Lamellar thickening and cocrystallization of poly(hydroxyalkanoate)s on annealing.

Lamellar thickening behavior of microbial polyesters, poly(3-hydroxybutyrate) [P(3HB)], poly(3-hydroxybutyrate-co-3-hydroxyvalerate) [P(3HB-co-3HV)] and poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] annealed at various temperatures was investigated to make sure of the occurrence of cocrystallization of both components. All the copolymers showed steep increases in melting points accompanied by partial melting as the annealing temperature increased up to just below the melting points. In contrast, long periods of P(3HB-co-7mol% 3HV) increased to twice, similar to those of P(3HB), with increasing annealing temperature up to just below the melting point, while long periods of P(3HB-co-7mol% 4HB) and P(3HB-co-92mol% 3HV) only increased up to one and a half times. Lattice indices of unit cell of the former crystal were increased slightly, while those of the latter crystal remained unchanged. These results imply that the P(3HB) crystal can occlude the 3HV component to some extent, but hardly includes the 4HB component, and P(3HV) crystal also excludes the 3HB component.     

Extracellular poly(hydroxyalkanoate) depolymerases and their inhibitor from Pseudomonas lemoignei.

Enzymatic degradation processes of microbial copolyesters, poly(3-hydroxybutyrate-co-3-hydroxyvalerate): P(3HB-co-3HV) and poly(3-hydroxybutyrate-co-4-hydroxybutyrate): P(3HB-co-4HB), were studied by the weight loss (erosion) of copolyester films. These studies employed three extracellular depolymerases which degrade poly(3-hydroxybutyrate): P(3HB). Two enzymes were purified from the culture supernatant of Pseudomonas lemoignei and one from Alcaligenes faecalis T1. The rate of enzymatic degradation of microbial copolyester films with various compositions showed an almost similar tendency to three different P(3HB) depolymerases, and decreased in the following order: P(3HB-co-4HB) greater than P(3HB) greater than P(3HB-co-3HV). An inhibitory protein of P(3HB) depolymerases in the succinate culture medium of P. lemoignei was isolated and characterized. The molecular weight of P(3HB) depolymerase inhibitor was 35,000 as determined by polyacrylamide gel electrophoresis in the presence of sodium dodecyl sulphate. This inhibitor of a single polypeptide chain may reversibly bind the serine residues at the active site of P(3HB) depolymerase. This inhibitory protein was not induced in the culture medium when P. lemoignei was grown on P(3HB) as the sole carbon source.     

Local sequence dependence of polyhydroxyalkanoic acid degradation in Hydrogenophaga pseudoflava

The first order intracellular degradation of various polyhydroxyalkanoic acid (PHA) inclusions in Hydrogenophaga pseudoflava cells was investigated by analyzing the compositional and microstructural changes of the PHA using gas chromatography, (13)C NMR spectroscopy, and differential scanning calorimetry. Two types of PHA, copolymers and blend-type polymers, were separately accumulated in cells for comparison. The constituent monomers were 3-hydroxybutyric acid (3HB), 4-hydroxybutyric acid (4HB), and 3-hydroxyvaleric acid (3HV). It was found that the 3HB-4HB copolymer was degraded only when the polymer contained a minimal level of 3HB units. With the cells containing a 3HB/4HB blend-type polymer, only poly(3HB) was degraded, whereas poly(4HB) was not degraded, indicating the totally inactive nature of the intracellular depolymerase against poly(4HB). On the basis of the magnitude of the first order degradation rate constants, the relative substrate specificity of the depolymerase toward the constituting monomer units was determined to decrease in the order 3HB > 3HV > 4HB. (13)C NMR resonances of the tetrad, triad, and dyad sequences were analyzed for the samples isolated before and after degradation experiments. The results showed that the intracellular degradation depended on the local monomer sequence of the copolymers. The relative substrate specificity of the depolymerase determined from the NMR local sequence analysis agreed well with that obtained from the kinetics analysis. It is suggested that, without isolation and purification of the intracellular PHA depolymerase and "native" PHA substrates, the relative specificity of the enzyme as well as the microstructural heterogeneity of the PHA could be determined by measuring in situ the first order degradation rate constants of the PHA in cells.     

Biosynthesis of poly(3-hydroxybutyrate-co-3-hydroxyvalerate-co-3-hydroxyhexanoate) by metabolically engineered Escherichia coli strains

The recombinant Escherichia coli strain, equipped with the newly cloned Aeromonas PHA biosynthesis genes, could produce a terpolymer of 3-hydroxybutyrate (3HB), 3-hydroxyvalerate (3HV), and 3-hydroxyhexanoate (3HHx) [P(3HB-co-3HV-co-3HHx)] from dodecanoic acid plus odd carbon number fatty acid. In addition, the orf1 gene of Aeromonas hydrophila was found to play a critical role in assimilating the 3HV monomer and in regulating the monomer fraction in the terpolymer.     

Structure and enzymatic degradation of poly(3-hydroxybutyrate) copolymer single crystals with an extracellular PHB depolymerase from Alcaligenes faecalis T1.

Lamellar single crystals of four random copolymers of (R)-3-hydroxybutyrate with different hydroxyalkanoates: poly(3-hydroxybutyrate-co-8 mol%-3-hydroxyvalerate) (P(3HB-co-8%-3HV)), poly(3-hydroxybutyrate-co-10 mol%-4-hydroxybutyrate) (P(3HB-co-10%-4HB)), poly(3-hydroxybutyrate-co-8 mol%-3-hydroxyhexanoate) (P(3HB-co-8%-3HH)) and poly(3-hydroxybutyrate-co-10 mol%-6-hydroxyhexanoate) (P(3HB-co-10%-6HH)), were grown from dilute solutions of chloroform and ethanol. All single crystals have lath-shaped morphology and the second monomer units seem to be excluded from the P(3HB) crystal, on the basis of the electron diffraction diagrams. The enzymatic degradation of P(3HB-co-8%-3HH) and P(3HB-co-10%-6HH) single crystals was investigated with an extracellular PHB depolymerase from Alcaligenes faecalis T1. Adsorption of an extracellular PHB depolymerase, examined using an immuno-gold labelling technique, demonstrated a homogeneous distribution of enzyme molecules with a low concentration on the crystal surfaces. Enzymatic degradation of single crystals progressed from the edges and ends of crystals to yield narrow cracks along their long axes and the small crystal fragments. Lamellar thicknesses of single crystals and molecular weights of copolymer chains remained unchanged during the enzymatic hydrolysis. The above results support the hypothesis that the hydrophobic adsorption of the enzyme contributes to increase the mobility of molecular chains of single crystals and generate the disordered chain-packing regions. The active-site of PHB depolymerase takes place preferentially at the disordered chain-packing regions of crystal edges and ends with endo-exo enzymatic hydrolysis behaviour, termed processive degradation.     

A fed-batch strategy to produce high poly(3-hydroxybutyrate-co-3-hydroxyvalerate-co-4-hydroxybutyrate) terpolymer yield with enhanced mechanical properties in bioreactor

Bioprocess and Biosystems Engineering - This study reports an efficient fed-batch strategy to improve poly(3-hydroxybutyrate-co-3-hydroxyvalerate-co-4-hydroxybutyrate) [P(3HB-co-3HV-co-4HB)]...     

Production of poly(3-hydroxybutyric acid-co-4-hydroxybutyric acid) and poly(4-hydroxybutyric acid) without subsequent degradation by Hydrogenophaga pseudoflava

A Hydrogenophaga pseudoflava strain was able to synthesize poly(3-hydroxybutyric acid-co-4-hydroxybutyric acid) [P(3HB-co-4HB)] having a high level of 4-hydroxybutyric acid monomer unit (4HB) from gamma-butyrolactone. In a two-step process in which the first step involved production of cells containing a minimum amount of poly(3-hydroxybutyric acid) [P(3HB)] and the second step involved polyester accumulation from the lactone, approximately 5 to 10 mol% of the 3-hydroxybutyric acid (3HB) derived from the first-step culture was unavoidably reincorporated into the polymer in the second cultivation step. Reincorporation of the 3HB units produced from degradation of the first-step residual P(3HB) was confirmed by high-resolution 13C nuclear magnetic resonance spectroscopy. In order to synthesize 3HB-free poly(4-hydroxybutyric acid) [P(4HB)] homopolymer, a three-stage cultivation technique was developed by adding a nitrogen addition step, which completely removed the residual P(3HB). The resulting polymer was free of 3HB. However, when the strain was grown on gamma-butyrolactone as the sole carbon source in a synthesis medium, a copolyester of P(3HB-co-4HB) containing 45 mol% 3HB was produced. One-step cultivation on gamma-butyrolactone required a rather long induction time (3 to 4 days). On the basis of the results of an enzymatic study performed with crude extracts, we suggest that the inability of cells to produce 3HB in the multistep culture was due to a low level of 4-hydroxybutyric acid (4HBA) dehydrogenase activity, which resulted in a low level of acetyl coenzyme A. Thus, 3HB formation from gamma-butyrolactone is driven by a high level of 4HBA dehydrogenase activity induced by long exposure to gamma-butyrolactone, as is the case for a one-step culture. In addition, intracellular degradation kinetics studies showed that P(3HB) in cells was completely degraded within 30 h of cultivation after being transferred to a carbon-free mineral medium containing additional ammonium sulfate, while P(3HB-co-4HB) containing 5 mol% 3HB and 95 mol% 4HB was totally inert in interactions with the intracellular depolymerases. Intracellular inertness could be a useful factor for efficient synthesis of the P(4HB) homopolymer and of 4HB-rich P(3HB-co-4HB) by the strain used in this study.     

Biosynthesis of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) copolymer by Cupriavidus sp. USMAA1020 isolated from Lake Kulim, Malaysia

Cupriavidus sp. USMAA1020 was isolated from Malaysian environment and able to synthesize poly(3-hydroxybutyrate-co-4-hydroxybutyrate), [P(3HB-co-4HB)] when grown on gamma-butyrolactone as the sole carbon source. The polyester was purified from freeze-dried cells and analyzed by nuclear magnetic resonance (NMR) spectroscopy. 1H and 13C NMR results confirmed the presence of 3HB and 4HB monomers. In a one-step cultivation process, P(3HB-co-4HB) accumulation by Cupriavidus sp. USMAA1020 was affected by carbon to nitrogen ratio (C/N). A two-step cultivation process accumulated P(3HB-co-4HB) copolyester with a higher 4HB fraction (53 mol%) in nitrogen-free mineral medium containing gamma-butyrolactone. The biosynthesis of P(3HB-co-4HB) was also achieved by using 4-hydroxybutyric acid and alkanediol as 1,4-butanediol. The composition of copolyesters varied from 32 to 51 mol% 4HB, depending on the carbon sources supplied. The copolyester produced by Cupriavidus sp. USMAA1020 has a random sequence distribution of 3-hydroxybutyrate (3HB) and 4-hydroxybutyrate (4HB) units when analyzed by nuclear magnetic resonance (NMR) spectroscopy. When gamma-butyrolactone was used as the sole carbon source, the 4HB fraction in copolyester increased from 25 to 60 mol% as the concentration of gamma-butyrolactone in the culture medium increased from 2.5 g/L to 20.0 g/L.     

Comparative evaluation of physico-chemical characteristics of biopolyesters P(3HB) and P(3HB-co-3HV) produced by endophytic <Emphasis Type="Italic">Bacillus cereus</Emphasis> RCL 02

Background

Bacteria endogenously residing within the plant tissues have attracted significant attention for production of biopolyester, polyhydroxyalkanoates (PHAs). Bacillus cereus RCL 02 (MCC 3436), a leaf endophyte of oleaginous plant Ricinus communis L. accumulates 81% poly(3-hydroxybutyrate) [P(3HB)] of its cell dry biomass when grown in mineral salts (MS) medium.

Methods

The copolymer production efficiency of B. cereus RCL 02 was evaluated in valeric acid supplemented MS medium under biphasic cultivation condition. The copolymer so produced has been compared with the P(3HB) isolated from RCL 02 in terms of thermal, mechanical and chemical properties.

Results

Valeric acid supplementation as co-substrate in the medium has led to the production of copolymer of 3-hydroxybutyrate (3HB) and 3-hydroxyvalerate (3HV) [P(3HB-co-3HV)] with 14.6 mol% 3HV. The identity of the polymers has been confirmed by X-ray diffraction (XRD) analysis, Fourier transform infrared (FTIR) and nuclear magnetic resonance (NMR) spectroscopic studies. Thermogravimetric analysis (TGA) revealed that P(3HB) and P(3HB-co-3HV) films degraded at 278.66°C and 273.49°C, respectively. The P(3HB-co-3HV) showed lower melting temperature (165.03°C) compared to P (3HB) (170.74°C) according to differential scanning calorimetry (DSC). Incorporation of 3HV monomers decreased the tensile strength (21.52 MPa), tensile modulus (0.93 GPa), storage modulus (E′) (0.99 GPa) and increased % elongation at break (12.2%) of the copolyester. However, P(3HB) showed better barrier properties with lower water vapor transmission rate (WVTR) of 0.55 g-mil/100 in²/24 h.

Conclusion

These findings emphasized exploration of endophytic bacterial strain (RCL 02) to produce biodegradable polyesters which might have significant potential for industrial application.

     

Degradation of microbial polyester poly(3-hydroxybutyrate) in environmental samples and in culture

Poly(3-hydroxybutyrate) [P(3HB)] test-pieces prepared from the polymer produced by Azotobacter chroococcum were degraded in natural environments like soil, water, compost and sewage sludge incubated under laboratory conditions. Degradation in terms of % weight loss of the polymer was maximum (45%) in sewage sludge after 200 days of incubation at 30°C. The P(3HB)-degrading bacterial cultures (36) isolated from degraded test-pieces showed different degrees of degradation in polymer overlayer method. The extent of P(3HB) degradation increases up to 12 days of incubation and was maximum at 30°C for majority of the cultures. For most efficient cultures the optimum concentration of P(3HB) for degradation was 0.3% (w/v). Supplementation of soluble carbon sources like glucose, fructose and arabinose reduced the degradation while it was almost unaffected with lactose. Though the cultures degraded P(3HB) significantly, they were comparatively less efficient in utilizing copolymer of 3-hydroxybutyrate and 3-hydroxyvalerate [P(3HB-co-3HV)].     

Synthesis of poly-(3-hydroxybutyrate-co-3-hydroxyvalerate) by recombinant Escherichia coli

Several recombinant Escherichia coli strains, including XL1-Blue, JM109, HB101, and DH5alpha harboring a stable high-copynumber plasmid pSYL105 containing the Alcaligenes eutrophus polyhydroxyalkanoate (PHA) biosynthesis genes were constructed. These recombinant strains were examined for their ability to synthesize and accumulate poly-(3-hydroxybutyrate-co-3-hydroxyvalerate) [P(3HB-co-3HV)] copolymer from glucose and either propionate or valerate. All recombinant E. coli strains could synthesize the P(3HB-co-3HV) copolymer in the medium containing glucose and propionate. However, only the homopolymer poly-(3-hydroxybutyrate) [P(3HB)] was synthesized from glucose and valerate. The PHA concentration and the 3HV fraction could be increased by inducing with acetate and/or oleate. When supplemented with oleate, the 3HV fraction increased by fourfold compared with that obtained without induction. Induction with propionate resulted in lower PHA concentration due to the inhibitory effect, but an 3HV fraction of as high as 33.0% could be obtained. These results suggest that P(3HB-co-3HV) can be efficiently produced from propionate by recombinant E. coli by inducing with acetate, propionate, or oleate. (c) 1996 John Wiley & Sons, Inc.     

Sequencing microbial copolymers of 3-hydroxybutyric and 3-mercaptoalkanoic acids by NMR, electrospray ionization mass spectrometry, and size exclusion chromatography NMR

Copolymers of 3-hydroxybutyrate (3HB) and 3-mercaptopropionate (3MP) or 3-mercaptobutyrate (3MB) units and minor amounts of 3-hydroxypropionate (3HP), 3-hydroxyvalerate (3HV), or 3-mercaptovalerate (3MV) were investigated regarding their microstructure by NMR, electrospray ionization mass spectrometry, and size exclusion chromatography NMR. These copolymers were produced by Ralstonia eutropha strain H16 when cells were cultivated in a mineral salts medium with gluconate as a carbon source for growth and 3MP or 3MB as precursor substrates for incorporation of 3-mercaptoalkanoates. Mass spectrometry analysis of partially methanolyzed or pyrolyzed samples proved the presence of true copolymers or terpolymers. (13)C NMR spectroscopy of intact polymer samples, with values of average block length and degree of randomness deviating from a random sequence model, suggested microblock structures; however, composition analysis by (1)H NMR of fractions obtained by size exclusion chromatography showed significant variations with molecular weight, revealing the presence of blends of poly(3HB-co-3MP-co-3HP) or poly(3HB-co-3MB) with poly(3HB). The experimental NMR carbonyl dyad signal intensities were satisfactorily matched by a random sequence model when the presence of poly(3HB) was taken into account.     

Accumulation of PHA and its copolyesters by Methylobacterium sp. KCTC 0048

Summary Methylobacterium sp. KCTC 0048 isolated from soil, could synthesize a variety of copolyesters when secondary carbon substrates were added to nitrogen-limited cultures containing methanol as a major carbon and energy source. The copolyester of 3-hydroxy-butyrate and 3-hydroxyvalerate, P(3HB-co-3HV) accumulated when valeric acid, pentanol or heptanoic acid was added to the nitrogen-limited medium containing methanol. The copolyester of 3-hydroxybutyrate and 4-hydroxybutyrate, P(3HB-co-4HB) was synthesized from 4-hydroxybutyrate, 1,4-butanediol, or -butyrolactone, and the copolyester of 3-hydroxybutyrate and 3-hydroxypropionate (P(3HB-co-3HP)), from 3-hydroxypropionate as the secondary carbon substrates, respectively.     

Biosynthesis and properties of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) polymers

In support of programs to identify polyhydroxyalkanoates with improved materials properties, we report on our efforts to characterize the mechanical and thermal properties of copolyesters of 3-hydroxybutyrate (3HB) and 3-hydroxyhexanoate (3HHx). The copolyesters, having molar fraction of 3HHx ranging from 2.5 to 35 mol % and average molecular weights ranging from 1.15 x 10(5) to 6.65 x 10(5), were produced by fermentation using Aeromonas hydrophila and a recombinant strain of Pseudomonas putida GPp104. The polymers were chloroform extracted and characterized by solution-state and solid-state nuclear magnetic resonance (NMR) spectroscopy and a variety of mechanical and thermal tests. Solution-state (1)H NMR data were used to determine polymer composition-of-matter, while solution-state (13)C NMR data provided polymer-sequence information. Solvent fractionation and NMR spectroscopic characterization of these polymers showed that polymers containing up to 9.5 mol % 3HHx had a Bernoullian compositional distribution. By contrast, polymers containing more than 9.5 mol % 3HHx had a bimodal polymer composition. Solvent fractionation of these 3HHx-rich polyesters produced two polymer fractions, each of which was again consistent with Bernoullian polymerization statistics. Solid-state NMR relaxation experiments provided insight into aging in poly(3HB-co-3HHx) copolymers, demonstrating increased polymer-chain motion with increasing 3HHx content. The elongation-to-break ratio in the polyesters increased with increasing molar fraction of 3HHx monomers. Aging properties of the poly(3HB-co-3HHx) copolymers were very similar to copolymers of 3HB and 3-hydroxyvalerate (3HV). However, poly(3HB-co-3HHx) exhibited increased activation energy to thermal degradation with increasing 3HHx content.     

Synthesis of 3-hydroxybutyrate-CO-4-hydroxybutyrate copolymers by hydrogen-oxidizing bacteria

Synthesis of 3- and 4-hydroxybutyrate copolymer (3HB-co-4HB), the most promising member of the biodegradable polyhydroxyalkanoate (PHA) family, has been studied. Cultivation conditions of naturally occurring strains of hydrogen-oxidizing bacteria Ralstonia eutropha B5786 and Cupriavidus eutrophus B10646 have been optimized to ensure efficient synthesis of the 3HB-co-4HB copolymer. A set of highly pure samples of the 3HB-co-4HB copolymer with 4HB content varying from 8.7 to 24.3 mol% has been obtained. Incorporation of 4HB into the copolymer was shown to cause a more pronounced decrease in polymer crystallinity than the incorporation of 3-hydroxyvalerate or 3-hydroxyhexanoate; samples with a degree of crystallinity below 30% have been obtained. The weight average molecular mass of the 3HB-co-4HB copolymers was shown to be independent on the monomer ratio and to vary broadly (from 540 to 1110 kDa).     

Enzymatic hydrolysis of bacterial poly(3-hydroxybutyrate-co-3-hydroxypropionate)s by poly(3-hydroxyalkanoate) depolymerase from Acidovorax Sp. TP4

Enzymatic degradability has been investigated for a series of bacterial poly(3-hydroxybutyrate-co-3-hydroxypropionate)s (P(3HB-co-3HP)s) with 3-hydroxypropionate (3HP) unit contents from 11 to 86 mol % as well as poly(3-hydroxybutyrate) (P(3HB)) and chemosynthesized poly(3-hydroxypropionate) (P(3HP)). The behavior of degradation by two types of extracellular poly(3-hydroxyalkanoate) (PHA) depolymerases purified from Ralstonia pikettii T1 and Acidovorax Sp. TP4, defined respectively as PHA depolymerase types I and II according to the position of the lipase box in the catalytic domain, were compared in relation to the thermal properties and crystalline structures of the PHA samples elucidated by differential scanning calorimetry and wide-angle X-ray diffraction. The degradation products were characterized by high-performance liquid chromatography and one- (1D) and two-dimension (2D) (1)H NMR spectroscopy. It was found that the PHA depolymerase of Acidovorax Sp. TP4 showed degradation behavior different from that shown by depolymerase of R. pikettii T1. PHA depolymerase from Acidovorax Sp. TP4 degraded the P(3HB-co-3HP) films with lower crystallinity in higher rates than those with higher crystallinity, no matter what kinds of crystalline structures they formed. In contrast, PHA depolymerase from R. pikettii T1 degraded P(3HB-co-3HP) films forming P(3HB) crystalline structure in higher rates than those forming P(3HP)s. The increase in amorphous nature of the P(3HB-co-3HP) films with P(3HB)-homopolymer-like crystalline structure increases and then decreases the rate of degradation by depolymerase from R. pikettii T1. The 3-hydroxybutyrate (3HB) monomer was produced as a major product by the hydrolysis of P(3HB) film by PHA depolymerase from Acidovorax Sp. TP4. The P(3HB-co-3HP) films could be degraded into 3HB and 3-hydroxypropionate (3HP) monomer at last, indicating that the catalytic domain of the enzyme recognized at least two monomeric units as substrates. While the PHA depolymerase from R. pikettii T1 hydrolyzed P(3HB) film into 3HB dimer as a major product, and the catalytic domain recognized at least three monomeric units. The degradation behavior of P(3HB-co-3HP) films by the PHA depolymerase of Acidovorax Sp. TP4 could be distinguished from that by the depolymerase of R. pikettii T1.     

Estimation of the number of polyhydroxyalkanoate (PHA)-degraders in soil and isolation of degraders based on the method of most probable number (MPN) using PHA-film.

A new method to estimate the number of polyhydroxyalkanoates (PHA)-degraders in soil and to isolate degraders, called the film-MPN method, is proposed. The incubation time was measured by the first order reaction (FOR) model. This method was used to estimate numbers of poly(3-hydroxybutyrate-co-3-hydroxyvalerate)[P(3HB-co-3HV)]- and poly(3-hydroxyvalerate-co-4-hydroxybutyrate)[P(3HB-co-4HB)]-degraders in garden soil (4.30 x 10(5) and 2.15 x 10(5) aerobic degraders per gram of dry soil, respectively). The number of P(3HB-co-3HV)-degraders in paddy field soil was 5.06 x 10(5) aerobic degraders per gram dry soil. Also, several P(3HB-co-3HV)-degraders were isolated directly from positive-growth tubes of high dilution.     

Degradation of poly(3-hydroxybutyrate) by soil streptomycetes

The ability of 64 soil streptomycetes to degrade poly(3-hydroxybutyrate) [P(3HB)] was evaluated on Pridham and Lyons mineral salts agar medium overlayered with the same medium containing 0.2% P(3HB). The streptomycete isolates were grown on this overlayered medium and the degradation was detected by the formation of clear zone surrounding the growth. Four potent degrader isolates identified as species of Streptomyces were selected. Degradation of P(3HB) by these isolates was studied for a period of 8 days. The rate of degradation increased with increase in concentration of P(3HB) in the medium while it decreased with the supplementation of readily utili- zable carbon sources like glucose, fructose and sucrose. All four isolates also degraded the copolymer of 3-hydroxybutyrate and 3-hydroxyvalerate [P(3HB–co–3HV)] in solid medium but to a lesser extent. However, the isolates were equally efficient in degrading P(3HB) in liquid medium.     

Structure and properties of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) produced by Alcaligenes latus

Summary Random copolymers of 3-hydroxybutyrate (3HB) and 4-hydroxybutyrate (4HB) with a wide range of compositions varying from 0 to 83 mol% 4HB were produced by Alcaligenes latus from the mixed carbon substrates of 3-hydroxybutyric and 4-hydroxybutyric acids. The structure and physical properties of P(3HB-co-4HB) were characterized by¹H and¹³C NMR spectroscopy, gel-permeation chromatography, and differential scanning calorimetry. The isothermal radial growth rates of spherulites of P(3HB-co-4HB) were much slower than the rate of P(3HB) homopolymer. The enzymatic degradation rates of P(3HB-co-4HB) films by a PHB depolymerase were strongly influenced by the copolymer composition.     

Estimation of the Number of Polyhydroxyalkanoate (PHA)-Degraders in Soil and Isolation of Degraders Based on the Method of Most Probable Number (MPN) Using PHA-Film

A new method to estimate the number of polyhydroxyalkanoates (PHA)-degraders in soil and to isolate degraders, called the film-MPN method, is proposed. The incubation time was measured by the first order reaction (FOR) model. This method was used to estimate numbers of poly (3-hydroxybutyrate-co-3-hydroxyvalerate)[P(3HB-co-3HV)]- and poly(3-hydroxyvalerate-co-4-hydroxybutyrate)[P(3HB-co-4HB)]-degraders in garden soil (4.30 × 10⁵ and 2.15 × 10⁵ aerobic degraders per gram of dry soil, respectively). The number of P(3HB-co-3HV)-degraders in paddy field soil was 5.06 × 10⁵ aerobic degraders per gram dry soil. Also, several P(3HB-co-3HV)-degraders were isolated directly from positive-growth tubes of high dilution.