Synthesis and luminescence properties of blue‐emitting phosphor Ca12Al14O32F2:Eu2+ for white light‐emitting diode

A blue‐emitting phosphor Ca₁₂Al₁₄O₃₂F₂:Eu²⁺ was synthesized using a high‐temperature solid‐state reaction under a reductive atmosphere. The X‐ray diffraction measurements indicate that a pure phase Ca₁₂Al₁₄O₃₂F₂:Eu²⁺ can be obtained for low doping concentration of Eu²⁺. The phosphor has a strong absorption in the range 270–420 nm with a maximum at ~340 nm and blue emission in the range 400–500 nm with chromatic coordination of (0.152, 0.045). The optimal doping concentration is ~0.24. In addition, the luminescence properties of the as‐synthesized phosphor were evaluated by comparison with those of Ca₁₂Al₁₄O₃₂Cl₂:Eu²⁺ and the commercially available phosphor BaMgAl₁₀O₁₇:Eu²⁺. The emission intensity of Ca₁₂Al₁₄O₃₂F₂:Eu²⁺ was ~72% that of BaMgAl₁₀O₁₇:Eu²⁺ under excitation at λ = 375 nm. The results indicate that Ca₁₂Al₁₄O₃₂F₂:Eu²⁺ has potential application as a near‐UV‐convertible blue phosphor for white light‐emitting diodes.