Hierarchical Zn–Co–S Nanowires as Advanced Electrodes for All Solid State Asymmetric Supercapacitors

A facile two‐step strategy is developed to design the large‐scale synthesis of hierarchical, unique porous architecture of ternary metal hydroxide nanowires grown on porous 3D Ni foam and subsequent effective sulfurization. The hierarchical Zn–Co–S nanowires (NWs) arrays are directly employed as an electrode for supercapacitors application. The as‐synthesized Zn–Co–S NWs deliver an ultrahigh areal capacity of 0.9 mA h cm^?2 (specific capacity of 366.7 mA h g^?1) at a current density of 3 mA cm^?2, with an exceptional rate capability (≈227.6 mA h g^?1 at a very high current density of 40 mA cm^?2) and outstanding cycling stability (≈93.2% of capacity retention after 10 000 cycles). Most significantly, the assembled Zn–Co–S NWs//Fe₂O₃@reduced graphene oxide asymmetric supercapacitors with a wide operating potential window of ≈1.6 V yield an ultrahigh volumetric capacity of ≈1.98 mA h cm^?3 at a current density of 3 mA cm^?2, excellent energy density of ≈81.6 W h kg^?1 at a power density of ≈559.2 W kg^?1, and exceptional cycling performance (≈92.1% of capacity retention after 10 000 cycles). This general strategy provides an alternative to design the other ternary metal sulfides, making it facile, free‐standing, binder‐free, and cost‐effective ternary metal sulfide‐based electrodes for large‐scale applications in modern electronics.     

A High‐Volumetric‐Capacity Cathode Based on Interconnected Close‐Packed N‐Doped Porous Carbon Nanospheres for Long‐Life Lithium–Sulfur Batteries

This study reports a Li–S battery cathode of high volumetric capacity enabled by novel micro‐ and mesostructuring. The cathode is based on monodisperse highly porous carbon nanospheres derived from a facile template‐ and surfactant‐free method. At the mesoscale, the nanospheres structure into interconnected close‐packed clusters of a few microns in extent, thus facilitating the fabrication of dense crack‐free high areal sulfur loading (5 mg cm^?2) cathodes with high electrical conductivity and low cathode impedance. A combination of the nitrogen doping (5 wt%), high porosity (2.3 cm³ g^?1), and surface area (2900 m² g^?1) at the microscale enables high sulfur immobilization and utilization. The cathode delivers among the best reported volumetric capacity to date, above typical Li‐ion areal capacity at 0.2 C over 200 cycles and low capacity fading of 0.1% per cycle at 0.5 C over 500 cycles. The compact cathode structure also ensures a low electrolyte requirement (6 µL mg^?1), which aids a low overall cell weight, and further, among the best gravimetric capacities published to date as well.     

An Improved Li–SeS2 Battery with High Energy Density and Long Cycle Life

Selenium–sulfur solid solutions are a class of potential cathode materials for high energy batteries, since they have higher theoretical capacities than selenium and improved conductivity over sulfur. Here, a high‐performance cathode material by confining 70 wt% of SeS₂ in a highly ordered mesoporous carbon (CMK‐3) framework with a polydopamine (PDA) protection sheath for novel Li–Se/S batteries is reported. With a relatively high SeS₂ mass loading of 2.6–3 mg cm^?2, the CMK‐3/SeS₂@PDA cathode exhibits a high capacity of >1200 mA h g^?1 at 0.2 A g^?1, excellent C‐rate capability of 535 mA h g^?1 at 5 A g^?1, and prolonged life over 500 cycles. Benefitting from the unique advantages of SeS₂ and the rationally designed host framework, this new cathode material demonstrates a feasible strategy to overcome the bottlenecks of current Li–S systems for high energy density rechargeable batteries.     

3D Vertically Aligned and Interconnected Porous Carbon Nanosheets as Sulfur Immobilizers for High Performance Lithium‐Sulfur Batteries

A unique nanostructure of 3D and vertically aligned and interconnected porous carbon nanosheets (3D‐VCNs) is demonstrated by a simple carbonization of agar. The key feature of 3D‐VCNs is that they possess numerous 3D channels with macrovoids and mesopores, leading to high surface area of 1750 m² g^?1, which play an important role in loading large amount of sulfur, while vertically aligned microporous carbon nanosheets act as the multilayered physical barrier against polysulfides anions and prevent their dissolution in the electrolyte due to strong adsorption during cycling process. As a result, the 3D hybrid (3D‐S‐VCNs) infiltered with 68.3 wt% sulfur exhibits a high and stable reversible capacity of 844 mAh g^?1 at the current density of 837 mA g^?1 with excellent Coulombic efficiency ≈100%, capacity retention of ≈80.3% over 300 cycles, and good rate ability (the reversible capacity of 738 mAh g^?1 at the high current density of 3340 mA g^?1). The present work highlights the vital role of the introduction of 3D carbon nanosheets with macrovoids and mesopores in enhancing the performance of LSBs.     

Metal Sulfide‐Decorated Carbon Sponge as a Highly Efficient Electrocatalyst and Absorbant for Polysulfide in High‐Loading Li2S Batteries

Owing to its high theoretical specific capacity (1166 mA h g^?1) and particularly its advantage to be paired with a lithium‐metal‐free anode, lithium sulfide (Li₂S) is regarded as a much safer cathode for next‐generation advanced lithium–sulfur (Li–S) batteries. However, the low conductivity of Li₂S and particularly the severe “polysulfide shuttle” of lithium polysulfide (LiPS) dramatically hinder their practical application in Li–S batteries. To address such issues, herein a bifuctional 3D metal sulfide‐decorated carbon sponge (3DTSC), which is constructed by 1D carbon nanowires cross‐linked with 2D graphene nanosheets with high conductivity and polar 0D metal sulfide nanodots with efficient electrocatalytic activity and strong chemical adsorption capability for LiPSs, is presented. Benefiting from the well‐designed multiscale, multidimensional 3D porous nanoarchitecture with high conductivity, and efficient electrocatalytic and absorption ability, the 3DTSC significantly mitigates LiPS shuttle, improves the utilization of Li₂S, and facilitates the transport of electrons and ions. As a result, even with a high Li₂S loading of 8 mg cm^?2, the freestanding 3DTSC‐Li₂S cathode without a polymer binder and metallic current collector delivers outstanding electrochemical performance with a high areal capacity of 8.44 mA h cm^?2.     

Sulfur/Oxygen Codoped Porous Hard Carbon Microspheres for High‐Performance Potassium‐Ion Batteries

Potassium‐ion batteries (KIBs) are very promising alternatives to lithium‐ion batteries (LIBs) for large‐scale energy storage. However, traditional carbon anode materials usually show poor performance in KIBs due to the large size of K ions. Herein, a carbonization‐etching strategy is reported for making a class of sulfur (S) and oxygen (O) codoped porous hard carbon microspheres (PCMs) material as a novel anode for KIBs through pyrolysis of the polymer microspheres (PMs) composed of a liquid crystal/epoxy monomer/thiol hardener system. The as‐made PCMs possess a porous architecture with a large Brunauer–Emmett–Teller surface area (983.2 m² g^?1), an enlarged interlayer distance (0.393 nm), structural defects induced by the S/O codoping and also amorphous carbon nature. These new features are important for boosting potassium ion storage, allowing the PCMs to deliver a high potassiation capacity of 226.6 mA h g^?1 at 50 mA g^?1 over 100 cycles and be displaying high stability by showing a potassiation capacity of 108.4 mA h g^?1 over 2000 cycles at 1000 mA g^?1. The density functional theory calculations demonstrate that S/O codoping not only favors the adsorption of K to the PCMs electrode but also reduces its structural deformation during the potassiation/depotassiation. The present work highlights the important role of hierarchical porosity and S/O codoping in potassium storage.     

Uniform Pomegranate‐Like Nanoclusters Organized by Ultrafine Transition Metal Oxide@Nitrogen‐Doped Carbon Subunits with Enhanced Lithium Storage Properties

Uniform pomegranate‐like nanoclusters (NCs) organized by ultrafine transition metal oxide@nitrogen‐doped carbon (TMO@N–C) subunits (diameter ≈ 4 nm) are prepared on a large scale for the first time through a facile, novel, and one‐pot approach. Taking pomegranate‐like Fe₃O₄@N–C NCs as an example, this unique structure provides short Li⁺/electron diffusion pathways for electrochemical reactions, structural stability during cycling, and high electrical conductivity, leading to superior electrochemical performance. The resulting pomegranate‐like Fe₃O₄@N–C NCs possess a high specific capacity (1204.3 mA h g^?1 at 0.5 A g^?1 over 100 cycles), a stable cycle life (1063.0 mA h g^?1 at 1 A g^?1, 98.4% retention after 1000 cycles), and excellent rate capacities (606.0 mA h g^?1 at 10 A g^?1, 92.0% retention; 417.1 mA h g^?1 at 20 A g^?1, 91.7% retention after 1000 cycles).     

A Conductive Molecular Framework Derived Li2S/N,P‐Codoped Carbon Cathode for Advanced Lithium–Sulfur Batteries

Li₂S is one of the most promising cathode materials for Li‐ion batteries because of its high theoretical capacity and compatibility with Li‐metal‐free anode materials. However, the poor conductivity and electrochemical reactivity lead to low initial capacity and severe capacity decay. In this communication, a nitrogen and phosphorus codoped carbon (N,P–C) framework derived from phytic acid doped polyaniline hydrogel is designed to support Li₂S nanoparticles as a binder‐free cathode for Li–S battery. The porous 3D architecture of N and P codoped carbon provides continuous electron pathways and hierarchically porous channels for Li ion transport. Phosphorus doping can also suppress the shuttle effect through strong interaction between sulfur and the carbon framework, resulting in high Coulombic efficiency. Meanwhile, P doping in the carbon framework plays an important role in improving the reaction kinetics, as it may help catalyze the redox reactions of sulfur species to reduce electrochemical polarization, and enhance the ionic conductivity of Li₂S. As a result, the Li₂S/N,P–C composite electrode delivers a stable capacity of 700 mA h g^?1 with average Coulombic efficiency of 99.4% over 100 cycles at 0.1C and an areal capacity as high as 2 mA h cm^?2 at 0.5C.     

Carbon Coated Bimetallic Sulfide Hollow Nanocubes as Advanced Sodium Ion Battery Anode

Sodium ion battery (SIB) as a next‐generation battery has been drawing much attention due to the abundance and even distribution of sodium source. Metal sulfides with high theoretical capacity and good electrical conductivity are promising anode candidates for SIB, however, the structural collapse caused by severe volume change during the de/sodiation process typically results in a fast capacity decay, limited rate capability, and cycling stability. In this work, by careful composition and structure design, polydopamine coated Prussian blue analogs derived carbon coated bimetallic sulfide hollow nanocubes (PBCS) are prepared with distinguished morphology, higher surface area, smaller charge transfer resistance, and higher sodium diffusion coefficient than the uncoated bimetallic sulfides. An optimum carbon coated bimetallic sulfide hollow nanocube anode delivers a specific capacity of ≈500 mA h g^?1 at 50 mA g^?1 with ethylene carbonate/dimethyl carbonate (1:1, vol%) electrolyte in the presence of fluoroethylene carbonate additives. A capacity of 122.3 mA h g^?1 can be realized at 5000 mA g^?1, showing good rate performance. In addition the carbon coated bimetallic sulfide hollow nanocubes can maintain capacity of 87 mA h g^?1 after being cycled at 500 mA g^?1 for 150 times, indicating its good cycling stability. The structure integrity, high specific capacity, good rate performance, and cycling stability of PBCS render it a promising anode material for advanced SIB.     

Yolk–Shell NiS2 Nanoparticle‐Embedded Carbon Fibers for Flexible Fiber‐Shaped Sodium Battery

Fiber‐shaped rechargeable batteries hold promise as the next‐generation energy storage devices for wearable electronics. However, their application is severely hindered by the difficulty in fabrication of robust fiber‐like electrodes with promising electrochemical performance. Herein, yolk–shell NiS₂ nanoparticles embedded in porous carbon fibers (NiS₂?PCF) are successfully fabricated and developed as high‐performance fiber electrodes for sodium storage. Benefiting from the robust embedded structure, 3D porous and conductive carbon network, and yolk–shell NiS₂ nanoparticles, the as‐prepared NiS₂?PCF fiber electrode achieves a high reversible capacity of about 679 mA h g^?1 at 0.1 C, outstanding rate capability (245 mA h g^?1 at 10 C), and ultrastable cycle performance with 76% capacity retention over 5000 cycles at 5 C. Notably, a flexible fiber‐shaped sodium battery is assembled, and high reversible capacity is kept at different bending states. This work offers a new electrode‐design paradigm toward novel carbon fiber electrodes embedded with transition metal oxides/sulfides/phosphides for application in flexible energy storage devices.     

Covalent Encapsulation of Sulfur in a MOF‐Derived S,N‐Doped Porous Carbon Host Realized via the Vapor‐Infiltration Method Results in Enhanced Sodium–Sulfur Battery Performance

Practical applications of room temperature sodium–sulfur batteries are still inhibited by the poor conductivity and slow reaction kinetics of sulfur, and dissolution of intermediate polysulfides in the commonly used electrolytes. To address these issues, starting from a novel 3D Zn‐based metal–organic framework with 2,5‐thiophenedicarboxylic acid and 1,4‐bis(pyrid‐4‐yl) benzene as ligands, a S, N‐doped porous carbon host with 3D tubular holes for sulfur storage is fabricated. In contrast to the commonly used melt‐diffusion method to confine sulfur physically, a vapor‐infiltration method is utilized to achieve sulfur/carbon composite with covalent bonds, which can join electrochemical reaction without low voltage activation. A polydopamine derived N‐doped carbon layer is further coated on the composite to confine the high‐temperature‐induced gas‐phase sulfur inside the host. S and N dopants increase the polarity of the carbon host to restrict diffusion of sulfur, and its 3D porous structure provides a large storage area for sulfur. As a result, the obtained composite shows outstanding electrochemical performance with 467 mAh g^?1 (1262 mAh g^?1_(sulfur)) at 0.1 A g^?1, 270 mAh g^?1 (730 mAh g^?1_(sulfur)) after 1000 cycles at 1 A g^?1 and 201 mAh g^?1 (543 mAh g^?1_(sulfur)) at 5.0 A g^?1.     

Tailored Plum Pudding‐Like Co2P/Sn Encapsulated with Carbon Nanobox Shell as Superior Anode Materials for High‐Performance Sodium‐Ion Capacitors

Sodium‐ion capacitors (SICs) are emerging energy storage devices with high energy, high power, and durable life. Sn is a promising anode material for lithium storage, but the poor conductivity of the a‐NaSn phase upon sodaition hinders its implementation in SICs. Herein, a superior Sn‐based anode material consisting of plum pudding‐like Co₂P/Sn yolk encapsulated with nitrogen‐doped carbon nanobox (Co₂P/Sn@NC) for high‐performance SICs is reported. The 8–10 nm metallic nanoparticles produced in situ are uniformly dispersed in the amorphous Sn matrix serving as conductive fillers to facilitate electron transfer in spite of the formation of electrically resistive a‐NaSn phase during cycling. Meanwhile, the carbon shell buffers the large expansion of active Sn and provides a stable electrode–electrolyte interface. Owing to these merits, the yolk–shell Co₂P/Sn@NC demonstrates a large capacity of 394 mA h g^?1 at 100 mA g^?1, high rate capability of 168 mA h g^?1 at 5000 mA g^?1, and excellent cyclability with 87% capacity retention after 10 000 cycles. By integrating the Co₂P/Sn@NC anode with a peanut shell‐derived carbon cathode in the SIC, high energy densities of 112.3 and 43.7 Wh kg^?1 at power densities of 100 and 10 000 W kg^?1 are achieved.     

Design Principles for Optimum Performance of Porous Carbons in Lithium–Sulfur Batteries

A series of experiments is presented that establishes for the first time the role of some of the key design parameters of porous carbons including surface area, pore volume, and pore size on battery performance. A series of hierarchical porous carbons is used as a model system with an open, 3D, interconnected porous framework and highly controlled porosity. Specifically, carbons with surface areas ranging from ≈500–2800 m² g^?1, pore volume from ≈0.6–5 cm³ g^?1, and pore size from micropores (≈1 nm) to large mesopores (≈30 nm) are synthesized and tested. At high sulfur loadings (≈80 wt% S), pore volume is more important than surface area with respect to sulfur utilization. Mesopore size, in the range tested, does not affect the sulfur utilization. No relationship between porosity and long‐term cycle life is observed. All systems fail after 200–300 cycles, which is likely due to the consumption of the LiNO₃ additive over cycling. Moreover, cryo‐scanning transmission electron microscopy imaging of these carbon–sulfur composites combined with X‐ray diffraction (XRD) provides further insights into the effect of initial sulfur distribution on sulfur utilization while also revealing the inadequacy of the indirect characterization techniques alone in reliably predicting distribution of sulfur within porous carbon matrices.     

Ion Transport Nanotube Assembled with Vertically Aligned Metallic MoS2 for High Rate Lithium‐Ion Batteries

Metallic phase molybdenum disulfide (MoS₂) is well known for orders of magnitude higher conductivity than 2H semiconducting phase MoS₂. Herein, for the first time, the authors design and fabricate a novel porous nanotube assembled with vertically aligned metallic MoS₂ nanosheets by using the scalable solvothermal method. This metallic nanotube has the following advantages: (i) intrinsic high electrical conductivity that promotes the rate performance of battery and eliminates the using of conductive additive; (ii) hierarchical, hollow, porous, and aligned structure that assists the electrolyte transportation and diffusion; (iii) tubular structure that avoids restacking of 2D nanosheets, and therefore maintains the electrochemistry cycling stability; and (iv) a shortened ion diffusion path, that improves the rate performance. This 1D metallic MoS₂ nanotube is demonstrated to be a promising anode material for lithium‐ion batteries. The unique structure delivers an excellent reversible capacity of 1100 mA h g^?1 under a current density of 5 A g^?1 after 350 cycles, and an outstanding rate performance of 589 mA h g^?1 at a current density of 20 A g^?1. Furthermore, attributed to the material's metallic properties, the electrode comprising 100% pure material without any additive provides an ideal system for the fundamental electrochemical study of metallic MoS₂. This study first reveals the characteristic anodic peak at 1.5 V in cyclic voltammetry of metallic MoS_2. This research sheds light on the fabrication of metallic 1D, 2D, or even 3D structures with 2D nanosheets as building blocks for various applications.     

Long Cycle Life,Low Self‐Discharge Sodium–Selenium Batteries with High Selenium Loading and Suppressed Polyselenide Shuttling

The use of selenium as a cathode in rechargeable sodium–selenium batteries is hampered by low Se loading, inferior electrode kinetics, and polyselenide shuttling between the cathode and anode. Here a high‐performance sodium–selenium cell is presented by coupling a binder‐free, self‐interwoven carbon nanofiber–selenium cathode with a light‐weight carbon‐coated bifunctional separator. With this strategy, electrodes with a high Se mass loading (4.4 mg cm^?2) render high reversible capacities of 599 mA h g^?1 at 0.1C rate and 382 mA h g^?1 at 5C rate. In addition, this novel cell offers good shelf‐life with a low self‐discharge, retaining 93.4% of its initial capacity even after resting for six months. As evidenced by experimental and density functional theory analysis, the remarkable dynamic (cycle life) and static (shelf‐life) stabilities originate from the high electrical conductivity, improved Na‐ion accessibility through the 3D interconnected open channels, and highly restrained polyselenide shuttle. The results demonstrate the viability of high‐performance sodium–selenium batteries with high selenium loading.     

Integration of FeOOH and Zeolitic Imidazolate Framework‐Derived Nanoporous Carbon as an Efficient Electrocatalyst for Water Oxidation

As a cost‐effective catalyst for the oxygen evolution reaction (OER), the potential use of FeOOH is hindered by its intrinsic poor electron conductivity. Here, the significant enhancement of OER activity and long‐term stability of electrodeposited FeOOH on zeolitic imidazolate framework‐derived N‐doped porous carbons (NPCs) are reported. In alkaline media, FeOOH/NPC supported on nickel foam as a 3D electrode delivers a current density of 100 mA cm^?2 at a small overpotential of 230 mV and exhibits a low Tafel slope of 33.8 mV dec^?1 as well as excellent durability, making it one of the most active OER catalysts. Such high performance is attributed to a combined effect of the excellent electron conductivity of NPC and the synergy between FeOOH and NiO derived from Ni substrate.     

Flexible and High‐Loading Lithium–Sulfur Batteries Enabled by Integrated Three‐In‐One Fibrous Membranes

Lithium–sulfur batteries are appealing as high‐energy storage systems and hold great application prospects in wearable and portable electronics. However, severe shuttle effects, low sulfur conductivity, and especially poor electrode mechanical flexibility restrict sulfur utilization and loading for practical applications. Herein, high‐flux, flexible, electrospun fibrous membranes are developed, which succeed in integrating three functional units (cathode, interlayer, and separator) into an efficient composite. This structure helps to eliminate negative interface effects, and effectively drives synergistic boosts to polysulfide confinement, electron transfer, and lithium‐ion diffusion. It delivers a high initial capacity of 1501 mA h g^?1 and a discharge capacity of 933 mA h g^?1 after 400 cycles, with slow capacity attenuation (0.069% per cycle). Even under high sulfur loading (13.2 mg cm^?2, electrolyte/sulfur ratio = 6 mL g^?1) or in an alternative folded state, this three‐in‐one membrane still exhibits high areal capacity (11.4 mA h cm^?2) and exceptional application performance (powering an array of over 30 light‐emitting diodes (LEDs)), highlighting its huge potential in high‐energy flexible devices.     

3D Nanowire Arrayed Cu Current Collector toward Homogeneous Alloying Anode Deposition for Enhanced Sodium Storage

Alloying electrodes are regarded as promising anodes for lithium/sodium storage thanks to their multielectron reaction capacity, moderate voltage plateau, and high electrical conductivity. However, huge volume change upon cycling, especially for sodium storage, usually causes the loss of electrical connection between active components and their delaminations from traditional current collectors, thus leading to rapid capacity decay. Herein, a unique 3D current collector is assembled from 1D nanowire arrays anchored on 3D porous Cu foams for constructing core‐shelled Cu@Sb nanowires as advanced sodium‐ion battery (SIB) anodes. The so‐formed hierarchical 3D anode with interconnected 3D micrometer sized pores and abundant voids between nanowires not only effectively accommodates the structural strains during repeated cycling but also ensures the structural integrity and contributes to a uniform ion/electron scattered distribution throughout the whole surface. When employed as anodes for SIBs, the obtained electrode shows a high capacity of 605.3 mAh g^?1 at 330 mA g^?1, and demonstrates a high capacity retention of 84.8% even at a high current density of 3300 mA g^?1. The 3D nanowire arrayed Cu current collector in this work can offer a promising strategy for designing and building advanced alloy anodes for lithium/sodium storage.     

High‐Performance All‐Solid‐State Lithium–Sulfur Batteries Enabled by Amorphous Sulfur‐Coated Reduced Graphene Oxide Cathodes

Safety and the polysulfide shuttle reaction are two major challenges for liquid electrolyte lithium–sulfur (Li–S) batteries. Although use of solid‐state electrolytes can overcome these two challenges, it also brings new challenges by increasing the interface resistance and stress/strain. In this work, the interface resistance and stress/strain of sulfur cathodes are significantly reduced by conformal coating ≈2 nm sulfur (S) onto reduced graphene oxide (rGO). An Li–S full cell consisting of an rGO@S‐Li₁₀GeP₂S₁₂‐acetylene black (AB) composite cathode is evaluated. At 60 °C, the all‐solid‐state Li–S cell demonstrates a similar electrochemical performance as in liquid organic electrolyte, with high rate capacities of 1525.6, 1384.5, 1336.3, 903.2, 502.6, and 204.7 mA h g^?1 at 0.05, 0.1, 0.5, 1.0, 2.0, and 5.0 C, respectively. It can maintain a high and reversible capacity of 830 mA h g^?1 at 1.0 C for 750 cycles. The uniform distribution of the rGO@S nanocomposite in the Li₁₀GeP₂S₁₂‐AB matrix generates uniform volume changes during lithiation/delithiation, significantly reducing the stress/strain, thus extending the cycle life. Minimization of the stress/strain of solid cells is the key for a long cycle life of all‐solid‐state Li–S batteries.     

Highly Stable Lithium–Sulfur Batteries Based on Laponite Nanosheet‐Coated Celgard Separators

Lithium–sulfur (Li–S) batteries are of great interest due to their high theoretical energy density. However, one of the key issues hindering their real world applications is polysulfide shuttle, which results in severe capacity decay and self‐discharge. Here, a laponite nanosheets/carbon black coated Celgard (LNS/CB‐Celgard) separator to inhibit polysulfide shuttle and to enhance the Li⁺ conductivity simultaneously is reported. The polysulfide shuttle is efficiently inhibited through strong interactions between the O active sites of the LNS and polysulfides by forming the Li···O and O? S bonds. Moreover, the separator features high Li⁺ conductivity, fast Li⁺ diffusion, excellent electrolyte wettability, and high thermal stability. Consequently, the Li–S batteries with the LNS/CB‐Celgard separator and the pure S cathode show a high initial reversible capacity of 1387 mA h g^?1 at 0.1 C, high rate performance, superior cycling stability (with a capacity decay rate of 0.06% cycle^?1 at 0.2 C and 0.028% cycle^?1 at 1.0 C over 500 cycles), and ultralow self‐discharge. The separator could also enhance the performance of other batteries such as the LiFePO₄/separator/Li battery. This work sheds a new light on the design and preparation of novel separators for highly stable Li–S batteries via a “green” and cost‐effective approach.