Promotion of human mesenchymal stem cell differentiation on bioresorbable polycaprolactone/biphasic calcium phosphate composite scaffolds for bone tissue engineering

An artificial construct mimicking the intrinsic properties of the natural extracellular matrix in bones has been considered an ideal platform for bone tissue engineering, as it can present an appropriate microenvironment and regulate cell behaviours. In this report, we introduce biodegradable composite scaffolds consisting of polycaprolactone (PCL) and biphasic calcium phosphate (BCP). The scaffolds were fabricated by a salt-leaching process, and the ability of the scaffolds to facilitate osteogenic differentiation was investigated using human mesenchymal stem cells (hMSCs). The scaffolds had an inter-connected porous structure with quadrilateral pores of approximately 200 ～ 500 μm in width. The mechanical properties of the scaffolds changed as the BCP content was increased in the starting mixture. In the hMSC experiment, although we found that hMSCs adhered to the surface, as well as the inside, of the scaffolds, the incorporated BCP did not increase the proliferation of the hMSCs over 7 days in culture. Interestingly, the alkaline phosphatase (ALP) activity was 4 times higher on the PCL/BCP composite scaffold (0.12 ± 0.03 nmol/min/μg protein) thanon the PCL scaffold (0.03 ± 0.01 nmol/min/μg protein), suggesting that BCP can aid in generating a local environment that promotes bone regeneration. Therefore, a strategy combining polymers and ceramics can be considered a useful platform for bone tissue engineering.