A new method for preparation of undecalcified bone sections

A new method for preparation of sections of undecalcified bone is described. Samples of ovine bone were embedded in methylmethacrylate and thick-sectioned with a cutoff machine or commercial band saw. Composite slides were prepared by gluing white acrylic to glass using cyanoacrylate glue. Bone sections were glued to the composite slide and then surface polished by grinding or ultramilling. The polished surface of the section was then etched and stained. The techniques described in this paper reduce the time spent grinding or milling sections and improve resolution of surface-stained features of undecalcified bone sections.     

Automatic grinding of undecalcified bone sections with exact adjustment of thickness]

A new grinding machine for preparing thin undecalcified bone sections after methylmethacrylate embedding is described. About 20 rather small bone sections can be ground at the same time; bigger specimens, up to 8 cm of length, are allowed. Bone sections are mounted on a cylindrical specimen holder by an adhesive film. Then the final thickness of the sections is exactly adjusted by screwing three rubies out of the holder's bottom. Now the prepared holder is set in a guide ring on a turntable carrying a rough ended glass plate. The desired thickness of the sections is reached as soon as the three rubies touch the glass surface. The variation in the thickness of the sections is less than +/- 3 micron. The machine is simply constructed, easily to handle and rapidly to clean.     

A Method for Histological Preparation of Undecalcified Bone Sections Containing Acrylic Bone Cement

An improved and time reducing method is presented for the histological evaluation of bone containing polymethylmethacrylate (PMMA) bone cement. The undecalcified bone was embedded in epoxy resin and sections of 50-100 μm thickness were produced using a commercially available cutting grinding system. The sections were stained with Stevenel's blue and van Gieson picrofuchsin or a modified hematoxylin-eosin. PMMA bone cement was not dissolved and remained enabling examination in situ of an intact cement bone interface and tissue reaction without decalcification.     

Evaluation of LR white resin for histology of the undecalcified rat tibia

Histology of plastic embedded undecalcified bone represents a challenging problem to the histotechnologist. We outline here an exploration of LR White resin as a suitable medium for histologic study of undecalcified rat tibia. A procedure was developed for light microscopy of rat tibia embedded in LR White and sectioned by sawing-grinding technics. The specimens were fixed in 10% neutral buffered formalin or alcohol-acetic acid-formol, dehydrated in ethanol, defatted in chloroform followed by resin infiltration and heat-curing of embedded blocks. The procedure of dehydration, defatting, infiltration, and polymerization can be completed within 10 days. Cold curing with accelerator provided by the manufacturer did not yield superior results compared to blocks cured with heat. Thick sections were obtained using a diamond wire saw, attached to plexiform slides, then ground and polished. Surface staining with Von Kossa silver reagent or toluidine blue revealed satisfactory morphological preservation of the mineralized bone sections. Artifacts like small bubbles appeared occasionally and could not be avoided despite prolonged infiltration or cold curing of blocks. Our method is relatively simple for base-line histologic study of rat tibia. The method offers advantages such as easy adaptability, reliable stainability, contrast, and resolution of bone architecture and marrow cells. Two other embedding media, Micro-Bed resin and Unicryl, were also tested, but produced inferior results.     

A Method for Histological Examination of Undecalcified Teeth

A method is presented for histological examination of undecalcified ground sections of tooth roots affected with periodontal disease. The roots were placed in Karnovsky's fixative overnight, postfixed in 2% buffered osmic acid, and dehydrated in an ascending series of ethanol. The specimens were then infiltrated with propylene-oxide and Epon-Araldite resin, embedded in Epon-Araldite, and sections were prepared using a cutting and grinding system. The resulting ground sections were 8-12 μm thick. The sections were allowed to air dry at room temperature. When thoroughly dried, a coverglass was applied using resinous mounting medium DPX. The specimens were examined by phase-contrast microscopy. The method is useful for simultaneous examination of mineralized dental tissue and bacterial morphotypes covering the root surface of teeth involved with periodontal disease.     

A Method for Histological Examination of Undecalcified Teeth

A method is presented for histological examination of undecalcified ground sections of tooth roots affected with periodontal disease. The roots were placed in Karnovsky's fixative overnight, postfixed in 2% buffered osmic acid, and dehydrated in an ascending series of ethanol. The specimens were then infiltrated with propylene-oxide and Epon-Araldite resin, embedded in Epon-Araldite, and sections were prepared using a cutting and grinding system. The resulting ground sections were 8-12 μm thick. The sections were allowed to air dry at room temperature. When thoroughly dried, a coverglass was applied using resinous mounting medium DPX. The specimens were examined by phase-contrast microscopy. The method is useful for simultaneous examination of mineralized dental tissue and bacterial morphotypes covering the root surface of teeth involved with periodontal disease.     

Enzyme, Lectin and Immunohistochemistry of Plastic Embedded Undecalcified Bone and other Hard Tissues for Light Microscopic Investigations

Enzymes and tissue antigens were localized on plastic embedded undecalcified bones and teeth using Technovit 7200 VLC (Kulzer, Germany). This resin is hard enough for cutting and grinding procedures on rotating plates with diamond layers. The pores between the diamond grains are not obstructed with this resin. The procedure described here permits localization of antigens in the soft tissues adjacent to, or in the biological hard tissues themselves and in dental implants (ceramic or metallic) on the light microscopic level. The undecalcified bone is fixed and embedded in plastic and cut at 100-150 μm. The slices are ground automatically by a grinding machine to a thickness of 5-10 μm. After application of the substrates for alkaline and acid phosphatases and the required dyes, the distribution of these enzymes can be demonstrated. Tissue antigens also can be detected with slightly modified standard techniques of immunohistochemistry and lectin histochemistry using the peroxidase technique or fluorescence microscopy.     

Embedding and Sectioning Undecalcified Bone, and its Application to Radioautography

A method is described for embedding and sectioning hard, undecalcified bone, which is designed for use by technical personnel. Bone fixed in a variety of ways is progressed through alcohols to ether-alcohol and then infiltrated with ether-alcohol solvented plastic (plasticized nitrocellulose) by a combination of centrifugation and high pressure embedding technics. The ether-alcohol is evaporated in a partially closed container in a manner similar to that employed in celloidin embedding, but differs from the latter by the removal of all of the solvent. Celloidin is the source of nitrocellulose and Amoil-S, the added plasticizer. Undecalcified adult bone of all types is readily cut at a thickness of 5-8μ on a heavy duty sliding microtome. The sections are then mounted on gelatinized slides. The procedures for preparing strip film radio-autograms of bone sections and subsequent staining of the preparation are given. The results obtained are illustrated.     

A simplified procedure for preparation of undecalcified human bone sections

A new type of apparatus for sectioning samples of hard, undecalcified bone is described. Slices of fresh or archeological human bone 4-5 mm thick are dehydrated and then embedded in epoxy resin. The apparatus used to prepare sections from the resulting blocks consists of a low-speed rim-type diamond cut-off wheel and a slowly advancing table carrying the specimen held in a rotating mount. Sections may be cut at a thickness of 80 micron +/- 1%. After cleaning in an ultrasonic bath, these can be mounted on slides for quantitative microscopic examination with transmitted light. Grinding and polishing are not necessary. The results obtained are illustrated.     

A simple method for preparing thin (10 microM) histological sections of undecalcified plastic embedded bone with implants

A simple method for preparing undecalcified thin sections of bone with implants has been developed. After exposing a surface of bone and implant in a plastic block by sawing thick sections, the surface is stained prior to making a thin section. A glass coverslip is affixed with a thin layer of cement to the stained surface to stabilize the tissue and implant during sectioning. A mixture of glycerine and water is used as a coolant and lubricant. The orientation in situ is preserved allowing demonstration of bone architecture and cells, and the tissue-implant interface.     

Inhibition of Alveoloar Bone Loss During Maturation of the Rat

The effects of dichloromethylene diphosphonate (C1₂MDP) on previously described maturational bone loss were quantified in 24 Wistar rats. Four groups of six animals each were treated daily from 18 to 28 weeks of age with a subcutaneous injection of a 0.1, 1.0 or 10mg/kg dose of C1₂MDP or were sham treated with 0.9% NaC1. Prior to sacrifice, all animals were double-labeled with tetracycline. The interdental bone between first and second maxillary molars was evaluated on decalcified stained sections and on undecalcified ground sections by digitizing morphometry. No significant differences in periodontal ligament width, bone height, osteoclast numbers or tetracycline labeled surface were detected. Significantly greater bone area (p<0.01) and bone width (p<0.005), and significantly fewer osteoblasts/mm of bone surface (p<0.001) were measured in rats treated with 10 mg/kg doses of C1₂MDP; and a dose response was demonstrated. It was concluded that C1₂MDP prevented interdental bone loss by inhibiting bone resorption, and that bone formation may have been indirectly reduced through a coupling mechanism.     

A Simple Method for Preparing Thin (10 μm) Histological Sections of Undecalcified Plastic Embedded Bone with Implants

A simple method for preparing undecalcified thin sections of bone with implants has been developed. After exposing a surface of bone and implant in a plastic block by sawing thick sections, the surface is stained prior to making a thin section. A glass coverslip is affixed with a thin layer of cement to the stained surface to stabilize the tissue and implant during sectioning. A mixture of glycerine and water is used as a coolant and lubricant. The orientation in situ is preserved allowing demonstration of bone architecture and cells, and the tissue-implant interface.     

A Simplified Procedure for Preparation of Undecalcified Human Bone Sections

A new type of apparatus for sectioning samples of hard, undecalcified bone is described. Slices of fresh or archeological human bone 4-5 mm thick are dehydrated and then embedded in epoxy resin. The apparatus used to prepare sections from the resulting blocks consists of a low-speed rim-type diamond cut-off wheel and a slowly advancing table carrying the specimen held in a rotating mount. Sections may be cut at a thickness of 80 μm ± 1%. After cleaning in an ultrasonic bath, these can be mounted on slides for quantitative microscopic examination with transmitted light. Grinding and polishing are not necessary. The results obtained are illustrated.     

Enzyme histochemical reactions in unfixed and undecalcified cryostat sections of mouse knee joints with special reference to arthritic lesions

Summary The use of unfixed and undecalcified cryostat sections of mouse knee joints is described for the study of enzyme histochemical reactions. Non-inflamed knee joints and knee joints of mice with antigen induced arthritis have been used. Joints were embedded in gelatin and subsequently cut at low speed with a motor-driven cryostat fitted with a tungsten carbide knife at an obtuse angle (10°). The sections were attached to transparent tape to keep the integrity of the tissue intact. The following histochemical reactions were carried out succesfully: the tetrazolium salt reaction for dehydrogenase and reductase activity, the post-azocoupling method for acid phosphatase and cathepsin B activity and the simultaneous azo-coupling method for esterase activity. In all cases the morphology and integrity of the sections were well kept and serial sections were obtained without any difficulty. Nonspecific staining of the tape did not occur. The localization of the final reaction product was meeting criteria for specific and precise histochemical methods with the exception of the metal salt method because of nonspecific staining of undecalcified bone. Cytophotometry of the final reaction product appeared to be reproducible and valid as demonstrated by reaction for glucose-6-phosphate dehydrogenase activity in synoviocytes from knee joints with induced arthritis. End point measurements as well as kinetic measurements of the formazan production were performed and linear relationships were found between the specific formazan formation and section thickness or incubation time, respectively. It is concluded that cryostat sections attached to transparent tape are an excellent tool for the study of the metabolism in tissues adjacent to bone matrix. Changes of enzyme activities in synoviocytes, chondrocytes and osteoclasts during induced arthritis are discussed.     

A novel method for embedding neonatal murine calvaria in methyl methacrylate suitable for visualizing mineralization,cellular and structural detail

The study of undecalcified bone by histological methods is essential in the field of bone research. Culturing skeletal tissues such as neonatal murine calvaria provides a reliable bridge between assessment of bone formation in vitro and anabolic activity in vivo and contains most of the essential elements of bone for studying bone formation. Neonatal calvarial assay, supported by histological methods, is used to study the anabolic effects of a wide variety of factors and compounds on bone tissue. To optimize visualization and histomorphometric measurements using neonatal calvaria, we developed a method that provides high quality tissue sections suitable for routine and histochemical staining. Undecalcified neonatal mouse calvaria were processed and embedded using a low temperature methyl methacrylate procedure. Various staining methods were performed on deplastisized and floated sections to examine mineralization and to identify cells. The Von Kossa stain counterstained with a modified H & E yielded precise images of unmineralized bone including mineralization sites, and distinct osteoblasts and osteoclasts. Toluidine blue, Ladewig's trichrome, tartrate-resistant acid phosphatase, Goldner, H & E and Villanueva stains also were tested on the undecalcified neonatal calvaria sections.     

Enzyme histochemical reactions in unfixed and undecalcified cryostat sections of mouse knee joints with special reference to arthritic lesions

The use of unfixed and undecalcified cryostat sections of mouse knee joints is described for the study of enzyme histochemical reactions. Non-inflamed knee joints and knee joints of mice with antigen induced arthritis have been used. Joints were embedded in gelatin and subsequently cut at low speed with a motor-driven cryostat fitted with a tungsten carbide knife at an obtuse angle (10 degrees). The sections were attached to transparent tape to keep the integrity of the tissue intact. The following histochemical reactions were carried out successfully: the tetrazolium salt reaction for dehydrogenase and reductase activity, the post-azo-coupling method for acid phosphatase and cathepsin B activity and the simultaneous azo-coupling method for esterase activity. In all cases the morphology and integrity of the sections were well kept and serial sections were obtained without any difficulty. Nonspecific staining of the tape did not occur. The localization of the final reaction product was meeting criteria for specific and precise histochemical methods with the exception of the metal salt method because of nonspecific staining of undecalcified bone. Cytophotometry of the final reaction product appeared to be reproducible and valid as demonstrated by reaction for glucose-6-phosphate dehydrogenase activity in synoviocytes from knee joints with induced arthritis. End point measurements as well as kinetic measurements of the formazan production were performed and linear relationships were found between the specific formazan formation and section thickness or incubation time, respectively. It is concluded that cryostat sections attached to transparent tape are an excellent tool for the study of the metabolism in tissues adjacent to bone matrix.(ABSTRACT TRUNCATED AT 250 WORDS)     

A novel method for embedding neonatal murine calvaria in methyl methacrylate suitable for visualizing mineralization, cellular and structural detail.

The study of undecalcified bone by histological methods is essential in the field of bone research. Culturing skeletal tissues such as neonatal murine calvaria provides a reliable bridge between assessment of bone formation in vitro and anabolic activity in vivo and contains most of the essential elements of bone for studying bone formation. Neonatal calvarial assay, supported by histological methods, is used to study the anabolic effects of a wide variety of factors and compounds on bone tissue. To optimize visualization and histomorphometric measurements using neonatal calvaria, we developed a method that provides high quality tissue sections suitable for routine and histochemical staining. Undecalcified neonatal mouse calvaria were processed and embedded using a low temperature methyl methacrylate procedure. Various staining methods were performed on deplastisized and floated sections to examine mineralization and to identify cells. The Von Kossa stain counterstained with a modified H & E yielded precise images of unmineralized bone including mineralization sites, and distinct osteoblasts and osteoclasts. Toluidine blue, Ladewig's trichrome, tartrate-resistant acid phosphatase, Goldner, H & E and Villanueva stains also were tested on the undecalcified neonatal calvaria sections.     

A novel method for embedding neonatal murine calvaria in methyl methacrylate suitable for visualizing mineralization, cellular and structural detail

The study of undecalcified bone by histological methods is essential in the field of bone research. Culturing skeletal tissues such as neonatal murine calvaria provides a reliable bridge between assessment of bone formation in vitro and anabolic activity in vivo and contains most of the essential elements of bone for studying bone formation. Neonatal calvarial assay, supported by histological methods, is used to study the anabolic effects of a wide variety of factors and compounds on bone tissue. To optimize visualization and histomorphometric measurements using neonatal calvaria, we developed a method that provides high quality tissue sections suitable for routine and histochemical staining. Undecalcified neonatal mouse calvaria were processed and embedded using a low temperature methyl methacrylate procedure. Various staining methods were performed on deplastisized and floated sections to examine mineralization and to identify cells. The Von Kossa stain counterstained with a modified H & E yielded precise images of unmineralized bone including mineralization sites, and distinct osteoblasts and osteoclasts. Toluidine blue, Ladewig's trichrome, tartrate-resistant acid phosphatase, Goldner, H & E and Villanueva stains also were tested on the undecalcified neonatal calvaria sections.     

Cement Line Staining in Undecalcified Thin Sections of Cortical Bone

A technique for demonstrating cement lines in thin, undecalcified transverse sections of cortical bone has been developed. Cortical bone samples are processed and embedded undecalcified in methyl methacrylate plastic. After sectioning at 3-5 μm, cross-sections are transferred to a glass slide and flattened for 10 min. Sections of cortical bone are stained for 20 sec free-floating in a fresh solution of 1% toluidine blue dissolved in 0.1% formic acid. The section is dehydrated in t-butyl alcohol, cleared in xylene, and mounted with Eukitt's medium. Reversal lines appear as thin, scalloped, dark blue lines against a light blue matrix, whereas bone formation arrest lines are thicker with a smooth contour. With this technique cellular detail, osteoid differentiation, and fluorochrome labels are retained. Results demonstrate the applicability of a one-step staining method for cement lines which will facilitate the assessment of bone remodeling activity in thin sections of undecalcified cortical bone.     

Cement line staining in undecalcified thin sections of cortical bone.

A technique for demonstrating cement lines in thin, undecalcified transverse sections of cortical bone has been developed. Cortical bone samples are processed and embedded undecalcified in methyl methacrylate plastic. After sectioning at 3-5 microns, cross-sections are transferred to a glass slide and flattened for 10 min. Sections of cortical bone are stained for 20 sec free-floating in a fresh solution of 1% toluidine blue dissolved in 0.1% formic acid. The section is dehydrated in t-butyl alcohol, cleared in xylene, and mounted with Eukitt's medium. Reversal lines appear as thin, scalloped, dark blue lines against a light blue matrix, whereas bone formation arrest lines are thicker with a smooth contour. With this technique cellular detail, osteoid differentiation, and fluorochrome labels are retained. Results demonstrate the applicability of a one-step staining method for cement lines which will facilitate the assessment of bone remodeling activity in thin sections of undecalcified cortical bone.