Partially Reduced Holey Graphene Oxide as High Performance Anode for Sodium‐Ion Batteries

The current Na⁺ storage performance of carbon‐based materials is still hindered by the sluggish Na⁺ ion transfer kinetics and low capacity. Graphene and its derivatives have been widely investigated as electrode materials in energy storage and conversion systems. However, as anode materials for sodium‐ion batteries (SIBs), the severe π–π restacking of graphene sheets usually results in compact structure with a small interlayer distance and a long ion transfer distance, thus leading to low capacity and poor rate capability. Herein, partially reduced holey graphene oxide is prepared by simple H₂O₂ treatment and subsequent low temperature reduction of graphene oxide, leading to large interlayer distance (0.434 nm), fast ion transport, and larger Na⁺ storage space. The partially remaining oxygenous groups can also contribute to the capacity by redox reaction. As anode material for SIBs, the optimized electrode delivers high reversible capacity, high rate capability (365 and 131 mAh g^?1 at 0.1 and 10 A g^?1, respectively), and good cycling performance (163 mAh g^?1 after 3000 cycles at a current density of 2 A g^?1), which is among the best reported performances for carbon‐based SIB anodes.     

Molecular Engineering of Monodisperse SnO2 Nanocrystals Anchored on Doped Graphene with High‐Performance Lithium/Sodium‐Storage Properties in Half/Full Cells

The fabrication of ultrasmall and high‐content SnO₂ nanocrystals anchored on doped graphene can endow SnO₂ with superior electrochemical properties. Herein, an effective strategy, involving molecular engineering of a layer‐by‐layer assembly technique, is proposed to homogeneously anchor SnO₂ nanocrystals on nitrogen/sulfur codoped graphene (NSGS), which serves as an advanced anode material in lithium/sodium‐ion batteries (LIBs/SIBs). Benefiting from novel design and specific structure, the optimized NSGS for LIBs displays high initial capacity (2123.9 mAh g^?1 at 0.1 A g^?1), long‐term cycling performance (only 0.8% loss after 500 cycles), and good rate capability (477.4 mAh g^?1 at 5 A g^?1). In addition, the optimized NSGS for SIBs also delivers high initial capacity (791.7 mAh g^?1 at 0.1 A g^?1) and high reversible capacity (180.2 mAh g^?1 after 500 cycles at 0.5 A g^?1). Meanwhile, based on the detailed analysis of phase transition and electrochemical reaction kinetics, the reaction mechanisms of NSGS in LIBs and SIBs as well as the distinction in LIBs/SIBs are clearly articulated. Notably, to further explore the practical application, Li/Na⁺ full cells are also assembled by coupling the optimized NSGS anode with LiCoO₂ and Na₃V₂(PO₄)₃/C cathodes, respectively.     

3D Amorphous Carbon with Controlled Porous and Disordered Structures as a High‐Rate Anode Material for Sodium‐Ion Batteries

Sodium‐ion batteries (SIBs) have a promising application prospect for energy storage systems due to the abundant resource. Amorphous carbon with high electronic conductivity and high surface area is likely to be the most promising anode material for SIBs. However, the rate capability of amorphous carbon in SIBs is still a big challenge because of the sluggish kinetics of Na⁺ ions. Herein, a three‐dimensional amorphous carbon (3DAC) with controlled porous and disordered structures is synthesized via a facile NaCl template‐assisted method. Combination of open porous structures of 3DAC, the increased disordered structures can not only facilitate the diffusion of Na⁺ ions but also enhance the reversible capacity of Na storage. When applied as anode materials for SIBs, 3DAC exhibits excellent rate capability (66 mA h g^?1 at 9.6 A g^?1) and high reversible capacity (280 mA h g^?1 at a low current density of 0.03 A g^?1). Moreover, the controlled porous structures by the NaCl template method provide an appropriate specific surface area, which contributes to a relatively high initial Coulombic efficiency of 75%. Additionally, the high‐rate 3DAC material is prepared via a green approach originating from low‐cost pitch and NaCl template, demonstrating an appealing development of carbon anode materials for SIBs.     

Promoting Highly Reversible Sodium Storage of Iron Sulfide Hollow Polyhedrons via Cobalt Incorporation and Graphene Wrapping

Sodium ion batteries (SIBs) have drawn significant attention owing to their low cost and inherent safety. However, the absence of suitable anode materials with high rate capability and long cycling stability is the major challenge for the practical application of SIBs. Herein, an efficient anode material consisting of uniform hollow iron sulfide polyhedrons with cobalt doping and graphene wrapping (named as CoFeS@rGO) is developed for high‐rate and long‐life SIBs. The graphene‐encapsulated hollow composite assures fast and continuous electron transportation, high Na⁺ ion accessibility, and strong structural integrity, showing an extremely small volume expansion of only 14.9% upon sodiation and negligible volume contraction during the desodiation. The CoFeS@rGO electrode exhibits high specific capacity (661.9 mAh g^?1 at 100 mA g^?1), excellent rate capability (449.4 mAh g^?1 at 5000 mA g^?1), and long cycle life (84.8% capacity retention after 1500 cycles at 1000 mA g^?1). In situ X‐ray diffraction and selected‐area electron diffraction patterns show that this novel CoFeS@rGO electrode is based on a reversible conversion reaction. More importantly, when coupled with a Na₃V₂(PO₄)₃/C cathode, the sodium ion full battery delivers a superexcellent rate capability (496.8 mAh g^?1 at 2000 mA g^?1) and ≈96.5% capacity retention over 200 cycles at 500 mA g^?1 in the 1.0–3.5 V window. This work indicates that the rationally designed anode material is highly applicable for the next generation SIBs with high‐rate capability and long‐term cyclability.     

High‐Quality Graphene Microflower Design for High‐Performance Li–S and Al‐Ion Batteries

Poor quality and insufficient productivity are two main obstacles for the practical application of graphene in electrochemical energy storage. Here, high‐quality crumpled graphene microflower (GmF) for high‐performance electrodes is designed. The GmF possesses four advantages simultaneously: highly crystallized defect‐free graphene layers, low stacking degree, sub‐millimeter continuous surface, and large productivity with low cost. When utilized as carbon host for sulfur cathode, the GmF‐sulfur hybrid delivers decent areal capacities of 5.2 mAh cm^?2 at 0.1 C and 3.8 mAh cm^?2 at 0.5 C. When utilized as cathode of Al‐ion battery, the GmF affords a high capacity of 100 mAh g^?1 with 100% capacity retention after 5000 cycles and excellent rate capability from 0.1 to 20 A g^?1. This facile and large‐scale producible GmF represents a meaningful high‐quality graphene powder for practical energy storage technology. Meanwhile, this unique high‐quality graphene design provides an effective route to improve electrochemical properties of graphene‐based electrodes.     

Lithium‐Pretreated Hard Carbon as High‐Performance Sodium‐Ion Battery Anodes

Hard carbon (HC) is the state‐of‐the‐art anode material for sodium‐ion batteries (SIBs). However, its performance has been plagued by the limited initial Coulombic efficiency (ICE) and mediocre rate performance. Here, experimental and theoretical studies are combined to demonstrate the application of lithium‐pretreated HC (LPHC) as high‐performance anode materials for SIBs by manipulating the solid electrolyte interphase in tetraglyme (TEGDME)‐based electrolyte. The LPHC in TEGDME can 1) deliver > 92% ICE and ≈220 mAh g^?1 specific capacity, twice of the capacity (≈100 mAh g^?1) in carbonate electrolyte; 2) achieve > 85% capacity retention over 1000 cycles at 1000 mA g^?1 current density (4 C rate, 1 C = 250 mA g^?1) with a specific capacity of ≈150 mAh g^?1, ≈15 times of the capacity (10 mAh g^?1) in carbonate. The full cell of Na₃V₂(PO₄)₃‐LPHC in TEGDME demonstrated close to theoretical specific capacity of ≈98 mAh g^?1 based on Na₃V₂(PO₄)₃ cathode, ≈2.5 times of the value (≈40 mAh g^?1) with nontreated HC. This work provides new perception on the anode development for SIBs.     

Observation of Pseudocapacitive Effect and Fast Ion Diffusion in Bimetallic Sulfides as an Advanced Sodium‐Ion Battery Anode

Sodium‐ion batteries (SIBs) are promising next‐generation alternatives due to the low cost and abundance of sodium sources. Yet developmental electrodes in SIBs such as transition metal sulfides have huge volume expansion, sluggish Na⁺ diffusion kinetics, and poor electrical conductivity. Here bimetallic sulfide (Co₉S₈/ZnS) nanocrystals embedded in hollow nitrogen‐doped carbon nanosheets are demonstrated with a high sodium diffusion coefficient, pseudocapacitive effect, and excellent reversibility. Such a unique composite structure is designed and synthesized via a facile sulfidation of the CoZn‐MOFs followed by calcination and is highly dependant on the reaction time and temperature. The optimized Co₁Zn₁‐S(600) electrode exhibits excellent sodium storage performance, including a high capacity of 542 mA h g^?1 at 0.1 A g^?1, good rate capability at 10 A g^?1, and excellent cyclic stability up to 500 cycles for half‐cell. It also shows potential in full‐cell configuration. Such capabilities will accelerate the adoption of sodium‐ion batteries for electrical energy applications.     

An Air‐Stable Densely Packed Phosphorene–Graphene Composite Toward Advanced Lithium Storage Properties

Phosphorene, monolayer or few‐layer black phosphorus (BP), has recently triggered strong scientific interest for lithium/sodium ion batteries (LIBs/SIBs) applications. However, there are still challenges regarding large‐scale fabrication, poor air stability. Herein, we report the high‐yield synthesis of phosphorene with good crystallinity and tunable size distributions via liquid‐phase exfoliation of bulk BP in formamide. Afterwards, a densely packed phosphorene–graphene composite (PG‐SPS, a packing density of 0.6 g cm^?3) is prepared by a simple and easily up‐scalable spark plasma sintering (SPS) process. When working as anode materials of LIBs, PG‐SPS exhibit much improved first‐cycle Coloumbic efficiency (60.2%) compared to phosphorene (11.5%) and loosely stacked phosphorene–graphene composite (34.3%), high specific capacity (1306.7 mAh g^?1) and volumetric capacity (256.4 mAh cm^?3), good rate capabilities (e.g., 415.0 mAh g^?1 at 10 A g^?1) as well as outstanding long‐term cycling life (91.9% retention after 800 cycles at 10 A g^?1). Importantly, excellent air stability of PG‐SPS over the 60 days observation in maintaining its high Li storage properties can be achieved. On the contrary, 95.2% of BP in PG sample was oxidized after only 10 days exposure to ambience, leading to severe degradation of electrochemical properties.     

Mn‐Rich P′2‐Na0.67[Ni0.1Fe0.1Mn0.8]O2 as High‐Energy‐Density and Long‐Life Cathode Material for Sodium‐Ion Batteries

Herein, P′2‐type Na_0.67[Ni_0.1Fe_0.1Mn_0.8]O₂ is introduced as a promising new cathode material for sodium‐ion batteries (SIBs) that exhibits remarkable structural stability during repetitive Na⁺ de/intercalation. The O? Ni? O? Mn? O? Fe? O bond in the octahedra of transition‐metal layers is used to suppress the elongation of the Mn? O bond and to improve the electrochemical activity, leading to the highly reversible Na storage mechanism. A high discharge capacity of ≈220 mAh g^?1 (≈605 Wh kg^?1) is delivered at 0.05 C (13 mAg^?1) with a high reversible capacity of ≈140 mAh g^?1 at 3 C and excellent capacity retention of 80% over 200 cycles. This performance is associated with the reversible P′2–OP4 phase transition and small volume change upon charge and discharge (≈3%). The nature of the sodium storage mechanism in a full cell paired with a hard carbon anode reveals an unexpectedly high energy density of ≈542 Wh kg^?1 at 0.2 C and good capacity retention of ≈81% for 500 cycles at 1 C (260 mAg^?1).     

Nanosheets‐Assembled CuSe Crystal Pillar as a Stable and High‐Power Anode for Sodium‐Ion and Potassium‐Ion Batteries

Thanks to low costs and the abundance of the resources, sodium‐ion (SIBs) and potassium‐ion batteries (PIBs) have emerged as leading candidates for next‐generation energy storage devices. So far, only few materials can serve as the host for both Na⁺ and K⁺ ions. Herein, a cubic phase CuSe with crystal‐pillar‐like morphology (CPL‐CuSe) assembled by the nanosheets are synthesized and its dual functionality in SIBs and PIBs is comprehensively studied. The electrochemical measurements demonstrate that CPL‐CuSe enables fast Na⁺ and K⁺ storage as well as the sufficiently long duration. Specifically, the anode delivers a specific capacity of 295 mA h g^?1 at current density of 10 A g^?1 in SIBs, while 280 mA h g^?1 at 5 A g^?1 in PIBs, as well as the high capacity retention of nearly 100% over 1200 cycles and 340 cycles, respectively. Remarkably, CPL‐CuSe exhibits a high initial coulombic efficiency of 91.0% (SIBs) and 92.4% (PIBs), superior to most existing selenide anodes. A combination of in situ X‐ray diffraction and ex situ transmission electron microscopy tests fundamentally reveal the structural transition and phase evolution of CuSe, which shows a reversible conversion reaction for both cells, while the intermediate products are different due to the sluggish K⁺ insertion reaction.     

A Flexible Porous Carbon Nanofibers‐Selenium Cathode with Superior Electrochemical Performance for Both Li‐Se and Na‐Se Batteries

A flexible and free‐standing porous carbon nanofibers/selenium composite electrode (Se@PCNFs) is prepared by infiltrating Se into mesoporous carbon nanofibers (PCNFs). The porous carbon with optimized mesopores for accommodating Se can synergistically suppress the active material dissolution and provide mechanical stability needed for the film. The Se@PCNFs electrode exhibits exceptional electrochemical performance for both Li‐ion and Na‐ion storage. In the case of Li‐ion storage, it delivers a reversible capacity of 516 mAh g^?1 after 900 cycles without any capacity loss at 0.5 A g^?1. Se@PCNFs still delivers a reversible capacity of 306 mAh g^?1 at 4 A g^?1. While being used in Na‐Se batteries, the composite electrode maintains a reversible capacity of 520 mAh g^?1 after 80 cycles at 0.05 A g^?1 and a rate capability of 230 mAh g^?1 at 1 A g^?1. The high capacity, good cyclability, and rate capability are attributed to synergistic effects of the uniform distribution of Se in PCNFs and the 3D interconnected PCNFs framework, which could alleviate the shuttle reaction of polyselenides intermediates during cycling and maintain the perfect electrical conductivity throughout the electrode. By rational and delicate design, this type of self‐supported electrodes may hold great promise for the development of Li‐Se and Na‐Se batteries with high power and energy densities.     

Layer‐by‐Layer Na3V2(PO4)3 Embedded in Reduced Graphene Oxide as Superior Rate and Ultralong‐Life Sodium‐Ion Battery Cathode

Na₃V₂(PO₄)₃ (NVP) is regarded as a promising cathode for advanced sodium‐ion batteries (SIBs) due to its high theoretical capacity and stable sodium (Na) super ion conductor (NASICON) structure. However, strongly impeded by its low electronic conductivity, the general NVP delivers undesirable rate capacity and fails to meet the demands for quick charge. Herein, a novel and facile synthesis of layer‐by‐layer NVP@reduced graphene oxide (rGO) nanocomposite is presented through modifying the surface charge of NVP gel precursor. The well‐designed layered NVP@rGO with confined NVP nanocrystal in between rGO layers offers high electronic and ionic conductivity as well as stable structure. The NVP@rGO nanocomposite with merely ≈3.0 wt% rGO and 0.5 wt% amorphous carbon, yet exhibits extraordinary electrochemical performance: a high capacity (118 mA h g^?1 at 0.5 C attaining the theoretical value), a superior rate capability (73 mA h g^?1 at 100 C and even up to 41 mA h g^?1 at 200 C), ultralong cyclability (70.0% capacity retention after 15 000 cycles at 50 C), and stable cycling performance and excellent rate capability at both low and high operating temperatures. The proposed method and designed layer‐by‐layer active nanocrystal@rGO strategy provide a new avenue to create nanostructures for advanced energy storage applications.     

Chemical Synthesis of 3D Graphene‐Like Cages for Sodium‐Ion Batteries Applications

Sodium (Na) super ion conductor structured Na₃V₂(PO₄)₃ (NVP) is extensively explored as cathode material for sodium‐ion batteries (SIBs) due to its large interstitial channels for Na⁺ migration. The synthesis of 3D graphene‐like structure coated on NVP nanoflakes arrays via a one‐pot, solid‐state reaction in molten hydrocarbon is reported. The NVP nanoflakes are uniformly coated by the in situ generated 3D graphene‐like layers with the thickness of 3 nm. As a cathode material, graphene covered NVP nanoflakes exhibit excellent electrochemical performances, including close to theoretical reversible capacity (115.2 mA h g^?1 at 1 C), superior rate capability (75.9 mA h g^?1 at 200 C), and excellent cyclic stability (62.5% of capacity retention over 30000 cycles at 50 C). Furthermore, the 3D graphene‐like cages after removing NVP also serve as a good anode material and deliver a specific capacity of 242.5 mA h g^?1 at 0.1 A g^?1. The full SIB using these two cathode and anode materials delivers a high specific capacity (109.2 mA h g^?1 at 0.1 A g^?1) and good cycling stability (77.1% capacity retention over 200 cycles at 0.1 A g^?1).     

Boosting Sodium Storage in TiF3/Carbon Core/Sheath Nanofibers through an Efficient Mixed‐Conducting Network

Sodium‐ion batteries (SIBs) are considered to be promising energy storage devices for large‐scale grid storage application due to the vast earth‐abundance and low cost of sodium‐containing precursors. Designing and fabricating a highly efficient anode is one of the keys to improve the electrochemical performance of SIBs. Recently, fluoride‐based materials are found to show an exceptional anode function with high theoretical specific capacity, based on open‐framework structure enabling Na insertion and also exhibiting improved safety. However, fluoride‐based materials suffer from sluggish kinetics and poor capacity retention essentially due to low electric conductivity. Here, an efficient mixed‐conducting network offering fast pathways is proposed to address these issues. This network relies on titanium fluoride?carbon (TiF₃?C) core/sheath nanofibers that are prepared via electrospinning. Such highly interconnected electrodes exhibit an enhanced and faster sodium storage performance. Carbon sheath nanofibers are key to an efficient ion‐ and electron‐conducting network that enable Na⁺/e^? transfer to reach the nanosized TiF₃. In addition, in‐situ‐converted Ti and NaF particles embedded in the carbon matrix allow high reversible interfacial storage. As a result, the TiF₃?C core/sheath electrode exhibits a high capacity of 161 mAh g^?1 at a high current density of 1000 mA g^?1 over 2000 cycles.     

Ultrafine MoO2‐Carbon Microstructures Enable Ultralong‐Life Power‐Type Sodium Ion Storage by Enhanced Pseudocapacitance

The achievement of the superior rate capability and cycling stability is always the pursuit of sodium‐ion batteries (SIBs). However, it is mainly restricted by the sluggish reaction kinetics and large volume change of SIBs during the discharge/charge process. This study reports a facile and scalable strategy to fabricate hierarchical architectures where TiO₂ nanotube clusters are coated with the composites of ultrafine MoO₂ nanoparticles embedded in carbon matrix (TiO₂@MoO₂‐C), and demonstrates the superior electrochemical performance as the anode material for SIBs. The ultrafine MoO₂ nanoparticles and the unique nanorod structure of TiO₂@MoO₂‐C help to decrease the Na⁺ diffusion length and to accommodate the accompanying volume expansion. The good integration of MoO₂ nanoparticles into carbon matrix and the cable core role of TiO₂ nanotube clusters enable the rapid electron transfer during discharge/charge process. Benefiting from these structure merits, the as‐made TiO₂@MoO₂‐C can deliver an excellent cycling stability up to 10 000 cycles even at a high current density of 10 A g^?1. Additionally, it exhibits superior rate capacities of 110 and 76 mA h g^?1 at high current densities of 10 and 20 A g^?1, respectively, which is mainly attributed to the high capacitance contribution.     

Revealing Pseudocapacitive Mechanisms of Metal Dichalcogenide SnS2/Graphene‐CNT Aerogels for High‐Energy Na Hybrid Capacitors

SnS₂ nanoplatelet electrodes can offer an exceptionally high pseudocapacitance in an organic Na⁺ ion electrolyte system, but their underlying mechanisms are still largely unexplored, hindering the practical applications of pseudocapacitive SnS₂ anodes in Na‐ion batteries (SIBs) and Na hybrid capacitors (SHCs). Herein, SnS₂ nanoplatelets are grown directly on SnO₂/C composites to synthesize SnS₂/graphene‐carbon nanotube aerogel (SnS₂/GCA) by pressurized sulfidation where the original morphology of carbon framework is preserved. The composite electrode possessing a large surface area delivers a remarkable specific capacity of 600.3 mA h g^?1 at 0.2 A g^?1 and 304.8 mA h g^?1 at an ultrahigh current density of 10 A g^?1 in SIBs. SHCs comprising a SnS₂/GCA composite anode and an activated carbon cathode present exceptional energy densities of 108.3 and 26.9 W h kg^?1 at power densities of 130 and 6053 W kg^?1, respectively. The in situ transmission electron microscopy and the density functional theory calculations reveal that the excellent pseudocapacitance originates from the combination of Na adsorption on the surface/Sn edge of SnS₂ nanoplatelets and ultrafast Na⁺ ion intercalation into the SnS₂ layers.     

Frogspawn‐Coral‐Like Hollow Sodium Sulfide Nanostructured Cathode for High‐Rate Performance Sodium–Sulfur Batteries

Room‐temperature (RT) sodium–sulfur (Na–S) batteries are attractive cost‐effective platforms as the next‐generation energy storage systems by using all earth‐abundant resources as electrode materials. However, the slow kinetics of Na–S chemistry makes it hard to achieve high‐rate performance. Herein, a facile and scalable approach has been developed to synthesize hollow sodium sulfide (Na₂S) nanospheres embedded in a highly hierarchical and spongy conductive carbon matrix, forming an intriguing architecture similar to the morphology of frogspawn coral, which has shown great potential as a cathode for high‐rate performance RT Na–S batteries. The shortened Na‐ion diffusion pathway benefits from the hollow structures together with the fast electron transfer from the carbon matrix contributes to high electrochemical reactivity, leading to superior electrochemical performance at various current rates. At high current densities of 1.4 and 2.1 A g^?1, high initial discharge capacities of 980 and 790 mAh g^?1_sulfur can be achieved, respectively, with reversible capacities stabilized at 600 and 400 mAh g^?1_sulfur after 100 cycles. As a proof of concept, a Na‐metal‐free Na–S battery is demonstrated by pairing the hollow Na₂S cathode with tin‐based anode. This work provides guidance on rational materials design towards the success of RT high‐rate Na–S batteries.     

New Binder‐Free Metal Phosphide–Carbon Felt Composite Anodes for Sodium‐Ion Battery

Metal phosphides are promising anode candidates for sodium‐ion batteries (SIBs) due to their high specific capacity and low operating potential but suffer from poor cycling stability caused by huge volume expansion and poor solid‐state ion transfer rate. Herein, a new strategy to grow a new class of mesoporous metal phosphide nanoarrays on carbon felt (CF) as binder‐free anodes for SIBs is reported. The resultant integrated electrodes demonstrate excellent cycling life up to 1000 times (>90% retention rate) and high rate capability of 535 mAh g^?1 at a current density of 4 A g^?1. Detailed characterization reveals that the synergistic effect of unique mesoporous structure for accommodating huge volume expansion during sodiation/desodiation process, ultrasmall primary particle size (≈10 nm) for providing larger electrode/electrolyte contact area and shorter ion diffusion distance, and 3D conductive networks for facilitating the electrochemical reaction, leads to the extraordinary battery performance. Remarkably, a full SIB using the new CoP₄/CF anode and a Na₃V₂(PO₄)₂F₃ cathode delivers an average operating voltage of ≈3.0 V, a reversible capacity of 553 mAh g^?1, and very high energy density of ≈280 Wh kg^?1 for SIBs. A flexible SIB with outstanding mechanical strength based on this binder‐free new anode is also demonstrated.     

Rational Construction of Nitrogen‐Doped Hierarchical Dual‐Carbon for Advanced Potassium‐Ion Hybrid Capacitors

Potassium‐ion hybrid capacitors (PIHCs), elaborately integrate the advantages of high output power as well as long lifespan of supercapacitors and the high energy density of batteries, and exhibit great possibilities for the future generations of energy storage devices. The critical next step for future implementation lies in exploring a high‐rate battery‐type anode with an ultra‐stable structure to match the capacitor‐type cathode. Herein, a “dual‐carbon” is constructed, in which a three‐dimensional nitrogen‐doped microporous carbon polyhedron (NMCP) derived from metal‐organic frameworks is tightly wrapped by two‐dimensional reduced graphene oxide (NMCP@rGO). Benefiting from the synergistic effect of the inner NMCP and outer rGO, the NMCP@rGO exhibits a superior K‐ion storage capability with a high reversible capacity of 386 mAh g^?1 at 0.05 A g^?1 and ultra‐long cycle stability with a capacity of 151.4 mAh g^?1 after 6000 cycles at 5.0 A g^?1. As expected, the as‐assembled PIHCs with a working voltage as high as 4.2 V present a high energy/power density (63.6 Wh kg^?1 at 19 091 W kg^?1) and excellent capacity retention of 84.7% after 12 000 cycles. This rational construction of advanced PIHCs with excellent performance opens a new avenue for further application and development.     

Defect‐Rich Soft Carbon Porous Nanosheets for Fast and High‐Capacity Sodium‐Ion Storage

Soft carbon has attracted tremendous attention as an anode in rocking‐chair batteries owing to its exceptional properties including low‐cost, tunable interlayer distance, and favorable electronic conductivity. However, it fails to exhibit decent performance for sodium‐ion storage owing to difficulties in the formation of sodium intercalation compounds. Here, microporous soft carbon nanosheets are developed via a microwave induced exfoliation strategy from a conventional soft carbon compound obtained by pyrolysis of 3,4,9,10‐perylene tetracarboxylic dianhydride. The micropores and defects at the edges synergistically leads to enhanced kinetics and extra sodium‐ion storage sites, which contribute to the capacity increase from 134 to 232 mAh g^?1 and a superior rate capability of 103 mAh g^?1 at 1000 mA g^?1 for sodium‐ion storage. In addition, the capacitance‐dominated sodium‐ion storage mechanism is identified through the kinetics analysis. The in situ X‐ray diffraction analyses are used to reveal that sodium ions intercalate into graphitic layers for the first time. Furthermore, the as‐prepared nanosheets can also function as an outstanding anode for potassium‐ion storage (reversible capacity of 291 mAh g^?1) and dual‐ion full cell (cell‐level capacity of 61 mAh g^?1 and average working voltage of 4.2 V). These properties represent the potential of soft carbon for achieving high‐energy, high‐rate, and low‐cost energy storage systems.