Thermoluminescence studies of zinc borate (ZnB2O4) phosphor doped with rare earths for dosimetric aspects

A series of ZnB₂O₄ phosphors doped with different concentrations of Eu and Dy (0.05 0.1, 0.2, 0.5, 1.0 mol%) and co-doped with Ce (1, 2, 5, 7, 10 mol%) respectively was prepared via the solid-state reaction technique and the thermoluminescence (TL) behaviour of gamma ray-irradiated samples was studied. The synthesized samples were irradiated with γ-rays for the dose range 0.03–1.20 kGy. The TL intensity variations with dose, dopant concentration, and the effect of co-doping were studied. The TL response curves for ZnB₂O₄:Eu³⁺ and ZnB₂O₄:Dy³⁺, ZnB₂O₄:Eu³,Ce³⁺ and ZnB₂O₄:Dy³⁺,Ce³⁺ phosphor were observed. It was revealed that ZnB₂O₄:Eu³⁺ showed a linear TL behaviour for the dose 0.03–1.20 kGy and ZnB₂O₄:Dy³⁺ showed linearity for the gamma dose range 0.03–0.10 kGy. Furthermore, fading for all the samples was observed to be less than 10% for a storage period of 30 days. In addition to this, the trapping parameters, especially activation energies were evaluated using the Ilich method and the initial rise method. The activation energy values obtained from both methods were in complete agreement with each other.