Photoluminescence and thermoluminescence studies of CaAl2O4:Dy3+ phosphor

Calcium aluminate phosphors activated by Dy³⁺ have been prepared by a combustion method at a temperature of 600°C. Photoluminescence (PL) and thermoluminescence (TL) properties of gamma‐irradiated Dy‐doped calcium aluminate were investigated. The PL spectrum shows a broad peak around 488 nm and 573 nm, under 347 nm excitation. Thermoluminescence studies were performed for different concentrations of Dy. Optimum intensity of photoluminescence was found for 0.02 mol% concentration of Dy. It was found that initially the peak TL intensity increases with increasing concentration of Dy in the CaAl₂O₄ host, attains a maximum value for 0.05 mol% concentration and decreases with further increase in the doping concentration due to concentration quenching. Copyright © 2015 John Wiley & Sons, Ltd.     

Luminescence characteristics of Na3Ca2(SO4)3F: Ce3+ fluoride material

A new Na₃Ca₂(SO₄)₃F: Ce³⁺ phosphor synthesized by a solid state diffusion method is reported. The photoluminescence study showed a single high intensity emission peak at 307 nm wavelength when excited by UV light of wavelength 278 nm. An unresolved peak of comparatively less intensity was also observed at 357 nm along with the main peak. The characteristic emission of dopant Ce in Na₃Ca₂(SO₄)₃F phosphor clearly indicated that it resides in the host lattice in trivalent form. The emission peak can be attributed to 5d → 4f transition of rare earth Ce³⁺. The prepared sample is also characterized for its thermoluminescence properties. The TL glow curve of prepared sample showed a single broad peak at 147°C. The trapping parameters are also evaluated by Chen's method. The values of trap depth (E) and frequency factor (s) were found to be 0.64 ± 0.002 eV and 1.43 × 10⁷ s^–1 respectively. The study of PL and TL along with evaluation of trapping parameters has been undertaken and discussed for the first time. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescence study of Dy or Ce activated LiCaBO3 phosphor for γ‐ray and C5+ ion beam irradiation

The photoluminescence and thermoluminescence characteristics of rare earths (Dy or Ce) activated LiCaBO₃ phosphors have been studied. Phosphors were synthesized by modified solid state synthesis. The phosphors were characterized by X‐ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) and thermoluminescence (TL) for structural, morphological and luminescence studies. Dy³⁺ activated LiCaBO₃ shows emission at 486 and 577 nm due to ⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2 transition, respectively, whereas the PL emission spectra of Ce³⁺ activated LiCaBO₃ phosphor shows a broad band peaking at 432 nm, which is due to the transition from 5d level to the ground state of the Ce³⁺ ion. The thermoluminescence study was also carried out for both these phosphors for γ‐ray irradiation and carbon beam irradiation. Linearity was studied for a 0.4–3.1 Rad dose γ‐rays. Linear behaviour over this dose range was observed. Gamma ray‐irradiated phosphors were shown to be negligible fading upon storage. All the samples were also studied for 75 MeV C⁵⁺ ion beam exposure in the range of 3.75 × 10¹² – 7.5 × 10¹³ ion cm^–2 fluence. In addition to this, trapping parameters of all the samples were also calculated using Chen's peak shape method. Copyright © 2015 John Wiley & Sons, Ltd.     

Luminescence in Sr4Al14O25:Ce3+ aluminate phosphor

Cerium‐doped Sr₄Al₁₄O₂₅ phosphor is prepared using a single‐step combustion synthesis and its X‐ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) and thermoluminescence (TL) properties are characterized. XRD reveals the formation of the desired phase in the prepared sample. SEM micrographs of the prepared Sr₄Al₁₄O₂₅ phosphor show that the particle size is 10 µm. The prepared Sr₄Al₁₄O₂₅, along with Sr₄Al₁₄O₂₅:Ce_x (x = 0.5–5 mol%) shows a PL emission peak at 314 nm under UV excitation of 262 nm wavelength due to 5d → 4f transition. The phosphor is suitable for higher concentrations of Ce ions. The TL glow peak reveals three clearly visible distinct peaks at temperatures around 130, 231 and 336ºC. The three peaks are separated by deconvolution and kinetic parameters calculated using Chen's peak shape method. The calculation shows that the reaction follows second‐order kinetics with activation energy (E) values of 0.52, 0.81 and 1.12 eV, and frequency factor (s) values of 5.58 × 10⁵, 4.53 × 10⁷ and 4.57 × 10⁸ s^‐1 for the three individual peaks. Copyright © 2014 John Wiley & Sons, Ltd.     

Study of luminescence and effect of Dy3+ on NaMgSO4Cl:Ce chlorosulphate phosphor

Chlorosulphate NaMgSO₄Cl phosphor doped with Ce³⁺ and co‐doped by Dy³⁺ prepared by the wet chemical method was studied for its photoluminescence and thermoluminescence (TL) characteristics. The emission spectrum of Ce³⁺ shows dominant peaks at 346 nm (excitation 270 nm) due to 5d → 4f transition. Efficient energy transfer occurs from Ce³⁺ → Dy³⁺ ions. Dy³⁺ emission at 485 nm and 576 nm is due to ⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2 transitions of Dy³⁺ ion respectively. The TL glow curves of NaMgSO₄Cl:Ce and Ce,Dy have been recorded for various concentrations at a heating rate of 2 °C/s irradiated by γ‐rays at a dose rate of 0.995 kGy/h for 1 Gy, which peaks at about 241 °C and 247‐312 °C respectively. Further, in changing the concentration level, the general structure of the intensity is found to increase. The main property of this phosphor is its sensitivity even for low concentrations of rare earth ions and low γ‐ray dose. There is still scope for higher doses of γ‐radiation. The phosphor presented may be used as a lamp phosphor as well as for TL studies. Copyright © 2014 John Wiley & Sons, Ltd.     

Synthesis and effect of Ce and Mn co‐doping on photoluminescence characteristics of Ca6AlP5O20:Eu novel phosphors

A series of Ca₆AlP₅O₂₀ doped with rare earths (Eu and Ce) and co‐doped (Eu, Ce and Eu,Mn) were prepared by combustion synthesis. Under Hg‐free excitation, Ca₆AlP₅O₂₀:Eu exhibited Eu²⁺ (486 nm) emission in the blue region of the spectrum and under near Hg excitation (245 nm), Ca₆AlP₅O₂₀:Ce phosphor exhibited Ce³⁺ emission (357 nm) in the UV range. Photoluminescence (PL) peak intensity increased in Ca₆AlP₅O₂₀:Eu,Ce and Ca₆AlP₅O₂₀:Eu, Mn phosphors due to co‐activators of Ce³⁺ and Mn²⁺ ions. As a result, these ions played an important role in PL emission in the present matrix. Ca₆AlP₅O₂₀:Eu, Ce and Ca₆AlP₅O₂₀:Eu, Mn phosphors provided energy transfer mechanisms via Ce³⁺ → Eu²⁺ and Eu²⁺ → Mn²⁺, respectively. Eu ions acted as activators and Ce ions acted as sensitizers. Ce emission energy was well matched with Eu excitation energy in the case of Ca₆AlP₅O₂₀:Eu, Ce and Eu ions acted as activators and Mn ions acted as sensitizers in Ca₆AlP₅O₂₀:Eu, Mn. This study included synthesis of new and efficient phosphate phosphors. The impact of doping and co‐doping on photoluminescence properties and energy transfer mechanisms were investigated and we propose a feasible interpretation. Copyright © 2012 John Wiley & Sons, Ltd.     

Photoluminescence and thermoluminescence properties of Eu2+ doped and Eu2+,Dy3+ co‐doped Ba2MgSi2O7 phosphors

In this work, we report the preparation, characterization, comparison and luminescence mechanisms of Eu²⁺‐doped and Eu²⁺,Dy³⁺‐co‐doped Ba₂MgSi₂O₇ (BMSO) phosphors. Prepared phosphors were synthesized via a high temperature solid‐state reaction method. All prepared phosphors appeared white. The phase structure, particle size, and elemental analysis were analyzed using X‐ray diffraction (XRD), transmission electron microscopy (TEM) and energy‐dispersive X‐ray (EDX) analysis. The luminescence properties of the phosphors were investigated by thermoluminescence (TL) and photoluminescence (PL). The PL excitation and emission spectra of Ba₂MgSi₂O₇:Eu²⁺ showed the peak to be around 381 nm and 490 nm respectively. The PL excitation spectrum of Ba₂MgSi₂O₇:Eu²⁺Dy³⁺ showed the peak to be around 341 nm and 388 nm, and the emission spectrum had a broad band around 488 nm. These emissions originated from the 4f⁶ 5d¹ to 4f⁷ transition of Eu²⁺. TL analysis revealed that the maximum TL intensity was found at 5 mol% of Eu²⁺ doping in Ba₂MgSi₂O₇ phosphors after 15 min of ultraviolet (UV) light exposure. TL intensity was increased when Dy³⁺ ions were co‐doped in Ba₂MgSi₂O₇:Eu²⁺ and maximum TL intensity was observed for 2 mol% of Dy³⁺. TL emission spectra of Ba_1.95MgSi₂O₇:0.05Eu²⁺ and Ba_1.93MgSi₂O₇:0.05Eu²⁺,0.02Dy³⁺ phosphors were found at 500 nm. TL intensity increased with UV exposure time up to 15 min, then decreased for the higher UV radiation dose for both Eu doping and Eu,Dy co‐doping. The trap depths were calculated to be 0.54 eV for Ba_1.95MgSi₂O₇:0.05Eu²⁺ and 0.54 eV and 0.75 eV for Ba_1.93MgSi₂O₇:0.05Eu²⁺,0.02Dy³⁺ phosphors. It was observed that co‐doping with small amounts of Dy³⁺ enhanced the thermoluminescence properties of Ba₂MgSi₂O₇ phosphor. Copyright © 2016 John Wiley & Sons, Ltd. [Correction added on 5 April 2016, after first online publication: The following parts of the abstract have been edited for consistency. '4f65d1' has been corrected to '4f⁶ 5d¹', '4f7' has been corrected to '4f⁷', 'Ba1.95' has been corrected to 'Ba_1.95' and 'Ba1.93' has been corrected to 'Ba_1.93' respectively.]     

Effect of Dy3+ or Eu2+ co‐activator on a BaCa(SO4)2:Ce3+ mixed alkaline earth sulfate phosphor

The individual emission and energy transfer between Ce³⁺ and Eu²⁺ or Dy³⁺ in BaCa(SO₄)₂ mixed alkaline earth sulfate phosphor prepared using a co‐precipitation method is described. The phosphor was characterized by X‐ray diffraction (XRD) and photoluminescence (PL) studies and doped by Ce;Eu and Dy rare earths. All phosphors showed excellent blue–orange emission on excitation with UV light. PL measurements reveal that the emission intensity of Eu²⁺ or Dy³⁺ dopants is greater than when they are co‐doped with Ce³⁺. An efficient Ce³⁺ → Eu²⁺ [²T_2g(4f⁶5d) → ⁸S_7/2(4f₇)] and Ce³⁺ → Dy³⁺ (⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2) energy transfer takes place in the BaCa(SO₄)₂ host. A strong blue emission peak was observed at 462 nm for Eu²⁺ ions and an orange emission peak at 574 nm for Dy³⁺ ions. Hence, this phosphor may be used as a lamp phosphor. Copyright © 2015 John Wiley & Sons, Ltd.     

Characterization and luminescence properties of CaMgSi2O6:Eu2+ blue phosphor

A blue CaMgSi₂O₆:Eu²⁺ phosphor was prepared by the solid‐state reaction method and the phosphor characterized in terms of crystal structure, particle size, photoluminescence (PL), thermoluminescence (TL) and mechanoluminescence (ML) properties using X‐ray diffraction (XRD), transmission electron microscopy (TEM), PL spectroscopy, TLD reader and ML impact technique. The XRD result shows that phosphor is formed in a single phase and has a monoclinic structure with the space group C2/c. Furthermore, the PL excitation spectra of Eu²⁺‐doped CaMgSi₂O₆ phosphor showed a strong band peak at 356 nm and the PL emission spectrum has a peak at 450 nm. The depths and frequency factors of trap centers were calculated using the TL glow curve by deconvolution method in which the trap depths were found to be 0.48 and 0.61 eV. The formation of CaMgSi₂O₆:Eu²⁺ phosphor was confirmed by Fourier transform infrared spectroscopy. The ML intensity increased linearly with the impact velocity of the piston used to deform the phosphor. It was shown that the local piezoelectricity‐induced electron bombardment model is responsible for the ML emission. Finally, the optical properties of CaMgSi₂O₆:Eu²⁺ phosphors are discussed. Copyright © 2015 John Wiley & Sons, Ltd.     

Luminescence and dosimetry approach in terbium(III)-activated tungstate double perovskite

A series of tungstate double perovskite Ca₃WO₆ doped with Tb³⁺ was prepared by a combustion process using urea as a flux. The crystal structure identification of Ca₃WO₆:Tb³⁺ phosphors was done using X-ray diffraction patterns, and a monoclinic structure was discovered. The Fourier transform infrared spectrum of Ca₃WO₆:Tb³⁺ displayed characteristic vibrations of tungstate bonds. Under 278 nm excitation, Ca₃WO₆:Tb³⁺ exhibited intense downconversion green emission, which corresponded to the ⁵D₄–⁷F_J (J = 4,5) transitions of Tb³⁺. The phosphor exhibited the highest photoluminescence (PL) intensity when it was doped with 1 mol% of Tb³⁺; later intensity quenching appeared to be due to the multipolar interaction at higher dopant concentrations. Moreover, high-quality thermoluminescence (TL) was detected when phosphors were irradiated using beta rays. The effects of Tb³⁺ concentration and beta dose on TL intensity were the two major aspects studied in detail. The TL intensity demonstrated excellent linear response to the applied range of beta dose. The trap parameters of the studied phosphors were computed by the peak shape approach and glow curve deconvolution. The fading effect on TL intensity was studied by recording the TL glow curves after 1 month of beta irradiation. Obtained results from the PL and TL characterizations showed that the phosphors under study have the potential to be used in lighting displays and in thermoluminescence dosimetry.     

Luminescence investigation of CaY2Al4SiO12:Dy3+ phosphor synthesized by sol–gel method

Dy³⁺-doped CaY₂Al₄SiO₁₂ phosphors were prepared using the sol–gel method. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and energy dispersive spectroscopy analyses (EDS) were used to analyse the crystal structure, morphology, and elemental composition of the prepared samples. The luminescence behaviour of the sample was investigated using photoluminescence (PL) and thermoluminescence (TL) techniques. The prepared CaY₂Al₄SiO₁₂:xDy³⁺ phosphor showed a characteristic blue and yellow emission at ~480 and 583 nm, respectively, with an excitation wavelength of 350 nm. The most intense PL emission was found for a 4 mol% doping concentration of Dy³⁺ ions. The CIE diagram of the phosphor showed bluish-white colour emission. For TL studies, the prepared phosphors were irradiated with a ⁶⁰Co γ (gamma) source and the TL glow curve of the CaY₂Al₄SiO₁₂:0.04Dy³⁺ phosphor showed three overlapped peaks. For the Gaussian peaks, Chen's peak shape method was applied to determine the kinetic parameters of the samples.     

New UVA‐emitting BaAlBO3F2:Eu2+ phosphor with PL and TL properties for phototherapy lamp

We present a new phosphor material, BaAlBO₃F₂ doped with Eu²⁺ ions, having emission in the UVA region. The phosphor material is prepared by a simple wet chemical method. Phase confirmation was carried out using the Rietveld refinement program which shows that BaAlBO₃F₂:Eu²⁺ has an hexagonal crystal system. Using a Fourier transform infrared spectroscopy graph, we studied the bond stretching present in the phosphor material. Photoluminescence (PL) characterization, carried out using a RF spectrofluorophotometer, shows two types of PL excitation and emission. Before reduction, emission is in the blue region at 431 nm; after reduction, excitation is at 258 nm and emission is at 361 nm, which is in the UVA region. Some thermoluminescence (TL) studies were carried out in this material for the first time, for example, determination of the trapping parameters, linearity, fading, glow curve convolution and deconvolution (GCCD) function for curve fitting and the T_m–T_stop method for confirmation of the trapped centers in the TL glow peak. Copyright © 2016 John Wiley & Sons, Ltd.     

Mechanoluminescence,thermoluminescence, photoluminescence studies on Ca3Y2Si3O12:RE3+ (RE3+ = Dy3+and Eu3+) phosphors

Dy³⁺ and Eu³⁺ activated Ca₃Y₂Si₃O₁₂ phosphors were synthesized by the solid‐state synthesis method. The phosphors were characterized by X‐ray diffraction (XRD), mechanoluminescence (ML), thermoluminescence (TL) and photoluminescence (PL) to determine structure and luminescence. For ML glow curves, only one peak was observed, as only one type of luminescence centre was formed during irradiation. The Ca₃Y₂Si₃O₁₂:Dy³⁺ TL glow curve showed a single peak at 151.55°C and the Ca₃Y₂Si₃O₁₂:Eu³⁺ TL glow curve peaked at 323°C with a small peak at 192°C, indicating that two types of traps were activated. The trapping parameters for both the samples were calculated using Chen's peak shape method. Dy³⁺‐activated Ca₃Y₂Si₃O₁₂ showed emission at 482 and 574 nm when excited by a 351 nm excitation wavelength, whereas the Eu³⁺‐activated Ca₃Y₂Si₃O₁₂ phosphor PL emission spectra showed emission peaks at 613 nm, 591 nm, 580 nm when excited at 395 nm wavelength. When excited at 466 nm, prominent emission peaks were observed at their respective positions with very slight shifts. Copyright © 2015 John Wiley & Sons, Ltd.     

Synthesis and luminescent properties of novel BaGd2O4:Eu3+ scintillating phosphor

BaGd_2‐xO₄:xEu³⁺ and Ba_1‐yGd_1.79‐2yEu_0.21Na_3yO₄ phosphors were synthesized at 1300°C in air by conventional solid‐state reaction method. Phosphors were characterized by X‐ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence excitation (PLE) spectra, photoluminescence (PL) spectra and thermoluminescence (TL) spectra. Optimal PL intensity for BaGd_2‐xO₄:xEu³⁺ and Ba_1‐yGd_1.79‐2yEu_0.21Na_3yO₄ phosphors at 276 nm excitation were found to be x = 0.24 and y = 0.125, respectively. The PL intensity of Eu³⁺ emission could only be enhanced by 1.3 times with incorporation of Na⁺ into the BaGd₂O₄ host. Enhanced luminescence was attributed to the flux effect of Na⁺ ions. However, when BaGd₂O₄:Eu³⁺ phosphors were codoped with Na⁺ ions, the induced defects confirmed by TL spectra impaired the emission intensity of Eu³⁺ ions. Copyright © 2012 John Wiley & Sons, Ltd.     

Europium doped Sr2YNbO6 double perovskite phosphor for photoluminescence and thermoluminescence properties

A luminescent double perovskite phosphor Sr₂YNbO₆ doped with Eu³⁺ crystallized to the monoclinic phase and was synthesized successfully via a conventional high-temperature combustion method. The formation of the crystal structure, phase purity, and surface morphology were studied using X-ray diffraction patterns and scanning electron microscopy. The characteristic vibrations between the atoms of the functional groups present in phosphor were studied using Fourier transform infrared spectra analysis. The luminescence properties of the prepared phosphors were investigated in terms of photoluminescence (PL) and thermoluminescence (TL). PL excitation spectra exhibited charge transfer bands and the characteristic 4f⁶ transitions of Eu³⁺. A prominent PL emission was obtained for the phosphor doped with 4 mol% Eu³⁺ under the 396 nm excitation wavelength. PL emission quenching was observed for the higher doping concentrations due to a multipole–multipole interaction. A highly intense PL emission arose due to the hypersensitive ⁵D₀–⁷F₂ electric dipole transition of Eu³⁺ that dominated the emission spectra. The thermal stability of the phosphor was examined through temperature-dependent PL. The TL properties of the Sr₂YNbO₆ double perovskites irradiated with a ⁹⁰Sr beta source at different doses were measured. The double perovskite phosphors under study showed a linear dose–response with increasing beta dose, ranging from 1 Gy to 10 Gy. Trapping parameters of the TL glow curves were determined using Chen's peak shape method and computerized glow curve deconvolution (CGCD). CGCD fitting of the TL glow curves revealed that it was consisted of three major peaks and followed second-order kinetics. The estimated activation energies were determined using different methods and were comparable and significant.     

Optically stimulated luminescence in LiCaAlF6:Eu2+ phosphor

Results on optically stimulated luminescence (OSL) in LiCaAlF₆:Eu²⁺ are reported. Continuous wave OSL signal as recorded using blue (470 nm) stimulation was found to be ~31% that of standard phosphor lithium magnesium phosphate. The rate of OSL depletion for standard phosphor lithium magnesium phosphate is only three times less as compared with that of LiCaAlF₆:Eu²⁺. Strong photoluminescence (PL) in the near ultraviolet region is observed for LiCaAlF₆:Eu²⁺ with the characteristic Eu²⁺ emission at 369 nm for 254 nm excitation. The thermoluminescence (TL) glow peak for LiCaAlF₆:Eu²⁺ was observed at around 180°C. The glow peak was about six times more intense compared with the dosimetric peak of the well known thermoluminescence dosimetric (TLD) phosphor LiF‐TLD 100. Thus this phosphor deserves much more attention than it has received until now and may be useful as a dosimetric material in radiation dosimetry. Copyright © 2015 John Wiley & Sons, Ltd.     

Luminescence and spectroscopic studies of halosulfate phosphors: a review

This review discusses the photoluminescence (PL) characteristics of halosulfate phosphors developed by us. Halosulfate phosphors KCaSO₄Cl:X,Y (X = Eu or Ce; Y = Dy or Mn) and Na₆(SO₄)₂FCl (doped with Dy, Ce or Eu) were prepared using a solid‐state diffusion method. The mechanism of energy transfer from Eu²⁺→Dy³⁺, Ce³⁺→Dy³⁺ and Ce³⁺→Mn²⁺ has also been studied. Dy³⁺ emission in the host at 475 and 570 nm is observed due to ⁴F_9/2→⁶H_15/2 and ⁴F_9/2→⁶H_13/2 transition, whereas the PL emission spectra of Na₆(SO₄)₂FCl:Ce phosphor shows Ce³⁺ emission at 322 nm due to 5d→4f transition of the Ce³⁺ ion. The main property of KCaSO₄Cl is its very high sensitivity, particularly when doped by Dy, Mn or Pb activators. This review also discusses the PL characteristics of some new phosphors such as LiMgSO₄F, Na₆Pb₄(SO₄)₆Cl₂, Na₂₁Mg(SO₄)₁₀Cl₃ and Na₁₅(SO₄)₅F₄Cl. Copyright © 2014 John Wiley & Sons, Ltd.     

Luminescence of Eu and Ce in K3Ca2(SO4)3F fluoride material

A new halophosphor K₃Ca₂(SO₄)₃ F activated by Eu or Ce and K₃Ca₂(SO₄)₃ F:Ce,Eu co‐doped halosulfate phosphor has been synthesized by the co‐precipitation method and characterized for its photoluminescence (PL). The PL emission spectra of the K₃Ca₂(SO₄)₃ F :Ce phosphor show emission at 334 nm when excited at 278 nm due to 5d → 4f transition of Ce³⁺ ions. In the K₃Ca₂(SO₄)₃ F:Eu lattice, Eu²⁺ (440 nm) as well as Eu³⁺ (596 nm and 615 nm) emissions have been observed showing ⁵D₀ → ⁷ F₁ and ⁵D₀ → ⁷ F₂ transition of the Eu³⁺ ion, which is in the blue and red region of the visible spectrum respectively. The trivalent europium ion is very useful for studying the nature of metal coordination in various systems owing to its non‐degenerate emitting ⁵D₀ state. K₃Ca₂(SO₄)₃ F:Ce,Eu is suitable for Ce³⁺ → Eu²⁺ → Eu³⁺ energy transfer in which Ce³⁺and Eu²⁺ play the role of sensitizers and Eu²⁺ and Eu³⁺ act as the activators. The observations presented in this paper are relevant for lamp phosphors. Copyright © 2015 John Wiley & Sons, Ltd.     

Optical properties of CaAl(SO4)2Br:RE (RE = Dy,Eu, Ce) novel phosphors

A new phosphor CaAl(SO₄)₂Br doped with Dy, Ce and Eu is reported. Rare earth (Dy, Eu and Ce)‐doped polycrystalline CaAl(SO₄)₂Br phosphors were prepared using a wet chemical reaction method and studied for X‐ray diffraction and photoluminescence (PL) characteristics. Dy³⁺ emission in the CaAl(SO₄)₂Br lattice was observed at 484 and 574 nm in the blue and yellow regions of the spectrum, which are assigned to ⁴ F_9/2 → ⁶H_15/2 and ⁴ F_9/2 → ⁶H_13/2 transitions of the Dy³⁺ ion, respectively. While the PL emission spectra of CaAl(SO₄)₂Br:Ce phosphor showed Ce³⁺ emission at 347 nm due to 5d → 4f transition of the Ce³⁺ ion. In a CaAl(SO₄)₂Br:Eu lattice, Eu³⁺ emissions were observed at 593 and 617 nm, coming from the ⁵D₀ → ⁷ F₁ and ⁵D₀ → ⁷ F₂ electron transitions, respectively. The PL study showed that the intensity of electric dipole transition at 617 nm dominates over that of magnetic dipole transition at 590 nm. The maximum PL intensity was obtained for a 1 mol% concentration of Eu³⁺ in CaAl(SO₄)₂Br host lattice. The results showed that the material may be a promising candidate as a blue‐, yellow‐ and red‐emitting phosphor. Copyright © 2013 John Wiley & Sons, Ltd.     

Ca2Al2SiO7:Ce3+ phosphors for mechanoluminescence dosimetry

A series of Ce³⁺ ion single‐doped Ca₂Al₂SiO₇ phosphors was synthesized by a combustion‐assisted method at an initiating temperature of 600 °C. The samples were annealed at 1100 °C for 3 h and their X‐ray diffraction patterns confirmed a tetragonal structure. The phase structure, particle size, surface morphology and elemental analysis were analyzed using X‐ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscopy (SEM) and energy dispersive X‐ray (EDX) spectroscopy techniques. Thermoluminescence (TL) intensity increased with increase in ultraviolet (UV) light exposure time up to 15 min. With further increase in the UV irradiation time the TL intensity decreases. The increase in TL intensity indicates that trap concentration increased with UV exposure time. A broad peak at 121 °C suggested the existence of a trapping level. The peak of mechanoluminescence (ML) intensity versus time curve increased linearly with increasing impact velocity of the moving piston. Mechanoluminescence intensity increased with increase in UV irradiation time up to 15 min. Under UV‐irradiation excitation, the TL and ML emission spectra of Ca₂Al₂SiO₇:Ce³⁺ phosphor showed the characteristic emission of Ce³⁺ peaking at 400 nm (UV–violet) and originating from the Ce³⁺ transitions of 5d‐4f (²F_5/2 and ²F_7/2). The photoluminescence (PL) emission spectra for Ca₂Al₂SiO₇:Ce³⁺ were similar to the ML/TL emission spectra. The mechanism of ML excitation and the suitability of the Ca₂Al₂SiO₇:Ce³⁺phosphor for radiation dosimetry are discussed. Copyright © 2016 John Wiley & Sons, Ltd.