Cellulose nanocrystals as a reinforcing material for electrospun poly(methyl methacrylate) fibers: Formation, properties and nanomechanical characterization

Uniform fibers composed of poly(methyl methacrylate) (PMMA) reinforced with progressively increasing contents of cellulose nanocrystals (CNCs), up to 41 wt% CNCs, have been successfully produced by electrospinning. The morphological, thermal and nanomechanical properties of the composite sub-micron fibers were investigated. The CNCs derived from wood pulp by sulfuric acid hydrolysis were well dispersed in solutions of PMMA and the processing solvent N,N-dimethylformamide prior to fiber formation. Well-formed fibers with controllable diameters were generated reproducibly at all CNC contents investigated including 41 wt%. The orientation of the CNCs along the fiber axis was facilitated by the electrospinning process and observed directly from microscopy examination. Shifts in thermal transitions of PMMA with increasing CNC content suggest hydrogen bonding interactions between CNC hydroxyl groups and carbonyl groups on the PMMA matrix. Nanoscale dynamic mechanical analysis (nano-DMA) was performed using nanoindentation on single fibers perpendicular to the fiber axis. Many of the current challenges associated with single fiber nanoindentation are addressed, such as fiber diameter range and minimum, depth to diameter ratio, and valid depth range under these experimental conditions. Fibers that contained 17 wt% CNCs showed a modest increase of 17% in the storage modulus of PMMA, a high modulus polymer of interest for transparent composite applications.     

Electrospun polyethylene oxide/cellulose nanocrystal composite nanofibrous mats with homogeneous and heterogeneous microstructures

An electrospinning process was successfully used to fabricate polyethylene oxide/cellulose nanocrystal (PEO/CNC) composite nanofibrous mats. Transition of homogeneous to heterogeneous microstructures was achieved by tailoring the concentration of PEO/CNC mixture in the solution from 5 to 7 wt %. Morphology investigation of the obtained nanofibers demonstrated that rod-shaped CNCs were well-dispersed in the as-spun nanofibers and highly aligned along the nanofiber long-axis. PEO/CNC nanofibers became more uniform and smaller in diameter with increased CNC-loading level. The heterogeneous composite mats were composed of rigid-flexible bimodal nanofibers. Results of structure characterization indicated that the incorporated CNCs interacted strongly with the PEO matrix through hydrogen bonding. Mechanical properties of both types of mats were effectively improved by using CNCs, with heterogeneous mats being stronger than their homogeneous counterparts for all compositions (0-20 wt % CNC contents). When a smaller diameter needle was used to form homogeneous mats, enhanced thermal and mechanical properties were obtained.     

Polyelectrolyte brushes grafted from cellulose nanocrystals using Cu-mediated surface-initiated controlled radical polymerization

Herein we report the synthesis of cellulose nanocrystals (CNCs) grafted with poly(acrylic acid) (PAA) chains of different lengths using Cu-mediated surface initiated-controlled radical polymerization (SI-CRP). First, poly(tert-butylacrylate) (PtBA) brushes were synthesized; then, subsequent acid hydrolysis was used to furnish PAA brushes tethered onto the CNC surfaces. The CNCs were chemically modified to create initiator moieties on the CNC surfaces using chemical vapor deposition (CVD) and continued in solvent phase in DMF. A density of initiator groups of 4.6 bromine ester groups/nm(2) on the CNC surface was reached, suggesting a dense functionalization and a promising starting point for the controlled/living radical polymerization. The SI-CRP of tert-butylacrylate proceeded in a well-controlled manner with the aid of added sacrificial initiator, yielding polymer brushes with polydispersity values typically well below 1.12. We calculated the polymer brush grafting density to almost 0.3 chains/nm(2), corresponding to high grafting densities and dense polymer brush formation on the nanocrystals. Successful rapid acid hydrolysis to remove the tert-butyl groups yielded pH-responsive PAA-polyelectrolyte brushes bound to the CNC surface. Individually dispersed rod-like nanoparticles with brushes of PtBA or PAA were clearly visualized by AFM and TEM imaging.     

Manufacture of cellulose nanocrystals by cation exchange resin-catalyzed hydrolysis of cellulose

Cellulose nanocrystals (CNC) were prepared from microcrystalline cellulose (MCC) by hydrolysis with cation exchange resin (NKC-9) or 64% sulfuric acid. The cation exchange resin hydrolysis parameters were optimized by using the Box–Behnken design and response surface methodology. An optimum yield (50.04%) was achieved at a ratio of resin to MCC (w/w) of 10, a temperature of 48 °C and a reaction time of 189 min. Electron microscopy (EM) showed that the diameter of CNCs was about 10–40 nm, and the length was 100–400 nm. Regular short rod-like CNCs were obtained by sulfuric acid hydrolysis, while long and thin crystals of cellulose were obtained with the cation exchange resin. X-ray diffraction (XRD) showed that, compared with MCC, the crystallinity of H₂SO₄-CNC and resin-CNC increased from 72.25% to 77.29% and 84.26%, respectively. The research shows that cation exchange resin-catalyzed hydrolysis of cellulose could be an excellent method for manufacturing of CNC in an environmental-friendly way.     

Chromosome conformation capture uncovers potential genome-wide interactions between human conserved non-coding sequences

Comparative analyses of various mammalian genomes have identified numerous conserved non-coding (CNC) DNA elements that display striking conservation among species, suggesting that they have maintained specific functions throughout evolution. CNC function remains poorly understood, although recent studies have identified a role in gene regulation. We hypothesized that the identification of genomic loci that interact physically with CNCs would provide information on their functions. We have used circular chromosome conformation capture (4C) to characterize interactions of 10 CNCs from human chromosome 21 in K562 cells. The data provide evidence that CNCs are capable of interacting with loci that are enriched for CNCs. The number of trans interactions varies among CNCs; some show interactions with many loci, while others interact with few. Some of the tested CNCs are capable of driving the expression of a reporter gene in the mouse embryo, and associate with the oligodendrocyte genes OLIG1 and OLIG2. Our results underscore the power of chromosome conformation capture for the identification of targets of functional DNA elements and raise the possibility that CNCs exert their functions by physical association with defined genomic regions enriched in CNCs. These CNC-CNC interactions may in part explain their stringent conservation as a group of regulatory sequences.     

Formation and properties of chitosan-cellulose nanocrystal polyelectrolyte-macroion complexes for drug delivery applications

This study examines a novel polyelectrolyte-macroion complex (PMC) between chitosan, a cationic polysaccharide, and cellulose nanocrystals (CNCs), anionic, cylindrical nanoparticles, for potential applications in drug delivery. CNCs were prepared by H(2)SO(4) hydrolysis of wood pulp. The formation of PMCs was monitored by turbidimetric titration. In titrations of a chitosan solution with a CNC suspension, the turbidity reached a plateau, but it had a maximum and then decreased when the direction of titration was reversed. PMC particles were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy, dynamic light scattering, and laser Doppler electrophoresis. The particles were composed primarily of CNCs and ranged in size from a few hundred nanometers to several micrometers, depending on the cellulose/chitosan ratio. Particles formed at amino/sulfate group molar ratios >1 were nearly spherical in shape and positively charged, whereas particles formed at ratios <1 had well-defined nonspherical shapes and were negatively charged.     

Adaptive evolution of conserved noncoding elements in mammals

Conserved noncoding elements (CNCs) are an abundant feature of vertebrate genomes. Some CNCs have been shown to act as cis-regulatory modules, but the function of most CNCs remains unclear. To study the evolution of CNCs, we have developed a statistical method called the “shared rates test” to identify CNCs that show significant variation in substitution rates across branches of a phylogenetic tree. We report an application of this method to alignments of 98,910 CNCs from the human, chimpanzee, dog, mouse, and rat genomes. We find that ~68% of CNCs evolve according to a null model where, for each CNC, a single parameter models the level of constraint acting throughout the phylogeny linking these five species. The remaining ~32% of CNCs show departures from the basic model including speed-ups and slow-downs on particular branches and occasionally multiple rate changes on different branches. We find that a subset of the significant CNCs have evolved significantly faster than the local neutral rate on a particular branch, providing strong evidence for adaptive evolution in these CNCs. The distribution of these signals on the phylogeny suggests that adaptive evolution of CNCs occurs in occasional short bursts of evolution. Our analyses suggest a large set of promising targets for future functional studies of adaptation.     

Cellulose nanocrystals from celery stalk as quercetin scaffolds: A novel perspective of human holo-transferrin adsorption and digestion behaviours

In this study, cellulose nanocrystals (CNCs) were synthesized from celery stalks to be used as the platform for quercetin delivery. Additionally, CNCs and CNCs–quercetin were characterized using the results of scanning electron microscope (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and zeta potential, while their interactions with human holo-transferrin (HTF) were also investigated. We examined their interaction under physiological conditions through the exertion of fluorescence, resonance light scattering, synchronized fluorescence spectroscopy, circular dichroism, three-dimensional fluorescence spectroscopy, and fluorescence resonance energy transfer techniques. The data from SEM and TEM exhibited the spherical shape of CNCs and CNCs–quercetin and also, a decrease was detected in the size of quercetin-loaded CNCs from 676 to 473 nm that indicated the intensified water solubility of quercetin. The success of cellulose acid hydrolysis was confirmed based on the XRD results. Apparently, the crystalline index of CNCs–quercetin was reduced by the interaction of CNCs with quercetin, which also resulted in the appearance of functional groups, as shown by FTIR. The interaction of CNCs–quercetin with HTF was also demonstrated by the induced quenching in the intensity of HTF fluorescence emission and Stern–Volmer data represent the occurrence of static quenching. Overall, the effectiveness of CNCs as quercetin vehicles suggests its potential suitability for dietary supplements and pharmaceutical products.     

Connexin 43-mediated modulation of polarized cell movement and the directional migration of cardiac neural crest cells

Connexin 43 knockout (Cx43alpha1KO) mice have conotruncal heart defects that are associated with a reduction in the abundance of cardiac neural crest cells (CNCs) targeted to the heart. In this study, we show CNCs can respond to changing fibronectin matrix density by adjusting their migratory behavior, with directionality increasing and speed decreasing with increasing fibronectin density. However, compared with wild-type CNCs, Cx43alpha1KO CNCs show reduced directionality and speed, while CNCs overexpressing Cx43alpha1 from the CMV43 transgenic mice show increased directionality and speed. Altered integrin signaling was indicated by changes in the distribution of vinculin containing focal contacts, and altered temporal response of Cx43alpha1KO and CMV43 CNCs to beta1 integrin function blocking antibody treatment. High resolution motion analysis showed Cx43alpha1KO CNCs have increased cell protrusive activity accompanied by the loss of polarized cell movement. They exhibited an unusual polygonal arrangement of actin stress fibers that indicated a profound change in cytoskeletal organization. Semaphorin 3A, a chemorepellent known to inhibit integrin activation, was found to inhibit CNC motility, but in the Cx43alpha1KO and CMV43 CNCs, cell processes failed to retract with semaphorin 3A treatment. Immunohistochemical and biochemical analyses suggested close interactions between Cx43alpha1, vinculin and other actin-binding proteins. However, dye coupling analysis showed no correlation between gap junction communication level and fibronectin plating density. Overall, these findings indicate Cx43alpha1 may have a novel function in mediating crosstalk with cell signaling pathways that regulate polarized cell movement essential for the directional migration of CNCs.     

Preparation and characterization of cellulose nanocrystals from rice straw

Pure cellulose have been isolated from rice straw at 36% yield and hydrolyzed (64% H₂SO₄, 8.75 mL/g, 45 °C) for 30 and 45 min to cellulose nanocrystals (CNCs), i.e., CNC30 and CNC45, respectively. CNC45 was smaller (11.2 nm wide, 5.06 nm thick and 117 nm long) than CNC30 (30.7 nm wide, 5.95 nm thick and 270 nm long). Freeze-drying of diluted CNC suspensions showed both assembled into long fibrous structures: ultra-fine fibers (∼400 nm wide) from CNC45 and 1-2 μm wide broad ribbons interspersed with CNC clusters from CNC30. The self-assembled fibers from CNC30 and CNC45 were more highly crystalline (86.0% and 91.2%, respectively) and contained larger crystallites (7.36 nm and 8.33 nm, respectively) than rice straw cellulose (61.8%, 4.42 nm). These self-assembled fibers had essentially nonporous or macroporous structures with the CNCs well aligned along the fiber axis. Furthermore, the self-assembled ultra-fine fibers showed extraordinary structural stability, withstanding vigorous shaking and prolong stirring in water.     

A new approach to microhomogenization

A versatile microhomogenizer is described which is capable of handling sample volumes ranging from 1 μl to several millititers. The sample and homogenization buffer are sealed within a segment of flexible plastic tubing. The sample is disrupted by rubbing or rolling a metal rod back and forth over the length of tubing. Centrifugation of the homogenate is performed in the same sealed tubing segment. This method can be used to homogenize single cells.     

An Atlas of the Speed of Copy Number Changes in Animal Gene Families and Its Implications

The notion that gene duplications generating new genes and functions is commonly accepted in evolutionary biology. However, this assumption is more speculative from theory rather than well proven in genome-wide studies. Here, we generated an atlas of the rate of copy number changes (CNCs) in all the gene families of ten animal genomes. We grouped the gene families with similar CNC dynamics into rate pattern groups (RPGs) and annotated their function using a novel bottom-up approach. By comparing CNC rate patterns, we showed that most of the species-specific CNC rates groups are formed by gene duplication rather than gene loss, and most of the changes in rates of CNCs may be the result of adaptive evolution. We also found that the functions of many RPGs match their biological significance well. Our work confirmed the role of gene duplication in generating novel phenotypes, and the results can serve as a guide for researchers to connect the phenotypic features to certain gene duplications.     

Protein alignment using cellulose nanocrystals: practical considerations and range of application

Cellulose nanocrystals (CNCs) form liquid crystals in aqueous solution that confer alignment to macromolecules and permit the measurement of residual dipolar couplings. CNCs possess many attractive features as an alignment medium. They are inexpensive, non-toxic, chemically inert, and robust to denaturants and temperature. Despite these advantages, CNCs are seldom employed as an alignment medium and the range of their applicability has not yet been explored. We have re-examined the use of CNCs in biomolecular NMR by analyzing the effects concentration, ionic strength, and temperature on molecular alignment. Stable alignment was obtained over wide ranges of temperature (10–70°C) and pH (2.5–8.0), which makes CNCs potentially very useful in studies of thermophilic proteins and acid-stabilized molecules. Notably, we find that CNC suspensions are very sensitive to the concentrations of biological buffers, which must be taken into account when they are used in NMR analyses. These results have led us to develop a general procedure for preparing aligned samples with CNCs. Using the SH3 domain from the Fyn tyrosine kinase as a model system, we find that CNCs produce an alignment frame collinear with that of the commonly used Pf1 bacteriophage alignment medium, but of opposite magnitude.     

Biosafety of non-surface modified carbon nanocapsules as a potential alternative to carbon nanotubes for drug delivery purposes

Background

Carbon nanotubes (CNTs) have found wide success in circuitry, photovoltaics, and other applications. In contrast, several hurdles exist in using CNTs towards applications in drug delivery. Raw, non-modified CNTs are widely known for their toxicity. As such, many have attempted to reduce CNT toxicity for intravenous drug delivery purposes by post-process surface modification. Alternatively, a novel sphere-like carbon nanocapsule (CNC) developed by the arc-discharge method holds similar electric and thermal conductivities, as well as high strength. This study investigated the systemic toxicity and biocompatibility of different non-surface modified carbon nanomaterials in mice, including multi-walled carbon nanotubes (MWCNTs), single-walled carbon nanotubes (SWCNTs), carbon nanocapsules (CNCs), and C₆₀ fullerene (C₆₀). The retention of the nanomaterials and systemic effects after intravenous injections were studied.

Methodology and Principal Findings

MWCNTs, SWCNTs, CNCs, and C₆₀ were injected intravenously into FVB mice and then sacrificed for tissue section examination. Inflammatory cytokine levels were evaluated with ELISA. Mice receiving injection of MWCNTs or SWCNTs at 50 µg/g b.w. died while C₆₀ injected group survived at a 50% rate. Surprisingly, mortality rate of mice injected with CNCs was only at 10%. Tissue sections revealed that most carbon nanomaterials retained in the lung. Furthermore, serum and lung-tissue cytokine levels did not reveal any inflammatory response compared to those in mice receiving normal saline injection.

Conclusion

Carbon nanocapsules are more biocompatible than other carbon nanomaterials and are more suitable for intravenous drug delivery. These results indicate potential biomedical use of non-surface modified carbon allotrope. Additionally, functionalization of the carbon nanocapsules could further enhance dispersion and biocompatibility for intravenous injection.     

Allocare, predation risk, social structure and natal coat colour in anthropoid primates

Many primate species have a natal coat coloured differently from the coat colour of adults and, in some cases, the natal coat is very different from that of older animals with the infant being conspicuous and/or brightly coloured. This study uses data from 82 anthropoid species to investigate possible correlates of conspicuous natal coat colour (CNC), using comparative, phylogenetically controlled analyses. Five hypotheses were tested using statistical tests on both species data and phylogenetically controlled data. The analyses show some support for the hypothesis that CNCs have evolved to promote allocare but the degree of CNC does not correlate with predation rates, arboreality, or relative testes size.     

Incorporation of measurement of DNA integrity into qPCR assays

Optimal accuracy of quantitative PCR (qPCR) requires correction for integrity of the target sequence. Here we combine the mathematics of the Poisson distribution and exponential amplification to show that the frequency of lesions per base (which prevent PCR amplification) can be derived from the slope of the regression line between cycle threshold (Ct) and amplicon length. We found that the amplifiable fraction (AF) of a target can be determined from this frequency and the target length. Experimental results from this method correlated with both the magnitude of a damaging agent and with other measures of DNA damage. Applying the method to a reference sequence, we determined the values for lesions/base in control samples, as well as in the AFs of the target sequence in qPCR samples collected from leukemic patients. The AFs used to calculate the final qPCR result were generally >0.5, but were <0.2 in a few samples, indicating significant degradation. We conclude that DNA damage is not always predictable; quantifying the DNA integrity of a sample and determining the AF of a specific qPCR target will improve the accuracy of qPCR and aid in the interpretation of negative results.     

Preparation by grafting onto, characterization, and properties of thermally responsive polymer-decorated cellulose nanocrystals

The grafting of thermosensitive amine-terminated statistical polymers onto the surface of cellulose nanocrystals (CNCs) was achieved by a peptidic coupling reaction, leading to unusual properties like colloidal stability at high ionic strength, surface activity, and thermoreversible aggregation. We have used a large variety of experimental techniques to investigate the properties of the polymer-decorated CNCs at different length-scales and as a function of the different reaction parameters. A high grafting density could be obtained when the reaction was performed in DMF rather than water. Infrared and solid-state NMR spectroscopy data unambiguously demonstrated the covalent character of the bonding between the CNCs and the macromolecules, whereas TEM images showed a preserved individualized character of the modified objects. Dynamic light scattering and zeta potential measurements were also consistent with individual nanocrystals decorated by a shell of polymer chains. Surface tension measurements revealed that CNCs became surface-active after the grafting of thermosensitive amines. Decorated CNCs were also stable against high electrolyte concentrations. A thermoreversible aggregation was also observed, which paves the way for the design of stimuli-responsive biobased nanocomposite materials.     

Isolation of a Factor from Apple that Agglutinates Erwinia amylovora

Extracts prepared from apple seeds contain a factor (AF) capable of agglutinating cells of Erwinia amylovora. In drop agglutination tests, AF is more active in agglutinating an avirulent, acapsular strain of E. amylovora than a virulent, capsular strain. AF precipitates in agar plates with a receptor derived from boiled cells of avirulent acapsular strain and, therefore, can be located during fractionation by rocket electrophoresis. AF was heat-stable and had a pH optimum for agglutination near congruent with3.6 pH. The agglutination activity was not affected by the presence of Mg(2+), Ca(2+), or EDTA. AF was separated into two fractions (AF I and AF II) by elution from a Bio-Gel P-100 column. The precipitin and agglutination activities associated with AF II were found to be present in a positively charged molecule which was sensitive to treatment with protease and trypsin and, hence, presumably resides in a protein. The approximate molecular weight of AF II was determined to be 12,600 daltons. Besides precipitating the receptor derived from cells of avirulent acapsular strain, AF II was capable of precipitating extracellular polysaccharide from cultures of virulent capsular strain, sodium polygalacturonate, and carboxymethylcellulose. These three polymers also inhibited the agglutination activity associated with AF II. AF II could be replaced by poly-l-lysines in both the precipitin and agglutination assays. In addition, in antigen absorption experiments, poly-l-lysines were found to remove the receptors for AF II from the boiled extracts of avirulent acapsular strain. Based on these observations, it is proposed that the activity of AF II resides in a highly positively charged protein which causes agglutination of bacterial cells by interacting on a charge-charge basis with negatively charged components on the surface of the bacterial cells.     

Determination of 1-β-d-arabinofuranosylcytosine and 1-β-d-arabinofuranosyluracil in human plasma by high-performance liquid chromatography

A method is described for the determination of 1-β-d-arabinofuranosylcytosine (Ara-C) and its metabolite 1-β-d-arabinofuranosyluracil (Ara-U) in human plasma. After deproteinization of the plasma sample, separation is performed by reversed-phase liquid chromatography. For Ara-C concentrations exceeding 0.05 mg/l and for Ara-U concentrations exceeding 1 mg/l, injection volumes of 100 μl are applied. For lower concentrations an injection volume of 500 μl is used. Ara-C is detected at 280 nm with a lowest detection limit of 0.002 mg/l in plasma. Ara-U is detected at 264 nm with a lowest detection limit varying from 0.01 to 0.1 mg/l in plasma. This variation is caused by an unknown substance with the same elution properties as Ara-U and which appears to be present in plasma in variable concentrations. The coefficient of variation of the whole procedure is about 6% for Ara-C concentrations above 0.005 mg/l and for Ara-U concentrations above 0.1 mg/l. For lower concentrations the coefficient of variation is about 14%.     

Alkaline elution of rat testicular DNA: detection of DNA cross-links after in vivo treatment with chemical mutagens

The alkaline elution technique was used to measure DNA damage in the rat testis after intraperitoneal injection of 3 chemicals known to cause heritable mutations in rodents. These 3 chemicals are triethylenemelamine (TEM), mitomycin C, and cyclophosphamide. All three of these chemicals produced DNA damage which was readily detectable by alkaline elution. Both TEM and mitomycin C produced DNA interstrand cross-links, although TEM was a more potent cross-linker on an equimolar basis than mitomycin C. Cyclophosphamide produced both DNA cross-links and DNA strand breaks. Alkaline elution in the absence of proteinase K indicated that some of the strand breaks appeared to be closely associated with protein. These studied indicate that the alkaline elution technique is capable of detecting DNA damage in mammalian germ cells produced by chemical mutagens. This technique may prove useful as a screening tool for identifying chemicals which cause heritable mutations in mammals.