Luminescence properties of green‐emitting Ca2MgSi2O7:Eu2+ phosphor by a solid‐state reaction method

A europium (Eu)‐doped di‐calcium magnesium di‐silicate phosphor, Ca₂MgSi₂O₇:Eu²⁺, was prepared using a solid‐state reaction method. The phase structure, particle size, surface morphology, elemental analysis, different stretching mode and luminescence properties were analyzed by X‐ray diffraction (XRD), transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM) with energy dispersive X‐ray spectroscopy (EDX), Fourier transform infrared (FTIR) spectroscopy, photoluminescence (PL) and mechanoluminescence (ML). The phase structure of Ca₂MgSi₂O₇:Eu²⁺ was an akermanite‐type structure, which belongs to the tetragonal crystallography with space group P4?2₁m; this structure is a member of the melilite group and forms a layered compound. The surface of the prepared phosphor was not found to be uniform and particle distribution was in the nanometer range. EDX and FTIR confirm the components of Eu²⁺‐doped Ca₂MgSi₂O₇ phosphor. Under UV excitation, the main emission peak appeared at 530 nm, belonging to the broad emission ascribed to the 4f⁶5d¹→4f⁷ transition of Eu²⁺. The ML intensity of the prepared phosphor increased linearly with increasing impact velocity. A CIE color chromaticity diagram and ML spectrum confirmed that the prepared Ca₂MgSi₂O₇:Eu²⁺ phosphor would emit green color and the ML spectrum was similar to that of PL, which indicated that ML is emitted from the same center of Eu²⁺ ions. Copyright © 2015 John Wiley & Sons, Ltd.     

Persistent luminescence of CaMgSi2O6:Eu2+,Dy3+ and CaMgSi2O6:Eu2+,Ce3+ phosphors prepared using the solid‐state reaction method

CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors were synthesized using the solid‐state reaction method. X‐Ray diffraction (XRD) and photoluminescence (PL) analyses were used to characterize the phosphors. The XRD results revealed that the synthesized CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors were crystalline and are assigned to the monoclinic structure with a space group C2/c. The calculated crystal sizes of CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors with a main (221) diffraction peak were 44.87 and 53.51 nm, respectively. Energy‐dispersive X‐ray spectroscopy (EDX) confirmed the proper preparation of the sample. The PL emission spectra of CaMgSi₂O₆:Eu²⁺,Dy³⁺ and CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphors have a broad band peak at 444.5 and 466 nm, respectively, which is due to electronic transition from 4f⁶5d¹ to 4f⁷. The afterglow results indicate that the CaMgSi₂O₆:Eu²⁺,Dy³⁺ phosphor has better persistence luminescence than the CaMgSi₂O₆:Eu²⁺,Ce³⁺ phosphor. Copyright © 2015 John Wiley & Sons, Ltd.     

Strong green fluorescent hydrogels with Ba2MgSi2O7:Eu2+ phosphor embedded in cellulose

Non‐cytotoxic and green‐emitting fluorescent hydrogels were constructed from a cellulose solution containing Ba₂MgSi₂O₇:Eu²⁺ green phosphor in a NaOH/urea aqueous system. The structure, optical properties and cytotoxicity of these hydrogels were studied. The Ba₂MgSi₂O₇:Eu²⁺ phosphor particles were dispersed evenly in the cellulose hydrogel matrix. Good luminescent properties of Ba₂MgSi₂O₇:Eu²⁺ phosphor were maintained in the hydrogels, leading to strong green emission under ultraviolet excitation. Fluorescent hydrogels have no obvious cytotoxicity in a 3‐(4,5‐dimethylthiazol‐2‐yl)‐2,5‐diphenyltetrazolium bromide (MTT) proliferation test, and have potential use in in vivo applications like optical imaging and drug delivery.     

Photoluminescence and thermoluminescence properties of Eu2+ doped and Eu2+,Dy3+ co‐doped Ba2MgSi2O7 phosphors

In this work, we report the preparation, characterization, comparison and luminescence mechanisms of Eu²⁺‐doped and Eu²⁺,Dy³⁺‐co‐doped Ba₂MgSi₂O₇ (BMSO) phosphors. Prepared phosphors were synthesized via a high temperature solid‐state reaction method. All prepared phosphors appeared white. The phase structure, particle size, and elemental analysis were analyzed using X‐ray diffraction (XRD), transmission electron microscopy (TEM) and energy‐dispersive X‐ray (EDX) analysis. The luminescence properties of the phosphors were investigated by thermoluminescence (TL) and photoluminescence (PL). The PL excitation and emission spectra of Ba₂MgSi₂O₇:Eu²⁺ showed the peak to be around 381 nm and 490 nm respectively. The PL excitation spectrum of Ba₂MgSi₂O₇:Eu²⁺Dy³⁺ showed the peak to be around 341 nm and 388 nm, and the emission spectrum had a broad band around 488 nm. These emissions originated from the 4f⁶ 5d¹ to 4f⁷ transition of Eu²⁺. TL analysis revealed that the maximum TL intensity was found at 5 mol% of Eu²⁺ doping in Ba₂MgSi₂O₇ phosphors after 15 min of ultraviolet (UV) light exposure. TL intensity was increased when Dy³⁺ ions were co‐doped in Ba₂MgSi₂O₇:Eu²⁺ and maximum TL intensity was observed for 2 mol% of Dy³⁺. TL emission spectra of Ba_1.95MgSi₂O₇:0.05Eu²⁺ and Ba_1.93MgSi₂O₇:0.05Eu²⁺,0.02Dy³⁺ phosphors were found at 500 nm. TL intensity increased with UV exposure time up to 15 min, then decreased for the higher UV radiation dose for both Eu doping and Eu,Dy co‐doping. The trap depths were calculated to be 0.54 eV for Ba_1.95MgSi₂O₇:0.05Eu²⁺ and 0.54 eV and 0.75 eV for Ba_1.93MgSi₂O₇:0.05Eu²⁺,0.02Dy³⁺ phosphors. It was observed that co‐doping with small amounts of Dy³⁺ enhanced the thermoluminescence properties of Ba₂MgSi₂O₇ phosphor. Copyright © 2016 John Wiley & Sons, Ltd. [Correction added on 5 April 2016, after first online publication: The following parts of the abstract have been edited for consistency. '4f65d1' has been corrected to '4f⁶ 5d¹', '4f7' has been corrected to '4f⁷', 'Ba1.95' has been corrected to 'Ba_1.95' and 'Ba1.93' has been corrected to 'Ba_1.93' respectively.]     

Studies on the luminescence properties of cerium co‐doping on Ca2MgSi2O7:Eu2+ phosphor by solid‐state reaction method

Ca₂MgSi₂O₇:Ce³⁺, Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺,Ce³⁺ phosphors were prepared using the solid‐state reaction method. The crystal structures of the sintered phosphors were of melilite type, which has a tetragonal crystallography. The chemical compositions of the sintered phosphors was confirmed by energy dispersive X‐ray spectroscopy. The different thermoluminescence kinetic parameters [activation energy (E), frequency factor (s) and order of the kinetics (b)] of these phosphors were evaluated and compared using the peak shape method. Under ultraviolet excitation, the emission spectra of both Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺,Ce³⁺ phosphors were composed of a broad emission band peaking at 530 nm. When the Ca₂MgSi₂O₇:Eu²⁺ phosphor is co‐doped with Ce³⁺ ions, photoluminescence, afterglow and mechanoluminescence intensity was strongly enhanced. Ca₂MgSi₂O₇:Eu²⁺ showed some afterglow with a short persist time. On incorporation of Ce³⁺, efficient energy transfer from Ce³⁺ to Eu²⁺ was found and the emission intensity of Eu²⁺ was enhanced. The mechanoluminescence intensities of Ca₂MgSi₂O₇:Ce³⁺, Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺,Ce³⁺ phosphors increased proportionally increased with the increase in impact velocity, which suggests that these phosphors can be used as sensors to detect stress in an object.     

Combustion synthesis and luminescence properties of SrAl2O4:Eu2+, Dy3+, Tb3+ phosphor.

Eu(2+), Dy(3+) and Tb(3+) co-doped strontium aluminate phosphor with high brightness and long afterglow was synthesized by a combustion method, using urea as a reducer. The properties of SrAl(2)O(4):Eu(2+),Dy(3+),Tb(3+) phosphor with a series of initiating combustion temperatures, urea concentrations and boric acid molar fractions were investigated. The sample at initiating combustion temperature of 600 degrees C exhibited an intense emission peak at 513 nm, in which the phosphor existed as a single-phase monoclinic structure. The experimental results showed that the optimum ratio of urea is 2.0 times higher than theoretical quantities and that the suitable molar fraction of H(3)BO(3) is 0.08. The average particle size of the phosphor was 50-80 nm and its luminescence properties were studied systematically. Compared with SrAl(2)O(4):Eu(2+),Dy(3+) phosphor, the initial luminescence brightness improved from 2.50 candela (cd)/m(2) to 3.55 cd/m(2) and the long afterglow time was prolonged from 1290 s to 2743 s.     

Insights into the discrepant luminescence for BaSiO3:Eu2+ phosphors prepared by solid‐state reaction and precipitation reaction methods

Two synthesis routes, solid‐state reaction and precipitation reaction, were employed to prepare BaSiO₃:Eu²⁺ phosphors in this study. Discrepancies in the luminescence green emission at 505 nm for the solid‐state reaction method sample and in the yellow emission at 570 nm for the sample prepared by the precipitation reaction method, were observed respectively. A detail investigation about the discrepant luminescence of BaSiO₃:Eu²⁺ phosphors was performed by evaluation of X‐ray diffraction (XRD), photoluminescence (PL)/photoluminescence excitation (PLE), decay time and thermal quenching properties. The results showed that the yellow emission was generated from the BaSiO₃:Eu²⁺ phosphor, while the green emission was ascribed to a small amount of Ba₂SiO₄:Eu²⁺ compound that was present in the solid‐state reaction sample. This work clarifies the luminescence properties of Eu²⁺ ions in BaSiO₃ and Ba₂SiO₄ hosts.     

Photoluminescence properties and energy transfer in Ce3+/Dy3+ co‐doped Sr3MgSi2O8 phosphors for potential application in ultraviolet white light‐emitting diodes

Sr₃MgSi₂O₈:Ce³⁺, Dy³⁺ phosphors were prepared by a solid‐state reaction technique and the photoluminescence properties were investigated. The emission spectra show not only a band due to Ce³⁺ ions (403 nm) but also as a band due to Dy³⁺ ions (480, 575 nm) (UV light excitation). The photoluminescence properties reveal that effective energy transfer occurs in Ce³⁺/Dy³⁺ co‐doped Sr₃MgSi₂O₈ phosphors, and the co‐doping of Ce³⁺ could enhance the emission intensity of Dy³⁺ to a certain extent by transferring its energy to Dy³⁺. The Ce³⁺/Dy³⁺ energy transfer was investigated by emission/excitation spectra, and photoluminescence decay behaviors. In Sr_2.94MgSi₂O₈:0.01Ce³⁺, 0.05Dy³⁺ phosphors, the fluorescence lifetime of Dy³⁺ (from 3.35 to 27.59 ns) is increased whereas that of Ce³⁺ is greatly decreased (from 43.59 to 13.55 ns), and this provides indirect evidence of the Ce³⁺ to Dy³⁺ energy transfer. The varied emitted color of Sr₃MgSi₂O₈:Ce³⁺, Dy³⁺ phosphors from blue to white were achieved by altering the concentration ratio of Ce³⁺ and Dy³⁺. These results indicate Sr₃MgSi₂O₈:Ce³⁺, Dy³⁺ may be as a candidate phosphor for white light‐emitting diodes. Copyright © 2012 John Wiley & Sons, Ltd.     

Enhancement of the photoluminescence and long afterglow properties of Sr2MgSi2O7:Eu2+ phosphor by Dy3+ co‐doping

Sr₂MgSi₂O₇:Eu²⁺ and Sr₂MgSi₂O₇:Eu²⁺,Dy³⁺ long afterglow phosphors were synthesized under a weak reducing atmosphere by the traditional high temperature solid state reaction method. The synthesized phosphors were characterized by powder X‐ray diffraction (XRD), energy dispersive X‐ray spectroscopy (EDX), and photo‐, thermo‐ and mechanoluminescence spectroscopic techniques. The phase structure of the sintered phosphor was an akermanite type structure, which belongs to tetragonal crystallography. The thermoluminescence properties of these phosphors were investigated and compared. Under ultraviolet light excitation, the emission spectra of both prepared phosphors were composed of a broad emission band peaking at 470 nm. When the Sr₂MgSi₂O₇:Eu²⁺ phosphor was co‐doped with Dy³⁺, the photoluminescence (PL), afterglow and mechanoluminescence (ML) intensity were strongly enhanced. The decay graph indicated that both the sintered phosphors contained fast decay and slow decay processes. The ML intensities of Sr₂MgSi₂O₇:Eu²⁺ and Sr₂MgSi₂O₇:Eu²⁺,Dy³⁺ phosphors were increased proportionally with increasing impact velocity, a finding that suggests that these phosphors could be used as sensors to detect the stress of an object. Copyright © 2015 John Wiley & Sons, Ltd.     

Photoluminescence properties of a novel phosphor CaB2O4:Eu3+ under NUV excitation

The new borate phosphor CaB₂O₄:Eu³⁺ was synthesized by solid‐state method and their photoluminescence properties were investigated. The results show that the pure phase of CaB₂O₄ could be available at 900°C, CaB₂O₄:Eu³⁺ phosphor could be effectively excited by the near ultraviolet light (NUV) (392 nm), and the luminescent intensity of CaB₂O₄:Eu³⁺ phosphor reached to the highest when the doped‐Eu³⁺ content was 4 mol%. The emission spectra of CaB₂O₄:Eu³⁺ phosphor could exhibit red emission at 612 nm and orange emission at 588 nm, which are ascribed to the ⁵D₀–⁷F₂ and ⁵D₀–⁷F₁ transitions of Eu³⁺ ions. Copyright © 2009 John Wiley & Sons, Ltd.     

Structural,morphological and steady state photoluminescence spectroscopy studies of red Eu3+‐doped Y2O3 nanophosphors prepared by the sol‐gel method

Europium trivalent (Eu³⁺)‐doped Y₂O₃ nanopowders of different concentrations (0.5, 2.5, 5 or 7 at.%) were synthesized by the sol‐gel method, at different pH values (pH 2, 5 or 8) and annealing temperatures (600°C, 800°C or 1000°C). The nanopowders samples were characterized by X‐ray diffraction (XRD), field emission scanning electron microscopy (FE‐SEM), Fourier transform infrared spectroscopy (FT‐IR) and steady state photoluminescence spectroscopy. The effect of pH of solution and annealing temperatures on structural, morphological and photoluminescence properties of Eu³⁺‐doped Y₂O₃ were studied and are discussed. It was found that the average crystallite size of the nanopowders increased with increasing pH and annealing temperature values. The Y₂O₃:Eu³⁺ material presented different morphology and its evolution depended on the pH value and the annealing temperature. Activation energies at different pH values were determined and are discussed. Under ultraviolet (UV) light excitation, Y₂O₃:Eu³⁺ showed narrow emission peaks corresponding to the ⁵D_0–⁷F_J (J = 0, 1, 2 and 3) transitions of the Eu³⁺ ion, with the most intense red emission at 611 assigned to forced electric dipole ⁵D₀→⁷F₂. The emission intensity became more intense with increasing annealing temperature and pH values, related to the improvement of crystalline quality. For the 1000°C annealing temperature, the emission intensity presented a maximum at pH 5 related to the uniform cubic‐shaped particles. It was found that for lower annealing temperatures (small crystallite size) the CTB (charge transfer band) position presented a red shift. Copyright © 2015 John Wiley & Sons, Ltd.     

Structural characterization of Er3+,Yb3+‐doped Gd2O3 phosphor,synthesized using the solid‐state reaction method,and its luminescence behavior

We report the synthesis and structural characterization of Er³⁺,Yb³⁺‐doped Gd₂O₃ phosphor. The sample was prepared using the conventional solid‐state reaction method, which is the most suitable method for large‐scale production. The prepared phosphor sample was characterized using X‐ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), thermoluminescence (TL), photoluminescence (PL) and CIE techniques. For PL studies, the excitation and emission spectra of Gd₂O₃ phosphor doped with Er³⁺ and Yb³⁺ were recorded. The excitation spectrum was recorded at a wavelength of 551 nm and showed an intense peak at 276 nm. The emission spectrum was recorded at 276 nm excitation and showed peaks in all blue, green and red regions, which indicate that the prepared phosphor may act as a single host for white light‐emitting diode (WLED) applications, as verified by International de I'Eclairage (CIE) techniques. From the XRD data, the calculated average crystallite size of Er³⁺ and Yb³⁺‐doped Gd₂O₃ phosphor is ~ 38 nm. A TL study was carried out for the phosphor using UV irradiation. The TL glow curve was recorded for UV, beta and gamma irradiations, and the kinetic parameters were also calculated. In addition, the trap parameters of the prepared phosphor were also studied using computerized glow curve deconvolution (CGCD). Copyright © 2015 John Wiley & Sons, Ltd.     

Mechanoluminescence of SrAl2O4:Eu,Dy nanophosphors induced by low impact velocity

The present paper reports the impulsive excitation of mechanoluminescence (ML) in Sr_0.97Al₂O₄:Eu_0.01,Dy_0.02 nanophosphors prepared using a combustion technique. The phosphors are characterized using X‐ray powder diffraction (XRD), high‐resolution transmission electron microscopy (HRTEM) and photoluminescence (PL). The XRD results show that the samples exhibit a monoclinic α‐phase in the crystal structure. The space group of SrAl₂O₄:Eu,Dy nanophosphors is monoclinic P2₁. The PL and ML spectra of SrAl₂O₄:Eu,Dy nanophosphors are excited using light with a wavelength of 365 nm and emission is found at 516 nm. The prepared nanophosphors exhibits an intense ML that can be seen in daylight with the naked eye. When a sample powder is deformed impulsively by the impact of a moving piston, the ML intensity initially increases linearly with time, attains a peak value, I_m, at time t_m, and then decreases with time. The peak ML intensity, I_m, and total ML intensity, I_T, increase linearly with applied pressure and impact velocity. The ML intensity decreases with successive impacts of load onto the phosphors, and the diminished ML intensity can be approximately recovered by UV irradiation. The activation energy using thermoluminescence is found to be 0.57 eV for SrAl₂O₄:Eu,Dy nanophosphors. Copyright © 2016 John Wiley & Sons, Ltd.     

Photoluminescence and thermoluminescence studies of CaAl2O4:Dy3+ phosphor

Calcium aluminate phosphors activated by Dy³⁺ have been prepared by a combustion method at a temperature of 600°C. Photoluminescence (PL) and thermoluminescence (TL) properties of gamma‐irradiated Dy‐doped calcium aluminate were investigated. The PL spectrum shows a broad peak around 488 nm and 573 nm, under 347 nm excitation. Thermoluminescence studies were performed for different concentrations of Dy. Optimum intensity of photoluminescence was found for 0.02 mol% concentration of Dy. It was found that initially the peak TL intensity increases with increasing concentration of Dy in the CaAl₂O₄ host, attains a maximum value for 0.05 mol% concentration and decreases with further increase in the doping concentration due to concentration quenching. Copyright © 2015 John Wiley & Sons, Ltd.     

Characterization and luminescence properties of CaMgSi2O6:Eu2+ blue phosphor

A blue CaMgSi₂O₆:Eu²⁺ phosphor was prepared by the solid‐state reaction method and the phosphor characterized in terms of crystal structure, particle size, photoluminescence (PL), thermoluminescence (TL) and mechanoluminescence (ML) properties using X‐ray diffraction (XRD), transmission electron microscopy (TEM), PL spectroscopy, TLD reader and ML impact technique. The XRD result shows that phosphor is formed in a single phase and has a monoclinic structure with the space group C2/c. Furthermore, the PL excitation spectra of Eu²⁺‐doped CaMgSi₂O₆ phosphor showed a strong band peak at 356 nm and the PL emission spectrum has a peak at 450 nm. The depths and frequency factors of trap centers were calculated using the TL glow curve by deconvolution method in which the trap depths were found to be 0.48 and 0.61 eV. The formation of CaMgSi₂O₆:Eu²⁺ phosphor was confirmed by Fourier transform infrared spectroscopy. The ML intensity increased linearly with the impact velocity of the piston used to deform the phosphor. It was shown that the local piezoelectricity‐induced electron bombardment model is responsible for the ML emission. Finally, the optical properties of CaMgSi₂O₆:Eu²⁺ phosphors are discussed. Copyright © 2015 John Wiley & Sons, Ltd.     

Tunable white light emission from single‐phased Li2SrSiO4:Dy3+ phosphors by co‐doping with Eu3+

A series of single‐phase full‐color emitting Li₂Sr_1−x−ySiO₄:xDy³⁺,yEu³⁺ phosphors were synthesized by solid‐state reaction and characterized by X‐ray diffraction and photoluminescence analyses. The samples showed emission peaks at 488 nm (blue), 572 nm (yellow), 592 nm (orange) and 617 nm (red) under 393 nm excitation. The photoluminescence excitation spectra, comprising the Eu–O charge transfer band and 4f–4f transition bands of Dy³⁺ and Eu³⁺, range from 200 to 500 nm. The Commission Internationale de I'Eclairage chromaticity coordinates for Li₂Sr_0.98−xSiO₄:0.02Dy³⁺,xEu³⁺ phosphors were simulated. By manipulating Eu³⁺ and Dy³⁺ concentrations, the color points of Li₂Sr_1−x−ySiO₄:xDy³⁺,yEu³⁺ were tuned from the greenish‐white region to white light and eventually to reddish‐white region, demonstrating that a tunable white light can be obtained by Li₂Sr_1−x−ySiO₄:xDy³⁺,yEu³⁺ phosphors. Li₂Sr_0.98−xSiO₄:0.02Dy³⁺, xEu³⁺ can serve as a white‐light‐emitting phosphor for phosphor‐converted light‐emitting diode. Copyright © 2014 John Wiley & Sons, Ltd.     

Mechanoluminescence,thermoluminescence, photoluminescence studies on Ca3Y2Si3O12:RE3+ (RE3+ = Dy3+and Eu3+) phosphors

Dy³⁺ and Eu³⁺ activated Ca₃Y₂Si₃O₁₂ phosphors were synthesized by the solid‐state synthesis method. The phosphors were characterized by X‐ray diffraction (XRD), mechanoluminescence (ML), thermoluminescence (TL) and photoluminescence (PL) to determine structure and luminescence. For ML glow curves, only one peak was observed, as only one type of luminescence centre was formed during irradiation. The Ca₃Y₂Si₃O₁₂:Dy³⁺ TL glow curve showed a single peak at 151.55°C and the Ca₃Y₂Si₃O₁₂:Eu³⁺ TL glow curve peaked at 323°C with a small peak at 192°C, indicating that two types of traps were activated. The trapping parameters for both the samples were calculated using Chen's peak shape method. Dy³⁺‐activated Ca₃Y₂Si₃O₁₂ showed emission at 482 and 574 nm when excited by a 351 nm excitation wavelength, whereas the Eu³⁺‐activated Ca₃Y₂Si₃O₁₂ phosphor PL emission spectra showed emission peaks at 613 nm, 591 nm, 580 nm when excited at 395 nm wavelength. When excited at 466 nm, prominent emission peaks were observed at their respective positions with very slight shifts. Copyright © 2015 John Wiley & Sons, Ltd.     

Mechanoluminescence of Ba2MgSi2O7 doped with Eu2+ and Dy3+ phosphor by impulsive deformation

Di‐barium magnesium silicate phosphor doped with Eu²⁺ and Dy³⁺ was prepared using a solid‐state reaction technique under a reducing atmosphere. The sample underwent impulsive deformation by impact from a piston for mechanoluminescence (ML) investigations. The temporal ML characteristics of the phosphor were observed, which expressed a single sharp peak with a long decaying period. To investigate the luminescence centre responsible for the ML peak, the ML spectrum of the phosphor was also observed. The recorded ML spectrum was similar in shape and peak wavelength to the photoluminescence (PL) spectrum, which verifies the existence of a single emission centre due to the transition of Eu²⁺ ions, i.e. transitions from any of the sublevels of the 4f⁶5d¹ configuration to the ⁸S_7/2 level of the 4f⁷ configuration. Decay rates for different impact velocities were also calculated using curve‐fitting techniques. The time of the ML peak and the rate of decay did not change significantly with respect to increasing impact velocity of the load and peak ML intensity varied linearly. The mechanism of the ML emission was also discussed. Copyright © 2015 John Wiley & Sons, Ltd.     

A novel red phosphor Ca2YNbO6:Eu3+ for WLEDs

Due to the advantages of good physicochemical properties, thermal stability, and optical properties, double perovskite compounds have received extensive attention. On this basis, a new type of red phosphor, Ca₂YNbO₆:xEu³⁺, was synthesized using a high-temperature solid-phase method. Its phase purity, morphology, elemental composition, absorption spectrum, photoluminescence, thermal stability, and Commission Internationale de l'éclairage (CIE) chromaticity coordinates were thoroughly investigated. The results display that there is no impurity phase in the samples and the convergence factor R_wp = 14.2%; the microscopic particles are uniform and full, and the distribution of each element is uniform. The energy band gap ΔE is between 3.71 eV and 3.65 eV. The luminescence intensity is the best when the doped Eu³⁺ concentration x reaches 0.4, and emits 612 nm red light (⁵D₀→⁷F₂) under 465 nm excitation, and the concentration quenching is attributed to a d–d interaction. The luminescence intensity at 425 K was still 75% of the room temperature luminescence intensity, which indicates that the thermal stability is extremely superior. The CIE chromaticity coordinates (0.6534, 0.3455) of the Ca2YNbO6:0.4Eu³⁺ phosphors are very close to National Television Standards Committee (0.670, 0.330), and the samples have low correlated colour temperature (2656 K) and high colour purity (99.90%). All findings suggest that Ca₂YNbO₆:Eu³⁺ can serve as a substitute for red phosphor in WLEDs.     

Tunable luminescence properties and energy transfer in LaAl11O18:Eu,Tb phosphor

Eu²⁺ and Tb³⁺ singly doped and co‐doped LaAl₁₁O₁₈ phosphors were prepared by a combustion method using urea as a fuel. The phase structure and photoluminescence (PL) properties of the prepared phosphors were characterized by powder X‐ray diffraction (XRD), scanning electron microscopy (SEM), and photoluminescence excitation and emission spectra. When the content of Eu²⁺ was fixed at 0.01, the emission chromaticity coordinates could be adjusted from blue to green region by tuning the contents of Tb³⁺ ions from 0.01 to 0.03 through an energy transfer (ET) process. The fluorescence data collected from the samples with different contents of Tb³⁺ into LaAl₁₁O₁₈: Eu, show the enhanced green emission at 545 nm associated with ⁵D₄ –⁷F₅ transitions of Tb³⁺. The enhancement was attributed to ET from Eu²⁺ to Tb³⁺, and therefore Eu²⁺ ion acts as a sensitizer (an energy donor) while Tb³⁺ ion as an activator. The ET from Eu²⁺ to Tb³⁺ is performed through dipole–dipole interaction. The ET efficiency and critical distance were also calculated. The present Eu²⁺–Tb³⁺ co‐doped LaAl₁₁O₁₈ phosphor will have potential application for UV convertible white light‐emitting diodes. Copyright © 2015 John Wiley & Sons, Ltd.