Insights into the discrepant luminescence for BaSiO3:Eu2+ phosphors prepared by solid‐state reaction and precipitation reaction methods

Two synthesis routes, solid‐state reaction and precipitation reaction, were employed to prepare BaSiO₃:Eu²⁺ phosphors in this study. Discrepancies in the luminescence green emission at 505 nm for the solid‐state reaction method sample and in the yellow emission at 570 nm for the sample prepared by the precipitation reaction method, were observed respectively. A detail investigation about the discrepant luminescence of BaSiO₃:Eu²⁺ phosphors was performed by evaluation of X‐ray diffraction (XRD), photoluminescence (PL)/photoluminescence excitation (PLE), decay time and thermal quenching properties. The results showed that the yellow emission was generated from the BaSiO₃:Eu²⁺ phosphor, while the green emission was ascribed to a small amount of Ba₂SiO₄:Eu²⁺ compound that was present in the solid‐state reaction sample. This work clarifies the luminescence properties of Eu²⁺ ions in BaSiO₃ and Ba₂SiO₄ hosts.