Spontaneously Self‐Assembly of a 2D/3D Heterostructure Enhances the Efficiency and Stability in Printed Perovskite Solar Cells

As perovskite solar cells (PSCs) are highly efficient, demonstration of high‐performance printed devices becomes important. 2D/3D heterostructures have recently emerged as an attractive way to relieving the film inhomogeneity and instability in perovskite devices. In this work, a 2D/3D ensemble with 2D perovskites self‐assembled atop 3D methylammonium lead triiodide (MAPbI₃) via a one‐step printing process is shown. A clean and flat interface is observed in the 2D/3D bilayer heterostructure for the first time. The 2D perovskite capping layer significantly suppresses nonradiative charge recombination, resulting in a marked increase in open‐circuit voltage (V_OC) of the devices by up to 100 mV. An ultrahigh V_OC of 1.20 V is achieved for MAPbI₃ PSCs, corresponding to 91% of the Shockley–Queisser limit. Moreover, notable enhancement in light, thermal, and moisture stability is obtained as a result of the protective barrier of the 2D perovskites. These results suggest a viable approach for scalable fabrication of highly efficient perovskite solar cells with enhanced environmental stability.     

Record Open‐Circuit Voltage Wide‐Bandgap Perovskite Solar Cells Utilizing 2D/3D Perovskite Heterostructure

In this work, the authors realize stable and highly efficient wide‐bandgap perovskite solar cells that promise high power conversion efficiencies (PCE) and are likely to play a key role in next generation multi‐junction photovoltaics (PV). This work reports on wide‐bandgap (≈1.72 eV) perovskite solar cells exhibiting stable PCEs of up to 19.4% and a remarkably high open‐circuit voltage (V_OC) of 1.31 V. The V_OC‐to‐bandgap ratio is the highest reported for wide‐bandgap organic?inorganic hybrid perovskite solar cells and the V_OC also exceeds 90% of the theoretical maximum, defined by the Shockley–Queisser limit. This advance is based on creating a hybrid 2D/3D perovskite heterostructure. By spin coating n‐butylammonium bromide on the double‐cation perovskite absorber layer, a thin 2D Ruddlesden–Popper perovskite layer of intermediate phases is formed, which mitigates nonradiative recombination in the perovskite absorber layer. As a result, V_OC is enhanced by 80 mV.     

Highly stable and Efficient Perovskite Solar Cells Based on FAMA‐Perovskite‐Cu:NiO Composites with 20.7% Efficiency and 80.5% Fill Factor

To solve critical issues related to device stability and performance of perovskite solar cells (PSCs), FA_0.026MA_0.974PbI_3?yCl_y‐Cu:NiO (formamidinium methylammonium (FAMA)‐perovskite‐Cu:NiO) and Al₂O₃/Cu:NiO composites are developed and utilized for fabrication of highly stable and efficient PSCs through fully‐ambient‐air processes. The FAMA‐perovskite‐Cu:NiO composite crystals prepared without using any antisolvents not only improve the perovskite film quality with large‐size crystals and less grain boundaries but also tailor optical and electronic properties and suppress charge recombination with reduction of trap density. A champion device based on the composites as light absorber and Al₂O₃/Cu:NiO interfacial layer between electron transport layer and active layer yields power conversion efficiency (PCE) of 20.67% with V_OC of 1.047 V, J_SC of 24.51 mA cm^?2, and fill factor of 80.54%. More importantly, such composite‐based PSCs without encapsulation show significant enhancement in long‐term air‐stability, thermal‐ and photostability with retaining 97% of PCE over 240 d under ambient conditions (25–30 °C, 45–55% humidity).     

High‐Efficiency Low‐Temperature ZnO Based Perovskite Solar Cells Based on Highly Polar,Nonwetting Self‐Assembled Molecular Layers

Herein, this study reports high‐efficiency, low‐temperature ZnO based planar perovskite solar cells (PSCs) with state‐of‐the‐art performance. They are achieved via a strategy that combines dual‐functional self‐assembled monolayer (SAM) modification of ZnO electron accepting layers (EALs) with sequential deposition of perovskite active layers. The SAMs, constructed from newly synthesized molecules with high dipole moments, act both as excellent surface wetting control layers and as electric dipole layers for ZnO‐EALs. The insertion of SAMs improves the quality of PbI₂ layers and final perovskite layers during sequential deposition, while charge extraction is enhanced via electric dipole effects. Leveraged by SAM modification, our low‐temperature ZnO based PSCs achieve an unprecedentedly high power conversion efficiency of 18.82% with a V_OC of 1.13 V, a J_SC of 21.72 mA cm^?2, and a FF of 0.76. The strategy used in this study can be further developed to produce additional performance enhancements or fabrication temperature reductions.     

SrTiO3/Al2O3‐Graphene Electron Transport Layer for Highly Stable and Efficient Composites‐Based Perovskite Solar Cells with 20.6% Efficiency

For practical use of perovskite solar cells (PSCs) the instability issues of devices, attributed to degradation of perovskite molecules by moisture, ions migration, and thermal‐ and light‐instability, have to be solved. Herein, highly efficient and stable PSCs based on perovskite/Ag‐reduced graphene oxide (Ag‐rGO) and mesoporous Al₂O₃/graphene (mp‐AG) composites are reported. The mp‐AG composite is conductive with one‐order of magnitude higher mobility than mp‐TiO₂ and used for electron transport layer (ETL). Compared to the mp‐TiO₂ ETL based cells, the champion device based on perovskite/Ag‐rGO and SrTiO₃/mp‐AG composites shows overall a best performance (i.e., V_OC = 1.057 V, J_SC = 25.75 mA cm^?2, fill factor (FF) = 75.63%, and power conversion efficiency (PCE) = 20.58%). More importantly, the champion device without encapsulation exhibits not only remarkable thermal‐ and photostability but also long‐term stability, retaining 97–99% of the initial values of photovoltaic parameters and sustaining ≈93% of initial PCE over 300 d under ambient conditions.     

Solution Processable Inorganic–Organic Double‐Layered Hole Transport Layer for Highly Stable Planar Perovskite Solar Cells

Perovskite solar cells (PSCs) have reached their highest efficiency with 2,2′,7,7′‐tetrakis(N,N′‐di‐p‐methoxyphenylamine)‐9,9′‐spirobifluorene (spiro‐OMeTAD). However, this material can cause problems with respect to reproducibility and stability. Herein, a solution‐processable inorganic–organic double layer based on tungsten oxide (WO₃) and spiro‐OMeTAD is reported as a hole transport layer in PSCs. The device equipped with a WO₃/spiro‐OMeTAD layer achieves the highest efficiency (21.44%) in the tin (IV) oxide planar structure. The electronic properties of the double layer are thoroughly analyzed using photoluminescence, space‐charge–limited current, and electrochemical impedance spectroscopy. The WO₃/spiro‐OMeTAD layer exhibits better hole extraction ability and faster hole mobility. The WO₃ layer particularly improves the open‐circuit voltage (V_OC) by lowering the quasi‐Fermi energy level for holes and reducing charge recombination, resulting in high V_OC (1.17 V in the champion cell). In addition, the WO₃ layer as a scaffold layer promotes the formation of a uniform and pinhole‐free spiro‐OMeTAD overlayer in the WO₃/spiro‐OMeTAD layer. High stability under thermal and humid conditions stems from this property. The study presents a facile approach for improving the efficiency and stability of PSCs by stacking an organic layer on an inorganic layer.     

Stability and Dark Hysteresis Correlate in NiO‐Based Perovskite Solar Cells

In perovskite solar cells (PSCs), the interfaces are a weak link with respect to degradation. Electrochemical reactivity of the perovskite's halides has been reported for both molecular and polymeric hole selective layers (HSLs), and here it is shown that also NiO brings about this decomposition mechanism. Employing NiO as an HSL in p–i–n PSCs with power conversion efficiency (PCE) of 16.8%, noncapacitive hysteresis is found in the dark, which is attributable to the bias‐induced degradation of perovskite/NiO interface. The possibility of electrochemically decoupling NiO from the perovskite via the introduction of a buffer layer is explored. Employing a hybrid magnesium‐organic interlayer, the noncapacitive hysteresis is entirely suppressed and the device's electrical stability is improved. At the same time, the PCE is improved up to 18% thanks to reduced interfacial charge recombination, which enables more efficient hole collection resulting in higher V_oc and FF.     

The Introduction of Fluorine and Sulfur Atoms into Benzotriazole‐Based p‐Type Polymers to Match with a Benzotriazole‐Containing n‐Type Small Molecule: “The Same‐Acceptor‐Strategy” to Realize High Open‐Circuit Voltage

“The Same‐Acceptor‐Strategy” (SAS) adopts benzotriazole (BTA)‐based p‐type polymers paired with a new BTA based non‐fullerene acceptor BTA13 to minimize the trade‐off between the open‐circuit voltage (V_OC) and short circuit current (J_SC). The fluorination and sulfuration are introduced to lower the highest occupied molecular orbitals (HOMO) of the polymers. The fluorinated polymer of J52‐F shows the higher power conversion efficiency (PCE) of 8.36% than the analog polymer of J52, benefited from a good balance between an improved V_OC of 1.18 V and a J_SC of 11.55 mA cm^?2. Further adding alkylthio groups on J52‐F, the resulted polymer, J52‐FS, exhibits the highest V_OC of 1.24 V with a decreased energy loss of 0.48 eV, compared with 0.67 eV for J52 and 0.54 eV for J52‐F. However, J52‐FS shows an inferior PCE (3.84%) with a lower J_SC of 6.74 mA cm^?2, because the small ΔE_HOMO between J52‐FS and BTA13 (0.02 eV) gives rise to the inefficient hole transfer and high charge recombination, as well as low carrier mobilities. The results of this study clearly demonstrate that the introduction of different atoms in p‐type polymers is effective to improve the SAS and realize the high (V_OC) and PCE.     

Contact‐Induced Mechanisms in Organic Photovoltaics: A Steady‐State and Transient Study

The role of the contacts in thin‐film, blended heterojunctions (<100 nm thick) organic photovoltaics is explored, specifically considering concepts of carrier selectivity, injection, and extraction efficiency, relative to recombination. Contact effects are investigated by comparing two hole‐collecting interlayers: a phosphonic acid monolayer on indium tin oxide (ITO) and a nickel oxide thin film. The interlayers have equivalent work functions (≈5.4 eV) but widely variant energy band offsets relative to the lowest unoccupied molecular orbital of the acceptor (electron blocking versus not), which are coupled to large differences in carrier density. Trends in open‐circuit voltages (V_OC) as a function of light intensity and temperature are compared and it is concluded that the dominant mechanism limiting V_OC for high density of states contacts is free carrier injection, not surface recombination or extraction barriers. Transient photocurrent decay measurements confirm excess reinjected carriers decrease the extraction efficiency via increased recombination and decrease free carrier lifetime, even at high internal electric fields, due to space charge accumulation. These results demonstrate that the energetics and injection dynamics of the interface between interlayers and high carrier density electrodes (typically ITO and metals) must be considered with fabrication and processing of interlayers, in addition to possible carrier selectivity and the interface with the active layer.     

Energetics and Energy Loss in 2D Ruddlesden–Popper Perovskite Solar Cells

2D Ruddlesden–Popper perovskites (RPPs) are emerging as potential challengers to their 3D counterpart due to superior stability and competitive efficiency. However, the fundamental questions on energetics of the 2D RPPs are not well understood. Here, the energetics at (PEA)₂(MA)_n?1Pb_nI_3n+1/[6,6]‐phenyl‐C61‐butyric acid methyl ester (PCBM) interfaces with varying n values of 1, 3, 5, 40, and ∞ are systematically investigated. It is found that n–n junctions form at the 2D RPP interfaces (n = 3, 5, and 40), instead of p–n junctions in the pure 2D and 3D scenarios (n = 1 and ∞). The potential gradient across phenethylammonium iodide ligands that significantly decreases surface work function, promotes separation of the photogenerated charge carriers with electron transferring from perovskite crystal to ligand at the interface, reducing charge recombination, which contributes to the smallest energy loss and the highest open‐circuit voltage (V_oc) in the perovskite solar cells (PSCs) based on the 2D RPP (n = 5)/PCBM. The mechanism is further verified by inserting a thin 2D RPP capping layer between pure 3D perovskite and PCBM in PSCs, causing the V_oc to evidently increase by 94 mV. Capacitance–voltage measurements with Mott–Schottky analysis demonstrate that such V_oc improvement is attributed to the enhanced potential at the interface.     

Hot‐Substrate Deposition of Hole‐ and Electron‐Transport Layers for Enhanced Performance in Perovskite Solar Cells

Charge transport layers play an important role in determining the power conversion efficiencies (PCEs) of perovskite solar cells (PSCs). However, it has proven challenging to produce thin and compact charge transport layers via solution processing techniques. Herein, a hot substrate deposition method capable of improving the morphology of high‐coverage hole‐transport layers (HTLs) and electron‐transport layers (ETLs) is reported. PSC devices using HTLs deposited on a hot substrate show improvement in the open‐circuit voltage (V_oc) from 1.041 to 1.070 V and the PCE from 17.00% to 18.01%. The overall device performance is then further enhanced with the hot substrate deposition of ETLs as the V_oc and PCE reach 1.105 V and 19.16%, respectively. The improved performance can be explained by the decreased current leakage and series resistance, which are present in PSCs with rough and discontinuous HTLs and ETLs.     

3D–2D–0D Interface Profiling for Record Efficiency All‐Inorganic CsPbBrI2 Perovskite Solar Cells with Superior Stability

All‐inorganic CsPbBrI₂ perovskite has great advantages in terms of ambient phase stability and suitable band gap (1.91 eV) for photovoltaic applications. However, the typically used structure causes reduced device performance, primarily due to the large recombination at the interface between the perovskite, and the hole‐extraction layer (HEL). In this paper, an efficient CsPbBrI₂ perovskite solar cell (PSC) with a dimensionally graded heterojunction is reported, in which the CsPbBrI₂ material is distributed within bulk–nanosheet–quantum dots or 3D–2D–0D dimension‐profiled interface structure so that the energy alignment is optimized in between the valence and conduction bands of both CsPbBrI₂ and the HEL layers. Specifically, the valence‐/conduction‐band edge is leveraged to bend with synergistic advantages: the graded combination enhances the hole extraction and conduction efficiency with effectively decreased recombination loss during the hole‐transfer process, leading to an enhanced built‐in electric field, hence a high V_OC of as much as 1.19 V. The profiled structure induces continuously upshifted energy levels, resulting in a higher J_SC of as much as 12.93 mA cm^?2 and fill factor as high as 80.5%, and therefore record power conversion efficiency (PCE) of 12.39%. As far as it is known, this is the highest PCE for CsPbBrI₂ perovskite‐based PSC.     

Open‐Circuit Voltage in Organic Solar Cells: The Impacts of Donor Semicrystallinity and Coexistence of Multiple Interfacial Charge‐Transfer Bands

In organic solar cells (OSCs), the energy of the charge‐transfer (CT) complexes at the donor–acceptor interface, E _CT, determines the maximum open‐circuit voltage (V _OC). The coexistence of phases with different degrees of order in the donor or the acceptor, as in blends of semi‐crystalline donors and fullerenes in bulk heterojunction layers, influences the distribution of CT states and the V _OC enormously. Yet, the question of how structural heterogeneities alter CT states and the V _OC is seldom addressed systematically. In this work, we combine experimental measurements of vacuum‐deposited rubrene/C₆₀ bilayer OSCs, with varying microstructure and texture, with density functional theory calculations to determine how relative molecular orientations and extents of structural order influence E _CT and V _OC. We find that varying the microstructure of rubrene gives rise to CT bands with varying energies. The CT band that originates from crystalline rubrene lies up to ≈0.4 eV lower in energy compared to the one that arises from amorphous rubrene. These low‐lying CT states contribute strongly to V _OC losses and result mainly from hole delocalization in aggregated rubrene. This work points to the importance of realizing interfacial structural control that prevents the formation of low E _CT configurations and maximizes V _OC.     

In Situ Polymerization of Cross-Linked Perovskite–Polymer Composites for Highly Stable and Efficient Perovskite Solar Cells

Mixed-halide perovskites have emerged as outstanding light absorbers that enable the fabrication of efficient solar cells; however, their instability hinders the commercialization of such systems. Grain-boundary (GB) defects and lattice tensile strain are critical intrinsic-instability factors in polycrystalline perovskite films. In this study, the light-induced cross-linking of acrylamide (Am) monomers with non-crystalline perovskite films is used to fabricate highly efficient and stable perovskite solar cells (PSCs). The Am monomers induce the preferred crystal orientation in the polycrystalline perovskite films, enlarge the perovskite grain size, and cross-link the perovskite grains. Additionally, the liquid properties of Am effectively releases lattice strain during perovskite-film crystallization. The cross-linked interfacial layer functions as an airtight wall that protects the perovskite film from water corrosion. Devices fabricated using the proposed strategy show an excellent power conversion efficiency (PCE) of 24.45% with an open-circuit voltage (V_OC) of 1.199 V, which, to date, is the highest V_OC reported for hybrid PSCs with electron transport layers (ETLs) comprised of TiO₂. Large-area PSC modules fabricated using the proposed strategy show a power conversion efficiency of 20.31% (with a high fill factor of 77.1%) over an active area of 33 cm², with excellent storage stability.     

Molecular Understanding of the Open‐Circuit Voltage of Polymer:Fullerene Solar Cells

The origin of open‐circuit voltage (V_OC) was studied for polymer solar cells based on a blend of poly(3‐hexylthiophene) (P3HT) and seven fullerene derivatives with different LUMO energy levels and side chains. The temperature dependence of J–V characteristics was analyzed by an equivalent circuit model. As a result, V_OC increased with the decrease in the saturation current density J₀ of the device. Furthermore, J₀ was dependent on the activation energy E_A for J₀, which is related to the HOMO–LUMO energy gap between P3HT and fullerene. Interestingly, the pre‐exponential term J₀₀ for J₀ was larger for pristine fullerenes than for substituted fullerene derivatives, suggesting that the electronic coupling between molecules also has substantial impact on V_OC. This is probably because the recombination is non‐diffusion‐lmilited reaction depending on electron transfer at the P3HT/fullerene interface. In summary, the origin of V_OC is ascribed not only to the relative HOMO–LUMO energy gap but also to the electronic couplings between fullerene/fullerene and polymer/fullerene.     

Quantifying and Understanding Voltage Losses Due to Nonradiative Recombination in Bulk Heterojunction Organic Solar Cells with Low Energetic Offsets

Open‐circuit voltage (V_OC) losses in organic photovoltaics (OPVs) inhibit devices from reaching V_OC values comparable to the bandgap of the donor–acceptor blend. Specifically, nonradiative recombination losses (?V_nr) are much greater in OPVs than in silicon or perovskite solar cells, yet the origins of this are not fully understood. To understand what makes a system have high or low loss, an investigation of the nonradiative recombination losses in a total of nine blend systems is carried out. An apparent relationship is observed between the relative domain purity of six blends and the degree of nonradiative recombination loss, where films exhibiting relatively less pure domains show lower ?V_nr than films with higher domain purity. Additionally, it is shown that when paired with a fullerene acceptor, polymer donors which have bulky backbone units to inhibit close π–π stacking exhibit lower nonradiative recombination losses than in blends where the polymer can pack more closely. This work reports a strategy that ensures ?V_nr can be measured accurately and reports key observations on the relationship between ?V_nr and properties of the donor/acceptor interface.     

Surface Engineering of TiO2 ETL for Highly Efficient and Hysteresis‐Less Planar Perovskite Solar Cell (21.4%) with Enhanced Open‐Circuit Voltage and Stability

Interfacial studies and band alignment engineering on the electron transport layer (ETL) play a key role for fabrication of high‐performance perovskite solar cells (PSCs). Here, an amorphous layer of SnO₂ (a‐SnO₂) between the TiO₂ ETL and the perovskite absorber is inserted and the charge transport properties of the device are studied. The double‐layer structure of TiO₂ compact layer (c‐TiO₂) and a‐SnO₂ ETL leads to modification of interface energetics, resulting in improved charge collection and decreased carrier recombination in PSCs. The optimized device based on a‐SnO₂/c‐TiO₂ ETL shows a maximum power conversion efficiency (PCE) of 21.4% as compared to 19.33% for c‐TiO₂ based device. Moreover, the modified device demonstrates a maximum open‐circuit voltage (V_oc) of 1.223 V with 387 mV loss in potential, which is among the highest reported value for PSCs with negligible hysteresis. The stability results show that the device on c‐TiO₂/a‐SnO₂ retains about 91% of its initial PCE value after 500 h light illumination, which is higher than pure c‐TiO₂ (67%) based devices. Interestingly, using a‐SnO₂/c‐TiO₂ ETL the PCE loss was only 10% of initial value under continuous UV light illumination after 30 h, which is higher than that of c‐TiO₂ based device (28% PCE loss).     

Interface‐Modification‐Induced Gradient Energy Band for Highly Efficient CsPbIBr2 Perovskite Solar Cells

Inorganic cesium lead halide perovskite solar cells (PSCs) have received enormous attention due to their excellent stability compared with that of their organic–inorganic counterparts. However, the lack of optimization strategies leads the inorganic PSCs to suffer from low efficiency arising from significant recombination. To overcome this dilemma, a surface modification of the electron transport layer (ETL)/perovskite interface is undertaken by using SmBr₃ to improve the crystallization and morphology of the perovskite layer for enhanced ETL/perovskite interface interaction. Encouragingly, a gradient energy band is created at the interface with an outstanding hole blocking effect. As a result, both the charge recombination occurring at the interface and the nonradiative recombination inside the perovskite are suppressed, and, simultaneously, the charge extraction is improved successfully. Therefore, the power conversion efficiency of the CsPbIBr₂ PSCs is increased to as high as 10.88% under one sun illumination, which is 30% higher than its counterparts without the modification. It is logically inferred that this valuable optimization strategy can be extended to other analogous structures and materials.     

Interfacing Pristine C60 onto TiO2 for Viable Flexibility in Perovskite Solar Cells by a Low‐Temperature All‐Solution Process

A low‐temperature solution‐processed strategy is critical for cost‐effective manufacture of flexible perovskite solar cells (PSCs). Based on an aqueous‐processed TiO₂ layer, and conventional fullerene derivatives replaced by a pristine fullerene interlayer of C₆₀, herein a facile interface engineering for making all‐solution‐processed TiO₂/C₆₀ layers in flexible n‐i‐p PSCs is reported. Due to the improvement of the perovskite grain quality, promotion of interfacial charge transfer and suppression of interfacial charge recombination, the stabilized power conversion efficiency for the flexible PSCs reaches as high as 16% with high bending resistance retention (≈80% after 1500 cycles) and high light‐soaking retention (≈100% after 100 min). In addition, the stabilized efficiency is over 19% for the rigid TiO₂/C₆₀‐based PSCs. The present work with the facile low‐temperature solution process renders the practicability for high‐performance flexible PSCs applied to wearable devices, portable equipment, and electric vehicles.     

Disorder‐Induced Open‐Circuit Voltage Losses in Organic Solar Cells During Photoinduced Burn‐In

The photoinduced open‐circuit voltage (V_oc) loss commonly observed in bulk heterojunction organic solar cells made from amorphous polymers is investigated. It is observed that the total charge carrier density and, importantly, the recombination dynamics are unchanged by photoinduced burn‐in. Charge extraction is used to monitor changes in the density of states (DOS) during degradation of the solar cells, and a broadening over time is observed. It is proposed that the V_oc losses observed during burn‐in are caused by a redistribution of charge carriers in a broader DOS. The temperature and light intensity dependence of the V_oc losses can be described with an analytical model that contains the amount of disorder broadening in a Gaussian DOS as the only fit parameter. Finally, the V_oc loss in solar cells made from amorphous and crystalline polymers is compared and an increased stability observed in crystalline polymer solar cells is investigated. It is found that solar cells made from crystalline materials have a considerably higher charge carrier density than those with amorphous materials. The effects of a DOS broadening upon aging are suppressed in solar cells with crystalline materials due to their higher carrier density, making crystalline materials more stable against V_oc losses during burn‐in.