Noncytotoxic Dy3+-activated glass emits cool white light for near ultraviolet-based white light-emitting diodes,visible lasers,and biomedical applications

Using the melt quenching technique, a lithium zinc borate glass (LZB) system with trivalent dysprosium ions (Dy³⁺) was synthesized, and the luminescence and lasing properties of these materials were examined for the generation of white light. Structural investigation through X-ray diffraction revealed that the prepared glass had an amorphous nature. The optimized glass containing 0.5 Dy³⁺ had a direct optical band gap of 2.782 eV and an indirect optical band gap of 3.110 eV. A strong excitation band at 386 nm (⁶H_15/2→⁴I_13/2) was recognized in the ultraviolet (UV) light region of its excitation spectrum. Emission bands could be seen in the photoluminescence spectrum at 659, 573, and 480 nm under the 386 nm excitation. These transitions of emission resembled electronic transitions such as (⁴F_9/2→⁶H_11/2), (⁴F_9/2→⁶H_13/2), and (⁴F_9/2→⁶H_15/2). In a pristine glass matrix, the higher intensity ratio of yellow to blue can result in the production of white light. The optimized Dy³⁺ ion concentration was observed to be 0.5 mol%. In addition, an analysis of lifetime decay was conducted for all synthesized glasses, and their decay trends were systematically investigated. Noticeably, we assessed the photometric parameters and found that they were close to the white light standard. Furthermore, a cytotoxicity study was carried out using lung fibroblast (WI-38) cell lines for the optimized 0.5Dy³⁺-doped LZB glass and it appeared to be noncytotoxic. It is clear from the results that the noncytotoxic LZB glass doped with 0.5 Dy³⁺ ions could be a suggestive choice for the manufacture of white light-emitting diodes and lasers using near-UVs.