Prescribing Functional Additives for Treating the Poor Performances of High‐Voltage (5 V‐class) LiNi0.5Mn1.5O4/MCMB Li‐Ion Batteries

In this paper, tris(trimethylsilyl) phosphite (TMSP) and 1,3‐propanediolcyclic sulfate (PCS) are unprecedentedly prescribed as binary functional additives for treating the poor performances of high‐voltage (5 V‐class) LiNi_0.5Mn_1.5O₄/MCMB (graphitic mesocarbon microbeads) Li‐ion batteries at both room temperature and 50 °C. The high‐voltage LiNi_0.5Mn_1.5O₄/MCMB cell with binary functional additives shows a preponderant discharge capacity retention of 79.5% after 500 cycles at 0.5 C rate at room temperature. By increasing the current intensity from 0.2 to 5 C rate, the discharge capacity retention of the high‐voltage cell with binary functional additives is ≈90%, while the counterpart is only ≈55%. By characterizations, it is rationally demonstrated that the binary functional additives decompose and participate in the modification of solid–electrolyte interface layers (both electrodes), which are more conductive, protective, and resistant to electrolyte oxidative/reductive decompositions (accompanying active‐Li⁺ consuming parasitic reactions) due to synergistic effects. Specifically, the TMSP additive can stabilize LiPF₆ salt and scavenge erosive hydrofluoric acid. More encouragingly, at 50 °C, the high‐voltage cell with binary functional additives holds an ultrahigh discharge capacity retention of 79.5% after 200 cycles at 1 C rate. Moreover, a third designed self‐extinguishing flame‐retardant additive of (ethoxy)‐penta‐fluoro‐cyclo‐triphosphazene (PFPN) is introduced for reducing the flammability of the aforementioned binary functional additives containing electrolyte.