐O‐based composite with a unique mesoporous nanowire network structure is designed and synthesized. The composite exhibits exceptionally low overpotential (10 mA cm^?2 at an overpotential of 244 mV), low Tafel slope (39 mV dec^?1), and superior long‐term stability (remains 10 mA cm^?2 for over 60 h without degradation) toward oxygen evolution reaction (OER) in 1 m KOH. Moreover, an alkaline water electrolyzer is constructed with the Ni‐Fe‐O composite as catalyst for both anode and cathode. This electrolyzer displays superior electrolysis performance (affording 10 mA cm^?2 at 1.64 V) and long‐term durability. The remarkable features of the catalyst lie in its unique mesoporous nanowire network architecture and the synergistic effect of the metal core and the active metal oxide, giving rise to the strikingly enhanced active surface area, accelerated electron/ion transport, and further promoted reaction kinetics of OER.     

Earth‐Abundant Iron Diboride (FeB2) Nanoparticles as Highly Active Bifunctional Electrocatalysts for Overall Water Splitting

Developing efficient, durable, and earth‐abundant electrocatalysts for both hydrogen and oxygen evolution reactions is important for realizing large‐scale water splitting. The authors report that FeB₂ nanoparticles, prepared by a facile chemical reduction of Fe²⁺ using LiBH₄ in an organic solvent, are a superb bifunctional electrocatalyst for overall water splitting. The FeB₂ electrode delivers a current density of 10 mA cm^?2 at overpotentials of 61 mV for hydrogen evolution reaction (HER) and 296 mV for oxygen evolution reaction (OER) in alkaline electrolyte with Tafel slopes of 87.5 and 52.4 mV dec^?1, respectively. The electrode can sustain the HER at an overpotential of 100 mV for 24 h and OER for 1000 cyclic voltammetry cycles with negligible degradation. Density function theory calculations demonstrate that the boron‐rich surface possesses appropriate binding energy for chemisorption and desorption of hydrogen‐containing intermediates, thus favoring the HER process. The excellent OER activity of FeB₂ is ascribed to the formation of a FeOOH/FeB₂ heterojunction during water oxidation. An alkaline electrolyzer is constructed using two identical FeB₂‐NF electrodes as both anode and cathode, which can achieve a current density of 10 mA cm^?2 at 1.57 V for overall water splitting with a faradaic efficiency of nearly 100%, rivalling the integrated state‐of‐the‐art Pt/C and RuO₂/C.     

An Efficient and Earth‐Abundant Oxygen‐Evolving Electrocatalyst Based on Amorphous Metal Borides

Cost‐effective and efficient oxygen‐evolving electrocatalysts are urgently required for energy storage and conversion technologies. In this work, an amorphous trimetallic boride nanocatalyst (Fe–Co–2.3Ni–B) prepared by a simple approach is reported as a highly efficient oxygen evolution reaction electrocatalyst. It exhibits an overpotential (η) of 274 mV to deliver a geometric current density (j_geo) of 10 mA cm^?2, a small Tafel slope of 38 mV dec^?1, and excellent long‐term durability at a mass loading of 0.3 mg cm^?2. The impressive electrocatalytic performance originates from the unique amorphous multimetal–metalloid complex nanostructure. From application's point of view, this work holds great promise as this process is simple and allows for large‐scale production of cheap, yet efficient, material.     

Ultralow Ru Loading Transition Metal Phosphides as High‐Efficient Bifunctional Electrocatalyst for a Solar‐to‐Hydrogen Generation System

Water splitting is a promising technology for sustainable conversion of hydrogen energy. The rational design of oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) bifunctional electrocatalysts with superior activity and stability in the same electrolyte is the key to promoting their large‐scale applications. Herein, an ultralow Ru (1.08 wt%) transition metal phosphide on nickel foam (Ru–MnFeP/NF) derived from Prussian blue analogue, that effectively drivies both the OER and the HER in 1 m KOH, is reported. To reach 20 mA cm^?2 for OER and 10 mA cm^?2 for HER, the Ru–MnFeP/NF electrode only requires overpotentials of 191 and 35 mV, respectively. Such high electrocatalytic activity exceeds most transition metal phosphides for the OER and the HER, and even reaches Pt‐like HER electrocatalytic levels. Accordingly, it significantly accelerates full water splitting at 10 mA cm^?2 with 1.470 V, which outperforms that of the integrated RuO₂ and Pt/C couple electrode (1.560 V). In addition, the extremely long operational stability (50 h) and the successful demonstration of a solar‐to‐hydrogen generation system through full water splitting provide more flexibility for large‐scale applications of Ru–MnFeP/NF catalysts.     

Electroless Plating of Highly Efficient Bifunctional Boride‐Based Electrodes toward Practical Overall Water Splitting

Exploring highly‐efficient and low‐cost electrodes for both hydrogen and oxygen evolution reaction (HER and OER) is of primary importance to economical water splitting. Herein, a series of novel and robust bifunctional boride‐based electrodes are successfully fabricated using a versatile Et₂NHBH₃‐involved electroless plating (EP) approach via deposition of nonprecious boride‐based catalysts on various substrates. Owing to the unique binder‐free porous nodule structure induced by the hydrogen release EP reaction, most of the nonprecious boride‐based electrodes are highly efficient for overall water splitting. As a distinctive example, the Co‐B/Ni electrode can afford 10 mA cm^?2 at overpotentials of only 70 mV for HER and 140 mV for OER, and can also survive at large current density of 1000 mA cm^?2 for over 20 h without performance degradation in 1.0 m KOH. Several boride‐based two‐electrode electrolyzers can achieve 10 mA cm^?2 at low voltages of around 1.4 V. Moreover, the facile EP approach is economically viable for flexible and large size electrode production.     

Ultrafine Pt Nanoparticle‐Decorated Pyrite‐Type CoS2 Nanosheet Arrays Coated on Carbon Cloth as a Bifunctional Electrode for Overall Water Splitting

To improve the utilization efficiency of precious metals, metal‐supported materials provide a direction for fabricating highly active and stable heterogeneous catalysts. Herein, carbon cloth (CC)‐supported Earth‐abundant CoS₂ nanosheet arrays (CoS₂/CC) are presented as ideal substrates for ultrafine Pt deposition (Pt‐CoS₂/CC) to achieve remarkable performance toward the hydrogen and oxygen evolution reactions (HER/OER) in alkaline solutions. Notably, the Pt‐CoS₂/CC hybrid delivers an overpotential of 24 mV at 10 mA cm^?2 and a mass activity of 3.89 A Pt_mg^?1, which is 4.7 times higher than that of commercial Pt/C, at an overpotential of 130 mV for catalyzing the HER. An alkali‐electrolyzer using Pt‐CoS₂/CC as a bifunctional electrode enables a water‐splitting current density of 10 mA cm^?2 at a low voltage of 1.55 V and can sustain for more than 20 h, which is superior to that of the state‐of‐the‐art Pt/C+RuO₂ catalyst. Further experimental and theoretical simulation studies demonstrate that strong electronic interaction between Pt and CoS₂ synergistically optimize hydrogen adsorption/desorption behaviors and facilitate the in situ generation of OER active species, enhancing the overall water‐splitting performance. This work highlights the regulation of interfacial and electronic synergy in pursuit of highly efficient and durable supported catalysts for hydrogen and oxygen electrocatalytic applications.