Resorbable and highly elastic block copolymers from 1,5-dioxepan-2-one and L-lactide with controlled tensile properties and hydrophilicity

New resorbable and elastomeric ABA tri- and multiblock copolymers have been successfully synthesized by combining ring-opening polymerization with ring-opening polycondensation. Five different poly(L-lactide-b-1,5-dioxepan-2-one-b-L-lactide) triblock copolymers and one new poly(L-lactide-b-1,5-dioxepan-2-one) multiblock copolymer have been synthesized. The triblock copolymers were obtained by ring-opening polymerization of 1,5-dioxepan-2-one (DXO) and L-lactide (LLA) with a cyclic tin initiator. The new multiblock copolymer was prepared by ring-opening polycondensation of a low molecular weight triblock copolymer with succinyl chloride. The molecular weight and the composition of the final copolymers were easily controlled by adjusting the monomer feed ratio, and all of the polymers obtained had a narrow molecular weight distribution. It was possible to tailor the hydrophilicity of the materials by changing the DXO content. Copolymers with a high DXO content had a more hydrophilic surface than those with a low DXO content. The receding contact angle varied from 27 to 44 degrees. The tensile properties of the copolymers were controlled by altering the PDXO block length. The tensile testing showed that all the polymers were very elastic and had very high elongations-at-break (epsilon(b)). The copolymers retained very good mechanical properties (epsilon(b) approximately 600-800% and sigma(b) approximately 8-20 MPa) throughout the in vitro degradation study (59 days).     

Effective enhancement of short-chain-length-medium-chain-length polyhydroxyalkanoate copolymer production by coexpression of genetically engineered 3-ketoacyl-acyl-carrier-protein synthase III (fabH) and polyhydroxyalkanoate synthesis genes

Polyhydroxyalkanoates (PHAs) are biodegradable polyesters that have a wide variety of physical properties dependent on the lengths of the pendant groups of the monomer units in the polymer. PHAs composed of mostly short-chain-length (SCL) monomers are often stiff and brittle, whereas PHAs composed of mostly medium-chain-length (MCL) monomers are elastomeric in nature. SCL-MCL PHA copolymers can have properties between the two states, dependent on the ratio of SCL and MCL monomers in the copolymer. It is desirable to elucidate new and low cost ways to produce PHA composed of mostly SCL monomer units with a small mol % of MCL monomers from renewable resources, since this type of SCL-MCL PHA copolymer has superior qualities compared to SCL homopolymer. To address this issue, we have created strains of recombinant E. coli capable of producing beta-ketothiolase (PhbA) and acetoacetyl-CoA synthase (PhbB) from Ralstonia eutropha, genetically engineered 3-ketoacyl-ACP synthase III (FabH) from Escherichia coli, and genetically engineered PHA synthases (PhaC) from Pseudomonas sp. 61-3 to enhance the production of SCL-MCL PHA copolymers from glucose. The cumulative effect of having two monomer-supplying pathways and genetically engineered PHA synthases resulted in higher accumulated amounts of SCL-MCL PHA copolymer from glucose. Polymers were isolated from two recombinant E. coli strains, the first harboring the phbAB, fabH(F87T), and phaC1(SCQM) genes and the second harboring the phbAB, fabH(F87W), and phaC1(SCQM) genes. The thermal and physical properties of the isolated polymers were characterized. It was found that even a very low mol % of MCL monomer in a SCL-MCL PHA copolymer had dramatic effects on the thermal properties of the copolymers.     

Genetic network driven control of PHBV copolymer composition

We developed a detailed mathematical model describing the coupling between the molecular weight distribution dynamics of poly(3-hydroxybutyrate-co-3hydroxyvalerate) (PHBV) copolymer chains with those of hydroxybutyrate (HB) and hydroxyvalerate (HV) monomer formation. Sensitivity analysis of the model revealed that both the monomer composition and the molecular weight distribution of the copolymer chains are strongly affected by the ratio between the rates at which the two-monomer units are incorporated into the chains. This ratio depends on the relative HB and HV availability, which in turn is a function of the expression levels of genes encoding enzymes that catalyze monomer formation. Regulation of gene expression was accomplished through the aid of an artificial genetic network, the patterns of expression of which can be controlled by appropriately tuning the concentration of an extracellular inducer. Extensive simulations were used to study the effects of operating conditions and parameter uncertainties on the range of achievable copolymer compositions. Since the predicted conditions fell in the range of feasible bioprocessing manipulations, it is expected that such strategy could be successfully employed. Thus, the presented model constitutes a powerful tool for designing genetic networks that can drive the formation of PHBV copolymer structures with desirable characteristics.     

Accumulation of a poly(hydroxyalkanoate) copolymer containing primarily 3-hydroxyvalerate from simple carbohydrate substrates by Rhodococcus sp. NCIMB 40126

A number of taxonomically-related bacteria have been identified which accumulate poly(hydroxyalkanoate) (PHA) copolymers containing primarily 3-hydroxyvalerate (3HV) monomer units from a range of unrelated single carbon sources. One of these, Rhodococcus sp. NCIMB 40126, was further investigated and shown to produce a copolymer containing 75 mol% 3HV and 25 mol% 3-hydroxybutyrate (3HB) from glucose as sole carbon source. Polyesters containing both 3HV and 3HB monomer units, together with 4-hydroxybutyrate (4HB), 5-hydroxyvalerate (5HV) or 3-hydroxyhexanoate (3HHx), were also produced by this organism from certain accumulation substrates. With valeric acid as substrate, almost pure (99 mol% 3HV) poly(3-hydroxyvalerate) was produced. N.m.r. analysis confirmed the composition of these polyesters. The thermal properties and molecular weight of the copolymer produced from glucose were comparable to those of PHB produced by Alcaligenes eutrophus.     

Biodegradable films of partly branched poly(l-lactide)-co-poly(epsilon-caprolactone) copolymer: modulation of phase morphology, plasticization properties and thermal depolymerization

We report on the modulation of phase morphology, plasticization properties, and thermal stability of films of partly branched poly(l-lactide)-co-poly(epsilon-caprolactone) copolymer (PLLA-co-PCL) with additions of low molecular weight compounds, namely, triethyl citrate ester, diethyl phthalate, diepoxy polyether (poly(propylene glycol) diglycidyl ether), and with epoxidized soybean oil (ESO). The PLLA-co-PCL/polyether films showed significant stability against thermal depolymerization, high film flexibility, and good plasticizing properties, probably due to cross-linking and chain branching formation between diepoxy groups with both the end carboxyl and hydroxyl groups of the PLLA copolymer (initially present or generated during the degradation process) to produce primary ester and ether bonds, respectively. Diethyl phthalate and triethyl citrate ester were found to be efficient plasticizers for PLLA copolymer in terms of glass transition and mechanical properties, but the more water-soluble plasticizer triethyl citrate induced a dramatic loss in the molecular weight of the copolymer. Although ESO cannot play the role of a plasticizer, it substantially stabilizes and retards thermal depolymerization of the PLLA copolymer matrix, possibly because of a reaction between epoxy groups with the end carboxyl and hydroxyl groups of the PLLA copolymer. The presence of ESO in PLLA-co-PCL/ESO/triethyl citrate blends enhanced the compatibility and miscibility of the plasticizer with the PLLA copolymer matrix, considerably improved the mechanical properties (elongation at break), and substantially stabilized the copolymer against thermal depolymerization. It seems likely that the epoxy groups interact not only with the end hydroxyl and carboxyl group of the copolymer but as well with the hydroxyl group of triethyl citrate plasticizer to produce a new ether bond (C-O-C) as the cross-linking unit. On the other hand, for PLLA-co-PCL/ESO/polyether blends, (80/10/10) epoxidized oil distorts the compactness of the blend by diminishing the proposed entanglements between carboxyl, hydroxyl, and diepoxy groups of polyether and reduces the high elongation properties otherwise observed in the PLLA-co-PCL/polyether films. The multicomponent approach toward modulating poly(l-lactide)-co-poly(epsilon-caprolactone) copolymer films using epoxy compounds and plasticizers and the insight into the nature of various PLLA matrixes presented here offer advantages to a broad engineering of PLLA copolymer films having desirable physical properties and multiphase behavior for efficient uses in future technical applications.     

Design and synthesis of self-degradable antibacterial polymers by simultaneous chain- and step-growth radical copolymerization

Self-degradable antimicrobial copolymers bearing cationic side chains and main-chain ester linkages were synthesized using the simultaneous chain- and step-growth radical polymerization of t-butyl acrylate and 3-butenyl 2-chloropropionate, followed by the transformation of t-butyl groups into primary ammonium salts. We prepared a series of copolymers with different structural features in terms of molecular weight, monomer composition, amine functionality, and side chain structures to examine the effect of polymer properties on their antimicrobial and hemolytic activities. The acrylate copolymers containing primary amine side chains displayed moderate antimicrobial activity against E. coli but were relatively hemolytic. The acrylate copolymer with quaternary ammonium groups and the acrylamide copolymers showed low or no antimicrobial and hemolytic activities. An acrylate copolymer with primary amine side chains degraded to lower molecular weight oligomers with lower antimicrobial activity in aqueous solution. This degradation was due to amidation of the ester groups of the polymer chains by the nucleophilic addition of primary amine groups in the side chains resulting in cleavage of the polymer main chain. The degradation mechanism was studied in detail by model reactions between amine compounds and precursor copolymers.     

Synthesis and characterization of a photo-cross-linked biodegradable elastomer

The synthesis and characterization of a photocurable biodegradable elastomer as a potential biomaterial for the delivery of thermosensitive drugs are described. The elastomer was prepared from UV initiated cross-linking of an acrylated star-poly(epsilon-caprolactone-co-D,L-lactide) prepolymer. The influence of the molecular weight of the acrylated prepolymer on the final elastomer mechanical and thermal properties was determined. The glass-transition temperature of the elastomers was independent of the prepolymer molecular weight and was from -6 to -8 degrees C. The Young's modulus and stress at break of the elastomers was proportional to the inverse of the prepolymer molecular weight, while the strain at break increased in a linear fashion with the prepolymer molecular weight. Over a degradation period of 12 weeks in phosphate buffered saline, the elastomers exhibited little mass loss, appreciable mechanical strength loss, and little dimensional or strain at break change.     

Synthesis and characterization of six-arm star poly(delta-valerolactone)-block-methoxy poly(ethylene glycol) copolymers

Novel amphiphilic six-arm star diblock copolymers based on biocompatible and biodegradable poly(delta-valerolactone) (PVL) and methoxy poly(ethylene glycol) (MePEG) were synthesized by a two-step process. First, the hydrophobic star-shaped PVL with hydroxyl terminated functional groups was synthesized using a multifunctional alcohol, dipentaerythritol (DPE), as the initiator and fumaric acid as the catalyst. The amphiphilic six-arm star copolymer of poly(delta-valerolactone)-b-methoxy poly(ethylene glycol), (PVL-b-MePEG)(6), was then synthesized by coupling the hydroxyl terminated six-arm PVL homopolymer with alpha-methoxy-omega-chloroformate-poly(ethylene glycol) (MePEG-COCl). (1)H NMR and GPC analyses confirmed the successful synthesis of star-shaped copolymers with predicted compositions and narrow molecular weight distributions. DSC analysis revealed that the glass transition temperatures of the star PVL homopolymers with M(n) between 5000 and 49 000 are not dependent on their molecular weights, whereas the melting temperatures of both the PVL homopolymers and the amphiphilic (PVL-b-MePEG)(6) copolymers increase with an increase in the PVL molecular weight. Micelles were prepared from the (PVL-b-MePEG)(6) copolymers via the dialysis method and found to have effective mean diameters ranging from 10 to 45 nm, depending on the copolymer composition. In addition, the (PVL-b-MePEG)(6) copolymers having lower PVL content were found to form micelles with a narrow monomodal size distribution, whereas the copolymers having higher PVL content tended to form aggregates with a bimodal size distribution. The noncytotoxicity of the copolymers was also confirmed in CHO-K1 fibroblast cells using a cell viability assay, indicating that the (PVL-b-MePEG)(6) copolymers are suitable for biomedical applications such as drug delivery.     

Physical properties of poly(hydroxybutyrate) and copolymers of hydroxybutyrate and hydroxyvalerate

Abstract The major physical properties of poly(hydroxybutyrate) (PHB) and its copolymers with hydroxyvalerate (PHB/HV) and those of their blends are summarised. Cases of liquid-liquid phase separation in homopolymer copolymer blends are reported and conditions where further phase separation occurs during crystallisation are documented. The crystallinity and degree of comonomer inclusion in the crystallisation of copolymers are described and quantified. It is argued that the mechanism for the inclusion of comonomer units in the crystals is of a kinetic rather than an equilibrium nature.     

Synthesis of copolymers containing an active ester of methacrylic acid by RAFT: controlled molecular weight scaffolds for biofunctionalization

We report the controlled radical copolymerization of N-(2-hydroxypropyl)methacrylamide (HPMA) with a monomer containing an active ester, N-methacryloyloxysuccinimide (NMS), by reversible addition fragmentation chain transfer (RAFT). The large difference in the reactivity ratios of HPMA and NMS resulted in significant variations in copolymer composition with increasing conversion during batch copolymerization. The use of a semi-batch copolymerization method, involving the gradual addition of the more reactive NMS, allowed uniformity of copolymer composition to be maintained during the polymerization. We synthesized polymers in a wide range of molecular weights (M(n) = 3000-50,000 Da) with low polydispersities (1.1-1.3). The effect of the ratio of monomer to chain transfer agent (CTA) on the molecular weight of the polymer was investigated. Given the numerous applications of poly(HPMA)-based conjugates in designing polymeric therapeutics, these controlled molecular weight activated polymers represent attractive scaffolds for biofunctionalization. As a demonstration, we attached a peptide to the activated polymer backbone to synthesize a potent controlled molecular weight polyvalent inhibitor of anthrax toxin.     

Substrate Resistance to Traction Forces Controls Fibroblast Polarization

The mechanics of fibronectin-rich extracellular matrix regulate cell physiology in a number of diseases, prompting efforts to elucidate cell mechanosensing mechanisms at the molecular and cellular scale. Here, the use of fibronectin-functionalized silicone elastomers that exhibit considerable frequency dependence in viscoelastic properties unveiled the presence of two cellular processes that respond discreetly to substrate mechanical properties. Weakly cross-linked elastomers supported efficient focal adhesion maturation and fibroblast spreading because of an apparent stiff surface layer. However, they did not enable cytoskeletal and fibroblast polarization; elastomers with high cross-linking and low deformability were required for polarization. Our results suggest as an underlying reason for this behavior the inability of soft elastomer substrates to resist traction forces rather than a lack of sufficient traction force generation. Accordingly, mild inhibition of actomyosin contractility rescued fibroblast polarization even on the softer elastomers. Our findings demonstrate differential dependence of substrate physical properties on distinct mechanosensitive processes and provide a premise to reconcile previously proposed local and global models of cell mechanosensing.     

DNA binding proteins from Tetrahymena thermophila

We have used DNA-cellulose chromatography to isolate single-strand binding proteins from Tetrahymena thermophila. Three major proteins which bind to denatured DNA-cellulose were obtained. The predominant protein has a molecular weight of 20 000 in sodium dodecyl sulfate - polyacrylamide gel electrophoresis and possesses many of the properties of the helix destabilizing proteins isolated from prokaryotic and eukaryotic sources. The protein facilitates denaturation of the synthetic copolymer poly[d(A-T).d(A-T)], depressing the melting temperature by nearly 40 degrees C. It also permits the renaturation of poly[d(A-T)].d(A-T)] in high salt concentration. Two other binding proteins have molecular weight of 25 000 and 23 000 in sodium dodecyl sulfate - polyacrylamide gel electrophoresis. The protein with a molecular weight of 25 000 is probably the "M protein" previously isolated from Tetrahymena thermophila which has been shown to stimulate Tetrahymena DNA polymerase. These two proteins failed to show helix destabilizing, DNA dependent ATPase, or deoxyribonuclease activities. These three proteins are abundant in the cell with approximately 1.0 x 10(6) to 10.0 x 10(6) molecules of each protein monomer per cell. One molecule of each protein monomer binds to 7 to 10 nucleotides as detected by a nitrocellulose filter binding assay. Peptide mapping of the three proteins suggests that they are all distinct. We have also found that the binding proteins can interact with Tetrahymena DNA polymerase and some other proteins to form an enzyme complex, a putative replication complex.     

Synthesis, swelling behavior, and biocompatibility of novel physically cross-linked polyurethane-block-poly(glycerol methacrylate) hydrogels

Physically cross-linked novel block copolymer hydrogels with tunable hydrophilic properties for biomedical applications were synthesized by controlled radical polymerization of polyurethane macroiniferter and (2,2-dimethyl-1,3-dioxolane) methyl methacrylate. The block copolymers were converted to hydrogels by the selective hydrolysis of poly[(2,2-dimethyl-1,3-dioxolane) methyl methacrylate] block to poly(glycerol methacrylate). The block copolymerization has been monitored by monomer conversion and molecular weight increase as a function of time. It was observed that the polymerization proceeded with a characteristic "living" behavior where both monomer conversion and molecular weight increased linearly, with increasing reaction time. The resulting hydrogels were investigated for their equilibrium water content (EWC), dynamic water contact angles, swelling kinetics, thermodynamic interaction parameters, plasma protein adsorption, and platelet adhesion. Similar to our previous mechanically responsive hydrogels (Mequanint, K.; Sheardown, H. J. Biomater. Sci. Polym. Ed. 2005, 10, 1303-1318), the present results indicated that block copolymer hydrogels have excellent hydrophilicity and swelling behavior with improved modulus of elasticity. The equilibrium swelling was affected by the hydrolysis time, block length of poly(glycerol methacrylate), temperature, and the presence of soluble salts. Fibrinogen adsorption and platelet adhesion were significantly lower for the hydrogels than for the control polyurethane, whereas albumin adsorption increased for the hydrogels in proportion to the contents of poly(glycerol methacrylate). These hydrogels have potential in a number of biomedical applications such as drug delivery and scaffolds for tissue engineering.     

UV-induced graft copolymerization of monoacrylate-poly(ethylene glycol) onto poly(3-hydroxyoctanoate) to reduce protein adsorption and platelet adhesion

Homogeneous solutions of poly(3-hydroxyoctanoate) (PHO) and the monoacrylate-poly(ethylene glycol) (PEGMA) monomer in chloroform were irradiated with UV light to obtain PEGMA-grafted PHO (PEGMA-g-PHO) copolymers. Variables affecting the degree of grafting (DG), such as the time of UV irradiation and the concentrations of the PEGMA monomer and initiator, were investigated. The PEGMA-g-PHO copolymers were characterized by measuring the water contact angle, molecular weight, thermal transition temperatures and mechanical properties, as well as by nuclear magnetic resonance spectroscopy. The results from all of these measurements indicate that PEGMA groups were present on the PHO polymer. The protein adsorption and platelet adhesion on the PEGMA-g-PHO surfaces were examined using poly(L-lactide) (PLLA) surfaces as the control. The proteins and platelets had a significantly lower tendency to adhere to the PEGMA-g-PHO copolymers than to PLLA. The graft copolymer with a high DG of PEGMA was very effective in reducing the protein adsorption and platelet adhesion and did not activate the platelets. The results obtained in this study suggest that PEGMA-g-PHO copolymers have the potential to be used as blood-contacting devices in a broad range of biomedical applications.     

Synthesis and characterization of triblock copolymers of methoxy poly(ethylene glycol) and poly(propylene fumarate)

Amphiphilic block copolymers were synthesized by transesterification of hydrophilic methoxy poly(ethylene glycol) (mPEG) and hydrophobic poly(propylene fumarate) (PPF) and characterized. Four block copolymers were synthesized with a 2:1 mPEG:PPF molar ratio and mPEGs of molecular weights 570, 800, 1960, and 5190 and PPF of molecular weight 1570 as determined by NMR. The copolymers synthesized with mPEG of molecular weights 570 and 800 had 1.9 and 1.8 mPEG blocks per copolymer, respectively, as measured by NMR, representing an ABA-type block copolymer. The number of mPEG blocks of the copolymer decreased with increasing mPEG block length to as low as 1.5 mPEG blocks for copolymer synthesized with mPEG of molecular weight 5190. At a concentration range of 5-25 wt % in phosphate-buffered saline, copolymers synthesized with mPEG molecular weights of 570 and 800 possessed lower critical solution temperatures (LCST) between 40 and 45 degrees C and between 55 and 60 degrees C, respectively. Aqueous solutions of copolymer synthesized with mPEG 570 and 800 also experienced thermoreversible gelation. The sol-gel transition temperature was dependent on the sodium chloride concentration as well as the mPEG block length. The copolymer synthesized from mPEG 570 had a transition temperature between 40 and 20 degrees C with salt concentrations between 1 and 10 wt %, while the sol-gel transition temperatures of the copolymer synthesized from mPEG molecular weight 800 were higher in the range 75-30 degrees C with salt concentrations between 1 and 15 wt %. These novel thermoreversible copolymers are the first biodegradable copolymers with unsaturated double bonds along their macromolecular chain that can undergo both physical and chemical gelation and hold great promise for drug delivery and tissue engineering applications.     

Protein-based block copolymers

Advances in genetic engineering have led to the synthesis of protein-based block copolymers with control of chemistry and molecular weight, resulting in unique physical and biological properties. The benefits from incorporating peptide blocks into copolymer designs arise from the fundamental properties of proteins to adopt ordered conformations and to undergo self-assembly, providing control over structure formation at various length scales when compared to conventional block copolymers. This review covers the synthesis, structure, assembly, properties, and applications of protein-based block copolymers.     

Synthesis and flocculation property in dye solutions of β-cyclodextrin-acrylic acid-[2-(Acryloyloxy)ethyl] trimethyl ammonium chloride copolymer

In aqueous solution a cationic copolymer, poly (β-CD-AA-DMC) was synthesized via free radical copolymerization of acrylic acid (AA) esterified β-CD (β-CD-AA), and a cationic monomer [2-(Acryloyloxy)ethyl] trimethyl ammonium chloride (DMC). The copolymer's structure, morphology and thermal stability were demonstrated by FT-IR, ¹H NMR, SEM and TGA analysis. The flocculation properties of the copolymer were evaluated by the decolorization solutions of two reactive dyes using a jar test method. The decolorization efficiency is influenced by both the nature of the anionic dyes and the pH of the initial dye solution. Electrostatic adsorption played a more important role in flocculation of dyes than bridging of the polymer. Moreover, the inorganic salt decreased the efficiency of color removal.     

Polymeric gadolinium chelate magnetic resonance imaging contrast agents: design, synthesis, and properties.

We have synthesized and evaluated five series of polymeric gadolinium chelates which are of interest as potential MRI blood pool contrast agents. The polymers were designed so that important physical properties including molecular weight, relaxivity, metal content, viscosity, and chelate stability could be varied. We have shown that, by selecting polymers of the appropriate MW, extended blood pool retention can be achieved. In addition, relaxivity can be manipulated by changing the polymer rigidity, metal content affected by monomer selection, viscosity by polymer shape, and chelate stability by chelator selection.     

Graft copolymers of starch and its application in textiles

The graft copolymerization of styrene (ST), methyl methacrylate (MMA)/butyl acrylate (BA) with starch was carried chemically using ferrous ion-peroxide redox system. The grafting was performed at 60 °C and the monomer ratios of ST/MMA and ST/BA was varied with their % composition as 80/20, 50/50 and 20/80 parts by weight. The effect of initiator concentration, starch concentration and the monomer ratio on the grafting efficiency was studied. The grafted starch granules (GSG) were further analyzed for their particle size, bulk density and by sizing on cotton yarn for its physico-mechanical properties such as tensile strength, elongation at break, etc. The rheological properties of the resulting granular product in water as well as the starch graft copolymer emulsion were studied.     

Star structure of antibody-targeted HPMA copolymer-bound doxorubicin: a novel type of polymeric conjugate for targeted drug delivery with potent antitumor effect

The aim of this study was to compare the properties and antitumor potential of a novel type of antibody-targeted N-(2-hydroxypropyl)methacrylamide (HPMA) copolymer-bound doxorubicin conjugates with star structure with those of previously described classic antibody-targeted or lectin-targeted HPMA copolymer-bound doxorubicin conjugates. Classic antibody-targeted conjugates were prepared by aminolytic reaction of the multivalent HPMA copolymer containing side-chains ending in 4-nitrophenyl ester (ONp) reactive groups with primary NH(2) groups of the antibodies. The star structure of antibody-targeted conjugates was prepared using semitelechelic HPMA copolymer chains containing only one reactive N-hydroxysuccinimide group at the end of the backbone chain. In both types of conjugates, B1 monoclonal antibody (mAb) was used as a targeting moiety. B1 mAb recognizes the idiotype of surface IgM on BCL1 cells. The star structure of the targeted conjugate had a narrower molecular mass distribution than the classic structure. The peak in the star structure was around 300-350 kDa, while the classic structure conjugate had a peak around 1300 kDa. Doxorubicin was bound to the HPMA copolymer via Gly-Phe(D,L)-Leu-Gly spacer to ensure the controlled intracellular delivery. The release of doxorubicin from polymer conjugates incubated in the presence of cathepsin B was almost twice faster from the star structure of targeted conjugate than from the classic one. The star structure of the targeted conjugate showed a lower binding activity to BCL1 cells in vitro, but the cytostatic activity measured by [(3)H]thymidine incorporation was three times higher than that seen with the classic conjugate. Cytostatic activity of nontargeted and anti-Thy 1.2 mAb (irrelevant mAb) modified HPMA copolymer-bound doxorubicin was more than hundred times lower as compared to the star structure of B1 mAb targeted conjugate. In vivo, both types of conjugates targeted with B1 mAb bound to BCL1 cells in the spleen with approximately the same intensity. The classic structure of the targeted conjugate bound to BCL1 cells in the blood with a slightly higher intensity than the star structure. Both types of targeted conjugates had a much stronger antitumor effect than nontargeted HPMA copolymer-bound doxorubicin and free doxorubicin. The star structure of targeted conjugate had a remarkably higher antitumor effect than the classic structure: a single intravenous dose of 100 microg of doxorubicin given on day 11 completely cured five out of nine experimental animals whereas the classic structure of targeted conjugate given in the same schedule only prolonged the survival of experimental mice to 138% of control mice. These results show that the star structure of antibody-targeted HPMA copolymer-bound doxorubicin is a suitable conjugate for targeted drug delivery with better characterization, higher cytostatic activity in vitro, and stronger antitumor potential in vivo than classic conjugates.