Preparation and characterization of cellulose/chitosan blend films

Cellulose and chitosan were mixed in N-methylmorpholine-N-oxide (NMMO) and heated to 100 °C, and then were processed under a pressure of 70 kg/cm² exerted by a compression molding machine at 100 °C for 8 min. As a result, transparent orange viscose films were obtained. After rinsing with deionized water and drying transparent yellowish blend films were obtained. Scanning electron microscope (SEM) indicated that when the chitosan content in the blend increased up to 3% the surface structure became smoother, but the film containing 5% (w/w) chitosan, became coarse again probably due to phase separation. Tensile strength test results were consistant with this. Antibacterial assessment proved that addition of chitosan to the films results in slight antibacterial properties. The halo zone test confirmed that the blend films made in this research have non-diffusible antibacterial properties.     

Preparation and characterization of surface crosslinked TPS/PVA blend films

Surface crosslinked thermoplastic starch (TPS)/PVA blend films were prepared by applying ultra violet (UV) irradiation. Sodium benzoate was used as photosensitizer and induced onto film surface layer by soaking the TPS/PVA films in the photosensitizer aqueous solution. The effects of concentration of photosensitizer aqueous solution, soaking time and UV irradiation dose on the surface photocrosslinking reaction were investigated. Physical properties, such as water contact angle, moisture absorption, swelling degree and solubility in water as well as mechanical properties of the films were measured to characterize the influence of the surface photocrosslinking modification. The obtained results showed that the surface modification considerably reduced the surface hydrophilic character of the TPS/PVA films, enhanced the film’s water resistance and also increased tensile strength and Young’s modulus but decreased elongation at break of the films.     

Preparation and properties of alginate/carboxymethyl chitosan blend fibers

Alginate/carboxymethyl chitosan blend fibers, prepared by spinning their mixture solution through a viscose-type spinneret into a coagulating bath containing aqueous CaCl₂, were studied for structure and properties with the aid of infrared spectroscopy (IR), X-ray diffraction (XRD) and scanning electron micrography (SEM). The analyses indicated a good miscibility between alginate and carboxymethyl chitosan, because of the strong interaction from the intermolecular hydrogen bonds. The best values of the dry tensile strength and breaking elongation were obtained when carboxymethyl chitosan content was 30 and 10 wt%, respectively. The wet tensile strength and breaking elongation decreased with the increase of carboxymethyl chitosan content. Introduction of CM-chitosan in the blend fiber improved water-retention properties of blend fiber compared to pure alginate fiber. Antibacterial fibers, obtained by treating the fibres with aqueous solution of N-(2-hydroxy)-propyl-3-trimethylammonium chitosan chloride and silver nitrate, respectively, exhibited good antibacterial activity to Staphylococcus aureus.     

Preparation and characterization of biodegradable poly-3-hydroxybutyrate-starch blend films

Bacterial polyesters have attracted much attention as biodegradable biocompatible polymers. Poly-3-hydroxybutyrate, a microbially produced thermoplastic, has similar material properties to polypropylene. Its potential application as biodegradable and biocompatible plastics is well documented. However, due to high cost it is used mainly in biomaterials for medical applications. Materials with useful properties may result from blending bacterial polyhydroxybutyrate (PHB) with other polymers. In this paper, the compatibility of PHB with starch for improved properties and cost reduction is discussed. The thermal and mechanical properties of the blended films were studied by means of thermogravimetry, differential scanning calorimetry and an automated material testing system. The results revealed that blend films had a single glass transition temperature for all the proportions of PHB:starch tested. The nature of all combinations was found to be crystalline. The tensile strength was optimum for the PHB:starch ratio of 0.7:0.3 (wt/wt). The variation in tensile strength, Young's modulus, extension needed to break, thermal stability, glass transition temperature, melting temperature, for the different proportions of PHB:starch are discussed.     

Preparation and characterization of konjac glucomannan/poly(diallydimethylammonium chloride) antibacterial blend films

A novel antibacterial film was prepared by blending konjac glucomannan (KGM) and poly(diallydimethylammonium chloride) (PDADMAC) in an aqueous system. The antibacterial activity of the films against Staphylococcus aureus, Bacillus subtilis, Escherichia coli, Pseudomonas aeruginosa, and Saccharomyces were measured by the halo zone test and the double plate method. The films exhibited an excellent antibacterial activity against B. subtilis and S. aureus but not against E. coli, P. aeruginosa or Saccharomyces. The miscibility, morphology, thermal stability, water vapour permeability and mechanical properties of the blend films were investigated by density determination, SEM, ATR-IR, XRD, DSC, TGA, WVA and tensile tests. The results of density determination predicted that the blends of KGM and PDADMAC were miscible when the PDADMAC content was less than 70 wt%. Moreover, SEM and XRD confirmed the result. ATR-IR showed that strong intermolecular hydrogen bonds and electrostatic interactions occurred between KGM and PDADMAC in the blends. The tensile strength and the break elongation of the blends were improved largely to 106.5 MPa and 32.04% and the water vapour permeability decreased when the PDADMAC content was 20 wt%. The thermal stability of the blends was higher than pure KGM. The blends should be good antibacterial materials.     

Biomimetic nanofibrous scaffolds: preparation and characterization of PGA/chitin blend nanofibers

Electrospinning of poly(glycolic acid) (PGA)/chitin blend solutions in 1,1,1,3,3,3-hexafluoro-2-propanol was investigated to fabricate biodegradable and biomimetic nanostructured scaffolds for tissue engineering. The morphology of the electrospun PGA/chitin blend nanofibers was investigated with a field emission scanning electron microscope. The PGA/chitin blend fibers have average diameters of around 140 nm, and their diameters have a distribution in the range 50-350 nm. The miscibility of PGA/chitin blend fibers was examined by differential scanning calorimetry. The PGA and chitin were immiscible in the as-spun nanofibrous structure. An in vitro degradation study of PGA/chitin blend nanofibers was conducted in phosphate-buffered saline, pH 7.2. It was found that the hydrolytic cleavage of PGA in the blend nanofibers was accelerated by the coexistence of hydrophilic chitin. To assay the cytocompatability and cell behavior on the PGA/chitin blend nanofibrous scaffolds, cell attachment and spreading of normal human epidermal fibroblasts seeded on the scaffolds were studied. Our results indicate that the PGA/chitin blend nanofibrous matrix, particularly the one that contained 25% PGA and 75% chitin with bovine serum albumin coating, could be a good candidate for tissue engineering scaffolds, because it has an excellent cell attachment and spreading for normal human fibroblasts.     

Preparation and characterization of polyaniline/chitosan blend film

Films consisting of a blend of a chitosan hydrogel and a conductive polymer, polyaniline (PANI), were prepared and characterized for their electrical and mechanical properties. Polyaniline in emeraldine base (EB) form was dispersed in chitosan solution and blend films were obtained by solution casting. The PANI particles in the blend films were then doped with HCl where we observed reductions in the film tensile strength and Young's modulus by about 30%, but the films electrical conductivity increased by 6 orders of magnitude. The highest electrical conductivity of the blend films was of the order 10⁻⁴ S/cm. The electrical and mechanical properties of the films varied with polyaniline content, acid dopant type, acid dopant concentration, and doping time.     

Biomimetic nanofibrous scaffolds: preparation and characterization of chitin/silk fibroin blend nanofibers

Electrospinning of chitin/silk fibroin (SF) blend solutions in 1,1,1,3,3,3-hexafluoro-2-propanol (HFIP) was investigated to fabricate a biomimetic nanostructured scaffolds for tissue engineering. The morphology of the electrospun chitin/SF blend nanofibers was investigated with a field emission scanning electron microscope (FE-SEM). The average diameters of chitin/SF blend fibers decreased from 920 to 340 nm, with the increase of chitin content in blend compositions. The miscibility of chitin/SF blend fibers was examined by solution viscosity measurement. The chitin and SF were immiscible in the as-spun nanofibrous structure. The dimensional stability of chitin/SF blend nanofibers, with or without water vapor after-treatment, was conducted by immersing in water. As-spun SF-rich blend nanofibrous matrices were lost their fibrous structure after the water immersion for 24 h, and then changed into membrane-like structure. On the contrary, nanofibrous structures of water vapor-treated SF-rich blends were almost maintained. To assay the cytocompatibility and cell behavior on the chitin/SF blend nanofibrous scaffolds, cell attachment and spreading of normal human epidermal keratinocyte and fibroblasts seeded on the scaffolds were studied. Our results indicate that chitin/SF blend nanofibrous matrix, particularly the one that contained 75% chitin and 25% SF, could be a potential candidate for tissue engineering scaffolds because it has both biomimetic three-dimensional structure and an excellent cell attachment and spreading for NHEK and NHEF.     

Preparation, characterization and properties of aminoethyl chitin hydrogels

Aminoethyl chitins (AEC) with different amino contents were synthesized from chitin and 2-chlorethylamine hydrochloride, and the AEC hydrogels were prepared by crosslinking with glutaraldehyde. The microstructures, swelling behaviors and antibacterial activities of the hydrogels were investigated. The results of Fourier transform infrared spectroscopy (FTIR), (1)H nuclear magnetic resonance ((1)H NMR) spectrum and scanning electron microscopy (SEM) showed that the hydrogels were prepared by forming the Schiff base from AEC and glutaraldehyde. The aminoethyl chitin hydrogels were sensitive to acidic environment. The swelling ratio changed with the amino content of AEC, declined with the increase of the crosslinking agent concentration and increased with the increase of the AEC concentration. In addition, the antibacterial results of the hydrogels against Staphylococcus aureus (S. aureus) indicated that the hydrogels had good antibacterial activities, and the antibacterial properties were affected by the amino content of AEC and the crosslinking agent concentration.     

Structural characterization and properties of starch/konjac glucomannan blend films

In this work, a series of glycerol-plasticized pea starch/konjac glucomannan (ST/KGM) blend films was prepared by a casting and solvent evaporation method. The structure, thermal behavior, and mechanical properties of the films were investigated by means of Fourier Transform Infrared Spectroscopy, wide-angle X-ray diffraction, scanning electron microscopy, differential scanning calorimetry, and tensile testing. The results indicated that strong hydrogen bonding formed between macromolecules of starch (ST) and konjac glucomannan (KGM), resulting in a good miscibility between ST and KGM in the blends. Compared with the neat ST, the tensile strength of the blend films were enhanced significantly from 7.4 to 68.1 MPa with an increase of KGM content from 0 to 70 wt%. The value of elongation at break of the blend films was higher than that of ST and reached a maximum value of 59.0% when the KGM content was 70 wt% and 20% of glycerol as plasticizer. The incorporation of KGM into the ST matrix also led to an increase of moisture uptake for the ST-based materials. The structure and properties of pea starch-based films were modified and improved by blending with KGM.     

Preparation and characterization of water-soluble chitin phosphate

New water-soluble chitin derivatives, chitin phosphate of various degrees of substitution, were successfully prepared by the reaction of chitin with phosphorus pentoxide in methanesulphonic acid. These materials behaved hydrodynamically as typical polyelectrolyte, and showed high ability to adsorb metal ions.     

Preparation of chitin/cellulose composite gels and films with ionic liquids

In this study, we performed preparation and characterizations of the chitin/cellulose composite gels and films using the two ionic liquids, 1-allyl-3-methylimidazolium bromide and 1-butyl-3-methylimidazolium chloride. First, chitin and cellulose were dissolved in each appropriate ionic liquid. Then, the two liquids were mixed in the desired ratios at 100 °C to give the homogeneous mixtures. The gels were obtained by standing the mixtures for 4 days. On the other hand, the films were obtained by casting the mixtures on glass plates, followed by soaking in water and drying. The obtained gels and films were characterized by XRD and TGA measurements. The mechanical properties of the gels and films were evaluated under compressive and tensile modes, respectively.     

Preparation and characterization of ultra violet (UV) radiation cured bio-degradable films of sago starch/PVA blend

Polymer films of sago starch/polyvinyl alcohol (PVA) were prepared by casting and cured under ultra violet (UV) radiation. Different blends were made varying the concentration of sago starch and PVA. Tensile strength (TS) and elongation at break (Eb) of the prepared films were studied. Films made up of sago starch and PVA with a ratio of 1:2 showed the highest TS and Eb. The physico-mechanical properties of prepared films were improved by grafting with acrylic monomers with the aid of UV radiation. A series of formulations was prepared with two monomers 2-ethyl 2-hydroxymethyl 1,3 methacrylate (EHMPTMA) and 2-ethylhexylacrylate (EHA) and a photoinitiator. Monomer concentration, soaking time and radiation dose were optimized in terms of grafting and mechanical properties. The highest TS was at 50% EHMPTMA and 48% EHA and 2% photo initiator at 5 min soaking time and recorded value was 6.58 MPa. The prepared films were further characterized with NMR spectroscopy and scanning electron microscope (SEM).     

Properties of pullulan-based blend films as affected by alginate content and relative humidity

Pullulan-sodium alginate blend films were prepared and characterized as a function of water activity (a_w). At low a_w, the incorporation of alginate into pullulan film increased the tensile strength and elastic modulus, but decreased the elongation at break of the composite films; the opposite trends were observed at elevated a_w. Above 0.43 a_w, water exerted a typical plasticization effect upon the biopolymer blends. As a_w increased from 0.23 to 0.43, an anti-plasticization effect was observed as tensile strength and elastic modulus increased. The glass transition temperature of all samples decreased substantially as aw increased from 0.23 to 0.84 due to the plasticization effect of water. Within this a_w range, one transition temperature was observed for all film specimens. The stretching vibration band of O-H was investigated using attenuated total reflection Fourier transform infrared spectroscopy to identify the various species of water interacting with the polysaccharide films.     

Comparative characterization of aqueous dispersions and cast films of different chitin nanowhiskers/nanofibers

Water dispersions of TEMPO-oxidized α-chitin nanowhisker (TOChN), partially deacetylated α-chitin nanowhisker/nanofiber mixture (DEChN), HCl-hydrolyzed chitin nanowhisker (HHChN) and squid-pen β-chitin nanofiber (SQChN) were prepared, and the properties of nano-dispersions and their cast films were characterized between the four chitin nano-samples. Because SQChN has the highest aspect ratio, its 0.1% dispersion had the highest shear stress and viscosity at the same shear rate in the four chitin nano-samples, and showed gel-like behavior in the whole shear rate range from 10⁻³ to 10³ s⁻¹. AFM images of the self-standing films showed that film surfaces consisted of characteristic chitin nano-elements with different morphologies and degrees of orientation between the four chitin samples, whereas all chitin nanowhisker/nanofiber films had similar thermal degradation points at ∼200 °C. The DEChN film had the highest tensile strength of ∼140 MPa, elongation at break of ∼10% and light-transmittance of 87% at 400 nm. In contrast, the SQChN film had the lowest tensile strength, Young's modulus and light-transmittance. All chitin nanowhisker/nanofiber films had similar oxygen permeabilities of ∼1 mL μm m⁻² day⁻¹ kPa⁻¹, which was clearly lower than that (184 mL μm m⁻² day⁻¹ kPa⁻¹) of a poly(lactic acid) film.     

Sodium alginate/Na(+)-rectorite composite microspheres: Preparation, characterization, and dye adsorption

Sodium alginate/Na(+)-rectorite (SA/Na(+)REC) intercalated nano-composite microspheres were prepared in an inverse suspension system. The effect of the preparation conditions of SA/Na(+)REC composite microspheres on adsorption capacity for Basic Blue 9 was investigated. The structure and morphology were analyzed by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscope (SEM). The results showed that the optimal condition was that the amount of Na(+)-rectorite was 2wt%, the amount of cross-linker was 0.384% and the amount of the initiator was 8%. SEM showed that it is porous products with spherical particulate surface. XRD showed that intercalation is formed between Na(+)-rectorite and sodium alginate. The adsorption capacity of SA/Na(+)REC was investigated in comparison with Na(+)-rectorite and sodium alginate using different cationic dyes. The SA/Na(+)REC composite microspheres showed the highest adsorption capacity. The reason lies in the existence of intercalated sodium alginate. It could enlarge the pore structure of microspheres, facilitating the penetration of macromolecular dyes.     

Kinetic analysis of metal uptake by dry and gel alginate particles

The kinetics of metal uptake by gel and dry calcium alginate beads was analysed using solutions of copper or lead ions. Gel beads sorbed metal ions faster than the dry ones and larger diffusivities of metal ions were calculated for gel beads: approximately 10⁻⁴ cm²/min vs. 10⁻⁶ cm²/min for dry beads. In accordance, scanning electron microscopy and nitrogen adsorption data revealed a low porosity of dry alginate particles. However, dry beads showed higher sorption capacities and a mechanical stability more suitable for large-scale use. Two sorption models were fitted to the kinetic results: the Lagergren pseudo-first order and the Ho and McKay pseudo-second order equations. The former was found to be the most adequate to model metal uptake by dry alginate beads and kinetic constants in the orders of 10⁻³ and 10⁻² min⁻¹ were obtained for lead solutions with concentrations up to 100 g/m³. The pseudo-first order model was also found to be valid to describe biosorbent operation with a real wastewater indicating that it can be used to design processes of metal sorption with alginate-based materials.     

Studies of chitosan: II. Preparation and characterization of chitosan/poly(vinyl alcohol)/gelatin ternary blend films

Chitosan/poly(vinyl alcohol)/gelatin (CS/PVA/GA) ternary blend films were prepared by solution blending method in this study. The thermal properties of the CS/PVA/GA ternary blend films were examined by differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). The melting point of the CS/PVA/GA ternary blend film was increased when the amount of GA in the blend film was increased based upon the DSC thermal analysis. Results of X-ray diffraction (XRD) analyses indicated that the intensity of diffraction peak at 19 degrees of PVA became lower and broader with increasing the amount of GA in the CS/PVA/GA ternary blend film. Although CS, PVA, and GA are hydrophilic biodegradable polymers, the results of water contact angle measurements are still as high as 83 degrees, 68 degrees, and 66 degrees, respectively. A minimum water contact angle (56 degrees) was observed when the ternary blend film contains 50 wt.% GA (i.e. GA5). This behavior is primarily due to the reorientation of polar functional groups toward to the top surface of CS/PVA/GA ternary blend films.     

明胶/海藻酸钠/沙蒿胶复合水凝胶的制备及表征

为探究明胶（G）、海藻酸钠（SA）,沙蒿胶（ASKG）对复合水凝胶的力学性能、溶胀和保湿性能的影响,采用共混-离子交联法制备海藻酸钠/明胶/沙蒿胶复合水凝胶,并对制得的水凝胶进行结构表征和溶血率测试。结果表明:当G质量分数为2.5%,SA为1.5%,ASKG为0.7%时,复合水凝胶压缩强度达到427.2 kPa,拉伸强度达到563.449 kPa,断裂伸长率为117%,溶胀率为744%,且具有较好的保湿性能。红外光谱表明,由于沙蒿胶中存在大量羟基,因此加入沙蒿胶后在3 300 cm^-1～3 600 cm^-1羟基峰形变宽。G/SA/ASKG复合水凝胶溶血率低于5%,具有较好的网络孔结构和血液相容性,为复合水凝胶在医用敷料方面的应用提供一定的参考价值。