Production of poly(3-hydroxybutyrate-<Emphasis Type="Italic">co</Emphasis>-3-hydroxyhexanoate) with flexible 3-hydroxyhexanoate content in<Emphasis Type="Italic"> Aeromonas hydrophila</Emphasis> CGMCC 0911

Aeromonas hydrophila CGMCC 0911 isolated from lake water was found to be able to synthesize a polyhydroxyalkanoate (PHA) copolymer (PHBHHx) consisting of 3-hydroxybutyrate (HB) and 4–6 mol% 3-hydroxyhexanoate (HHx). The wild-type bacterium accumulated 49% PHBHHx containing 6 mol% HHx in terms of cell dry weight (CDW) when grown on lauric acid for 48 h. When A. hydrophila CGMCC 0911 expressed the Acyl-CoA dehydrogenase gene (yafH) of Escherichia coli, the recombinant strain could accumulate 47% PHBHHx, while the HHx content reached 17.4 mol%. The presence of changing glucose concentration in the culture changed the HHx content both in wild type and recombinant A. hydrophila CGMCC 0911. When 5 g l^–1 glucose was added to a culture containing 5 g l^–1 lauric acid as co-substrate, 45% PHBHHx/CDW consisting of 8.8 mol% HHx was produced by wild-type A. hydrophila CGMCC 0911 compared with only 5% in the absence of glucose. When the recombinant A. hydrophila CGMCC 0911 was grown on a mixed substrate containing lauric acid and 8–10 g l^–1 glucose, the HHx content could be further increased to 35.6 mol%. When the glucose concentration exceeded 10 g l^–1, cell growth, PHA content and mole percentages of HHx in PHBHHx were significantly reduced.