A methodology for evaluating biocide release rate, surface roughness and leach layer formation in a TBT-free, self-polishing antifouling coating

Due to the forthcoming IMO ban on the use of tributyltin (TBT) antifouling paints, a new generation of TBT-free coatings has been developed that typically contain cuprous oxide and an organic co-biocide. Accurate and reproducible test methods are needed to evaluate the performance and environmental impact of these new coatings. This study investigated a methodology for evaluating TBT-free, AF coatings containing cuprous oxide. A commercially available AF coating underwent rotary immersion testing at 0, 0.51 and 2.05 m s-1. Scanning electron microscopy (SEM) and energy dispersive x-ray (EDX) analysis were used to assess leach layer formation, percentage cuprous oxide by weight and particle size distribution (PSD). Biocide release rates and surface roughness were also measured. An increase in rotary speed caused a spike in Cu2+ release rate after which the release rate stabilised to previous levels. An increase in leach layer thickness was also observed after the rotary speed increase. A model is suggested to account for the observations.     

Biomimetic helical rosette nanotubes and nanocrystalline hydroxyapatite coatings on titanium for improving orthopedic implants

Natural bone consists of hard nanostructured hydroxyapatite (HA) in a nanostructured protein-based soft hydrogel template (ie, mostly collagen). For this reason, nanostructured HA has been an intriguing coating material on traditionally used titanium for improving orthopedic applications. In addition, helical rosette nanotubes (HRNs), newly developed materials which form through the self-assembly process of DNA base pair building blocks in body solutions, are soft nanotubes with a helical architecture that mimics natural collagen. Thus, the objective of this in vitro study was for the first time to combine the promising attributes of HRNs and nanocrystalline HA on titanium and assess osteoblast (bone-forming cell) functions. Different sizes of nanocrystalline HA were synthesized in this study through a wet chemical precipitation process following either hydrothermal treatment or sintering. Transmission electron microscopy images showed that HRNs aligned with nanocrystalline HA, which indicates a high affinity between both components. Some of the nanocrystalline HA formed dense coatings with HRNs on titanium. More importantly, results demonstrated enhanced osteoblast adhesion on the HRN/nanocrystalline HA-coated titanium compared with conventional uncoated titanium. Among all the HRN/nanocrystalline HA coatings tested, osteoblast adhesion was the greatest when HA nanometer particle size was the smallest. In this manner, this study demonstrated for the first time that biomimetic HRN/nanocrystalline HA coatings on titanium were cytocompatible for osteoblasts and, thus, should be further studied for improving orthopedic implants.     

A methodology for evaluating biocide release rate,surface roughness and leach layer formation in a TBT-free,self-polishing antifouling coating

Abstract

Due to the forthcoming IMO ban on the use of tributyltin (TBT) antifouling paints, a new generation of TBT-free coatings has been developed that typically contain cuprous oxide and an organic co-biocide. Accurate and reproducible test methods are needed to evaluate the performance and environmental impact of these new coatings. This study investigated a methodology for evaluating TBT-free, AF coatings containing cuprous oxide. A commercially available AF coating underwent rotary immersion testing at 0, 0.51 and 2.05 m s^?1. Scanning electron microscopy (SEM) and energy dispersive x-ray (EDX) analysis were used to assess leach layer formation, percentage cuprous oxide by weight and particle size distribution (PSD). Biocide release rates and surface roughness were also measured. An increase in rotary speed caused a spike in Cu²⁺ release rate after which the release rate stabilised to previous levels. An increase in leach layer thickness was also observed after the rotary speed increase. A model is suggested to account for the observations.     

碳/碳材料含硅羟基磷灰石涂层体外成骨细胞相容性研究

目的:成骨细胞在碳/碳复合材料表面羟基磷灰石涂层上有良好的长入,该实验在羟基磷灰石(hydroxyapatite HA)涂层中掺入硅后,研究成骨细胞对该涂层的生物活性,为临床骨科应用提供实验基础。方法:本研究采用化学液相气化沉积/水热法在碳/碳材料表面制备了含硅羟基磷灰石(silicon-hydroxyapatite Si-HA)涂层。在体外成骨细胞相容性的研究中,以HA涂层为对照,通过甲基噻唑基四唑(methylthiazolyl tetrazolium MTT)法测定细胞增殖反应和对细胞毒性反应,碱性磷酸酶(alkaline phosphatase ALP)测定细胞的分化,扫描电镜观察细胞生长形态,免疫荧光显影技术测定细胞的长入。结果:在HA涂层中引入硅后,Si-HA涂层和HA涂层在第2天、第4天的成骨细胞增殖实验表明前者的细胞长入数较后者多,两者的差异有统计学意义,而Si-HA涂层浸泡液中的ALP活性下降较HA涂层而言更明显,两者的差异有统计学意义,电镜扫描及荧光染色均提示在Si-HA涂层中成骨细胞的增值数更多。结论:在HA涂层中引入硅后,改变了涂层自身的晶体结构及表面电荷,同时诱导成骨细胞分泌胶原,使得成骨细胞更好的贴壁生长和增殖,成骨能力增加。在临床骨科植入物表面涂层改性上有很好的应用前景。     

Fabrication of gelatin-hyaluronic acid hybrid scaffolds with tunable porous structures for soft tissue engineering

The development of three-dimensional (3-D) scaffolds with highly open porous structure is one of the most important issues in tissue engineering. In this study, 3-D macroporous gelatin/hyaluronic acid (GE/HA) hybrid scaffolds with varying porous morphology were prepared by freeze-drying their blending solutions and subsequent chemical crosslinking by using 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide hydrochloride (EDC). The resulting scaffolds were characterized by scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR). Their swelling, in vitro degradation properties and compressive strength were also investigated. To evaluate in vitro cytocompatibility of scaffolds, mouse L929 fibroblasts were seeded onto the scaffolds for cell morphology and cell viability studies. It was found that the porous structure of scaffolds can be tailored by varying the ratios of gelatin to HA, both the swelling ratios and degradation rate increased with the increase of HA content in hybrid scaffolds, and crosslinking the scaffolds with EDC improved the degradation resistance of the scaffold in culture media and increased the mechanical strength of scaffolds. The in vitro results revealed that the prepared scaffolds do not induce cytotoxic effects and suitable for cell growth, especially in the case of scaffolds with higher gelatin content. The combined results of the physicochemical and biological studies suggested that the developed GE/HA hybrid scaffolds exhibit good potential and biocompatibility for soft tissue engineering applications.     

Enhance Stability and in vitro Cell Response to a Bioinspired Coating on Zr Alloy with Increasing Chitosan Content

The aim of the present paper is to characterize bioinspired chitosan (CS) + hydroxyapatite (HA) coatings with various components ratio on a zirconium alloy with titanium.The coatings were characterized by FT-IR,SEM,hydrophilic/hydrophobic balance,adherence,roughness,electrochemical stability and in vitro cell response.Electrochemical tests,including potentiodynamic polarization curves and electrochemical impedance spectroscopy,were performed in normal saline physiological solution.Cell viability of MC3T3-E1 osteoblasts,lactate dehydrogenase,nitric oxide,and Reactive Oxygen Species (ROS) levels,as well as actin cytoskeleton morphology,were evaluated as biological in vitro tests.The results on in vitro cell response indicated good cell membrane integrity and viability for all samples,but an increased cell number,a decreased ROS level and a better cytoskeleton organization were noticed for the sample with a higher CS content.The coating with highest CS concentration indicated the best performance based on the experimental data.The highest hydrophilic character,highest resistance to corrosion and best biocompatibility as well recommend this coating for bioapplications in tissue engineering.     

Long-term microstructural analyses of hydroxyapatite implanted in rats using laser-Raman spectrometry and scanning electron microscopy.

To investigate the long-term surface microstructure of a synthetic auditory ossicle (Apaceram) composed of dense hydroxyapatite (HA), thin HA disks were implanted subcutaneously into the interscapular regions of 12 rats. After 6, 14 and 20 months, implanted HA surfaces were observed using stereoscopic microscopy, scanning electron microscopy (SEM) and laser-Raman spectrometry. Visual observation by SEM at 6 months and by stereoscopic microscopy at 14 months indicated a progressive degradation of the HA disk surfaces implanted in the subcutaneous tissue. Visual observation by SEM at 14 and 20 months and by stereoscopic microscopy at 20 months indicated a progressive redeposition on the surfaces of the implants. Raman spectra compared half-peak breadths of v1 signal (PO4(3-), 960 cm(-1)) on the gray and white surface areas of implanted HA disks observed by stereoscopic microscopy. Analysis demonstrates that demineralization at 14 months and remineralization at 20 months occur on the gray areas; demineralization at 6 months and remineralization at 14 months occur on the white areas.     

In vitro and in vivo bioactivity of CoBlast hydroxyapatite coating and the effect of impaction on its osteoconductivity

The novel non-thermal CoBlast process has been used recently to create a hydroxyapatite coating on metallic substrates with improved biological response compared to an uncoated implant. In this study, we compared the biological effect of coatings deposited by this process and the industrial standard technique - plasma-spray. Physicochemical properties of these two coatings have been found to be significantly different in that CoBlast HA is less rough but more hydrophilic than the plasma-spray HA as evidenced by data obtained from profilometry and goniometry. Mesenchymal stem cell attachment and adhesion are enhanced on CoBlast HA. Analysis by a combination of EDX and ICP suggests that the higher crystallinity retained by the CoBlast HA result in slower coating dissolution. Detailed in vitro evaluation reveals that plasma-spray HA might induce slightly faster cell proliferation and earlier osteogenic differentiation, but CoBlast HA becomes equivalent to it by the late osteogenic stage. PCR array facilitated the identification of differentially regulated genes involved in various functional aspects of in vitro osteogenesis by the CoBlast HA coating. The expression level of the functional protein products of these genes are in agreement with the PCR data. Coating metallic screws with HA significantly improves the in vivo osseointegration. By measuring of removal force using torque measurement instrument and analyzing the patterns found in X-ray images it is demonstrated that the two HA coatings elicit comparable osseointegration. Using simulated impaction model, CoBlast HA is shown to maintain better performance in cell attachment and mineralization than plasma-spray HA, especially following significant impactions. This might indicate a potentially greater osteoconductivity of CoBlast HA coating in shear-stress associated surgical applications. Collectively, it was demonstrated that CoBlast HA is an effective alternative to plasma-spray HA coating and a promising replacement for specialized surgical applications.     

Mechanistic Insights into Interaction of Humic Acid with Silver Nanoparticles

Humic acid (HA) is one of the major components of the natural organic matter present in the environment that alters the fate and behavior of silver nanoparticles (Ag NPs). Transformation of Ag NPs happens upon interaction with HA, thereby, changing both physical and chemical properties. Fluorescence spectroscopy and scanning electron microscopy (SEM) were used to analyze the interaction of Ag NPs with HA. In pH and time-dependent studies, the near field electro dynamical environment of Ag NPs influenced the fluorescence of HA, indicated by fluorescence enhancement. SEM revealed not only morphological changes, but also significant reduction in size of Ag NPs after interaction with HA. Based on these studies, a probable mechanism was proposed for the interaction of HA with Ag NPs, suggesting the possible transformation that these nanoparticles can undergo in the environment.     

Unique advantages of using low temperature scanning electron microscopy to observe bacteria

Summary Electron microscopy (EM) has greatly helped to elucidate our understanding of bacterial structure and function. However, several recent studies have cautioned investigators about artifacts that result from the use of conventional EM preparation procedures. To avoid these problems, the use of low temperature scanning electron microscopy (LTSEM) was evaluated for examining frozen, fully hydrated specimens. Spinach leaves (Spinacia oleracea L. cv. New Jersey), which were naturally infected or inoculated with bacteria, were used as the experimental material. 1 cm segments of the infected leaves were plunge frozen in liquid nitrogen, transferred to a cryochamber for sputter coating and then moved onto a cryostage in an SEM. After observation, some of the frozen, hydrated leaf segments were transferred onto agar medium to determine whether preparation for LTSEM was nondestructive to the bacteria. The other tissue segments were chemically fixed by freeze-substitution. The results indicated that after cryopreparation and observation in the LTSEM: (i) viable bacteria, which were recovered from the leaf sample, could be cultured on agar medium for subsequent study, and (ii) the frozen samples could be freeze substituted and embedded so that transmission electron microscopic (TEM) observations could be carried out on the same specimen. In conclusion, frozen, hydrated leaf tissue infected with bacteria can be observed using LTSEM and then can be either processed for TEM observation to obtain further structural details or recovered to culture the pathogenic bacteria for supplementary studies.Abbreviations EPS extracellular polysaccharide - EM electron microscopy - LTSEM low temperature scanning electron microscopy - SEM scanning electron microscopy - TEM transmission electron microscopy - TSA tryptic soy agar - TSB tryptic soy broth Dedicated to Professor Eldon H. Newcomb in recognition of his contributions to cell biology     

Monitoring tablet surface roughness during the film coating process

The purpose of this study was to evaluate the change of surface roughness and the development of the film during the film coating process using laser profilometer roughness measurements, SEM imaging, and energy dispersive X-ray (EDX) analysis. Surface roughness and texture changes developing during the process of film coating tablets were studied by noncontact laser profilometry and scanning electron microscopy (SEM). An EDX analysis was used to monitor the magnesium stearate and titanium dioxide of the tablets. The tablet cores were film coated with aqueous hydroxypropyl methylcellulose, and the film coating was performed using an instrumented pilot-scale side-vented drum coater. The SEM images of the film-coated tablets showed that within the first 30 minutes, the surface of the tablet cores was completely covered with a thin film. The magnesium signal that was monitored by SEM-EDX disappeared after ∼15 to 30 minutes, indicating that the tablet surface was homogeneously covered with film coating. The surface roughness started to increase from the beginning of the coating process, and the increase in the roughness broke off after 30 minutes of spraying. The results clearly showed that the surface roughness of the tablets increased until the film coating covered the whole surface area of the tablets, corresponding to a coating time period of 15 to 30 minutes (from the beginning of the spraying phase). Thereafter, the film only became thicker. The methods used in this study were applicable in the visualization of the changes caused by the film coating on the tablet surfaces.     

Engineering the microstructure and permeability of thin multilayer latex biocatalytic coatings containing E. coli.

The microstructure and permeability of rehydrated 20-100 microm thick partially coalesced (vinyl-actetate acrylic copolymer) SF091 latex coatings and a 118 microm thick model trilayer biocatalytic coating consisting of two sealant SF091 layers containing a middle layer of viable E. coli HB101 + latex were studied as delaminated films in a diffusion apparatus with KNO(3) as the diffussant. The permeability of the hydrated coatings is due to diffusive transport through the pore space between the partially coalesced SF091 latex particles. Coating microstructure was visualized by fast freeze cryogenic scanning electron microscopy (cryo-SEM). The effective diffusion coefficient of SF091 latex coatings (diffusive permeability/film thickness) was determined as the ratio of the effective diffusivity of KNO(3) to its diffusivity in water (D(eff)/D). Polymer particle coalescence was arrested by two methods to increase coating permeability. The first used glycerol with coating drying at 4 degrees C, near the glass transition temperature (T(g)). The second method used sucrose or trehalose as a filler to arrest coalescence; the filler was then dissolved away. D(eff)/D was measured as a function of film thickness; content of glycerol, sucrose, and trehalose; drying time; and rehydration time. D(eff)/D varied from 3 x 10(-4) for unmodified SF091 coatings to 6.8 x 10(-2) for coatings containing sucrose. D(eff)/D was reduced by the flattening of latex particles against the surface of the solid substrate, as well as by the presence of the colloid stabilizer hydroxyethylcellulose (HEC). When corrected for the flattened particle layer, D(eff)/D of HEC-free coatings was as high as 0.20, which agreed with the value predicted from analysis of cryo-SEM images of the coat surface. D(eff)/D decreased by one-half in approximately 5 days in rehydrated SF091 coatings, indicating that significant wet coalescence occurs after glycerol, sucrose, or trehalose are leached from the films. D(eff)/D of SF091 latex trilayer coatings containing viable E. coli HB101 cells decreased as cell loading was increased from 2.2 x 10(-2) for 64 g dry cell weight per liter of coat volume to 5 x 10(-3) for 151 g DCW/L of coat volume. The reduction in coating permeability with increasing cell loading is predicted by Maxwell's equation for D(eff)/D in periodic composites.     

Influence of collagen and chondroitin sulfate (CS) coatings on poly-(lactide-co-glycolide) (PLGA) on MG 63 osteoblast-like cells

Poly-(lactide-co-glycolide) (PLGA) is an FDA-approved biodegradable polymer which has been widely used as a scaffold for tissue engineering applications. Collagen has been used as a coating material for bone contact materials, but relatively little interest has focused on biomimetic coating of PLGA with extracellular matrix components such as collagen and the glycosaminoglycan chondroitin sulfate (CS). In this study, PLGA films were coated with collagen type I or collagen I with CS (collagen I/CS) to investigate the effect of CS on the behaviour of the osteoblastic cell line MG 63. Collagen I/CS coatings promoted a significant increase in cell number after 3 days (in comparison to PLGA) and after 7 days (in comparison to PLGA and collagen-coated PLGA). No influence of collagen I or collagen I/CS coatings on the spreading area after 1 day of culture was observed. However, the cells on collagen I/CS formed numerous filopodia and displayed well developed vinculin-containing focal adhesion plaques. Moreover, these cells contained a significantly higher concentration of osteocalcin, measured per mg of protein, than the cells on the pure collagen coating. Thus, it can be concluded that collagen I/CS coatings promote MG 63 cell proliferation, improve cell adhesion and enhance osteogenic cell differentiation.     

D-mannose-modified iron oxide nanoparticles for stem cell labeling

New surface-modified iron oxide nanoparticles were developed by precipitation of Fe(II) and Fe(III) salts with ammonium hydroxide according to two methods. In the first method, precipitation was done in the presence of D-mannose solution (in situ coating); the second method involved oxidation of precipitated magnetite with sodium hypochlorite followed by addition of D-mannose solution (postsynthesis coating). Selected nanoparticles were characterized by transmission electron microscopy (TEM), atomic force microscopy (AFM), elemental analysis, dynamic light scattering, infrared (IR), X-ray powder analysis, and ultrasonic spectrometry. While the first preparation method produced very fine nanoparticles ca. 2 nm in diameter, the second one yielded ca. 6 nm particles. Addition of D-mannose after synthesis did not affect the iron oxide particle size. UV-vis spectroscopy suggested that D-mannose suppresses the nonspecific sorption of serum proteins from DMEM culture medium on magnetic nanoparticles. Rat bone marrow stromal cells (rMSCs) were labeled with uncoated and d-mannose-modified iron oxide nanoparticles and with Endorem (Guerbet, France; control). Optical and transmission electron microscopy confirmed the presence of D-mannose-modified iron oxide nanoparticles inside the cells. D-mannose-modified nanoparticles crossed the cell membranes and were internalized well by the cells. Relaxivity measurements of labeled cells in gelatin revealed very high relaxivities only for postsynthesis D-mannose-coated iron oxide nanoparticles.     

In vitro biocompatibility of chitosan/hyaluronic acid-containing calcium phosphate bone cements

The need for bone repair has increased as the population ages. In this research, calcium phosphate cements, with and without chitosan (CS) and hyaluronic acid (HA), were synthesized. The composition and morphological properties of cements were evaluated by X-ray diffraction and scanning electron microscopy. The acellular in vitro bioactivity revealed that different apatite morphologies were formed on the surfaces of cements after soaking in simulated body fluid. The in vitro osteoblastic cell biocompatibility of in situ forming cements was evaluated and compared with those of conventional calcium phosphate cements (CPCs). The viability and growth rate of the cells were similar for all CPCs, but better alkaline phosphatase activity was observed for CPC with CS and HA. Calcium phosphate cements supported attachment of osteoblastic cells on their surfaces. Spindle-shaped osteoblasts with developed cytoplasmic membrane were found on the surfaces of cement samples after 7 days of culture. These results reveal the potential of the CPC–CS/HA composites to be used in bone tissue engineering.     

Mineralization of pristine chitosan film through biomimetic process

The biomineralization of pristine chitosan film without any prior surface treatment was evaluated by immersing the film in simulated body fluid (SBF) at 37 °C for 3 weeks. The film was prepared by solvent casting method using chitosan of known degree of deacetylation (DD). The formation of the hydroxyapatite (HA) phase on the film surface after immersion was studied periodically by X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), energy dispersive X-ray analysis (EDX) and scanning electron microscopy (SEM) methods. The electron micrographs showed the morphology of the deposited apatite as small globules appearing uniformly throughout the films surfaces. The Ca/P ratio of the apatite was found to increase with increase in immersion time and approaching towards the stoichiometric value of the HA phase. The mineralized chitosan film could be of promising support to hard tissue regeneration.     

Microscale Characterization and Trace Element Distribution in Bacteriogenic Ferromanganese Coatings on Sand Grains from an Intertidal Zone of the East China Sea

An ancient wood layer dated at about 5600 yr BP by accelerator mass spectrometry (AMS) ¹⁴C was discovered in an intertidal zone of the East China Sea. Extensive and horizontally stratified sediments with black color on the top and yellowish-red at the bottom, and some nodule-cemented concretions with brown surface and black inclusions occurred in this intertidal zone. Microscale analysis methods were employed to study the microscale characterization and trace element distribution in the stratified sediments and concretions. Light microscopy, scanning electron microscopy (SEM) and backscattered electron imaging (BSE) revealed the presence of different coatings on the sand grains. The main mineral compositions of the coatings were ferrihydrite and goethite in the yellowish-red parts, and birnessite in the black parts using X-ray powder diffraction (XRD). SEM observations showed that bacteriogenic products and bacterial remnants extensively occurred in the coatings, indicating that bacteria likely played an important role in the formation of ferromanganese coatings. Post-Archean Australian Shale (PAAS)-normalized middle rare earth element (MREE) enrichment patterns of the coatings indicated that they were caused by two sub-sequential processes: (1) preferentially release of Fe-Mn from the beach rocks by fermentation of ancient woods and colloidal flocculation in the mixing water zone and (2) preferential adsorption of MREE by Fe-Mn oxyhydroxides from the seawater. The chemical results indicated that the coatings were enriched with Sc, V, Cr, Co, Ni, Cu, Zn, Ba, especially with respect to Co, Ni. The findings of the present study provide an insight in the microscale features of ferromanganese coatings and the Fe-Mn biogeochemical cycling during the degradation of buried organic matter in intertidal zones or shallow coasts.     

Ability of various inserts to promote endothelium cell culture for the establishment of coculture models

To select an insert suitable for human umbilical vein endothelial cell (HUVEC) culture, we compared several available inserts of 0.2 to 0.45 m porosity: Cellagen (ICN), Transwell-COL (Costar), Millicell-HA and CM (Millipore), Anopore (Nunc), Cyclopore (Falcon) in comparison with a control surface (Thermanox). The requirements were: (i) to promote attachment, adhesion and proliferation of HUVEC (judged by [³H]thymidine incorporation into DNA at days 1, 3, 7); (ii) to allow HUVEC visualization by inverted, fluorescence microscopy for uptake of DiI-Ac-LDL and scanning electron microscopy, performed at day 9 after seeding.Because Transwell and Cellagen are collagen precoated and CM has to be coated for cell culture, we performed collagen coating (types I + III or IV) for non-pretreated inserts for the purpose of comparison. Our preferences comprise Transwell-COL, Cyclopore not coated or coated (whatever the collagen type), and Cellagen. However, on a quality/price ratio criterion, Cyclopore, even uncoated, is the insert of choice. The HA, CM and Anopore inserts, even coated, do not allow HUVEC growth but do not alter positive uptake of acetylated LDL.Abbreviations HUVEC human umbilical vein endothelial cells     

Extracellular matrix of plant callus tissue visualized by ESEM and SEM

Actinidia deliciosa endosperm-derived callus culture is stable over a long period of culture. This system was used to investigate the ultrastructure of extracellular matrix occurring in morphogenic tissue. Specimens were prepared by different biological techniques (chemical fixation, liquid nitrogen fixation, glycerol substitution, critical-point drying, lyophilization) and observed by scanning electron microscopy (SEM). Fresh and wet samples were analyzed with the use of environmental scanning electron microscopy (ESEM). Extracellular matrix was observed on the surface of cell clusters as a membranous layer or reticulated network, shrunken or wrinkled, depending on the procedure. Generally, shrunken membranous layers with a globular appearance and fibrils were noted after critical-point drying and liquid nitrogen fixation. Smoother surface layers without visible fibrils and showing porosity were typically seen by environmental scanning electron microscopy. Preservation with glycerol substitution caused wrinkled appearance of examined layer. Analysis of fresh samples yielded images closer to their natural state than did critical-point drying or fixation in liquid nitrogen, but it seems best to compare the results of different visualization methods. This is the first report of ESEM observations of plant extracellular matrix and comparison with SEM images from fixed material.